• Journal of Surface Science and Engineering
• /
• v.49 no.2
• /
• pp.172-177
• /
• 2016

In this paper, various electrochemical experiments were conducted in seawater solution to evaluate corrosion damage behavior of arc thermal sprayed Inconel 625 coating on SS400 steel in marine environment. As a result, corrosion damages of thermal sprayed Inconel 625 coating preferentially occurred at the defect area, and they were observed as a form of pitting corrosion in the galvanostatic experiments. In Tafel analysis, corrosion current density of Inconel 625 coating was relatively high due to influence of interconnected pores and Cr oxides in the thermal spray coating layer. On the other hand, the result of the potential measurement, thermal sprayed Inconel 625 coating should need the post-treatment which can compensate the defects like pores and cracks because Inconel 625 coating presented a higher potential of about 290 mV than that of the SS400 steel.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.27 no.4
• /
• pp.521-528
• /
• 2021

In this study, to repair damaged economizer fin tubes on ships, sealing treatment was performed after applying arc thermal spray coating technology using Inconel 625. A solid particle erosion (SPE) experiment was conducted according to ASTM G76-05 to evaluate the durability of the substrate, thermal spray coating (TSC), and thermal spray coating+sealing treatment (TSC+Sealing) specimens. The surface damage shape was observed using a scanning electron microscope and 3D laser microscope, and the durability was evaluated through the weight loss and surface roughness analysis. Consequently, the durability of the substrate was superior to that of TSC and TSC+Sealing, which was believed to be owing to numerous pore defects in the TSC layer. In addition, the mechanism of solid particle erosion damage was accompanied by plastic deformation and fatigue, which were the characteristics of ductile materials in the case of the substrate, and the tendency of brittle fracture in the case of TSC and TSC+Sealing was confirmed.

• Journal of Surface Science and Engineering
• /
• v.33 no.5
• /
• pp.329-338
• /
• 2000

In this study, as an effort to improve the brittlement of coating layer, aluminum bronze coatings formed on steel substrates by arc jet spray process were subjected to post heat treatment. After each treatment, mechanical properties such as hardness, and UTS, and microstructural characterization of the specimens were investigated. The results showed that the hardness in the coatings slightly decreased with increasing heat treatment tine and temperature. The UTS of as-sprayed coatings was 4.31kgf/$\textrm{mm}^2$ and slightly increased to 5.51kgf/$\textrm{mm}^2$ after heat treatment at $900^{\circ}C$ for 120min. On the other hand, the interdiffusion of copper and aluminum particles after heat treatment lead to decrease of the porosity density and increase the bond strength.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.05a
• /
• pp.140-141
• /
• 2021

Arc thermal spray process is widely used to protect the steel from corrosion and abrasion. In the present study, two different coatings i.e. Al and Al-5%Mg were used to compare their corrosion resistance performance and the effect of 5% Mg addition in the properties of deposited coating. The SEM results showed the more compact and less porous morphology of Al-5%Mg coating compared to Al. The corrosion resistance performance of both deposited coatings was studied in artificial ocean water with exposure periods and results are compared. The total impedance values of Al-5%Mg at 0.01 Hz exhibited highest with exposure periods might be attributed to the coating and corrosion products nature and morphology compared to Al coating.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.81-82
• /
• 2022

Al and Zn are used to protect the steel structures from corrosion. In the present studies, 15Al-85Zn alloy wires has been used for the deposition of coating by arc thermal spray process. Moreover, this process of coating exhibited severe defects formation, therefore, this coating was post-treated with different concentrations i.e. 0.05, 0.1 and 0.5M sodium hexa meta phosphate (Na6[(PO3)6]: SHMP) to fill to defects of deposited coatings and assessed their corrosion resistance in 3.5 wt.% NaCl solution with exposure periods. After the treatment, the porosity of the coating reduced significantly by formation of composite oxide films onto the coating surface. Initially, 0.5 M SHMP treated coating exhibited highest in total impedance due to significant reduction of porosity but once the exposure periods are extended, the composite oxides are dissolved, thus, total impedance is decreased.

• Journal of Power System Engineering
• /
• v.9 no.4
• /
• pp.90-95
• /
• 2005

The wire-arc process is a low-cost thermal spray method simply utilizes electrical energy to melt the feedstock wire. It is more userful for field applications, especially to coat large surface area. In this paper, a special Fe-based alloy coatings by using the wire-arc process were developed. Nanoscale composite coatings were achieved either during spraying or through a post heat treatment. As-sprayed Fe-based alloy coatings had been an amorphous matrix structure, after heating to $700^{\circ}C$ for 10 minutes a solid state transformation occurred in the some fraction of amorphous matrix which resulted in the formation of nanostructured recrystallized phase. Scanning electron microscopy (SEM) and field emotional scanning electron microscope(FE-SEM) were applied to analyze the microstructure of the coatings. Additionally hardness and bend resistance of the Fe-based alloy coatings were examined, and these results were compared with those of partially stabilized zirconia(PSZ) coatings by using the plasma spray process.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.27 no.1
• /
• pp.187-192
• /
• 2021

In this study, Inconel 625 was used as a thermal spray material to prevent dew point corrosion damage to the economizer tube, and sealing treatment was performed after applying the arc thermal spray coating technology. Various electrochemical experiments were conducted in the 0.5 wt% sulfuric acid solution to analyze the corrosion resistance of the thermal spray coating (TSC) layer. After the anodic polarization experiment, the degree of corrosion damage was determined through a scanning electron microscope and EDS component analysis. When measuring the open circuit potential, the effect of the sealing treatment was confirmed through stable potential formation of the TSC+sealing treatment (TSC+Sealing). As a result of the anodic polarization experiment, the passivation region was confirmed in TSC and TSC+Sealing, and corrosion resistance was improved as no corrosion damage was observed. In addition, the corrosion resistance of TSC+Sealing was the best when analyzing the corrosion potential and corrosion current density calculated by Tafel analysis.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.59-60
• /
• 2023

The corrosion of steel rebar embedded in the coastal areas is corroding once the chloride ions ingress through the pores of the concrete. Therefore, in the present study, a 100 ㎛ thick Al and Zn coating was deposited by an arc thermal spray process onto the steel. The corrosion studies of these deposited coatings were assessed in 3.5 wt.% NaCl contaminated concrete pore (CP) solution with immersion periods. The results show that the Al coating is more corrosion resistance compared to the Zn coating attributed to the formation of gibbsite (γ-Al(OH)₃) whereas Zn coating exhibits Zn(OH)₂ onto the coating surface as passive layer. The Zn(OH)₂ is readily soluble in an alkaline solution. Alternatively, γ-Al(OH)₃ on the Al coating surface is less solubility in the alkaline pH, which further provides barrier protection against corrosion.

• Journal of the Korea Institute of Building Construction
• /
• v.21 no.6
• /
• pp.539-550
• /
• 2021

In this study, Zn and Zn-15Al were coated on general carbon steel by plasma arc metal spraying and then immersed in a 3.5wt.% NaCl solution similar to the seawater environment to evaluate the corrosion resistance properties. Through the surface shape analysis test by SEM and XRD, it was found that the Zn coating was porous and needle-shaped, so the penetration of the electrolyte was easy, and thus the corrosion rate was rapid. On the other hand, the Zn-15Al coating had a uniform and dense shape and was shown to suppress corrosion.

• Proceedings of the KWS Conference
• /
• v.43
• /
• pp.211-212
• /
• 2004

Characteristics of the wear resistance thermal sprayed coatings was investigated in order to determine proper coating process. Hardness evaluation and microstructural observation were conducted to find relationship between coating characteristics and its wear performance. It was found that HVOF process would give better properties than arc thermal process in terms of hardness and adhesion strength which resultantly determine wear performance of the coatings.