• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.18-19
• /
• 2006

The bismuth zinc niobate(BZN) pyrochlore thin films were fabricated on Pt(111)/Ti/$SiO_2$/p-Si(100) substrates using a reactive rf magnetron sputtering method at the conditions of working gas ratio Ar:$O_2$=90:10, substrate temperate $R.T{\sim}600^{\circ}C$, rf power 50 W. The dielectric constant, tunability, leakage current density and crystallinity of thin films changed with a substrate temperate. The BZN pyrochlore thin films sputtered with a substrate temperature of $600^{\circ}C$ and RTA at $800^{\circ}C$ showed a leakage current density lower than $10^{-8}\;A/cm^2$ at the range of ${\pm}300\;kV/cm$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.92.2-92.2
• /
• 2007

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.96-96
• /
• 2007

Low voltage organic TFTs (OTFTs) and ZnO based TFTs (<5V), utilizing room temperature deposited $Bi_{1.5}Zn_{1.0}Nb_{1.5}O_7$ (BZN) thin films were recently reported, pointing to high-k gate insulators as a promising route for realizing low voltage operating flexible electronics. $Bi_{1.5}Zn_{1.0}Nb_{1.5}O_7$ (BZN) thin film is one of the most promising materials for gate insulator because of its large dielectric constant (~60) at room temperature. However their tendency to suffer from relatively high leakage current at low electric field (>0.3MV/cm) hinder the application of BZN thin films for gate insulator. In order to improve leakage current characteristics of BZN thin film, we mixed 30mol% MgO with 70mol% BZN and their dielectric and electric properties were characterized. We fabricated field-effect transistors with transparent oxide semiconductor ZnO serving as the electron channel and high-k $(Bi_{1.5}Zn_{1.0}Nb_{1.5}O_7)_{0.7}(MgO)_{0.3}$ as the gate insulator. The devices exhibited low operation voltages (<4V) due to high capacitance of the $(Bi_{1.5}Zn_{1.0}Nb_{1.5}O_7)_{0.7}(MgO)_{0.3}$ dielectric.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.230-231
• /
• 2009

펄스 레이저 층착법 (이하 PLD)은 다성분계 산화물 박막 또는 다층구조의 박막 제작에 매우 유용한 기술이다. 본 실험에서는 KrF 엑시머 레이저를 이용하여 pt on Si 기판 위에 150nm 두께의 $Bi_{1.5}ZnNb_{1.5}O_7$(이하 BZN) 박막을 다양한 기판온도에서 제작하였다. XRD를 이용하여 BZN 박막의 구조적 특성을 분석하였고, 박막을 MIM 구조로 제작하여 유정적 특성을 측정하였다. 제조한 BZN 박막은 $500^{\circ}C$ 이상에서 결정질을, $500^{\circ}C$ 이하의 온도에서는 비정질 특성을 보였다. 유전 특성은 100 - 400$^{\circ}C$ 영역에서는 온도가 증가함에 따라 졸은 특성을 나타내었고, $500^{\circ}C$에서부터는 감소하였다. 증착 온도 $400^{\circ}C$에서 제작한 BZN 박막이 유전상수가 67.8, 유전 손실이 0.006으로 가장 줄은 유전특성을 나타내었다.

• Transactions on Electrical and Electronic Materials
• /
• v.8 no.2
• /
• pp.84-88
• /
• 2007

[ $Bi_{1.5}Zn_{1.0}Nb_{1.5}O_7$ ] (BZN), $Bi_2Mg_{2/3}Nb_{4/3}O_7$ (BMN), and $Bi_2Cu_{2/3}Nb_{4/3}O_7$ (BCN) pyrochlore thin films were prepared on $Cu/Ti/SiO_2/Si$ substrates by pulsed laser deposition and the micro-structural and electrical properties were characterized for embedded capacitor applications. The BZN, BMN, and BCN films deposited at $25\;^{\circ}C$ and $150\;^{\circ}C$, respectively show smooth surface morphologies and dielectric constants of about $39\;{\sim}\;58$. The high dielectric loss of the films deposited at $150\;^{\circ}C$ compared with films deposited at $25\;^{\circ}C$ was attributed to the defects existing at interface between the films and copper electrode by an oxidation of copper bottom electrode. The leakage current densities and breakdown voltages in 200 nm thick-BMN and BZN films deposited at $150\;^{\circ}C$ are approximately $2.5\;{\times}\;10^{-8}\;A/cm^2$ at 3 V and above 10 V, respectively. Both BZN and BMN films are considered to be suitable materials for embedded capacitor applications.

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.17 no.9 s.112
• /
• pp.860-865
• /
• 2006

In this paper, a novel tunable inter-digital capacitor using dielectric tunable $Bi_2O_3-ZnO-Nb_2O_5(BZN)$ pyrochlore thin films is proposed. In order to improve the tunability and reduce DC bias voltage using the fringing electric field, the electrodes of the inter-digital capacitor are embedded in the thin film. Designed results using a 2.5 D simulator show that the tunability of the proposed inter-digital capacitor improves by 10 %, compared to the conventional inter-digital capacitor. The proposed IDC, which is based on the simulation results, was fabricated, using the BZN thin film deposited by a reactive RF magnetron sputtering on the on the silicon substrate. The fabricated inter-digital capacitor shows the maximum tunability of 50 % at 5.8 GHz and 18 V DC applied.