• Journal of the Korean Ceramic Society
• /
• v.27 no.4
• /
• pp.501-512
• /
• 1990

Al2O3 and 0.25wt% MgO-doped Al2O3 powders were made from the alcohol solution of Al(NO3)3.9H2O and Mg(NO3)2.6H2O by spray pyrolysis method. Each powder was prepared at 900 and 100$0^{\circ}C$. Powders prepared at 90$0^{\circ}C$ were amorphous phase, but prepared at 100$0^{\circ}C$ wre mainly ${\gamma}$-Al2O3 crystalline form. Particle size of the MgO-doped Al2O3 powders was in the range of 0.2-2${\mu}{\textrm}{m}$, but undooped powders shwoed comparatively wider range of particle size. All the powders prepared at 900 and 100$0^{\circ}C$ were transformed to $\alpha$-Al2O3 crystalline form by calcination at 110$0^{\circ}C$ for 1hr. Each powder was sintered at 1600, 1650 and 1$700^{\circ}C$ for 2hrs. MgO-doped Al2O3 body sintering at 1$650^{\circ}C$ showed 99% of relative density but undooped Al2O3 showed 95% of relative density, even sintered at higher temperature of 1$700^{\circ}C$.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.4
• /
• pp.647-651
• /
• 2007

In order to investigate the excited-state intramolecular proton transfer (ESIPT) process of dihydroxyanthraquinones (DHAQ; 1,5-DHAQ and 1,8-DHAQ) in organic-inorganic hybrid matrices, transparent SiO2, SiO2- Al2O3, and Al2O3 matrices chemically bonded with DHAQ were prepared using a sol-gel technique. The absorption maxima of 1,5- and 1,8-DHAQ in SiO2 matrices are observed at around 420 nm, whereas those of DHAQ in both SiO2-Al2O3 and Al2O3 matrices are markedly shifted to longer wavelength compared with those in SiO2 matrix. This indicates that DAHQ forms a chemical bond with an Al atom of Al2O3. The DHAQ in SiO2 matrix shows a markedly Stokes-shifted emission which is originated from the ESIPT in DHAQ. Based on the emission lifetimes of DHAQ, the ESIPT of DHAQ was found to be strongly affected by the chemical interaction with Al atom in the Al2O3-related matrices.

• Journal of the Korean Ceramic Society
• /
• v.34 no.5
• /
• pp.535-543
• /
• 1997

The surface of SiC particles were partially oxidized to produce SiO2 layers on the SiC particles to prepare Al2O3/SiC composite by formation of mullite bonds between the grains of Al2O3 and SiC during sintering at 1$600^{\circ}C$. This process is considered to enable the sintering of Al2O3/SiC composite at lower temperature and also to relieve the stress, produced by thermal expansion mismatch between Al2O3 and SiC. In fact, Al2O3/SiC composite prepared by oxidation of SiC was observed to be more effectively sintered and densified at lower temperature. Maximum density, flexural strength and microhardness were obtained with 5.65 vol% of mullite content in Al2O3/SiC composite.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.4
• /
• pp.154-159
• /
• 2001

(Li,Al)$MnO_2(OH)_2$:Co compound was synthesized by hydrothermal method. $MnO_2$, LiOH.$H_2$O, $Co_3O_4$ and $Al(OH)_3$ were used as starting materials and the optimum conditions for synthesis of monolithic (Li,Al)$MnO_2(OH)_2$:Co compound were as follows : reaction temperature; $200^{\circ}C$, reaction time; 3 days, hydrothermal solvent; 3M-KOH solution, reaction apparatus; seesaw type, atomic ratio of Li:Al:Mn;Co = 1:2.1:2.5~2:0.5~1. Monolithic(Li,Al)$MnO_2(HO)_2$:Co compound synthesized in this work had a god crystallinity and excellent color forming effect as a blue pigment compatible with natural mineral. The particles of the synthesized (Li,Al)$MnO_2(OH)_2$:Co compound have hexagonal plate shape with the size of 0.5~1 $\mu\textrm{m}$.

• Journal of the Korean Ceramic Society
• /
• v.20 no.1
• /
• pp.49-54
• /
• 1983

The main object of this study is to investigate the effect of Al powder as an additive on the sintering of calcined alumina comparing with that of calcined alumina alone. The degree of Al oxidation is calculated by measuring the weight increase during the firing Water absorption bulk density and compressive strength of the $Al_2O_3+Al$ system at each temperature are compared with those of $Al_2O_4$ alone. The $Al_2O_3+Al$ system shows better physical propeties than Al2O3 alone and it seems by the SEM observation that the fine oxidized Al particles(fine $Al_2O_3$ particles submicron unit) fill the interstices of the original $Al_2O_3$ par-ticles and thus result in the well-close-packed arrangement of the particles.

• Journal of the Korean Ceramic Society
• /
• v.27 no.1
• /
• pp.55-61
• /
• 1990

Effect of Al2O3 addition on the mechanical properties and microstructure of Ce-TZP were studied. 12, 14, 16Ce-TZP containing 0-40wt% Al2O3 were prepared by sintering at 155$0^{\circ}C$ for 2h. in air. Density, linear shrinkage, bending strength, Vickers hardness, microstructuer and the amount of stress induced phase transformation were examined. Vickers hardness increased linearly with increasing amounts of Al2O3. The amount of transformation and fracture toughness decreased linearly with increasing amount of Al2O3. Linear shrinkage and relative density decreased with increasing Al2O3 content in all composition of Ce-TZP. Grain growth of Ce-TZP was inhibited by Al2O3 dispersion and fracture mode of Ce-TZP/Al2O3 composites transformed from intergranular to transgranular fracture as the amount of Al2O3 increased. TEM observation revealed that Al2O3 particles were located mainly at grain boundaries of ZrO2.

• Journal of the Korean Vacuum Society
• /
• v.22 no.1
• /
• pp.20-25
• /
• 2013

ZnO:Al thin films deposited by RF magnetron sputtering were post-annealed and the electrical and optical properties of ZnO:Al thin films were investigated before and after anneling. We confirmed that the ZnO:Al thin film was affected by post-annealing temperature. As post-annealing temperature increases, crystallinity and transmittance in visible area (400~800 nm) of ZnO:Al thin films decreased. While sheet resistance of thin films increased sharply with increasing to $400^{\circ}C$. This result is due to reduce of carrier concentration caused by absorption of $O_2$ or $N_2$ at surface of thin film.

• Journal of the Korean Ceramic Society
• /
• v.15 no.2
• /
• pp.66-71
• /
• 1978

The cobalt blue spinel stains (main composition; CoO:$Al_2O_3$=1 : 1) in CoO-NiO-$Al_2O_$3 and $CoO-Al_2O_3-Cr_2O_3$ system were prepared by the calcination of each component oxides to be adequate for the factory. The color development, the change of the lattice constnat of the spinel and its application to colored glazes were studied. The results were summarized as follows. 1) In CoO-Al_2O_3$ spinel, the excess addition of each component hardly made any variation in lattice constantand alumina-rich spinel specimens caused the brilliant blue color fade. 2) An increase of $Ni^{2+}$ in $CoO-NiO-Al_2O_3$ system, made the lattice constnat of the $CoO-Al_2O_3$ spinel smaller, and an increase of $Cr^{3+}$ in $CoO-Al_2O_3-Cr_2O_3$, larger. 3) Glazed stains under lead glaze were colored nearly same dark blue color fade.

• Journal of the Korean Ceramic Society
• /
• v.22 no.6
• /
• pp.42-52
• /
• 1985

Several $Al_2O_3$-based polycrystalline which had different dopant ratio in the range of 0.5mol% were prepared by doping pure $Cr_2O_3$ $HfO_2$. Single crystalline which had same composition with above polycrystalline were made by means of floating zone method. This study examined the role of each dopant for enhancing the mechanical properties of $Al_2O_3$-based Ceramics. Optical micrographs $({ imes}200)$ of $Al_2O_3-Cr_2O_3$ single crystal showing not only radial crack (rc) on the specimen surface but median crack(mc) and lateral crack(lc) under surface at the edge of indentation mark. Fracture toughness of Al2O3-based Ceramics was increased with $ZrO_2$ content. Alloying effect of $Cr_2O_3$ contributed to the hardness of $Al_2O_3$ based ceramics.

• Journal of the Korean Ceramic Society
• /
• v.23 no.2
• /
• pp.38-42
• /
• 1986

The adsorption behavior of 3CaO.$Al_2O_3$-sodium gluconate-$H_2O$ system by measuring adsorp-tion isotherm DTA and IR sepctra. The adsorbed amount of sodium gluconate on 3CaO.$Al_2O_3$ is exceedingly larger than 3CaO.$SiO_2$ and portland cement. From the DAT experiment the formation of complex is observed by the characteristic exothermic peak of the complex at 45$0^{\circ}C$ It is now strong deduced that the chemical bonding between gluconate anion and 3CaO.$Al_2O_3$ should be coordinative due to the complex formation on the surface 3CaO.$Al_2O_3$ from the IR spectra of sod-ium gluconate only and 3CaO.$Al_2O_3$ -sodium gluconate-$H_2O$.