• Clean Technology
• /
• v.15 no.4
• /
• pp.273-279
• /
• 2009

$SF_6$, which has a high global warming potential, can be decomposed to sulfur and fluorine compounds through hydrolysis by $H_2O$ or oxidation by $O_2$ over solid acid catalysts. In this study ${\gamma}-Al_2O_3$ was employed as the solid acid catalyst for the abatement of $SF_6$ and its catalytic activity was investigated with respect to the reaction temperature and the space velocity. The catalytic activity for $SF_6$ decomposition by the hydrolysis reached the maximum at and above 973 K with the space velocity of $20,000\;ml/g_{-cat}{\cdot}h$, exhibiting a conversion very close to 100%. When the space velocity was lower than $45,000\;ml/g_{-cat}{\cdot}h$, the conversion was maintained at the maximum value. On the other hand, the conversion of $SF_6$ by the oxidation was about 20% under the same conditions. The SEM and XRD analyses revealed that the ${\gamma}-Al_2O_3$ was transformed to ${\alpha}-Al_2O_3$ during the hydrolysis and to $AlF_3$ during the oxidation, respectively. The size of $AlF_3$ after the oxidation was over $20\;{\mu}m$, and its catalytic activity was low due to the low surface area. Therefore, it was concluded that the hydrolysis over ${\gamma}-Al_2O_3$ was much more favorable than the oxidation for the catalytic decomposition of $SF_6$.

• Journal of the Korean Society for Heat Treatment
• /
• v.6 no.4
• /
• pp.237-242
• /
• 1993

The fatigue behaviors of mechanically alloyed Al-4Mg alloys dispersed with either $Al_2O_3$ or $MgAl_2O_4$ oxide particles were investigated. This study maily concerned with the role of coherency of dispersed particles with the matrix on the fatigue behavior of the alloys. The $MgAl_2O_4$ which has a spinel structure with the lattice parameter of exactly the twice of Al showed the habit relation with the matrix. The mechanically alloyed Al-4Mg alloys showed stable stress responses with fatigue cycles from start to failure regadless of strain amplitudes and of existence of dispersoids. The Al-4Mg alloy dispersed with $MgAl_2O_4$ showed not only the better static mechanical properties but also the better low cycle fatigue resistance than that with $Al_2O_3$, i.e., much higher plastic strain energy dissipated to failure, at low strain amplitude. However, this alloy showed inferior fatigue resistance to that dispersed with $Al_2O_3$ or that without dispersion at high strain amplitude. These results imply that $MgAl_2O_4$ may promote lowering the stacking fault energy of the alloy inherited from the coherency with the matrix so that dislocations shuttle back and forth on the same slip plane without cross slipping to other planes during fatigue at low strain amplitude resulting in long fatigue life.

• Korean Journal of Materials Research
• /
• v.27 no.7
• /
• pp.374-380
• /
• 2017

Properties of coatings produced by warm spray were investigated in order to utilize this technique as a repair method for Al tire molds. $Al-(0-10%)Al_2O_3$ composite powder was sprayed on Al substrate by warm spraying, and the microstructure and mechanical properties of the composite coating layer were investigated. For comparative study, the properties of the coating produced by plasma spray, which is a relatively high-temperature spraying process, were also investigated. The composite coating layers produced by the two spray techniques exhibited significantly different morphology, perhaps due to their different process temperatures and velocities of particles. Whereas the $Al_2O_3$ particles in the warm sprayed coating layer maintained their initial shape before the spray, flattened and irregular shape $Al_2O_3$ particles were distributed in the plasma sprayed coating layer. The coating layer produced by warm spray showed significantly higher adhesive strength compared to that produced by plasma spray. Hardness was also higher in the warm sprayed coating layer compared to the plasma sprayed one. Moreover, with increasing the fraction of $Al_2O_3$, hardness gradually increased in both spray coating processes. In conclusion, an $Al-Al_2O_3$ composite coating layer with good mechanical properties was successfully produced by warm spray.

• Korean Journal of Materials Research
• /
• v.2 no.6
• /
• pp.389-397
• /
• 1992

Workability and aging behavior of Mg-Li-Al alloys hate been investigated with variation of Li and Al contents. It was found that ${\alpha}$(HCP) + ${\beta}$(BCC) two phase structure reveals better workability than ${\alpha}$(HCP) single phase structure. Increase of workability is attributed to the additional slip on pyramidal and prism planes besides the slip on basal plane of HCP Mg. Workability of ${\alpha}$+${\beta}$ two phase structure is improved with increased amount of Al. Among alloys studied in the present study, reduction limit up to 62 % was obtained for Mg-8.08Li-4.26Al. MgL$i_2$Al(${\theta}$) aging precipitation was observed in ${\alpha}$+ ${\beta}$ two phase structure, while it was not in a single phase structure. Result of microhardness reveals peak hardness for ${\alpha}$ +${\beta}$ two phase structure due to $\theta$ precipitate in ${\theta}$ phase. In ${\alpha}$+${\beta}$ two phase Mg-Li-Al alloys, hardness increased with increasing amount of Al. It is believed that addition of Al raised the amount Al partition in u phase and ${\theta}$ precipitation in ${\beta}$ phase.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.228.1-228.1
• /
• 2010

선택적 CO 산화반응(PrOx)을 위한 Ru이 고분산 담지된 $Ru/{\alpha}-Al_2O_3$ 촉매를 증착-침전법(deposition-precipitation)으로 제조하였다. 용액의 pH와 aging 시간에 따른 Ru 입자의 크기 변화와 분산도의 영향을 살펴보았으며 함침법(impregnation)으로 비교 촉매를 제조하였다. 촉매의 특성분석은 BET, TPR, CO-Chemisorption분석을 수행하여 촉매의 비표면적, 환원특성, 분산도를 알 수 있었다. 특성분석결과, 증착-침전법으로 제조한 $Ru/{\alpha}-Al_2O_3$ 촉매가 함침법으로 제조한 촉매에 비해 분산도가 높았으며, pH별 촉매 제조에서는 pH6.5로 제조한 촉매가 22.06%로 가장 높은 분산도를 보였다. 또한, 담체의 비표면적 영향에 따른 Ru 입자의 분산도를 살펴보기 위해 ${\gamma}-Al_2O_3$와 ${\alpha}-Al_2O_3$ 담체를 적용한 결과, 비표면적이 작은 ${\alpha}-Al_2O_3$ 담체 표면에서 Ru 분산도가 ${\gamma}-Al_2O_3$ 담체에 비해 높았다. 이는 기공이 발달하여 비표면적이 넓은 ${\gamma}-Al_2O_3$ 담체는 소량의 Ru을 고분산 담지 시 담체 표면보다는 기공 내에 담지 되는 양이 많아 실제 반응 시 반응에 참여하는 표면 활성 금속양이 적음을 알 수 있다. 특히, 선택적 산화반응과 같이 표면에서 빠른 반응이 일어나는 경우, 기공 내부의 활성금속이 반응에 참여하기 어려워 반응 활성이 낮음을 PrOx 반응실험을 통해 확인할 수 있었다. PrOx test 조건은 GHSV 250000~60000, 온도는 80~200도, 람다값은 2~4로 성능 비교하여 실험 하였다. PrOx의 성능평가 결과 담체를 ${\alpha}-Al_2O_3$를 사용하여 deposition-precipitation방법으로 제조한 pH6.5 촉매에서 $100{\sim}160^{\circ}C$에서 90%의 가장 높은 CO conversion을 가지고 18%의 선택도를 가졌다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.211-211
• /
• 2012

The electrical loss of the photo-generated carriers is dominated by the recombination at the metal- semiconductor interface. In order to enhance the performance of the solar cells, many studies have been performed on the surface treatment with passivation layer like SiN, SiO2, Al2O3, and a-Si:H. In this work, Al2O3 thin films were investigated to reduce recombination at surface. The Al2O3 thin films have two advantages, such as good passivation properties and back surface field (BSF) effect at rear surface. It is usually deposited by atomic layer deposition (ALD) technique. However, ALD process is a very expensive process and it has rather low deposition rate. In this study, the ICP-assisted reactive magnetron sputtering method was used to deposit Al2O3 thin films. For optimization of the properties of the Al2O3 thin film, various fabrication conditions were controlled, such as ICP RF power, substrate bias voltage and deposition temperature, and argon to oxygen ratio. Chemical states and atomic concentration ratio were analyzed by x-ray photoelectron spectroscopy (XPS). In order to investigate the electrical properties, Al/(Al2O3 or SiO2,/Al2O3)/Si (MIS) devices were fabricated and characterized using the C-V measurement technique (HP 4284A). The detailed characteristics of the Al2O3 passivation thin films manufactured by ICP-assisted reactive magnetron sputtering technique will be shown and discussed.

• The Journal of Engineering Research
• /
• v.2 no.1
• /
• pp.139-145
• /
• 1997

The effect of Ba addition on the thermal stabilization of $\gamma$-$Al_2O_3$ powders were studied. Ba additive was introduced into $\gamma$-$Al_2O_3$ powders by wet impregnation of $Ba(No_3)_3$.$6H_2O$. Ba additive was proved to be effective on the thermal stabilization of $\gamma$-$Al_2O_3$ powders by suppression of sintering. The optimum content of Ba was determined by 5 mol%, through the calcinations temperature range. It is suggested that the main reason of thermal stabilizaton is the substitution effect of large $Ba^{2+}$ ions into the $\Al^{3+}$ sites, which suppressed the surface diffusion of $\Al^{3+}$ ions.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.3
• /
• pp.219-224
• /
• 2020

Al₂O₃ powders with particle sizes of 0.35 ㎛, 0.5 ㎛, 1.5 ㎛, and 2.5 ㎛ are deposited onto glass and Cu substrates using the aerosol deposition (AD) process. The deposition characteristics of Al₂O₃ films using those four types of Al₂O₃ powders are investigated to determine the influence of the particle size on the films. To observe detailed micro-structures of the films, the cross-section and surface morphology are observed. Then, the crystalline size and internal strain are calculated from X-ray diffraction peaks in order to confirm the hammering effect as well as the micro-strain during the AD deposition. From the above results, deposition mechanisms related to the particle size are studied. The results of this study indicate the optimal particle size and formation mechanisms for dense Al₂O₃ film with a smooth surface roughness as well as for a porous Al₂O₃ film with a rough surface roughness.

• Journal of the Korean Physical Society
• /
• v.73 no.10
• /
• pp.1555-1560
• /
• 2018

$AlFe_2B_2$ produced by using a conventional arc melter has a ferromagnetic material with a Curie temperature ($T_C$) of around 300 K, but the arc-melt generates paramagnetic $Al_{13}Fe_4$ impurities during the synthesis of $AlFe_2B_2$. Impurities are brought to cause a decrease in magnetocaloric effects (MCEs). To investigate the effects of $Al_{13}Fe_4$ impurities on MCEs, we prepared and compared ascast and acid-treated samples, where the acid treatment was performed to remove the $Al_{13}Fe_4$ impurities. For the structural analysis, powder X-ray diffraction was carried out, and the measured data were subjected to a Rietveld refinement. The presence of $Al_{13}Fe_4$ impurities in the as-cast sample was observed in the phase analysis measurements. Magnetic properties were investigated by using Superconducting Quantum Interference Device (SQUID) measurements for the as-cast and the acid-treated $AlFe_2B_2$ samples. From isothermal magnetization measurements, Arrott plots were obtained showing that the transition of $AlFe_2B_2$ has a second-order magnetic phase transition (SOMT). The $T_C$ and the saturation magnetization increased for the acid-treated sample due to removal of the paramagnetic impurities. As a consequence, the magnetic entropy change ($-{\Delta}S$) increased in the pure $AlFe_2B_2$ samples, but the full width at half maximum in the plot of $-{\Delta}S$ vs. T decreased due to the absence of impurities.

• Journal of Welding and Joining
• /
• v.14 no.6
• /
• pp.109-118
• /
• 1996

Al$_2$O$_3$-TiO$_2$powders of six different compositions were plasma-sprayed on Ti substrate. The spray powders and the spray coated layers were analysed and compared using SEM and X-RD. The elastic properties (specific elastic constant and damping coefficient) of the coated specimens were measured in order to select the optimum composition range of ceramics for use in a speaker diaphragm. A correlation between the microstructure and elastic properties was also investigated. When $Al_2$O$_3$powders with 0- 13% TiO$_2$were plasma sprayed, the coated layers were composed of metastable y-Al$_2$O$_3$with small amount of $\alpha$-Al$_2$O$_3$and the content of $\alpha$-Al$_2$O$_3$was increased with TiO$_2$content. Specific elastic constant was rapidly increased with 2 and 13% TiO$_2$addition to $Al_2$O$_3$. The internal damping was nearly unchanged with TiO$_2$content The specific elastic constant seemed to be dependent on the content of $\alpha$-Al$_2$O$_3$in the coated layer.