• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.2
• /
• pp.73-78
• /
• 2016

An increase in the transistor density of integrated circuit devices leads to a very high increase in heat dissipation density, which causes a long-term reliability and various thermal problems in microelectronics. In this study, liquid cooling method was investigated using straight microchannels with various metal bumps. Microchannels were fabricated on Si wafer using deep reactive ion etching (DRIE), and Ag, Cu, or Cr/Au/Cu metal bumps were placed on Si wafer by a screen printing method. The surface temperature of liquid cooling structures with various metal bumps was measured by infrared (IR) microscopy. For liquid cooling with Cr/Au/Cu bumps, the surface temperature difference before and after liquid cooling was $45.2^{\circ}C$ and the power density drop was $2.8W/cm^2$ at $200^{\circ}C$ heating temperature.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.55-62
• /
• 2000

The wetting balance test was performed in an attempt to estimate the wetting properties of the UBM-coated Si-wafer on one side to the Sn-Pb solder. The wetting curves of the one and both side-coated UBM layers had the similar shape and the parameters characterizing the curve shape showed the similar transition tendency to the temperature. The wetting property estimation was possible with the new wettability indices from the wetting curves of one side-coated specimen; $F_{min}$, $F_{s}t_{s}$ and $t_s$. For UBM of Si-chip, Au/Cu/Cr UBM was better than Au/Ni/Ti in the point of wetting time. The contact angle of the one side coated Si-plate to the Sn-Pb solder could be calculated from the force balance equation by measuring the static state force and the tilt angle.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.2
• /
• pp.13-21
• /
• 1999

Flip chip assembly directly on organic boards offers miniaturization of package size as well as reduction in interconnection distances resulting in a high performance and cost-competitive Packaging method. This paper describes the investigation of alternative low cost flip-chip mounting processes using electroless Ni/Au bump and anisotropic conductive adhesives/films as an interconnection material on organic boards such as FR-4. As bumps for flip chip, electroless Ni/Au plating was performed and characterized in mechanical and metallurgical point of view. Effect of annealing on Ni bump characteristics informed that the formation of crystalline nickel with $Ni_3$P precipitation above $300^{\circ}C$ causes an increase of hardness and an increase of the intrinsic stress resulting in a reliability limitation. As an interconnection material, modified ACFs composed of nickel conductive fillers for electrical conductor and non-conductive inorganic fillers for modification of film properties such as coefficient of thermal expansion(CTE) and tensile strength were formulated for improved electrical and mechanical properties of ACF interconnection. The thermal fatigue life of ACA/F flip chip on organic board limited by the thermal expansion mismatch between the chip and the board could be increased by a modified ACA/F. Three ACF materials with different CTE values were prepared and bonded between Si chip and FR-4 board for the thermal strain measurement using moire interferometry. The thermal strain of ACF interconnection layer induced by temperature excursion of $80^{\circ}C$ was decreased with decreasing CTEs of ACF materials.

• Korean Journal of Materials Research
• /
• v.22 no.10
• /
• pp.545-551
• /
• 2012

In semiconductor manufacturing, the circuit integrity of packaged BGA devices is tested by measuring electrical resistance using test sockets. Test sockets have been reported to often fail earlier than the expected life-time due to high contact resistance. This has been attributed to the formation of Sn oxide films on the Au coating layer of the probe pins loaded on the socket. Similar to contact failure, and known as "fretting", this process widely occurs between two conductive surfaces due to the continual rupture and accumulation of oxide films. However, the failure mechanism at the probe pin differs from fretting. In this study, the microstructural processes and formation mechanisms of Sn oxide films developed on the probe pin surface were investigated. Failure analysis was conducted mainly by FIB-FESEM observations, along with EDX, AES, and XRD analyses. Soft and fresh Sn was found to be transferred repeatedly from the solder bump to the Au surface of the probe pins; it was then instantly oxidized to SnO. The $SnO_2$ phase is a more stable natural oxide, but SnO has been proved to grow on Sn thin film at low temperature (< $150^{\circ}C$). Further oxidation to $SnO_2$ is thought to be limited to 30%. The SnO film grew layer by layer up to 571 nm after testing of 50,500 cycles (1 nm/100 cycle). This resulted in the increase of contact resistance and thus of signal delay between the probe pin and the solder bump.

• Korean Journal of Metals and Materials
• /
• v.49 no.3
• /
• pp.237-242
• /
• 2011

The effect of shearing speed on the shear force and energy of Sn-0Ag-0.5Cu solder ball was investigated. Various UBM (under bump metallurgy)'s on Cu pads were used such as ENEPIG (Electroless Nickel, Electroless Palladium, Immersion Gold; Ni/Pd/Au), ENIG (Electroless Nickel, Immersion Gold; Ni/Au), OSP (Organic Solderability Preservative). To fabricate a shear test specimen, a solder ball, $300{\mu}m$ in diameter, was soldered on a pad of FR4 PCB (printed circuit board) by a reflow soldering machine at $245^{\circ}C$. The solder bump on the PCB was shear tested by changing the shearing speed from 0.01 m/s to 3.0 m/s. As experimental results, the shear force increased with a shearing speed of up to 0.6 m/s for the ENIG and the OSP pads, and up to 0 m/s for the ENEPIG pad. The shear energy increased with a shearing speed up to 0.3 m/s for the ENIG and the OSP pads, and up to 0.6 m/s for the ENEPIG pad. With a high shear speed of over 0 m/s, the ENEPIG showed a higher shear force and energy than those of the ENIG and OSP. The fracture surfaces of the shear tested specimens were analyzed, and the fracture modes were found to have closer relationship with the shear energy than the shear force.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.332-336
• /
• 2001

In this study, the reaction at UBM(Under Bump Metallurgy) and solder interface was investigated. The UBM employed in conventional optical packages, Au/Pt/Ti layer, were found to dissolve into molten Au-Sn eutectic solder during reflow soldering. Therefore, the reaction with different diffusion barrier layer such as Fe, Co, Ni were investigated to replace the conventional Pt layer. The reaction behavior was investigated by reflowing the solder on the pad of the metals defined by Cr layer for 1, 2, 3, 4, and 5 minutes at $330^{\circ}C$. Among the metals, Co was found to be most suitable for the diffusion barrier layer as the wettability with the solder was reasonable and the reaction rate of intermetallic formation at the interface is relatively slow.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.332-336
• /
• 2001

In this study, the reaction at UBM(Under Bump Metallurgy) and solder interface was investigated. The UBM employed in conventional optical packages, Au/Pt/Ti layer, were found to dissolve into molten Au-Sn eutectic solder during reflow soldering. Therefore, the reaction with different diffusion barrier layer such as Fe, Co, Ni were investigated to replace the conventional R layer. The reaction behavior was investigated by reflowing the solder on the pad of the metals defined by Cr layer for 1, 2, 3, 4, and 5 minutes at 330$^{\circ}C$. Among the metals, Co was found to be most suitable for the diffusion barrier layer as the wettability with the solder was reasonable and the reaction rate of intermetallic formation at the interface is relatively slow.

• Korean Journal of Metals and Materials
• /
• v.49 no.5
• /
• pp.411-418
• /
• 2011

The current study investigates the electroplating characteristics of Sn-Cu eutectic micro-bumps electroplated on a Si chip for flip chip application. Under bump metallization (UBM) layers consisting of Cr, Cu, Ni and Au sequentially from bottom to top with the aim of achieving Sn-Cu bumps $10\times10\times6$ ${\mu}m$ in size, with 20${\mu}m$ pitch. In order to determine optimal plating parameters, the polarization curve, current density and plating time were analyzed. Experimental results showed the equilibrium potential from the Sn-Cu polarization curve is -0.465 V, which is attained when Sn-Cu electro-deposition occurred. The thickness of the electroplated bumps increased with rising current density and plating time up to 20 mA/$cm^2$ and 30 min respectively. The near eutectic composition of the Sn-0.72wt%Cu bump was obtained by plating at 10 mA/$cm^2$ for 20 min, and the bump size at these conditions was $10\times10\times6$ ${\mu}m$. The shear strength of the eutectic Sn-Cu bump was 9.0 gf when the shearing tip height was 50% of the bump height.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.5
• /
• pp.386-392
• /
• 2003

The electroplating process for a solder bump which can be applied for a flip chip was studied. Si-wafer was used for an experimental substrate, and the substrate were coated with UBM (Under Bump Metallization) of Al(400 nm)/Cu(300 nm)Ni(400 nm)/Au(20 nm) subsequently. The compositions of the bump were Sn-Cu and eutectic Sn-Pb, and characteristics of two bumps were compared. Experimental results showed that the electroplated thickness of the solders were increased with time, and the increasing rates were TEX>$0.45 <\mu\textrm{m}$/min for the Sn-Cu and $ 0.35\mu\textrm{m}$/min for the Sn-Pb. In the case of Sn-Cu, electroplating rate increased from 0.25 to $2.7\mu\textrm{m}$/min with increasing current density from 1 to 8.5 $A/dm^2$. In the case of Sn-Pb the rate increased until the current density became $4 A/dm^2$, and after that current density the rate maintains constant value of $0.62\mu\textrm{m}$/min. The electro plated bumps were air reflowed to form spherical bumps, and their bonded shear strengths were evaluated. The shear strength reached at the reflow time of 10 sec, and the strength was of 113 gf for Sn-Cu and 120 gf for Sn-Pb.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.708-711
• /
• 1999

The Cu/Ni/Au lamellar structure is extensively used as an under bump metallization on silicon file, and on printed circuit board(PCB) pads. Ni is plated Cu by either electroless Ni plating, or electrolytic Ni plating. Unlike the electrolytic Ni plating, the electroless Ni plating does not deposit pure Ni, but a mixture of Ni and phosphorous, because hypophosphite Is used in the chemical reaction for reducing Ni ions. The fracture crack extended at the interface between solder balls of plastic ball grid (PBGA) package and conducting pads of PCB. The fracture is duets to segregation at the interface between Ni$_3$Sn$_4$intermetallic and Ni-P layer. The XPS diffraction results of Cu/Ni/Au results of CU/Ni/AU finishs showed that the Ni was amorphous with supersaturated P. The XPS and EDXA results of the fracture surface indicated that both of the fracture occurred on the transition lesion where Sn, P and Ni concentrations changed.