Amorphous $Al_2O_3$ nanotubes have been fabricated by utilizing the ZnO nanowires as template with wet etching method. ZnO nanowires synthesized by thermal evaporation are conformally coated with $Al_2O_3$ by atomic-layer deposition(ALD) method. The $Al_2O_3$-coated ZnO nanowires are of core-shell structure; ZnO core nanowires and $Al_2O_3$ shells. When the $ZnO/Al_2O_3$ core-shell structure is dipped in $H_3PO_4$ solution at $25^{\circ}C$ for a 6 min, the core ZnO materials are completely etched, and only $Al_2O_3$ nanotubes are remained. This nanotube fabrication is technically easier than others, and simply approachable. Transmission electron microscopy shows that the $Al_2O_3$ nanotubes have various thicknesses that can be controlled.

• Journal of Magnetics
• /
• 제11권3호
• /
• pp.126-129
• /
• 2006

The phosphate coating on the $(Fe_{0.97}Cr_{0.03})_{76}(Si_{0.5}B_{0.5})_{22}C_2$ amorphous powders with an average size of 10 ${\mu}m$ in diameter has been carried out in aqueous 1.0-2.0 wt% $H_3PO_4$ solutions, and the consolidation behavior and magnetic properties of their compressed powder cores has been investigated. The phosphate coating could provide efficient electrical insulation between amorphous powders and improved consolidation ability at room temperature. Especially when the powders were treated in more concentrated phosphoric acid solution, enhanced phosphate covering and higher frequency/dc-bias stability were achieved. The powder cores phosphate-coated in 2.0 wt% $H_3PO_4$ solution exhibited constant permeability of 21 up to 10 MHz, 110 of the quality factor at 0.9 MHz, 610 mW/cm3 core loss at 100 kHz/0.1 T and 89 of percent permeability at 100 kHz.

• Journal of Magnetics
• /
• 제20권2호
• /
• pp.138-147
• /
• 2015

The unique nano-scale inter-lamellar microstructure and unparalleled heat treatment process give our developed metal powder composite its outstanding magnetic property for power inductor & motor applications. Compared to the conventional polycrystalline Fe or amorphous Fe-Cr-Si-B alloys, our unique designed inter-lamellar microstructure strongly decreases the intra-particle eddy current loss at high frequencies by blocking the mutual eddy currents. The combination of optimum permeability, magnetic flux and extremely low core loss makes this powder composite suitable for high frequency applications well above 10 MHz. Moreover, it can be also possible to SMC core for high speed motor applications in order to increase the motor efficiency by decreasing the core loss.

• 한국자기학회지
• /
• 제10권5호
• /
• pp.191-195
• /
• 2000

Fe$_{78}$Si$_{9}$B$_{13}$ 비정질 합금을 스위칭 전원의 평활용 쵸크 코어로 사용하기 위한 최적 열처리 조건을 조사하였다. 코어의 모양은 자기경로 상에 공극을 넣지 않는 무공극형으로 하였으며, 보다 효과적으로 쵸크 코어 특성을 얻기 위해 산화 분위기 중에서 열처리하였다. 이 합금에서 가장 양호한 쵸크 코어 특성은 44$0^{\circ}C$, 2시간의 열처리에 의하여 얻어졌으며, 그 때의 실효투자율은 180 정도로서 수 MHz의 높은 주파수 영역에 이르기까지 그 크기가 일정하게 유지되었다. 또 12A가지의 직류 바이어스 전류 또는 8,000 A/m의 직류 바이어스 자장을 가하여도 실효투자율의 저하가 나타나지 않는 우수한 직류중첩 특성을 나타내었다. 그리고 교류 자심 손실도 종래의 쵸크 코어에 비해 상당히 낮은 것으로 나타났다. 이와 같은 열처리 조건하에서 비정질상은 미세한 $\alpha$-Fe 결정상의 석출 입자를 포함하는 혼합상으로 변태하는데 , 상기의 쵸크코어 특성은 주로 이들 미세 결정 입자에 의해 효과적으로 자벽 이동이 억제되고 자구가 미세화 되는 것에 기인하는 것으로 생각되었다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2013년도 춘계학술대회 논문집
• /
• pp.1271-1272
• /
• 2013

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 1994년도 춘계연구발표회 논문개요집
• /
• pp.26-27
• /
• 1994

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 영호남학술대회 논문집
• /
• pp.13-16
• /
• 2000

In this study, we have fabricated nonequilibrium $Fe_{85.6}Zr_{3.3}B_{5.7}Ag_{5.4}$ thin film, which contains an additional insoluble element Ag, by using DC magnetron sputtering method. We have investigated the magnetic properties of amorphous $Fe_{85.6}Zr_{3.3}B_{5.7}Ag_{5.4}$ thin film as a function of rotational field annealing(RFA). After deposition, the amorphous $Fe_{85.6}Zr_{3.3}B_{5.7}Ag_{5.4}$ thin film annealed by rotational field annealing method at $350^{\circ}C$ for an hour was founded to have high permeability of 8680 of 100 MHz, 0.2 mOe, low coercivity of 0.86 De and very low core loss of 1.3 W/cc at 1 MHz, 0.1T.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.478-482
• /
• 1995

The iron-based Metglas 2605S3A amorphous alloy ribbons are annealed at $435^{\circ}C$ for various periods from 5 to 210 min, and the effect of annealing is investigated on the dc magnetic properties of the ribbon. Typical square-type hysteresis loops are observed for the ribbons annealed fo 5 min, indicative of the nearly complete removal of residual stresses which are produced during melt-quenching. As the annealing time increases, the coercivity increases and the shape of hysteresis loops transforms to round type and finally to sheared one at the longest annealing time of 210 min. These results may be explained by the formation of clusters with chemical shortorder and very fine crystallites (at the annealing time of 210 min), and the diffusion-induced stresses during the formation of the clusters. For the samples annealed for 5 min, very good dc properties of the squareness ratio, coercivity and maximum permeability are observed, but, rather unexpectedly, the initial permeability is found to be very low. These results are considered to be due to a simple domain structure consisting of very small number of $^{\circ}$ domains.

• 한국자기학회지
• /
• 제25권3호
• /
• pp.67-73
• /
• 2015

본 연구는 철기(Fe based) $Fe_{73.5}Si_{13.5}B_9Nb_3Cu_1$ 나노결정 합금의 분말코어(powder core)의 연자기적 특성 향상을 위한 기초연구로서, 절연 코팅제의 첨가량 및 분말입도에 따른 투자율, 코어손실 및 DC 바이어스 특성을 주로 조사하였다. 우선 합금조성을 PFC 장치를 이용하여 비정질 합금리본을 제조한 후, 열처리, 미분쇄 및 분급하여 얻어진 합금분말에 절연 코팅제(PEI)의 첨가량을 0.5, 1.0, 2.0, 2.5 wt%로 변화시켜 $16ton/cm^2$으로 압축성형 및 결정화 열처리하여 제조한 토로이달 나노결정 분말코어($OD12.7mm{\times}ID7.62mm{\times}H4.75mm$)는 절연 코팅제 함량이 증가할수록 투자율은 감소하였지만, 코어손실 및 DC 바이어스 특성은 향상됨을 확인하였다. 이러한 이유는 합금분말 절연 코팅제 첨가량이 증가할수록 비정질 합금분말 입자가 적어져 분말코어의 성형밀도가 낮아지기 때문으로 추정되었으며, 절연 코팅제의 함량은 1 wt%가 가장 적합한 것으로 판단되었다. 또한 절연 코팅제 함량을 1 wt%로 고정하고, 합금분말의 입도에 따라 제조한 분말코어의 경우, 실효투자율 및 코어손실은 입도가 클수록 우수하였지만, DC 바이어스 특성은 인가자장이 증가함에 따라 더욱 나빠짐을 확인하였다. 그 이유는 합금분말 표면의 코팅층 두께 차이에 의한 절연효과, 잔류기공 혹은 분말코어의 성형밀도 차이 등에 기인하는 것으로 추정되었다.

• 한국자기학회지
• /
• 제9권6호
• /
• pp.285-290
• /
• 1999

고투자율 및 고포화자화 특성을 동시에 만족하는 새로운 연자성 박막을 개발하기 위해 Fe-Zr-B계 조성에 Fe원소와 비고용 원소인 Ag를 첨가시킨 Fe86.7Zr3.3B4Ag6 비정질 박막을 DC 마그네트론 스퍼터링법으로 제조한 후 일축 자장중에서 1시간 동안 진공 열처리를 한 후 fan을 이용하여 냉각하여 특성을 조사하였다. Fe86.7Zr3.3B4Ag6 박막을 40$0^{\circ}C$에서 열처리한 후 1.7T의 높은 포화자화와 1 Oe의 낮은 보자력으로 인해 50 MHz에서 투자율이 7,800(0.2 mOe)으로 우수한 연자기 특성을 나타내었으며, 1 MHz에서 손실이 1.4 W/cc(B=0.1T)로 매우 낮았다. 이러한 고주파 연자기 특성은 Ag 첨가에 의해 비정질 기지에 미세한 bcc $\alpha$-Fe cluster가 균일하게 형성되었기 때문이라 생각된다.