• The Journal of Korean Institute of Communications and Information Sciences
• /
• v.40 no.5
• /
• pp.974-980
• /
• 2015

Arc thermal spray coating using Al-3%Mg thermal spray wire was carried out to prevent steel from corrosion damage under the marine environment. Post-sealing was applied to Al-3%Mg spray coating treatment using organic/inorganic composite ceramics in order to improve the corrosion resistance of the as-sprayed coating. The results of various electrochemical experiments with sealing treatment indicated that the improvement in corrosion resistance was observed due to low current density in all applied potential range during anodic and cathodic polarization experiments. Futhermore, the natural potential measurement exhibited severe potential fluctuation due to influence of micro-crack presence on the surface of sealed thermal spray coating layer. In addition, the sealed layer was easily eliminated during anodic polarization. Nevertheless, Al-3%Mg spray coating layer improved corrosion resistance by sealing treatment because the sealed coating efficiency was determined to be 92.11%, indicating the exterior environment barrier effect which is based on the Tafel analysis.

• Journal of the Korean Society for Heat Treatment
• /
• v.10 no.2
• /
• pp.81-92
• /
• 1997

The effect of alloying elements, precipitate size, its distribution, and dislocation substructure resulted from warm rolling or cold rolling in the superplastic Al-Mg alloy system was investigated. One of the major requirements for fine structure superplasticity is that the grain size should be very small. Fine grain structure is controlled by the dislocation substructure and the dynamic recrystallization during hot or warm working. The recovery of Al-Mg base alloys was constrained resulting in relatively high dislocation density when the alloys were warm rolled. In particular, Al-Mg-Zr alloy exhibited the smallest sub-grain size among Al-Mg alloys containing Mn, Cu, Zr as a third element. The Al-Mg-Mn alloy cold rolled 80% after hot rolling showed the maximun strain rate sensitivity exponent, m, of 0.75 under strain rate of $7.1{\times}10^{-4}/s$ at $500^{\circ}C$. The elongation of the alloys was limited in spite of high m values due to large dispersoids containing appreciable amount of Fe impurities.

• Journal of Welding and Joining
• /
• v.3 no.2
• /
• pp.42-51
• /
• 1985

The dynamic fracture toughness, fracture characteristics, impact tension and tensile properties of Al-Mg-Si T5 alloy and Al-Zn-Mg T6 alloy respectively welded with filler metal of Alcan 4043 were investigated. The dynamic fracture toughness values were obtained rapidly and simply for the specimen of small size by using instrumented Chirpy impact testing machine. the testing temperatures of the specimen were a range of room temperature and-196.deg. C. The results obtained in this experiment are summarized as follows. With decreasing the testing temperatures, dynamic tensile stress and fracture load were increased, on the other hand the deflection and impact value showed decreasing tendency in order of base metal>HAZ>weld. Changes of total absorbed energy were more influenced by the crack propagation energy than the crack initiation energy. At the low temperatures, the unstable rapid fracture representing the crack propagation appeared for the specimens of Charpy press side notched in Al-Zn-Mg alloy, but it was difficult to obtain the unstable rapid fracture in Al-Mg-Si alloy. Because of the development of plastic zone at the notch root, it was difficult to obtain thevalid $K_{1d}$ value in Al-Mg-Si alloy. Therefore the fatigue cracked specimens were effective in both Al-Mg-Si and Al-Zn-Mg alloys. With decreasing the impact testing temperatures, specimens underwent a transition from dimple-type transgranular fracture to lamella surface-type intergranular fracture because of the precipitate at the grain boundaries, impurities and crystal structure of the precipitates.s.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.112-113
• /
• 2013

Thin CrAlMgSiN films, whose composition were 30.6Cr-11.1Al-7.3Mg-1.2Si-49.8N (at.%), were deposited on steel substrates in a cathodic arc plasma deposition system. They consisted of alternating crystalline Cr-N and AlMgSiN nanolayers. After oxidation at $800^{\circ}C$ for 200 h in air, a thin oxide layer formed by outward diffusion of Cr, Mg, Al, Fe, and N, and inward diffusion of O ions. Silicon ions were relatively immobile at $800^{\circ}C$. After oxidation at $900^{\circ}C$ for 10 h in air, a thin $Cr_2O_3$ layer containing dissolved ions of Al, Mg, Si, and Fe formed. Silicon ions became mobile at $900^{\circ}C$. After oxidation at $900^{\circ}C$ for 50 h in air, a thin $SiO_2-rich$ layer formed underneath the thin $Cr_2O_3$ layer. The film displayed good oxidation resistance. The main factor that decreased the oxidation resistance of the film was the outward diffusion and subsequent oxidation of Fe at the sample surface, particularly along the coated sample edge.

• Korean Journal of Metals and Materials
• /
• v.49 no.8
• /
• pp.664-670
• /
• 2011

3-ply Mg/Al/STS clad-metal was fabricated by the roll bonding process. An interfacial reaction layer was formed at the Mg/Al interface at and above $300^{\circ}C$ whereas no interfacial reaction layer was observed up to $400^{\circ}C$. The effect of the interfacial reaction layer on the mechanical and fracture properties in clad metals after heat treatments were investigated The chemical compositions were analyzed at the Mg/Al interface by an Energy dispersive X-ray analysis (EDX). A tension test was performed to examine the interfacial cracking properties. The Mg layer fractured first, causing a sudden drop of the stress and Al/STS layer continued to deform until the final fracture. Periodic cracks and crack propagation was observed at the reaction layer between Mg and Al.

• Korean Journal of Materials Research
• /
• v.31 no.11
• /
• pp.642-648
• /
• 2021

The precipitation effect of Al-6%Si-0.4%Mg-0.9%Cu-(Ti) alloy (in wt.%) after various heat treatments was studied using a laser flash device (LFA) and differential scanning calorimetry (DSC). Solid solution treatment was performed at 535 ℃ for 6 h, followed by water cooling, and samples were artificially aged in air at 180 ℃ and 220 ℃ for 5 h. The titanium-free alloy Al-6%Si-0.4%Mg-0.9%Cu showed higher thermal diffusivity than did the Al-6%Si-0.4%Mg-0.9%Cu-0.2%Ti alloy over the entire temperature range. In the temperature ranges below 200 ℃ and above 300 ℃, the value of thermal diffusivity decreased with increasing temperature. As the sample temperature increased between 200 ℃ and 400 ℃, phase precipitation occurred. From the results of DSC analysis, the temperature dependence of the change in thermal diffusivity in the temperature range between 200 ℃ and 400 ℃ was strongly influenced by the precipitation of θ'-Al₂Cu, β'-Mg₂Si, and Si phases. The most important factor in the temperature dependence of thermal diffusivity was Si precipitation.

• Transactions of the Korean hydrogen and new energy society
• /
• v.34 no.2
• /
• pp.169-177
• /
• 2023

Phase stability diagrams were constructed for magnesium alanate (Mg(AlH₄)₂) nanoparticles to investigate the reversible hydrogen storage reaction by using density functional theory. Our findings indicate that bulk Mg(AlH₄)₂ shows favorable hydrogen release, but unfavorable hydrogen uptake (adsorption) reactions. However, for Mg(AlH₄)₂ nanoparticles, it was observed that hydrogen release and recharge can be achieved by controlling the particle size and temperature. Furthermore, by predicting the decomposition phase diagram of Mg(AlH₄)₂ nanoparticles with varying hydrogen partial pressure, it was discovered that reversible dehydrogenation reactions can occur even in relatively large nanoparticles by controlling the hydrogen partial pressure.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.4
• /
• pp.156-159
• /
• 2007

The red emission properties of $Mn^{4+}$ doped $SrAl_{12}O_{19}$ prepared by the solid-state reaction was investigated, in order to verify its potential to act as the red emitting phosphor of white LEDs. The emission spectrum exhibits a narrow band between $600{\sim}700 nm $ with four sharp peaks occurring at about 643, 656, 666, 671 nm due to the $^2E\to^4A_2$ transition of $Mn^{4+}$. The excitation spectrum exhibits a broad band between $200{\sim}500 nm$ with three peaks occurring at about 338, 398 and 468 nm, respectively. Moreover, the relative emission intensity of $SrAl_{12}O_{19}:Mn^{4+}$ with or without $CaF_2$ and MgO fluxes measured at excitation source 390 nm. The relative emission intensity of $SrAl_{12}O_{19}:Mn^{4+}$ containing 0.67mol% MgO was approximately 30% higher than that of the base composition sample. Strontium hexa-aluminate measured at room temperature as a function of the substituted Mg concentration. MgO was added to replace part of the $Al_2O_3$. Also, the relative emission intensity of $SrAl_{12}O_{19}:Mn^{4+}$ containing 0.67 mol% MgO and 0.67 mol% $CaF_2$ was approximately about 48% higher than that of the base composition $SrAl_{12}O_{19}:Mn^{4+}$.

• Journal of the Korean Society for Heat Treatment
• /
• v.32 no.4
• /
• pp.168-174
• /
• 2019

The microstructural features and relative room temperature mechanical properties were investigated in various compositions of Mg-xAl-yZn alloys by thxiomolding process. The microstructure was composed of ${\alpha}$-Mg particles and mixture of ${\alpha}$-Mg and ${\beta}-Mg_{17}Al_{12}$ eutectic phase. The amount of ${\beta}-Mg_{17}Al_{12}$ eutectic phase in mixture was increased with increasing Al and Zn contents without grain refinement. After adding Ti content, however, the morphology of ${\beta}-Mg_{17}Al_{12}$ eutectic phase transformed from net-like to discontinuous shape and the average grain size reduced. To determine the relationship between microstructural features and their mechanical properties, a tensile test was performed at room temperature. As a result, it was found that the mechanical properties were improved in all of Ti contained alloys due to increased elongation and the mechanisms are discussed in terms of microstructural evolution.

• Journal of Advanced Marine Engineering and Technology
• /
• v.23 no.3
• /
• pp.360-368
• /
• 1999

The paper describes spectroscopic characteristics of plasma induced in the pulsed YAG laser welding of alloys containing a large amount of volatile elements. The authors have conducted the spectroscopic analyses of laser induced Al-Mg alloys plasma in the air and argon atmosphere. In the air environment the identified spectra were atomic lines of Al, Mg, Cr, Mn, Cu, Fe and Zn and singly ionized Mg lines as well as the intense molecular spectra of ALO and MgO formed by chemi-cal reactions of evaporated Al and Mg atoms from the pool surface with oxygen in the air. In argon atmosphere MgO and AlO spectra vanished but AlH spectrum was detected. the hydrogen source was presumable hydrogen dissolved in the base metals water absorbed on the surface oxide layer or $H_2$ and $H_2O$ in the shielding gas. The resonant lines of Al and Mg were strongly self-absorbed in particular self-absorption of the Mg line was predominant. These results show that the laser induced plasma was made of metallic vapor with relatively low temperature and high density.