• 한국분말재료학회지
• /
• 제10권3호
• /
• pp.195-200
• /
• 2003

Ni coated $Al_2O_3$ composite was successfully Prepared by the electroless deposition Process. The average size of Ni particles coated on the $Al_2O_3$ matrix powder was about 20 nm. It was hard to find any reaction compound as an impurity at interface between $Al_2O_3$ and Ni particles after sintering. The characterization of microstructure crystal structure and fracture behavior of the sintered body were investigated using XRD, TEM and Victors hardness tester, and compared with those of the sintered $Al_2O_3$ monolithic body. Many dislocations were observed in the Ni phase due to the difference of thermal expansion coefficient between $Al_2O_3$ and Ni phase, and no observed microcracks at their $Al_2O_3$ and Ni interface. In the $Al_2O_3$/Ni composite, the main fracture mode showed a mixed fracture with intergranular and transgranuluar type having some ,surface roughness. The fracture toughness was slightly increased due to the plastic deformation mechanism of Ni phase in the $Al_2O_3$/Ni composite.

• 한국분말재료학회지
• /
• 제26권3호
• /
• pp.220-224
• /
• 2019

The aluminum (Al)/copper oxide (CuO) complex is known as the most promising material for thermite reactions, releasing a high heat and pressure through ignition or thermal heating. To improve the reaction rate and wettability for handling safety, nanosized primary particles are applied on Al/CuO composite for energetic materials in explosives or propellants. Herein, graphene oxide (GO) is adopted for the Al/CuO composites as the functional supporting materials, preventing a phase-separation between solvent and composites, leading to a significantly enhanced reactivity. The characterizations of Al/CuO decorated on GO(Al/CuO/GO) are performed through scanning electron microscopy, transmission electron microscopy, and energy dispersive X-ray spectroscopy mapping analysis. Moreover, the functional bridging between Al/CuO and GO is suggested by identifying the chemical bonding with GO in X-ray photoelectron spectroscopy analysis. The reactivity of Al/CuO/GO composites is evaluated by comparing the maximum pressure and rate of the pressure increase of Al/CuO and Al/CuO/GO. The composites with a specific concentration of GO (10 wt%) demonstrate a well-dispersed mixture in hexane solution without phase separation.

• 한국세라믹학회지
• /
• 제30권10호
• /
• pp.811-818
• /
• 1993

Al2O3/ZrO2-Spinel composites were prepared by infiltrating magnesium sulfate solution into the porous preform made from Al2O3-20wt% ZrO2 composite powders derived through an emulsion route. The microstructure and composition of the modified composites could be controlled by manipulating the presingtering temperature of the preform, infiltration time, and so on. It was found that spinel phases were concentrated near the surface than in the interior of the Al2O3/ZrO2-Spinel composites infiltrated for 6hrs, while spinel phases were uniformly distributed in the comosites infiltrated for 2 days. The relative density and fracture toughness of the composite infiltrated for 6 hrs were 98.6% and 7.2MN/m3/2, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.408-409
• /
• 2007

Al-doped p-type ZnO films were fabricated on n-Si (100) and homo-buffer layers in pure oxygen at $450^{\circ}C$ by RF magnetron sputtering. Target was ZnO ceramic mixed with 2wt% $Al_2O_3$. XRD spectra show that the Al-doped ZnO thin films have ZnO crystal structure and homo-buffer layers are beneficial to Al-doped ZnO films to grow along c-axis. Hall Effect experiments with Van der Pauw configuration show that p-type carrier concentrations are ranged from $1.66{\times}10^{16}\;to\;4.04{\times}10^{18}cm^{-3}$, mobilities from 0.194 to $2.3cm^2V^{-1}s^{-1}$ and resistivities from 7.97 to $18.4{\Omega}cm$. P-type sample has density of $5.40cm^{-3}$ which is smaller than theoretically calculated value of $5.67cm^{-3}$. XPS spectra show that O1s has O-O and Zn-O structures and A12p has only Al-O structure. P-ZnO:Al/n-ZnO:Al junctions were fabricated by magnetron sputtering. V-I curves show that the p-n junctions have rectifying characteristics.

• 한국자기학회지
• /
• 제8권1호
• /
• pp.27-33
• /
• 1998

스파터링법으로 Si(001) 기판 위에 증착된 Fe(1000 $\AA$)/Al2O3(t$\AA$)/Co(1000$\AA$) 자기 삼층 접합들의 터널링 자기저항 성질을 연구하였다. 두께 t=50~200$\AA$의 Al2O3층을 반응성 rf 스파터링법으로 바닥 자성층위에 직접 증착하였다. 비교응 위해, Pt/Al2O3/Pt 터널링 접합을 제조하여 상온에서 전류.전압(I.V)특성을 측정한 결과, 확인한 비선형 nonmhic 거동을 나타내었다. 이로부터 반응성 스파터링된 Al2O3가 상온에서도 phnhole이 없는 휼룔한 절연 터널링 장벽을 형성함을 확인할 수 있었다. Fe/Al2O3/Co 자기 터널링 접합즐은 Pt/Al2O3/Pt 접합들에 비해 상당한 접합저항의 열화를 보였으며, 상온에서 대략 0.1%의 터널링 자기저항비를 나타내었다. Fe를 꼭대기 전극으로 하는 전극으로 하는 접합들에 비해, Co을 꼭대기 전극으로 하는 대부분의 자기 터널링 접합들이 보다 안정된 I.V 및 터널링 자기저항 특성을 보였다. 이러한 실험결과들을 자기 터널링 접합들의 계면구조와 관련지어,Pt/Al2O3/Ptwjq합과 비교하여 논의하였다.

• 한국세라믹학회지
• /
• 제28권4호
• /
• pp.338-346
• /
• 1991

The alumina-titania composite powders coated with Al2O3 were prepared by the method of hydrolysis-deposition of mixed aluminium salt solution of Al2(SO)4-Al(NO3)3-Urea. The effects of coating-process parameters on the characteristics of coated composite powders were also investigated. As the content of TiO2 dispersed in deionized water increased, the coated composite powders were found to be more uniform in size and unagglomerated. When TiO2 powders were coated for 30 min, the optimum TiO2 content in the coating process was 400 mg/ι. The size of TiO2 particle was increased approximately from 0.7${\mu}{\textrm}{m}$ to 1.0${\mu}{\textrm}{m}$ through coating of Al2O3. The IEP of coated composite powders was pH=8.3 identical to the value of aluminium hydroxides and the zeta-potential showed nearly similar values each other. When heat treating coated composite powders at 130$0^{\circ}C$, only two phases of TiO2(rutile) and Al2TiO5 were observed. These results showed that the suface of TiO2 could be uniformly coated with the aluminium hydroxide.

• 한국세라믹학회지
• /
• 제37권4호
• /
• pp.359-367
• /
• 2000

Particulate composites of Al2O3/SiC, Al2O3/ZrO2 and Al2O3/ZrO2/SiC have been fabricated to investigate their R-curve behaviors and toughening mechanisms. Al2O3 containing 30 vol% SiC particles of 3${\mu}{\textrm}{m}$ showed rising R-curve behavior owing to the strong crack bridging by SiC particles. The fracture toughness reached 9.1 MPa {{{{ SQRT {m} }} at the crack length of 1000${\mu}{\textrm}{m}$. On the other hand, ZrO2-toughened Al2O3 had a high flat R-curve since it rose steeply in the short crack region due to the well known transformation toughening. For Al2O3/ZrO2/SiC composites, the R-curve behavior was similar to that of Al2O3/SiC but with slightly higher toughness. The SiC particles in this composite decreased the amount of transformable tetragonal phase to reduce the effect of transformation toughening by 50%. It was also found that the fracture toughness of this composite with two different toughening mechanisms was markedly lower than that estimated by the simple addition of two contributions.

• 한국진공학회지
• /
• 제22권3호
• /
• pp.119-125
• /
• 2013

In-line magnetron sputtering system을 사용하여 대면적($60{\times}60cm^2$) 소다라임 유리기판위에 투명전도성 ZnO(Al)와 ZnO(AlGa) 박막을 500 nm에서 1,450 nm까지 두께별로 증착하여 전기적, 광학적 특성을 연구하였다. XRD를 통해 c-축 방향성(002)을 가지고 성장된 것을 확인 하였다. Hall 특성 분석을 통해 이동도 및 캐리어 농도의 특성을 확인 하였으며, 그에 따른 ZnO(AlGa)의 비저항이 $9.03{\times}10^{-4}{\Omega}{\cdot}cm$에서 $7.83{\times}10^{-4}{\Omega}{\cdot}cm$으로 ZnO(Al) 보다 높게 나타났으며, 가시광선 영역에서 투과율은 87.6%에서 84.3%으로 나타났다. 따라서 ZnO(AlGa)는 전기적 특성이 우수하고 높은 투과율로 대면적용 투명전도성 재료로의 활용에 적합한 특성을 지닌 것을 확인 할 수 있었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.701-704
• /
• 2001

The dielectric and sintering properties of LaAlO$_3$ceramics synthesised with La$_2$O$_3$-Al$_2$O$_3$(LAO) and La$_2$O$_3$-Al(OH)$_3$(LAH) were investigated. In case of LAH samples, a single phase of LaAlO$_3$powders was formed at 100$0^{\circ}C$, density of the ceramics sintered at 140$0^{\circ}C$ was 6.41g/㎤, and the dielectric constant and loss were 22.4 and 0.003, respectively. In case of LAO samples, a single phase of LaAlO$_3$powders was formed at 130$0^{\circ}C$, density of the ceramics sintered at 150$0^{\circ}C$ was 6.35g/㎤, and the dielectric constant and loss were 22.16 and 0.009, respectively.

• 한국분말재료학회지
• /
• 제21권5호
• /
• pp.377-381
• /
• 2014

This work describes the coloration, chemical stability of $SiO_2$ and $SnO_2$-coated blue $CoAl_2O_4$ pigment. The $CoAl_2O_4$, raw materials, were synthesized by a co-precipitation method and coated with silica ($SiO_2$) and tin oxide ($SnO_2$) using sol-gel method, respectively. To study phase and coloration of $CoAl_2O_4$, we prepared nano sized $CoAl_2O_4$ pigments which were coated $SiO_2$ and $SnO_2$ using tetraethylorthosilicate, $Na_2SiO_3$ and $Na_2SiO_3$ as a coating material. To determine the stability of the coated samples and their colloidal solutions under acidic and basic conditions, colloidal nanoparticle solutions with various pH values were prepared and monitored over time. Blue $CoAl_2O_4$ solutions were tuned yellow color under all acidic/basic conditions. On the other hand, the chemical stability of $SiO_2$ and $SnO_2$-coated $CoAl_2O_4$ solution were improved when all samples pH values, respectively. Phase stability under acidic/basic condition of the core-shell type $CoAl_2O_4$ powders were characterized by transmission electron microscope, X-ray diffraction, CIE $L^*a^*b^*$ color parameter measurements.