• Journal of the Korean Ceramic Society
• /
• v.48 no.2
• /
• pp.168-172
• /
• 2011

Alumina powder was added in a general porcelain (Backja) with clay, feldspar and quartz contents to promote the mullite ($3Al_2O_3{\cdot}2SiO_2$) generation in the porcelain. Low melting materials ($B_2O_3(450^{\circ}C)$, $MnO_3(940^{\circ}C)$, CuO($1080^{\circ}C$)) were doped at ~3 wt% to modify the sinterability of porcelain with a high alumina contents and promote the mullite generation. Green body was made by slip casting method with blended slurry and then, they were fired at $1280^{\circ}C$ for 1hr by a $2^{\circ}C/min$. Densifications of samples with high alumina contents (20~30 wt%) were impeded. As the doping contents of low melting materilas increased, the sinterability of samples was improved. The shrinkage rate and bulk density of samples were improved by doping with low melting materials. Mullite phase increased with increasing the low melting contents in the phase analyses. This means lots of alumina and quartz were transformed into mullite phase by low melting contents doping. In the results, high bending strength of samples with high alumina contents was accomplished by improving the densification and mullite generation in the porcelain.

• Journal of Powder Materials
• /
• v.30 no.3
• /
• pp.249-254
• /
• 2023

The influence of MgO addition on the densification and microstructure of alumina (Al₂O₃) was studied. Compacted alumina specimens were manufactured using ball-milling and one-directional pressing followed by sintering at temperatures below 1700℃. Relative density, shrinkage, hardness, and microstructure were investigated using analytical tools such as FE-SEM, EDS, and XRD. When the MgO was added up to 5.0 wt% and sintered at 1500℃ and 1600℃, the relative density exhibited an average value of 97% or more at both temperatures. The maximum density of 99.2% was with the addition of 0.5 wt% MgO at 1500℃. Meanwhile, the specimens showed significantly lower density values when sintered at 1400℃ than at 1500℃ and 1600℃ owing to the relatively low sintering temperature. The hardness and shrinkage data also showed a similar trend in the change in density, implying that the addition of approximately 0.5 wt% MgO can promote the densification of Al₂O₃. Studying the microstructure confirmed the uniformity of the sintered alumina. These results can be used as basic compositional data for the development of MgO-containing alumina as high-dielectric insulators.

• Journal of the Korean Ceramic Society
• /
• v.30 no.11
• /
• pp.933-940
• /
• 1993

SO42-/Al2O3 powder was prepared by the coprecipitation method from the Al(NO3)3.9H2O and NH4OH and followed by being treated with various concentrations of sulfuric acid. The characterization of these powders was performed with XRD, BET and FT-IR. The surface charge density at alumina/KCl(aq) interface was measured by potentiometric titration method. From the experimental data it was shown that acid strength, specfic surface area, and structure of surface treated alumina were independent on the amount of exchanged SO42-. However, the acid amounts of alumina were increased with the amounts of SO42- formed on alumina surface. The relation between the acid amount of SO42- ion exchanged alumina surface and the surface charge density for SO42-/Al2O3/KCl(aq) interface was investigated.

• Journal of Power System Engineering
• /
• v.18 no.6
• /
• pp.166-173
• /
• 2014

In this study, a laminated composite material with dispersing aluminum oxide powder between the CFRP laminate plies, and also CFRP composites without aluminium oxide powder were fabricated for Mode I experiments using the DCB specimen and a tensile test. The behavior of the crack and the change of the interfacial fracture toughness were evaluated. Also in order to evaluate the damage mechanism for the crack extension, the AE sensor on the surface of the DCB test specimen was attached. AE amplitude was estimated for CFRP-alumina and CFRP composite. And the fracture toughness was evaluated by the stress intensity factor and energy release rate. The results showed that an unstable crack was propagated rapidly in CFRP composite specimen along with the interface, but crack propagation in CFRP-alumina specimen was relatively stable. From results, we show that aluminium oxide powder spreaded uniformly in the interface of the CFRP laminate carried out the role for preventing the sudden crack growth.

• Journal of the Korean Ceramic Society
• /
• v.49 no.2
• /
• pp.179-184
• /
• 2012

The size of various alumina ceramics used in semiconductor and display industry is required to increase with increase in wafer and panel size. In this research, large alumina ceramics were fabricated by uniaxial pressing, cold isostatic pressing and filter pressing with commercial powder and thereafter sintering at $1600^{\circ}C$ in gas furnace. The large alumina ceramics exhibited dense microstructure corresponding to 98.5% of theoretical density and 99.8% of high purity. The impurities and microstructural defects of the alumina were found to influence the resistance and dielectric properties. The volume resistances in these four aluminas were almost the same while the pure alumina was higher value. The dielectric constant, dielectric loss and dielectric strength of aluminas were placed within the range of 10.3~11.5, 0.018~0.036, and 10.1~12.4 kV/mm, respectively.

• Journal of the Korean Ceramic Society
• /
• v.38 no.11
• /
• pp.987-992
• /
• 2001

A refractory grade low-cost silicon nitride powder was chemically analyzed, purified, and gas pressure sintered with the sintering additives. As-received powder contained a significant amount of free-Si, 0.72 wt% of Fe, 0.5 wt% of al and 0.31 wt% of Ca. Oxygen and carbon contents of the powder were 3.3 wt% and 0.4 wt%, respectively, and it consisted of 96% of $\beta$-phase and 4% of $\alpha$-phase. After lowering the Fe content and nitriding treatment, the powder was sintered with 6 wt% yttria and 2 wt% alumina for 1 h between 1823 K and 2123 K in order to examine the sintering behavior. Fully dense samples were obtained by sintering at 2123k for 2h. For comparison, a commercially available high-grade powder was also sintered at the same time. The low-cost powder showed much slower densification rate than the high-grade powder. Fully dense sample prepared from the low-cost powder contained a number of coarse grains with a low aspect ratio, and its hardness, fracture toughness, flexural strength and thermal shock resistance were not as good as those of the sample prepared with the high-grade powder.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1997.04a
• /
• pp.8-8
• /
• 1997

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.457-458
• /
• 2006

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.11
• /
• pp.7-12
• /
• 2019

Generally, end effectors for automatic robots can use ceramics such as alumina(Al₂O₃) and silicon carbide(SiC). In this study, black alumina was developed and used in the semiconductor field through powder molding press forming. The black alumina can be mass produced.Alumina and black alumina were ground using a plane grinder to apply to the end effector of an automatic robot. The optimal cutting conditionswere found by analyzing the surface roughness(Ra) of black alumina through grinding. The alumina surface roughness is the feed rate was about 0.72 mm/sec, and the number of revolutions was best at 0.4879 ㎛ at 1700 rpm. In addition, the black alumina surface roughness shows a precision of less than 0.2 ㎛ in most cutting conditions. The feed rate was about 0.72 mm/sec, and the number of revolutions was best at 0.1361 ㎛ at 1900 rpm. The surface roughness of black alumina was better than that of alumina by about 0.35 to 0.47 ㎛.

• 한국신재생에너지학회:학술대회논문집
• /
• 2005.06a
• /
• pp.310-313
• /
• 2005

The conical fluidizing system of a binary mixture of Geldart C powders and Geldart A particles was defined as the conical powder-particle fluidized bed. We used a cold conical powder-particle fluidized bed model having a 0.104m-I.D. and 0.6m-high with an apex angle of $10^{\circ}$ for fluidization of a binary powder-particle mixture of 50 $vol\%$ fine carbon black powders (HI-900L, Korea Carbon Black Co.) and coarse alumina particles $(90{\mu}m)$ under different superficial gas velocities (0-0.1 m/s). The differential bed pressure drop increases with increasing gas velocity, and it goes from zero to a maximum value with increasing or decreasing gas velocity. In the conical fluidized beds of fine powders, demarcation velocities of the partial fluidization, full fluidization, partial defluidization was not observed.