• Journal of Electrochemical Science and Technology
• /
• v.8 no.1
• /
• pp.69-76
• /
• 2017

Crystallization of one-dimensional porous tin oxide during the anodic oxidation of tin at ambient temperatures is reported. Remarkable crystallinity is achieved when a substrate with a high elastic modulus (e.g., silicon) is used and the tin coating on it is very thin. It is suggested that the compressive stress applied to the anodic tin oxide during the anodization process is the key factor affecting the degree of crystallinity. The measured value of the stress generated during anodization matches well with the range of the most favorable theoretical pressure (stress) for crystallization.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.6
• /
• pp.393-399
• /
• 2018

Formation behavior of aluminum anodic oxide (AAO) films on Al6061 alloy was studied in view of thickness, morphology and defects in the anodic films in 20 vol.% sulfuric acid solution at a constant current density of $40mA/cm^2$, using voltage-time curve, observation of anodized specimen colors and surface and cross-sectional morphologies of anodic films with anodization time. With increasing anodizing time, voltage for film formation increased exponentially after about 12 min and its increasing rate decreased after 25 min, followed by a rapid decrease of the voltage after about 28 min. Surface color of anodized specimen became darker with increasing anodizing time up to about 20 min, while it appeared to be brighter with increasing anodizing time after 20 min. The darkened and brightened surfaces with anodizing time are attributed to an increase in thickness of porous anodic oxide film and a chemical damage of the films due to heat generated by increased resistance of the film, respectively. Cross-sectional observation of AAO films revealed the formation of defects of crack shape at the metal/oxide interface after 15 min which prevents the growth of AAO films. Width and length of the crack-like defect increased with anodizing time up to 25 min of anodizing, and finally the outer part of AAO films was partly dissolved or detached after 30 min of anodizing, resulting in non-uniform surface structures of the AAO films.

• Bulletin of the Korean Chemical Society
• /
• v.16 no.9
• /
• pp.808-810
• /
• 1995

A strong SERS effect has been observed on silver surfaces which were prepared by Ag deposition in anodic aluminum oxide nanotemplates and subsequent partial removal of the oxide layers. The advantage of these surfaces for SERS studies is that the controlled size and dispersion of Ag particles can be achieved.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.34 no.4
• /
• pp.242-245
• /
• 2021

In this work, we fabricated oxide on an n-type silicon substrate through local anodic oxidation (LAO) using atomic force microscopy (AFM). The resulting oxide thickness was measured and its correlation with load force, scan speed and applied voltage was analyzed. The surface oxide layer was stripped using a buffered oxide etch. Ohmic contacts were created by applying silver paste on the silicon substrate back face. LAO was performed at approximately 70% humidity. The oxide thickness increased with increasing the load force, the voltage, and reducing the scan speed. We confirmed that LAO/AFM can be used to create both lateral and, to some extent, vertical shapes and patterns, as previously shown in the literature.

• Journal of Sensor Science and Technology
• /
• v.17 no.1
• /
• pp.9-14
• /
• 2008

In this paper, the gas responses of tungsten oxide films prepared by anodic reaction was discussed. Sensing electrodes and heating electrodes were patterned by photolithography method on quartz substrate. Porous tungsten oxide was fabricated in electrolyte solutions of 5 % HF (HF :$C_2H_6OH:H_2O$=3 : 2 : 20) by anodic reaction. The anodic reaction with metal (platinum wire) as a cathode and the sensing device as an anode was conducted under the various reaction times (1-10 min) at 10 mA/$cm^2$ The surface structure and morphology of the fabricated sensor have been analysed by X-ray diffraction (XRD) and field-emission scanning electron microscopy (FE-SEM). All the peaks of XRD results were well indexed to the pure phase pattern. The average diameter of the porous tungsten oxide surface were ranged about 100 nm. The fabricaed sensor showed good sensitivity to 200 ppm toluene at operating temperature of $250^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.12 no.2
• /
• pp.121-128
• /
• 2002

Anodic alumina layer can be used as templates for preparation of nano-structured materials, because porous oxide layer on aluminum shows a uniform pore size and a high pore density. In order to find out possibility for template material to prepare nano wire, the effects of the anodic applied potential, anodic time and the temperature of electrolyte on pore diameter of anodic alumina layer were studied using SEM and AFM. The pore diameter of anodic alumina layer increased with applied anodic potential and electrolytic temperature. Especially, the pore diameter of anodic oxide layers formed in chromic acid can be well replicated by widening process in $H_3$$PO_4$solution.

• Journal of the Korean institute of surface engineering
• /
• v.33 no.5
• /
• pp.309-318
• /
• 2000

The 6063 Aluminium alloy were electrocolored and anodized at the same time in addition of $CoSO_4$, $FeSO_4$, in the electrolyte and investigated by AES/SAM. It was found that the thickness of anodic oxide film is increased linearly in DC type, and DC combined AC type, the more ratio of anodic Portion in AC, the more increased of anodic film thickness. The color of anodic film was changed from silver to yellow when the increase of the ratio of cathodic portion in AC. Also the increase of $CoSO_4$, $FeSO_4$ in the electrolyte, the coloring time is decreased. From the AES/SAM results, the element of anodic oxide film are Al,O and S. The result of depth profile, the most of the S distributed on the surface and the more S is in DC combined AC type than only DC type.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.900-903
• /
• 2003

Using $DV-X{\alpha}$ method, it is calculated that nickel reduces the energy band gap of manganese oxide in 3 additives of titanium, nickel and tin. Therefore, it is estimated that the electrical conductivity of manganese-nickel oxide has the lowest value in 3 kinds of manganese oxide. The manganese oxide and manganese-nickel oxide which were produced by anodic deposition under $30mA/cm^2$ at room temperature in manganese sulfate and manganese-nickel sulfate solution were thermal-analyzed by DTA and TGA. The weight change of manganese oxide continuously decreased below $508^{\circ}C$ and kept constant at $518{\sim}600^{\circ}C$. However, the manganeses-nickel oxide transformed at the temperature range of $510{\sim}537^{\circ}C$. It is observed that the nickel addition to manganese oxide increases transformation temperature and its range.

• Journal of the Korean Society for Precision Engineering
• /
• v.21 no.4
• /
• pp.186-193
• /
• 2004

Porous anodic alumina has been used widely for corrosion protection of aluminum surfaces or as dielectric material in micro-electronics applications. It exhibits a homogeneous morphology of parallel pores which can easily be controlled between 10 and 400nm. It has been applied as a template for fabrication of the nanometer-scale composite. In this study, mechanical properties of the AAO structures are measured by the nano indentation method. Nano indentation technique is one of the most effective methods to measure the mechanical properties of nano-structures. Basically, hardness and elastic modulus can be obtained by the nano-indentation. Using the nano-indentation method, we investigated the mechanical properties of the AAO structure with different size of nano-holes. In results, we find the hole effect that changes the mechanical properties as size of nano hole.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.144-149
• /
• 2004

Porous anodic alumina has been used widely for corrosion protection of aluminum surfaces or as dielectric material in micro-electronics applications. It exhibits a homogeneous morphology of parallel pores which can easily be controlled between 10 and 400nm. It has been applied as a template for fabrication of the nanometerscale composite. In this study, mechanical properties of the AAO structures are measured by the nano indentation method. Nano indentation technique is one of the most effective method to measure the mechanical properties of nano-structures. Basically, hardness and elastic modulus can be obtained by the nano-indentation. Using the nano-indentation method, we investigated the mechanical properties of the AAO structure with different size of nano-holes. In results, we find the hole effect that changes the mechanical properties as size of nano hole.