Precast concrete produced in the industry is advantage that easy to manage, and it save construction period in the field. The specimens according to the type of activator for AAS(Alkali-Activated Slag) mortar cured in an autoclave. The specimens of AAS mortar with sodium was shown the high rate of increase of the compressive strength.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.04a
• /
• pp.115-116
• /
• 2022

This study incorporates fine waste glass (GS) as a replacement for natural sand (NS) in fly ash (FA) based alkali activated mortar (AAm). AAms were heated at elevated temperature of 200℃, 400℃, 600℃, and 800℃ to explore the residual mass, compressive strength, thermal expansion and change in microstructure of matrix. Results showed greater resistance of AAms with increasing GS content to 50% at each temperature. Owing to the melting of GS at 800℃, the greater matrix bond was observed for AAm incorporating 75% and 100% GS as a result, the residual compressive strength was increased.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.613-616
• /
• 2008

Many researches on alkali-activated concrete that does not need the presence of cement as a binder have been carried out recently. Instead, the source of material such as fly ash and blast slag, that are rich in Silicon(Si) and Aluminium(Al), are activated by alkaline liquids to produce the binder. Hence concrete with no cement is effect reduction of CO$_2$ gas. In this study, we investigated the influence of the workability and compressive strength of mortar on water reducing agent, alkaline activator and curing method in oder to develop cementless blast slag based alkali-activated mortar. In view of the results, we found out that the flowability of mortar was lowered as increasing to mole concentration of NaOH, but not large the loss of flowability to 9M NaOH, most of water reducing agent was not effect. The compressive strength was improved as increasing to mole concentration of NaOH, was the most effect in 9M NaOH. The curing temperature and curing conditions on compressive strength of blast slag based alkali-activated mortar didn't influence.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.205-206
• /
• 2016

This study examines the effect of binding material and alkali activator on the rheology characteristics of alkali active mortar quantitatively, and a result is as follows. In the 1/2 slump flow, the higher mixing ratio of the fly ash has been shown to increase the table flow. the reason is that fly ash ball bearing action. When viewed in the consistency curve, the higher mixing ratio of the blast furnace slag powder was higher shear stress.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.27-32
• /
• 2002

In this research influences of type and concentration of alkali activator and curing condition on the hydration, and properties of alkali activated blast furnace slag(AAS) concrete were investigated. Sodium carbonate and sulfate were used as alkali activators and their concentration were 4~10 weight percent with Na$_2$O equivalent to binder. The curing conditions were standard curing using 23$^{\circ}C$ water and activated curing chamber at $65^{\circ}C$. Results show that in case of sodium carbonate addition high early strengths were gained by activation of early hydration, but later strength gained was slight. On the other side sodium sulfate strengths were continuously increased with adding amount and ages. Steam curing activated early hydration so that early strengths were improved but later strengths were similar to standard curing. The strength reduction of AAS mortar with sodium sulfate was less than OPC mortar in 5% sulfuric acid solution so that AAS concrete can be useful for acid-resistance concrete.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.1
• /
• pp.63-71
• /
• 2011

Portland cement production is under critical review due to high amount of $CO_2$ gas released to the atmosphere. Attempts to increase the utilization of a by-products such as fly ash and ground granulated blast-furnace slag to partially replace the cement in concrete are gathering momentum. But most of by-products is currently dumped in landfills, thus creating a threat to the environment. Many researches on alkali-activated concrete that does not need the presence of cement as a binder have been carried out recently. In this study, we investigated the influence of alkali activator and superplasticizer on the flowability and compressive strength of the alkali-activated mortar in oder to develop cementless alkali-activated concrete using blast furnace slag. In view of the results, we found out that the type and mixture ratio of alkali activator, the type and adding order of superplasticizer results to be significant factors. When cementless alkali-activated mortar using blast furnace slag manufactured with 1:1 the mass ratio of 9M NaOH and sodium silicate, and added superplasticizer before alkali activator in the mixer, we can be secured workability with 180 mm of flow during 1 hours and compressive strength of about 50 MPa under $20^{\circ}C$ curing condition at age of 28days.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.393-394
• /
• 2009

Recently, various researchers have studied alkali-activated concrete that do cementless as the binder. This study analyzed the effect on alkali-activated mortar by fineness of blast slag as the binder with no use of cement, by observing workability and compressive strength.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.6
• /
• pp.26-33
• /
• 2012

This paper reported on the effect of blended activator on the physical properties of alkali-activated slag mortar. Five different activators(caustic alkalis) were used: sodium hydroxide(NaOH, A Case), calsium hydroxide($Ca(OH)_2$, B Case), magnesium hydroxide($Mg(OH)_2$, C Case), aluminum hydroxide($Al(OH)_3$, D Case), and potassium hydroxide(KOH, E Case). We blended five caustic alkalis with sodium carbonate($Na_2CO_3$). The dosage of five caustic alkalis was 3M and sodium carbonate was 1M, 2M and 3M. The result of flow and setting time was decrease as the dosage of sodium carbonate increase. But the compressive strength was increase as the dosage of sodium carbonate increase. It was shown that there is a good effect of blended caustic alkalis with sodium carbonate in alkali-activated slag mortar.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.1 no.1
• /
• pp.58-66
• /
• 2013

This study investigated quality properties of alkali activated cement free mortar using industrial by-product such as cement kiln dust(CKD), silica fume(SF) and quartz sand powder(SP) to compare with previous research about blast furnace slag(BS) and fly ash(FA). The results were as following. All materials were effective to increase compressive strength, however they showed different tendency on flowability. CKD and SP increased flowability, but on the other hand SF did not because it's blain was great difference with other materials. Flowability and compressive strength were related with grading distributions of binders because CKD, SP and SF which had small particle size filled up BS and FA. Application of industrial by-products with various grading distributions could be effective for the high early strength and flowability of alkali activated cement free mortar using BS.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.627-630
• /
• 2005

This paper examines degradation properties of alkali-activated alumino-silicate composite body by NAS solution exposed to high temperature. Activators include sodium hydroxides and sodium silicate solution. In the result of experiment, flexural and compressive strength of AAS base mortar exposed to high temperature ($400\~600^{\circ}C$) was higher than alumina cement base mortar. Particularly, In case of compressive strength, alumina cement base mortar was decreased by about $60\~70\%$. While, AAS base mortar exposed to high temperature ($400\~600^{\circ}C$) was higher than that curing by room temperature. The above results showed that AAS base inorganic binder has a good mechanical properties exposed to high temperature($400\~600$).