• Journal of Powder Materials
• /
• v.9 no.6
• /
• pp.441-448
• /
• 2002

Dispersions of non-soluble ceramic particles in a metallic matrix can enhance the strength and heat resistance of materials. With the advent of mechanical alloying it became possible to put the theoretical concept into practice by incorporating very fine particles in a flirty uniform distribution into often oxidation- and corrosion- resistant metal matrices. e.g. superalloys. The present paper will give an overview about the mechanical alloying technique as a dry, high energy ball milling process for producing composite metal powders with a fine controlled microstructure. The common way is milling of a mixture of metallic and nonmetallic powders (e.g. oxides. carbides, nitrides, borides) in a high energy ball mill. The heavy mechanical deformation during milling causes also fracture of the ceramic particles to be distributed homogeneously by further milling. The mechanisms of the process are described. To obtain a homogeneous distribution of nano-sized dispersoids in a more ductile matrix (e.g. aluminium-or copper based alloys) a reaction milling is suitable. Dispersoid can be formed in a solid state reaction by introducing materials that react with the matrix either during milling or during a subsequent heat treatment. The pre-conditions for obtaining high quality materials, which require a homogeneous distribution of small dis-persoids, are: milling behaviour of the ductile phase (Al, Cu) will be improved by the additives (e.g. graphite), homogeneous introduction of the additives into the granules is possible and the additive reacts with the matrix or an alloying element to form hard particles that are inert with respect to the matrix also at elevated temperatures. The mechanism of the in-situ formation of dispersoids is described using copper-based alloys as an example. A comparison between the in-situ formation of dispersoids (TiC) in the copper matrix and the milling of Cu-TiC mixtures is given with respect to the microstructure and properties, obtained.

• Composites Research
• /
• v.14 no.5
• /
• pp.1-11
• /
• 2001

The particulates reinforced metal matrix composites(PMMC) have a number of interesting mechanical properties. including high strength and good resistance to wear at high temperature and low thermal expansion. The equipment structure to obtain the homogeneous distribution in composites are proposed for the continuous pouring of reinforcement at the desired temperature. The particulates reinforced metal matrix composites(A357/SiCp) were fabricated by the process of the combined stirring method with the various fabrication process. The combined stirring method to niform distribution of particle is consisted of two stirring force both electro-magnetic stirring generated from induction heating and mechanical stirring with graphite stirrer. PMMC billets were fabricated with the volume fractions ranged from 0% to 20% and particle sizes ranged from 14${\mu}{\textrm}{m}$ to 25${\mu}{\textrm}{m}$. It is important to cont the size of primary $\alpha$-Al solid particles because it could become the cause of the particle pushing or capture phenomena from the fact that secondary dendrite arm spacing size depends on the cooling rate during the solidification in hypoeutectic Al-Si alloy. Therefore, the effect of primary $\alpha$-Al on the reinforcement distribution in matrix alloys has been investigated. The microstructure of PMMC fabracated with various volume fractions(0%, 10%, and 20%) and particle size were observed.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.244-249
• /
• 2004

In this paper, shielding effectiveness(SE) of the shielding paint of electromagnetic(EM) waves was investigated with actual experiments. The shielding paint used in this study were made of powder of conductive materials - Ag, Cu, Al, Sn, Ni. Cr, Graphite and Charcoal etc. with a solubility in oil and water. Also, the paper was used as a base sheet. The experiment was carried out by using a shielding evaluator(Shielding box) TR17302 with an ADVANTEST spectrum analyzer, model R3361C. It was found from the experimental results that silver, copper, nickel were good candidates as a shielding material against the EM waves with increasing the SE as the composite was laminated. The characteristics of the SE against the EM waves depended on a mode of preparation of specimen. The effects of density of particles on the SE were studied about the EM shielding paint. The SE strongly depended on the electric resistance by density of painting particles. SE increased as the density of particles was increasing.