• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2002년도 춘계학술강연 및 발표대회
• /
• pp.11-11
• /
• 2002

Plastic deformation was observed by TEM around the intragranular SiC particles in the $Al_2O_3$ matrix for $Al_2O_3/SiC$ nanocomposite system. The dislocations are generated at selected planes and there is a tendency for the dislocations to form a subgrain boundary structure with low-angel grain boundaries and networks. In this study, dislocation generated in the $Al_2O_3$ matrix during cooling down from sintering temperatures by the highly localized thermal stresses within and/or around SiC particles caused from the thermal expansion mismatch between $Al_2O_3$ matrix and SiC particle was observed. In monolithic $Al_2O_3$ and $Al_2O_3/SiC$ microcomposite system. These phenomena is closely related to the plastic relaxation of the elastic stress and strain energy associated with both thermal misfitting inclusions and creep behaviors. The plastic relaxation behavior was explained by combination of yield stress and internal stress.

• 한국세라믹학회지
• /
• 제34권8호
• /
• pp.834-842
• /
• 1997

Controlled Ca impurity implanted inner crack-like pore in the high purity alumina single crystal, sapphire, had been created by micro-fabrication technique, which includes ion implantation, photo-lithography, Ar ion milling, and hot press technique. The morphological change and the healing of cracklike pore in Ca doped high purity single crystal alumina, sapphire, during high temperature heat treatment in vacuum were observed using optical microscopy. The dot-like surface roughening was developed and hexagon like crystal appeared on inner surface of crack-like pore after heat treatment. Bar type crystals, probably CaO.6Al2O3, were observed on the inner surface after 1 hour heat treatment at 1, 50$0^{\circ}C$, but this bar type crystal disappeared after 1 hour heat treatment at 1, $600^{\circ}C$. This disappearance means that there should be a little increase of Ca solubility limit to alumina at this temperatures.

• 한국세라믹학회지
• /
• 제34권11호
• /
• pp.1113-1120
• /
• 1997

The 2, 4, 6 and 8mol% Y2O3 doped-ZrO2 powders (20 kinds) with the addedtion of Al2O3 upto 8wt% were prepared by coprecipitation method using the zirconium oxyacetate, yttrium chloride and aluminum nitrate as starting materials. The coprecipitated powders were characterized by XRD, TG-DTA, FT-IR and SEM. The sintering properties of zirconia-alumina composites prepared by 2YSZ and 8YSZ powders containing various Al2O3 contents were also investigated. With increasing the yttria stabilizer contents, the amount of exothermic heat for zirconia crystallization decreased. And it was confirmed that the crystallizing temperature of coprecipitated zirconia powders increased and the crystallization process occurred in a wide temperature range, as Al2O3 content increased in 8YSZ.

• 한국재료학회지
• /
• 제2권1호
• /
• pp.3-11
• /
• 1992

점토 광물로부터 황산 처리법을 이용하여 수화 황산 알루미늄을 제조하였다. 하동 카올린 을 황산 처리하였을 때 수화 황산 알루미늄 형성에 미치는 카올린의 하소 온도와 하소 시간, 산처리 반응 온도와 반응 시간 및 황산의 농도의 영향을 조사하였다. 또한, 황산 처리된 용액으로부터 수화 황산 알루미늄이 석출되는 최적 조건을 구하였으며, 생성된 수화 황산 알루미늄을 상온에서 $1200^{\circ}C$ 까지 각각의 온도 구간에서 열처리한 분말에 대해서 XRD, TG-DTA, FT-IR, SEM, 입도 분석 및 불순물 분석을 하였다. 최적 조건 하에서, 카올린 중의 알루미나가 수화 황산 알루미늄으로 생성되는 전화율은 약 60%였고, XRD, TG-DTA, FT-IR 등의 분석 결과로 부터 생성된 수화 황산 알루미늄의 열분해 반응은 $Al_2(SO_4)_3{\cdot}18H_2O{\rightarrow}Al_2(SO_4)_3{\cdot}6H_2O{\rightarrow}Al_2(SO_4){\rightarrow}\;amorphous\;alumina{\rightarrow}{\gamma}-alumina{\rightarrow}{\delta}-alumina{\rightarrow}{\theta}-alumina{\rightarrow}{\alpha}-alumina$이었다. 또한 생성된 수화 황산 알루미늄을 $1200^{\circ}C$에서 하소 하여 얻은 알루미나 분말의 순도는 99.99%였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 하계학술대회 논문집 Vol.9
• /
• pp.314-314
• /
• 2008

The low temperature sintering and the dielectric properties of $Al_2O_3/SiO_2$-zinc borosilicate glass composites were investigated in the view of the application for LTCC. When the sintering was conducted at $900^{\circ}C$ $ZnAl_2O_4$ and $ZnB_2O_4$ compounds formed at the $Al_2O_3$-rich and the $SiO_2$-rich compositions, respectively. The reaction between ZBS glass and $Al_2O_3/SiO_2$ caused the formation of these compounds. The $Al_2O_3/SiO_2$ ratio affected the dielectric properties. The excellent dielectric properties, i.e., Q$\times$f value= 40,000 GHz and ${\varepsilon}_r$=4.5, were obtained in the $Al_2O_3/SiO_2$-ZBS glass system and fabricated the LTCC substrate materials.

• 공학논문집
• /
• 제3권1호
• /
• pp.215-222
• /
• 1998

촉매 연소용 촉매 담체인 $\gamma-Al_2O_3$ 분말의 열안정화에 미치는 La과 Si의 첨가 효과에 대하여 연구하였다. 첨가제의 첨가는 습식 impregnation방법으로 행하였고, 출발 물질은 $La(NO_3)_3{\cdot}6H_2O$와 $Si(OC_2H_5)_4$를 사용하였다. 열안정화 효과는 혼합분말을 고온에서 열처리 한 후 비표면적을 측정하여 고찰하였다. 첨가제로 첨가한 La과Si는 모두 순수한 $\gamma-Al_2O_3$분말에 비하여 소결을 억제함으로써 열 안정화 효과가 있음이 확인되었으며, 특히 Si 첨가한 경우에는 $\alpha-Al_2O_3$의 생성을 현저히 억제한다는 것을 확인하였다. 이들 첨가제에 의한 열안정화 효과는 첨가제에 의한 새로운 상의 생성과 표면 확산의 억제등이 주된 요인으로 판단되었다.

• 한국세라믹학회지
• /
• 제34권6호
• /
• pp.591-600
• /
• 1997

Al2O3/Al composites were produced by displacement reaction method, which was carried out by immersing the sintered silica preform, which was prepared from fused silica powder, in molten aluminum. Because the molten aluminum did not penetrate into the silica preform with higher than 20% of porosity when the displacement reaction was accomplished at 100$0^{\circ}C$ for 10 hours in air atmosphere, the optimum range of sintering temperature of silica preform was from 135$0^{\circ}C$ to 140$0^{\circ}C$. The microstructure of this Al2O3/Al composites showed three-dimentionally co-continuous alumina, which provides wear resistance and high stiffness, and aluminium which acts as a toughnening phase. The grain size of the alumina in composites did not change with the particle size of the silica preform. The exact shape of the preform was retained and a net-shaped composite was produced. The representative Al2O3/Al composite prepared in this study showed 3.30mg/㎤ of bulk density, 350-430 MPa of flexural strength, 7.0 MPa.m1/2 of fracture toughness, and good machinability.

• 한국세라믹학회지
• /
• 제29권1호
• /
• pp.23-28
• /
• 1992

Alumina ceramics was reinforced by in-situ formation of La-${\beta}$-aluminate in ${\alpha}$-alumina matrix. The powder mixture of which composition is (100-12x)Al2O3+x(La2O3+11Al2O3) was prepared for the formation of La-${\beta}$-aluminate in ${\alpha}$-alumina matrix. The amount of La-${\beta}$-aluminate in the matrix was controlled by varing x which is number of moles. The dense composite was produced by sintering at 1600$^{\circ}C$ in air or hot-pressing at 1550$^{\circ}C$ under 30 MPa. Bending strength and fracture toughness were increased, resulting from the grain growth inhibition and the crack deflection and crack bridging mechanism when La-${\beta}$-aluminate was produced in ${\alpha}$-alumina matrix.

• 한국세라믹학회지
• /
• 제33권10호
• /
• pp.1138-1146
• /
• 1996

Al2TiO5 powder was prepared by the sol-gel processing from th metal alkoxides ; aluminium sec-butoxide (Al(OC4H9)3 and tetraethyl orthotitanate (Ti(OC2H5)4) The particles of Al2TiO5 produced from alkoxides were measured to be below $1.5mutextrm{m}$ and mre than 90% weere below 1 ${\mu}{\textrm}{m}$ however those from commercial alumina and titania were over 0.5-7${\mu}{\textrm}{m}$ and only 60% were below 1${\mu}{\textrm}{m}$ and 90% were below 2.5${\mu}{\textrm}{m}$ Therefore Al2TiO5 powder produced from alkoxides had the narrower distributionin size than that produced from the commercial alumina and titania powders. The addition of mullite or Al2O3 powder to the prepared aluminum titanate inhibited the grain growth and this resulted in decreased and increase in density.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 추계학술대회 논문집
• /
• pp.81-81
• /
• 2009

Non-sintered Alumina films were fabricated via inkjet printing processes without a high temperature sintering process. The packing density of these inkjet-printed alumina films measured around 60%. Polymer resin was infiltrated thru these non-sintered films in order to fill out the 40% of voids constituting the rest of the inkjet-printed films. The concept of inkjet-printed Alumina-Resin hybrid materials was designed in order to be applicable to the ceramic package substrates for 3D-system module integration which may possibly substitute LTCC-based 3D module integration. So, the dielectric properties of these inkjet-printed $Al_2O_3$ hybridmaterialsareofourgreatinterest. We have measured dielectric constant and dissipation factor of the inkjet-printed $Al_2O_3$-resinhybridfilmsbyvaryingtheamountofresininfiltratedthruthe$Al_2O_3$films.