This study was carried out to investigate the current use and the demand for Jeonju-bibimbab rice and to suggest the suitable range of bibimbab rice. We conducted a survey on varieties and rice quality of Jeonju bibimbab restaurants from April to August 2016. In a survey of 12 bibimbab restaurants in Jeonju, the restaurants showed that 83% of the 10 restaurants were using shindongjin rice variety. Characteristics of rice suitable for bibimbab were showed low stickiness, high hardness, so it should keep the shape of rice when cooked and mixed with the ingredients. and people tend to prefer a large grain of rice. Also, the rice used in bibimbab restaurants were examined the average percentages of head rice ratio 89%, protein content 6% and moisture content 14.5%. These results suggest that the quality of rice, which is suitable for bibimbab, is similar to the range of common rice. Thousand grain weight over 24g is especially preferred. In conclusion, the quality and grain size of rice preferred for bibimbab rice was the level of Shindongjin.

• 한국세라믹학회지
• /
• 제42권2호
• /
• pp.140-144
• /
• 2005

The microstructures and mechanical properties of Tetragonal Zirconia Polycrystals (TZP) sintered bodies, which made by pressureless and spark plasma sintering techniques, were investigated using XRD, SEM, and TEM techniques. In the spark plasma sintered samples, the TZP grains were equiaxed type including many sub-grain boundaries regardless of sintering conditions. The biaxial strength of TZP having an average of 80 nm grains in diameter was high in value with 1025 MPa, but fracture toughness showed a low value due to the absence of a fracture toughening mechanism such as transformation toughening. In the Pressureless Sintered (PLSed) samples, the grain size of TZP was strongly dependent on the sintering temperature; i.e., it gradually increased as the sintering temperature increased. The value of fracture toughness increased as the grain size increased by the stress-induced phase transformation and Borne crack deflection.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제50권11호
• /
• pp.539-543
• /
• 2001

ln this paper, the $Sr_{l-x}Ca_xTiO_3(0\leqx\leq0.2)-based$ grain boundary layer ceramics were fabricated to measure dielectric properties with the sintering temperature and the thermal treatment time. The sintering temperature and time were $1420~15206{\circ}C$, 4hours, and the thermal treatment temperature and time of the specimen were $l150^{\circ}C$, 1, 2, 3hours, respectively. The structural and the dielectric properties were investigated by SEM, X-ray, HP4194A and K6517. The average grain size was increased with increasing the sintering temperature, but it decreased up to 15mo1% with increasing content of Ca. X-ray diffraction analysis results showed that all specimens were the cubic structure, and the main peaks were moved to right and the lattice constant were decreased with increasing content of Ca. The appropriate thermal treatment time and temperature of CuO to obtain dielectric properties of $\varepsilon_r>50000,\; tan \delta<0.05\; and \;\DeltaC<\pm10%$ were 2hrs and $l150^{\circ}C$, respectively.

• 자원환경지질
• /
• 제33권3호
• /
• pp.195-204
• /
• 2000

order to investigate physical characteristics and element concentrations of sediments, coastal bottom sediments were collected at 20 stations in the vicinity of Youngkwang Nuclear Power Plant. After air drying of samples in the laboratory. article size distribution was examined by Master sizer (X-350F), radio-activity by HPGe ${\gamma}$-spectrphotometer, and element concentrations by ICP-AES and AAS. According to particle size analysis , sediments are mainly composed of silt fraction weith 23% of sand, 65% of silt and 12% of clay on average. Most sediments are derived from muddy environment that silt dominates with the characteristics of 5.3${\varsigma}$ mean particle size, poorly sorted, very fine skewed and lepto-kurtic. Only two sediments are well sorted with sandy silt owing to wind, winnowing action, tide and current andits complex reactions. Element concentrations in the coastal bottom sediments are relatively high at finer sediment and show significant relationship with grain size. Index of geoaccumulation by heavy metals at every sampling station is classified as practically unpolluted. The radioactivities of the sediments were measured for 15 isotope elements, and 2 elements of K-40 and Cs-137 were detected in most sediments. The K-40 is the natural nuclide and the artificial nuclide of Cs-137 was thought to be derived from the fallout of past nuclear weapon test. The results of correlation coefficient between grain size and radioactivity shows that the activity of Cs-137 significantly increases in finer grain.

• KIEE International Transactions on Electrophysics and Applications
• /
• 제3C권4호
• /
• pp.140-145
• /
• 2003

The influence of microstructure nonuniformity on the electrical characteristics of ZnO varistors was analyzed with the added amount of $Al_2$O$_3$ dopants. $Al_2$O$_3$ doping can effectively inhibit grain growth. When $Al_2$O$_3$ content is in the range between 0-0.1 %, the average grain size and the standard deviation decrease quickly and the grain growth is strongly inhibited. Therefore, it is possible to increase the microstructure uniformity by accurate addition of $Al_2$O$_3$ to the ZnO varistor. The breakdown voltage increases with the decrease of standard deviation. The greater the uniformity of the Zno varistor means the higher the global breakdown voltage. The $Al_2$O$_3$ dopants having about 0-0.023 wt% content can effectively improve the voltage ratio, and the voltage ratio reaches a minimum value of 2.32 at an $Al_2$O$_3$ content of 0.005 wt%.

• Nuclear Engineering and Technology
• /
• 제29권3호
• /
• pp.196-200
• /
• 1997

The variation of sintered density and fain size in ex-AUC, ex-ADU and granulated ex-ADU UO$_2$ pellets in which 0.1~1.0wt% Nb$_2$O$_{5}$ were doped were examined. Pellets were sintered in an atmosphere of H$_2$ at 1$700^{\circ}C$ for 4h. All the specimens tested shooed more than 94% T.D.(Theoretical Density). Sintered density decreased with increasing the amount of Nb$_2$O$_{5}$. Powder types had little influence on the sintered density. Pore size distribution was shifted to the larger ones as Nb$_2$O$_{5}$ was added. The increase of total pore volume and grain growth due to the addition of Nb$_2$O$_{5}$ were thought to be the cause of the sintered density decrease. The largest grain size was seen in the 1. 0wt% Nb$_2$O$_{5}$ doped ex-AUC UO$_2$ pellets. Their average size was 13.9 ${\mu}{\textrm}{m}$.m}$.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2012년도 춘계학술발표대회
• /
• pp.56.1-56.1
• /
• 2012

The microstructures and mechanical properties of Co-29Cr-6Mo alloy with C and N additions, produced by additive manufacturing using electron beam melting (EBM) method, were studied using X-ray diffraction, electron back scatter diffraction, transmission electron microscope, Vickers hardness tests, and tensile tests, focusing on the influences on the build direction and the various heat treatments after build. It is found that the microstructures for the as built specimens were changed from columnar to equiaxed grain structure with average grain size of approximately $10-20{\mu}m$ due to the heat treatment employing the reverse transformation from a lamellar (hcp + $Cr_2N$) phase to an fcc. Our results will contribute to the development of biomedical Ni-free Co-Cr-Mo-N-C alloys, produced by EBM method, with refined grain size and good mechanical properties, without requiring any hot workings.

• 한국재료학회지
• /
• 제19권8호
• /
• pp.432-436
• /
• 2009

A Cu-Fe-P copper alloy was processed by accumulative roll-bonding (ARB) for ultra grain refinement and high strengthening. Two 1mm thick copper sheets, 30 mm wide and 300 mm long, were first degreased and wire-brushed for sound bonding. The sheets were then stacked on top of each other and roll-bonded by about 50% reduction rolling without lubrication at ambient temperature. The bonded sheet was then cut into two pieces of the same dimensions and the same procedure was repeated for the sheets up to eight cycles. Microstructural evolution of the copper alloy with the number of the ARB cycles was investigated by optical microscopy (OM), transmission electron microscopy(TEM), and electron back scatter diffraction(EBSD). The grain size decreased gradually with the number of ARB cycles, and was reduced to 290 nm after eight cycles. The boundaries above 60% of ultrafine grains formed exhibited high angle boundaries above 15 degrees. In addition, the average misorientation angle of ultrafine grains was 30 degrees.

• 한국자기학회지
• /
• 제11권1호
• /
• pp.1-7
• /
• 2001

열연판을 모재로 하여 압연 및 열처리 공정을 조합한 공정을 3회 냉간압연법을 사용하여 최종두께 100$\mu\textrm{m}$로 제작한 방향성 규소강대에 대하여, 직류자기 특성 및 결정입자의 열처리 의존성, 결정방위 등을 조사하였다. 그 결과, (110)면이 거의 시료 전체표면에 성장하는 것이 관측되었으며, B$_{8}$은 1.9 T정도, 평균$\alpha$각은 약 4.6$^{\circ}$이었다. 향후 약간의 (001)조직의 집적도 개선이 추가된다면, 염가의 열연판을 모재로 사용하여 기존의 방향성 규소강판의 경우보다 훨씬 제조공정수를 단순화함으로써, 경제성이 우수한 방향성 극박 규소강대를 제작할 수 있는 가능성을 확인하였다.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 춘계학술대회 논문집
• /
• pp.274-277
• /
• 2009

There have been a number of works on manufacturing ultrafine grained steels with average ferrite grain sizes of smaller than a few micrometers to develop beneficial high strength steels. Among microstructures in low carbon steels, lath martensite is known to be useful to produce an ultrafine grained ferrite matrix and finely globular cementite particle. Thus, severe plastic deformation and subsequent annealing at lower temperature of lath martensite would become an effective way to produce ultrafine grained steels. However, most ultrafine grained steels exhibited a total elongation of a few per cent in tensile tests. Such a defect is one of the primary factors restricting the potential applications of ultrafine grained steels. Therefore, the improvement of the strength-elongation balance is required for the application of ultrafine grained structural steels. In this study, the effect of deformation temperatures on microstructure, such as ferrite grain size and the distribution of cementite particles, and mechanical property of lath martensite steels, was investigated. Specimens were fabricated through cold rolling or warm rolling and subsequent annealing.