• Journal of the Korean Ceramic Society
• /
• v.53 no.6
• /
• pp.628-634
• /
• 2016

The 8 wt% yttria($Y_2O_3$) stabilized zirconia ($ZrO_2$), 8YSZ, a typical thermal barrier coating (TBC) for turbine systems, was fabricated under different starting powder conditions and coating parameters by atmospheric plasma spray (APS) coating process. Four different starting powders were prepared by conventional spray dry method with different additive and process parameter conditions. As a result, large- and small-size spherical-type particles and Donut-type particles were obtained. Dense structure of 8YSZ coating was produced when small size spherical-type or Donut-type particles were used. On the other hand, 8YSZ coating with a porous structure was formed from large-size spherical-type particles. Furthermore, a segmented coating structure with vertical cracks was observed after post heat treatment on the surface of dense structured coating by argon plasma flame at an appropriate gun distance and power condition.

• Applied Science and Convergence Technology
• /
• v.23 no.5
• /
• pp.261-264
• /
• 2014

$SrTiO_3$ (STO) single crystal irradiated with a 3-MeV proton beam exhibits blue and green mixed luminescence. However, the same proton beam when used to irradiate STO with a very thin layer of deposited Pt does not show any luminescence. This Pt layer prevents any damage which may otherwise be caused by arcing, which stems from the accumulated surface voltage of tens of kV due to the charge induced by secondary electrons on the surface of the insulator during the ion beam irradiation process. Hence, the luminescence of ion-irradiated STO originates from the modification of the STO surface layer caused by arcing rather than from any direct ion beam irradiation effect. STO treated with atmospheric-pressure plasma, a simple and cost-effective method, also exhibits the same type of blue and green mixed luminescence as STO treated with an ion beam, as the plasma also creates a layer of surface damage due to arcing.

• Transactions on Electrical and Electronic Materials
• /
• v.14 no.3
• /
• pp.133-138
• /
• 2013

Acrylonitrile-butadiene-styrene (ABS) plastic is a polymer material extensively used in electrical and electronic applications. Nickel (Ni) thin film was deposited on ABS by electroless plating, after its surface was treated and modified with atmospheric plasma generated by means of dielectric barrier discharges (DBDs) in air. The method in this study was developed as a pre-treatment for electroless plating using DBDs, and is a dry process featuring fewer processing steps and more environmentally friendliness than the chemical method. After ABS surfaces were modified, surface morphologies were observed using a scanning electron microscope (SEM) to check for any physical changes of the surfaces. Cross-sectional SEM images were taken to observe the binding characteristics between metallic films and ABS after metal plating. According to the SEM images, the depths of ABS by plasma are shallow compared to those modified by chemically treatment. The static contact angles were measured with deionized (DI) water droplets on the modified surfaces in order to observe for any changes in chemical activities and wettability. The surfaces modified by plasma showed smaller contact angles, and their modified states lasted longer than those modified by chemical etching. Adhesion strengths were measured using 3M tape (3M 810D standard) and by 90° peel-off tests. The peel-off test revealed the stronger adhesion of the Ni films on the plasma-modified surfaces than on the chemically modified surfaces. Thermal shock test was performed by changing the temperature drastically to see if any detachment of Ni film from ABS would occur due to the differences in thermal expansion coefficients between them. Only for the plasma-treated samples showed no separation of the Ni films from the ABS surfaces in tests. The adhesion strengths of metallic films on the ABS processed by the method developed in this study are better than those of the chemically processed films.

• Resources Recycling
• /
• v.22 no.2
• /
• pp.18-21
• /
• 2013

In this study, surface modification of wood powder by atmospheric pressure plasma treatment was investigated. The composites were manufactured using wood powder and polypropylene(wood powder : PP = 55 wt% : 45 wt%). Atmospheric pressure plasma was treated as condition of 3KV, $17{\pm}1$KHz, 2 g/min. Helium was used as carrier gas and monomer such as hexamethyl-disiloxane(HMDSO) was used to modify surface property by plasma polymerization. The tensile strength of untreated waste wood powder(W3) and homogeneous wood powder(H3) were about 18.5 MPa, 21.5 MPa while the tensile strength of plasma treated waste wood powder(PW3) and homogeneous wood powder(PH3) were about 21.2 MPa, 23.4 MPa, respectively. And tensile strength of W3 and H3 were improved by 14.6% and 8.8%, respectively. From the results for mechanical property, morphological analysis, we obtained improved interfacial bonding of polypropylene and wood powder modified by plasma treatment.

• Journal of Adhesion and Interface
• /
• v.8 no.3
• /
• pp.1-8
• /
• 2007

An atmospheric plasma pre-treatment method was applied to polyurethane foam to improve its contact angle and adhesion. In order to investigate the optimum reaction condition of plasma treatment, type of reaction gas (nitrogen, argon, oxygen, air), rate of gas flow (30~150 mL/min), and reaction time (0~30 sec) were examined in a plate plasma reactor. Also, the effects were compared to those of a conventional vacuum plasma pre-treatment system. The result of the surface modification with respect to the treatment procedure was characterized by using SEM and ATR-FTIR. Due to a decrease of the contact angle of polyurethane foam, the greatest adhesion strength was achieved at a flow rate of 100 mL/min and at a reaction time of 10s for N2 gas. Consequently, the atmospheric plasma treatment reduced the contact angle of the polyurethane foam and also resulted in the improvement of the peel strength.

• Journal of Korean Society for Atmospheric Environment
• /
• v.16 no.3
• /
• pp.247-256
• /
• 2000

Basic characteristics of non-thermal plasma process to remove C2H4 and NO have been experimentally investigated with a packed-bed type reactor and an ac power supply. The performance of the non-thermal plasma generated by ac power supply was compared with that of a wire-plate type reactor equipped with a pulsed power supply. The result shows that the non-thermal plasma can be effectively generated with an AC power supply that can be easily fabricated with conventional techniques. In order to understand the basic reaction mechanisms of the non-thermal plasma process, parametric tests for different carrier gases(air and nitrogen) and for different reaction pathways have been performed. The test results show that O3 generated by non-thermal plasma plays an dominant role to oxidize C2H4 and NO over N and O radicals when these pollutant gases are carried by dry air under room temperature condition. Experimental observations, however, indicate that N and O radicals can significantly affect on the removal process of the pollutant gases under certain conditions.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.96-96
• /
• 2010

To improve surface wettability, each sample was treated by atmospheric pressure plasma (APP) using dielectric barrier discharge (DBD) system. Argon and oxygen gases were used for treatment gas to modify the $TiO_2$ surface by APP with RF power range from 50 to 200 W. Water contact angle was decreased from $20^{\circ}$ to $10^{\circ}$ with argon only. However, water contact angle was decreased from $20^{\circ}$ to < $1^{\circ}$ with mixture of argon and oxygen. Water contact angle with $O_2$ plasma was lower than water contact angle with Ar plasma at the same RF power. It seems to be increasing the polar force of $TiO_2$ surface. Also, analysis result of X-ray photoelectron spectra (XPS) shows the increase of intensity of O1s shoulder peak, resulting in increasing of surface wettability by APP. Moreover, each water contact angle increased according to increase past time. However, contact angle increase with plasma treatment was lower than without plasma treatment. Additionally, the efficiency of $TiO_2$ photocatalyst was improved by plasma surface-treatment through the degradation experiment of phenol

• ANNALS OF ANIMAL RESOURCE SCIENCES
• /
• v.30 no.2
• /
• pp.69-78
• /
• 2019

The objective of this study was to investigate the quality properties of sausages added with the atmospheric pressure plasma treated extract of Perilla frutescens Britton var. acuta Kudo (red perilla). The lyophilized powder of red perilla extract treated by atmospheric-pressure plasma contained 7.5 g kg^-1 nitrite. Sausage samples were manufactured with the addition of sodium nitrite (Control), celery powder (Celery), or plasma-treated extract of red perilla (PTP) to obtain nitrite concentration of 70 mg kg^-1. The residual nitrite content was the lowest in PTP during storage for 21 days at 4℃ (p<0.05). The total aerobic bacteria counts were higher in PTP than in Control and Celery during storage at 4℃ (p<0.05). Malondialdehyde content of sausages was significantly lower in PTP than in Control and Celery during storage (p<0.05). PTP showed the lowest L^* value and the highest b^* value among the tested sausage samples during storage (p<0.05). PTP received the low scores in all the sensory properties of sausages because of its inherent color and flavor. The results suggested that the plasma-treated extract of red perilla was an unsuitable natural nitrite source for cured meat products because of its adverse effect on sensory quality. However, natural nitrite source with increased nitrite content can be produced by the treatment of the natural plant extract with atmospheric-pressure plasma.

• Journal of Korean Society for Atmospheric Environment
• /
• v.30 no.4
• /
• pp.339-349
• /
• 2014

$CO_2$ emission has been gradually increased due to rising fossil fuel use. A gliding arc plasma scrubber (GAPS) was proposed to destruct $CO_2$. For optimum design of GAPS, a CFD analysis has been conducted in different configuration for the system. The parameters considered included gas injection velocity at the nozzle and gas flow rate to gap between electrodes. The reactor configuration affected velocity fields which caused changes in the mixture fraction and the retention time. The mixing effect of $CO_2$ and supplied gas ($CH_4$ and steam) was enhanced by installing a orifice baffle. This revealed that the orifice baffle is effective in $CO_2$ conversion by positioning the reactants in the gas into the center of plasma discharge.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.51 no.3
• /
• pp.111-114
• /
• 2002

Using the plasma that we developed to generate a low-temperature plasma at atmospheric pressure, we have investigated the etching possibility of an air-exposed zinc oxide(ZnO) thin films. Hydrogen and methane radicals generated from the plasma were observed and their intensity was found to be dependent on the isomer of butyl acetate by an analysis with optical emission spectrosxopy. The etching ability of this plasma was evaluated by an emission intensity, etching time, rf power.