• Applied Chemistry for Engineering
• /
• v.16 no.6
• /
• pp.737-741
• /
• 2005

In this study, the effect of copper content on the NO removal efficiency by Cu/MCM-41 has been investigated. MCM-41 was prepared by hydrothermal synthesis using a gel mixture of colloidal silica solution and cetyltrimethylammonium. Cu/MCM-41 was manufactured with copper content (5, 10, 20, and 40%) in Cu(II) acetylacetonate. The surface properties of MCM-41 were investigated by using pH, XRD, and FT-IR analyses. $N_2/77K$ adsorption isotherm characteristics, including the specific surface area and micropore volume were studied by BET's equation and Boer's t-plot methods. NO removal efficiency was confirmed by gas chromatography technique. From the experimental results, the MCM-41 was analyzed to have the surface functional groups of Si-OH and Si-O-Si and the characteristic diffraction lines (100), (110), (200), and (210) corresponding to a hexagonal arrangement structure. The copper content supported on MCM-41 appeared to increase the NO removal efficiency in spite of decreasing the specific surface areas or micropore volumes. Consequently, it was found that the copper content in Cu/MCM-41 played an important role in improving the NO removal efficiency, which was mainly attributed to the catalytic reactions.

• Applied Chemistry for Engineering
• /
• v.29 no.1
• /
• pp.22-27
• /
• 2018

In this study, the effect of physical properties of $Pt/TiO_2$ on $NH_3$-selective catalytic oxidation (SCO) reaction at $200{\sim}350^{\circ}C$ was investigated. CO-chemisoption and BET analysis were carried out to verify physical properties of $Pt/TiO_2$. By characterizing physical properties of $Pt/TiO_2$ with respect to the Pt loading, the metal dispersion degree decreased as a function of the Pt loading amount. Also, the catalyst having a higher metal dispersion showed an excellent conversion efficiency of $NH_3$ to $N_2$. Since the specific surface area of the support affects the metal dispersion, $Pt/TiO_2$ catalysts were prepared using $TiO_2$ with different physical properties. As a result, it was confirmed that the catalyst having a wide specific surface area exhibited a excellent conversion of $NH_3$ to $N_2$.

• Applied Chemistry for Engineering
• /
• v.24 no.6
• /
• pp.587-592
• /
• 2013

In this study, we prepared pelletized porous carbon adsorbent (PCA) according to the different pyrolysis temperature using activated carbon and polyvinyl alcohol (PVA) as a binder for the removal of toluene, which is one of the representative volatile organic compounds (VOCs). We investigated physical characteristics of PCA using FE-SEM, BET, TGA and evaluated their adsorption capacity for toluene using GC. It was confirmed that the formability of pellets composed of the activated carbon, PVA and solvent of mass mixing ratio was 1 : 0.2 : 0.8 was the most outstanding. Toluene adsorption capacity was evaluated by measuring the maximum time when more than 99% of toluene adsorbed on the pellet. The specific surface area of the adsorbent pyrolyzed at $300^{\circ}C$ was measured as 4.7 times in $941.9m^2/g$ compared to that of the unpyrolyzed pellet. Micropore volume and toluene adsorption capacity of PCA increased fivefold to be 0.30 cc/g and thirteenfold to be 26 hours compared to that of the unpyrolyzed pellet, respectively. These results were attributed to the change of pore size and specific surface area due to the PVA content and the different pyrolysis temperature.

• Korean Chemical Engineering Research
• /
• v.52 no.1
• /
• pp.133-140
• /
• 2014

The experiment was designed to compare the char combustion kinetics of pulverized Indonesia coals commonly utilized in Korea power plants. The reaction rate of coal char has been formulated using the external and internal effectiveness factors to describe the diffusion effect quantitatively. The Random Pore Model (RPM) was used for applying internal specific surface area as a function of carbon conversion ratio. Reaction rate was obtained from reaction time using the Wire Heating Reactor (WHR) which can heat and measure the char particle temperature at the same time. BET and TGA were used to obtain physical properties such as internal specific surface area and structural parameter. Three kinds of Indonesia Sub-bituminous coals "BARAMULTI, ENERGYMAN, AGM" were used in order to derive the activation energy and pre-exponential factor. The results of this study showed that the effect of internal diffusion than that of external diffusion is the dominant as comparison of kinetics was reflected in external and internal effectiveness factors. For three kinds of coal char, finally, activation energy of intrinsic kinetics indicates 110~118 kJ/mol.

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.30 no.2
• /
• pp.189-195
• /
• 2004

Carbon black have not been used as pigment material in cosmetic because of very low density and dispersity, but carbon black have applicable character as black pigment because of non-toxic, stable physico-chemical property, and black colority. In this study, mesoporous silica samples were synthesized by sol-gel reaction using surfactants-template method; TEOS (tetraethoxysilane) - a) PEO/lecithin, b) PEO/polyethylene glycol, c) lecithin/polyethylene glycol in ethanol/water solution. Synthesized organic-inorganic hybrid - silica were heat-treated in N2 condition at 500$^{\circ}C$. Mesoporous silica with black carbon in pore have the effective density and show the good dispersity in both hydrophilic and hydrophobic solvent. Properties of the samples were measured; specific surface area (750㎡/g) and pore size (4-6nm) using BET, pore structure (cylindrical type) using XRD, morphology (spherical powder with 0.1-0.5$\mu\textrm{m}$ partical size) of the samples using SEM. Carbon-silica black color applied to mascara, it shows a dark black colority and good dispersity as compared with the general black color titania pigment. Moreover, it is possible to control the density of black color pigment because it is possible to control pore volume and particle size of mesoporous silica properly. It show the good volume effects in mascara. That is why possible to apply all kinds of cosmetic products.

• Resources Recycling
• /
• v.19 no.1
• /
• pp.40-48
• /
• 2010

It was investigated that effects of NaOH concentration on synthesis of mesoporous materials using municipal solid waste incinerator ash slag (MSWI-ash slag). In order to increase the purity and maximize the amount of extracted Si content the raw MSWI-ash slag was mechanically activated. Extraction of Si from the MSWI-ash slag was carried out by alkali treatment using concentrated NaOH solution, which varied from 1M to 4M. Physical properties (i.e., pore size, specific surface area and total pore volume) of the synthesized mesoporous silica were also evaluated as a function of NaOH concentration via BET, SEM, TEM and small-angle X-ray scattering analyses. Over the entire range of NaOH concentration investigated (i.e., 1-4M), the synthesized mesoporous materials were determined to be SBA-15, which exhibited a hexagonal structure with the pore size of approximately 7 nm. On the other hand, specific surface area and total pore volume increased with NaOH concentration up to 3M while the values decreased at 4M, indicating that the optimal NaOH concentration for the synthesized mesoporous silica was approximately 3M. Further comparison analysis between two conditions (3M versus 4M) showed that the decrease in two physical properties at 4M NaOH concentration was likely due to the potential inhibition by excess Na ions on the formation of mesophase and the consequent increase of pore wall thickness by remaining Si ions.

• Clean Technology
• /
• v.28 no.2
• /
• pp.110-116
• /
• 2022

In this study, iron oxide (FeO_x) nanoparticles were synthesized using iron (Fe) by-products recovered from NdFeB permanent magnet scraps, and the effect of heat-treatment temperature on the physical properties of the FeO_x nanoparticles was investigated. In order to prepare the FeO_x nanoparticles, 2.0 M ammonia (NH₄OH) solution was added to an iron by-product solution diluted to c.a. 10 wt% in D.I. water, which led to the precipitation of the iron oxide precursor. Then, the FeO_x nanoparticles were synthesized by heat-treatment at 300 ℃, 400 ℃, 500 ℃ and 600 ℃. After that, the physical properties of the FeO_x nanoparticles were investigated in order to understand the effect of the heat-treatment temperature. The results of the X-ray diffraction (XRD) analysis showed that the diffraction peak in accordance with the <104> direction increased as the heat-treatment increased, and a diffraction peak indicating the α-Fe₂O₃ crystal structure was detected at heat-treatment temperatures above 500 ℃. The BET specific surface area analysis revealed that the specific surface area decreased as the heat-treatment temperature increased to above 400 ℃. Observation with a high resolution transmission electron microscope (HRTEM) showed that rod-shaped nanoparticles were formed, and the size of the nanoparticles showed a tendency to increase as the heat-treatment temperature increased.

• Korean Chemical Engineering Research
• /
• v.61 no.3
• /
• pp.472-478
• /
• 2023

In this study, the acetaldehyde removal characteristics of activated carbon (AC) for air purifier filters were investigated using metal catalysts-impregnation and functional group-modification method. The AC with a high specific surface area(1700 m²/g) and micropores was prepared by KOH activation of coconut charcoal and the efficiency of catalyst and functional group immobilization was examined by varying the drying conditions within the pores after immersion. The physical properties of the prepared activated carbon were analyzed by BET, ICP, EA, and FT-IR, and the acetaldehyde adsorption performances were investigated using gas chromatography (GC) at various impregnation and modified conditions. As the concentration of impregnation solution increased, the amount of impregnated metal catalysts increased, while the specific surface area showed a decreasing trend. The adsorption tests of the metal catalyst-impregnated and functional group-modified activated carbons revealed that excellent adsorption performance in compositions MgO10@AC, CaO10@AC, EU10@AC, and H-U3N1@AC, respectively. The MgO10@AC, which showed the highest adsorption performance, had a breakthrough time of 533.8 minutes and adsorption capacity of 57.4 mg/g for acetaldehyde adsorption. It was found that the nano-sized MgO catalyst on the activated carbon improved the adsorption performance by interacting with carbonyl groups of acetaldehyde.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.765-768
• /
• 2009

In this work, we prepared the activated multi-walled carbon nanotubes (Acti-MWNTs) with well developed physical surface structures, high specific surface area, and higher adsorption capacity by a physical activation process, in order to enhance the hydrogen storage capacity. The Acti-MWNTs' changes in the crystalline phase and in their lattice distortions were characterized by X-ray diffraction (XRD). The textural properties of the Acti-MWNTs were investigated by a nitrogen adsorption isotherms by Brunauer-Emmett-Teller (BET) equation and Harvath-Kawazoe (H-K) calculation, respectively. The hydrogen storage capacity of the Acti-MWNTs was investigated by BEL-HP at 298 K/100 bar. The hydrogen storage capacity of the Acti-MWNTs was improved with the physical activation, resulted from the formation of new hydrogen-favorable sites on the Acti-MWNT surfaces. In conclusion, the physical activation was one of the effective method to enhance the hydrogen storage capacity of the MWNTs.

• Journal of Korean Society for Atmospheric Environment
• /
• v.31 no.6
• /
• pp.538-547
• /
• 2015

Test activated carbon fiber (ACF) was prepared from Polyacrylonirile (PAN) through oxidation and chemical activation. Immersion of ACF precursors in the aqueous KOH solution enhanced the surface structure, as examined by BET pore analysis. Specific surface area increased greatly from less than $70m^2/g$ to $1226m^2/g$ with 4 M KOH, and total pore volume also rose up to $0.483cm^3/g$. In particular, it was found that micropores favorable for $CO_2$ molecule capture occupied more than 95%. Maximum $CO_2$ adsorption capacity was 3.59 mmol/g at 298 K. Low depth of pores in the present ACF may facilitate the molecules' desorption for its regeneration.