• 한국전기전자재료학회논문지
• /
• 제29권6호
• /
• pp.380-385
• /
• 2016

Thermal characteristics of 20 W LED module on light thermal conductive plastic (TCP) heat sink were investigated in comparison with that on aluminum die casting alloy (ADC-12). Thermal simulations of the heat sinks were conducted by using flow simulation of SolidWorks with the following input parameters: density is 1.70 and $2.82kg/m^2$, thermal conductivity is 20 and $92W/(m{\cdot}K)$ for TCP and ADC-12, respectively. The simulated and measured temperatures of the LED modules on TCP heat sink were consistent with its measured temperature, which was $3^{\circ}C$ higher that on ADC-12. The fabricated LED module on TCP heat sink with a weight of 120.5 g was 30% lighter in weight than that of the ADC-12 reference with 171.0 g.

• 한국재료학회지
• /
• 제14권3호
• /
• pp.168-174
• /
• 2004

The aim of this study is to investigate the effect of process conditions on the microstructual changes and mechanical properties of large 7175 aluminum die forgings. The cast billets of 370 and 720 mm in diameter were homogenized and die forged after direct chill casting. The size and volume fraction of second phase particles in 720 mm billet were larger than those of 370 mm billet. The interdendritic sites containing the second phase particles was considered to be a crack initiation region in the process of cold upsetting. The tensile and yield strength of die forged specimens of 720 mm billet in the direction of Land L T were higher than those of 370 mm billet. However, the tensile strength of these specimens were 5 to 10% lower than that of American military specification. The plane strain fracture toughness of die forged specimens of 370 mm cast billet showed almost the same level of 720 mm billet, which was die forged after free forging.

• 한국주조공학회지
• /
• 제22권3호
• /
• pp.130-136
• /
• 2002

The growing use of aluminum for castings over the past decade has brought with it the increased scrutiny of component properties. One area that has received much attention is the effect of in inclusions - or impurities particles held in the metal - on casting properties. A new method of electromagnetic separation for removal of inclusions in aluminum alloy melts is proposed. The principle is that as the electromagnetic force induced in metal acts on inclusions due to low electric conductivity, they are moved to the direction opposite to electromagnetic force and can be separated and removed from the melt. Experiments were carried out on A356 melt mixed alumina particles and commercial Al alloys of ADC 10 and 12. In the experiment using A356, it was proved that $Al_2O_3$ particles was separated and removed continuously from matrix melt by electromagnetic force. Based on these results, the continuous separation experiment that used ADC 10, 12 was carried and the cleanliness of melt was assessed by the amount of porosity, hydrogen contents, PoDFA and mechanical properties through tensile test. As the results of analyses, the amount of porosity and hydrogen contents decreased without variation of chemical composition in the specimen that passed the electromagnetic continuous separator. In addition, tensile strength and elongation of this specimen increased by $20{\sim}30%$ because of reduction of inclusions.

• 한국추진공학회지
• /
• 제16권5호
• /
• pp.81-88
• /
• 2012

액체로켓엔진의 핵심부품인 터보펌프의 경량화를 위하여 케이싱에 알루미늄 합금 소재를 도입하였고 생산성 향상 및 생산 단가의 절감을 위하여 주조 공법을 도입하였다. 부품의 신뢰도가 생명인 액체로 켓엔진에 주조를 사용하기 위하여 올바른 주조 규격 수립 및 주조 공법의 최적화, 그리고 주조된 제품의 다방면에 걸친 철저한 검증을 실시하는 것이 필수적이다. 이번 연구에서는 알루미늄 합금인 A356.0-T6 합금을 이용하여 연료펌프 입구케이싱을 주조하였으며 주조 품질의 기본적인 구조 검증을 위하여 파열시험을 수행하였다. 주조된 형상에 맞추어 구조해석을 실시하여 파열 시점을 예측하였으며 파열시험 시 제품에 부착된 스트레인게이지를 이용하여 해석을 통한 변형률 예측과 비교하였다.

• 소성∙가공
• /
• 제26권5호
• /
• pp.306-313
• /
• 2017

This study investigated the microstructure, tensile strength, and high cycle fatigue properties of ADC12 aluminum alloys with different $Mg+Al_2Ca$ contents manufactured using die casting process. Microstructural observation identified the presence of ${\alpha}-Al$, eutectic Si, $Al_2Cu$, and Fe-intermetallic phases. The increase of $Mg+Al_2Ca$ content resulted in finer pore size and decreased pore distribution. Room temperature tensile strength tests were conducted at strain rate of $1{\times}10^{-3}/sec$. For 0.6%Mg ADC12, measured UTS, YS, and El were 305.2MPa, 157.0MPa, and 2.7%, respectively. For 0.8%Mg ADC12, measured UTS, YS, and El were 311.2 MPa, 159.4 MPa, and 2.4%, respectively. Therefore, 0.8% ADC12 alloy had higher strength and slightly decreased elongation compared to 0.6% Mg ADC12. High cycle fatigue tests revealed that 0.6% Mg ADC12 alloy had a fatigue limit of 150 MPa while 0.8% Mg ADC12 had a fatigue limit of 160MPa. It was confirmed that $Mg+Al_2Ca$ added ADC12 alloy achieved finer, spherical eutectic Si particles, and $Al_2Cu$ phases with greater mechanical and fatigue properties since size and distribution of pores and shrinkage cavities decreased as $Mg+Al_2Ca$ content increased.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1995년도 특별강연 및 춘계학술발표 개요집
• /
• pp.155-159
• /
• 1995

A16061 alloy reinforced with 10 vol% $\delta$-A1$_2$O$_3$ short fiber have been fabricated by Rheo-compocasting and squeeze casting and extruded at high temperature using conical shape die and curved shape die with various extrusion ratios.. Tensile and hardness tests were carried out to examine mechanical properties of extruded materials and SEM observation of fractured surface was capable of accounting for fracture mechanism and bonding state of fiber and matrix.

• 열처리공학회지
• /
• 제34권6호
• /
• pp.281-286
• /
• 2021

Arc ion plating (AIP), laser cladding, and nitriding are methods that can prevent mold damage or repair and create cracks and breakages on the die surface. The dissolution and soldering behavior of coated SKD61 by using arc ion plating, laser cladding, and nitriding was investigated. The structure of the coating was investigated as a function of deposition conditions by X-ray diffraction and the crystallographic orientation was determined using the texture factor. The TiAlN film deposited with AIP showed excellent corrosion resistance in the molten aluminum alloy at 680℃. In this paper, we have detailed the corrosion and mass loss phenomena associated with these steel-cast metal interactions.

• 한국주조공학회지
• /
• 제28권3호
• /
• pp.119-123
• /
• 2008

Wear test on two die steels for aluminum die casting was carried out by dipping and rotating the specimens into the molten aluminum maintained $680^{\circ}C{\sim}780^{\circ}C$. The rotating speed of the specimen was $4.5rpm{\sim}20.0rpm$. Diffusion layer was formed between the die steel and molten aluminum, and became thicker with dipping time. Wear rate was not proportional with the thickness of the diffusion layer, but was closely related to the density of the diffusion layer. Wear rate was little affected by the kind of die steel and by the microstructure such as martensite, tempered martensite, and pearlite. Specimen with nitrided surface showed good wear resistance, and its wear rate was decreased with increase in the thickness of nitrided layer. While whole surface was worn in heat treated specimens, wear of nitrided specimens was proceeded by pitting partially.

• The Journal of Advanced Prosthodontics
• /
• 제12권2호
• /
• pp.100-106
• /
• 2020

PURPOSE. The purpose of this in vitro study was to evaluate the fitting accuracy of single crowns made from a novel presintered Co-Cr alloy prepared with a computer-aided design and computer-aided manufacturing (CAD/CAM) technique, as compared with crowns manufactured by other digital and the conventional casting technique. Additionally, the influence of oxide layer on the fitting accuracy of specimens was tested. MATERIALS AND METHODS. A total of 40 test specimens made from Co-Cr alloy were investigated according to the fitting accuracy using a replica technique. Four different methods processing different materials were used for the manufacture of the crown copings (milling of presintered (Ceramill Sintron-group_cer_sin) or rigid alloy (Tizian NEM-group_ti_nem), selective laser melting (Ceramill NPL-group_cer_npl), and casting (Girobond NB-group_gir_nb)). The specimens were adapted to a resin model and the outer surfaces were airborne-particle abraded with aluminum oxide. After the veneering process, the fitting accuracy (absolute marginal discrepancy and internal gap) was evaluated by the replica technique in 2 steps, before removing the oxide layer from the intaglio surface of the crowns, and after removing the layer with aluminum oxide airborne-particle abrasion. Statistical analysis was performed by multifactorial analysis of variance (ANOVA) (α=.05). RESULTS. Mean absolute marginal discrepancy ranged between 20 ㎛ (group_cer_npl for specimens of Ceramill NPL) and 43 ㎛ (group_cer_sin for crowns of Ceramill Sintron) with the oxide layer and between 19 ㎛ and 28 ㎛ without the oxide layer. The internal gap varied between 33 ㎛ (group_ti_nem for test samples of Tizian NEM) and 75 ㎛ (group_gir_nb for the base material Girobond NB) with the oxide layer and between 30 ㎛ and 76 ㎛ without the oxide layer. The absolute marginal discrepancy and the internal gap were significantly influenced by the fabrication method used (P<.05). CONCLUSION. Different manufacturing techniques had a significant influence on the fitting accuracy of single crowns made from Co-Cr alloys. However, all tested crowns showed a clinically acceptable absolute marginal discrepancy and internal gap with and without oxide layer and could be recommended under clinical considerations. Especially, the new system Ceramill Sintron showed acceptable values of fitting accuracy so it can be suggested in routine clinical work.

• 한국주조공학회지
• /
• 제34권4호
• /
• pp.136-142
• /
• 2014

Numerical solution of thermal stress by CAE analysis could be an effective method in product development stage of castings to predict and treat the problem of solidification cracking of castings. Quantitative stress-strain data are necessary, in this case. Tension type apparatus of a solidification crack test which can measure stress-strain relationship quantitatively was developed and the test procedure was established by this research. Solidification crack strength obtained from the following test procedure could be utilized to evaluate it in terms of effect factors on thermo-plastic characteristic of solidifying alloy such as grain size of solid, grain morphology, distribution of solid grain, etc. Proposed test procedure is as follow: Prediction of temperature at the failure site of solidification cracked specimen by computer simulation of solidification, Calculation of solid fraction of the failure site from thermodynamic solution of solidification under Scheil condition.