• 한국재료학회지
• /
• 제11권9호
• /
• pp.733-739
• /
• 2001

In Al-25Nb binary system, it was observed only formation of $D0_{22}$ $Al_3Nb$ intermetallic compound after 5hr milling but it was not observed formation of meta stable phase like L1$_2$ phase. In this state, $D0_{22}$ $Al_3Nb$ fabricated had nano sized grain of approximately 20nm. Ternary systems, transition metals such as Cr, Cu, Fe, Mn were added 6~12at.% as substitution of Al, showed formation of $D0_{22}$ $Al_3Nb$ like Al-25Nb binary system. In Al- l2Cu-25Nb system, it was observed that broad XRD pattern like amorphization of Al and not observed formation of $D0_{22}$ $Al_3Nb$ after 5hr milling. But there was mixed phase of a lot of amorphous Al and little $D0_{22}$ $Al_3Nb$ through TEM. In the states of unalloyed, 5~7hr milling time, those showed exothermic reaction at 35$0^{\circ}C$, which was formation of $D0_{22}$ $Al_3Nb$ like Al-25Nb binary system. With increasing milling time to 10hr, $D0_{22}$ $Al_3Nb$ was transformed to mixed phase of amorphous and nanocryatlline, having approximately 10nm grain but the meta stable $Al_3Nb$ was not fabricated by adding transition metals.

• 한국환경과학회:학술대회논문집
• /
• 한국환경과학회 2008년도 추계학술발표회 발표논문집
• /
• pp.510-514
• /
• 2008

본 연구에서는 전극의 특성에 따른 돈사유래 축산폐수의 ECO 공법에 의한 처리특성을 평가하기 위해 ECO 시스템 모듈내 Fe-Fe 및 Al-Al 계열의 용해성 전극과 Al-SUS, Ir-SUS 등 불용성 전극을 대상으로 5$\sim$20mA/cm$^2$의 전류밀도하에서 축산폐수내 유기물 및 영양염류의 제거특성을 평가하여 다음과 같은 결론을 얻을 수 있었다. 1. 전기응집산화에 의한 축산폐수의 처리시 수중 유기물질 및 영양염류의 제거효율은 전류밀도의 증가에 비례하여 증가한다. 2. 불용성 전극조합 및 불용성-용해성 전극조합은 전류밀도가 높을수록 수중 유기물 및 오염물질 제거효율이 안정되고, 용해성 전극은 15mA/cm$^2$ 이하의 저 전류밀도의 조건하에서 전류밀도의 증가에 따라 안정된 제거효율 향상을 기대할 수 있다. 3. 불용성전극 조합인 Ir-SUS 전극조합을 사용하여 축산폐수를 처리할 경우 COD$_{Mn}$ 제거효율을 약 10% 향상시킬 수 있으며, TN 20mA/cm$^2$에서 Al-Al 전극조합과 TP 15mA/cm$^2$ 이하에서 Fe-Fe 전극조합은 제거효율이 저하되는 경향이 나타난다.

• 한국주조공학회지
• /
• 제32권2호
• /
• pp.86-90
• /
• 2012

Aluminium-silicon based casting alloys have received an attention for high electrical and thermal conductivity applications, however relatively low conductivity of Al-Si alloys often limits the application. Efforts have been made to develop new high conductivity aluminium casting alloys containing no or less silicon. In this study Al-Zn-Fe based alloys were selected as the new alloys, and the effect of Mg additions on their properties and casting characteristics were investigated. As the magnesium content was increased, the tensile strength of Al-2Zn-0.2Fe based alloy was remarkably increased, while the electrical conductivity was deteriorated. It was observed that the fluidity of the alloys was generally inversely proportional to the Mg content but the hot cracking resistance was rather proportional to it. Cooling curve analyses were carried out to measure the actual solidification range and dendrite coherency temperature.

• 한국주조공학회지
• /
• 제33권6호
• /
• pp.242-247
• /
• 2013

The most widely utilized commercial, aluminum-casting alloys are based on an aluminum-silicon system due to its excellent casting, and good mechanical, properties. Unfortunately, these Al-Si based alloys are inherently poor energy conductors; compared to pure aluminum, because of their high silicon content. This means that they are not suitable for applications demanding high eletrical or thermal conductivity. Therefore, efforts are currently being made to develop new, highly-conductive aluminum-casting alloys containing no silicon. In this research, a number of properties; including potential for castability, were investigated for a number of Al-Fe-Zn-Cu alloys with varying Cu content. As the copper content was increased, the tensile strength of Al-Fe-Zn-Cu alloy tended to increase gradually, while the electrical conductivity was slightly reduced. Fluidity was found to be lower in high-Cu alloys, and susceptibility to hot-cracking was generally high in all the alloys investigated.

• 한국세라믹학회지
• /
• 제31권9호
• /
• pp.1069-1075
• /
• 1994

When ceramics are used as the parts of an engine and a machine, the tribological properties are very important. For the preparation of the resistance material for wear applications by the method of Reaction-Bonded Sintering, metal silicon and carbon black are mixed up into SiC powder, and Al2O3 and Fe2O3 are put as an additive. As the general properties, the bending strength and water absortion are measured in the normal temperature and the phase changies are investigated with XRD. The property of the resistance for wear applications is measured with the amount of friction and wear, friction coefficient and maximum asperties. And, the surface of wear is observed with SEM. With the results of this study, the optimal mol ratio of Si : C and the suitable quantity of the mixture of SiC are 7 : 3 and 40 wt%, respectively. In the case of the addition of Al2O3 (2 wt%), the resistance for friction and wear applications is prominent. The bending strength showed the highest peak when Al2O3 (4 wt%) and Fe2O3 (4 wt%) were added. The properties of friction and wear were related with the propagation velocity of crack rather than the bending strength.

• 한국재료학회지
• /
• 제27권6호
• /
• pp.318-324
• /
• 2017

In this study, two Fe-30Mn-0.2C-(1.5Al) high-manganese steels with different surface conditions were hydrogen-charged under high temperature and pressure; then, tensile testing was performed at room temperature in air. The yield strength of the 30Mn-0.2C specimen increased with decreasing surface roughness(achieved via polishing), but that of the 30Mn-0.2C-1.5Al specimen was hardly affected by the surface conditions. On the other hand, the tendency of hydrogen embrittlement of the two high-manganese steels was not sensitive to hydrogen charging or surface conditions from the standpoints of elongation and fracture behavior. Based on the EBSD analysis results, the small decrease in elongation of the charged specimens for the Fe-30Mn-0.2C-(1.5Al) high-manganese steels was attributed to the enhanced dislocation pile-up around grain boundaries, caused by hydrogen.

• Journal of the Korean Physical Society
• /
• 제73권11호
• /
• pp.1679-1683
• /
• 2018

Polycrystalline $BaSrCo_2(Fe_{1-x}Al_x)_{12}O_{22}$ (x = 0.00, 0.01, 0.05, and 0.10) samples were synthesized by polymerizable complex method. Based on the Rietveld refinement, crystal structures of the samples were found to be single-phased and determined to be rhombohedral with space group of R-3m. The hysteresis curves of the samples were measured under 15 kOe at various temperatures ranging from 4.2 and 295 K. It shows that they were not saturated with increasing Al ion contents due to the reduction of magnetic anisotropy. $M_{15kOe}$ was decreased with increasing Al ions contents. We expect that non-magnetic Al ions preferentially occupy the up-spin site of $18h_{VI}$, $3b_{VI}$, and $3a_{VI}$. The $M{\ddot{o}}ssbauer$ spectra of the samples were obtained at 295 K, and analyzed with sixsextets for Fe sites corresponding to the Y-type hexaferrite crystallography sites. The <$E_Q$> shows abrupt changes, and the <$H_{hf}$> shows abrupt decreases around x = 0.05 due to the coexistence of magnetic secondary phases.

• 유기물자원화
• /
• 제10권1호
• /
• pp.68-74
• /
• 2002

본 연구는 매립지로의 재순환에 의해 생물학적으로 전처리된 생활폐기물 위생매립장의 침출수를 대상으로 잔류된 생물학적 난분해성 부식질(humus)과 잔류 색깔(color)의 제거를 위해 전기분해법의 적용가능성을 검토하기 위해서 수행되었다. 연구를 통해 얻어진 결과는 다음과 같다. 1) 매립층을 통과한 침출수의 전기분해에서 CODcr과 Color의 제거율은 70~80%범위였고, Color의 제거에서 전기분해만으로도 배출기준을 충족하고 있음을 나타내었다. 2) pH7~8범위에서 가장 높은 제거율을 나타내었다. 3) 양극(+)으로 Al, Fe, Stainless를 사용했을 때 CODcr과 Color의 제거율은 Fe, Al, Stainless순으로 높았고, 반응물의 침전성 또는 전기적인 응집 후의 제거효율을 고려하면 Fe전극이 가장 높았다. 4) 본 연구에서 CODcr과 Color의 동시 제거를 위한 조건은 양극(+)은 Fe, 전극간격은 2cm 그리고 8volt의 전압에서 40분간이었다.

• 한국결정성장학회지
• /
• 제2권2호
• /
• pp.71-76
• /
• 1992

$0.05Pb(Al_{2/3}W_{1/3})O_3-0.95Pb(Zr_{0.52}Ti0.48)O_3$를 기본 조성으로 $MnO_2,Fe_2O_3$를 첨가제로 하여 사진식각법(Photolithography)을 이용 세라믹 필터를 제작하였다. $MnO_2$의 첨가량이 증가함에 따라 전기 기계 결합 계수(Kp)가 낮아지며, $Fe_2O_3$의 경우 Kp값은 57% 정도로 우수하나 기계적 품질 계수(Qm)는 $MnO_2$첨가의 경우에 비해 상대적으로 낮은 값을 보여주고 있다. $MnO_2$0.3wt% 첨가의 경우 3dB 대역폭은 155kHz, $ Fe_2O_3$0.1wt%인 경우 260kHz로써 Qmr값이 크기에 반비례하였으며, 군지연시간 특성은 $MnO_2$의 경우 Gaussian 특성을,$Fe_2O_3$의 경우 Butterworth 특성을 나타내었다.

• 한국재료학회지
• /
• 제18권3호
• /
• pp.153-158
• /
• 2008

Fe-aluminides have the potential to replace many types of stainless steels that are currently used in structural applications. Once commercialized, it is expected that they will be twice as strong as stainless steels with higher corrosion resistance at high temperatures, while their average production cost will be approximately 10% of that of stainless steels. Self-propagating, high-temperature Synthesis (SHS) has been used to produce intermetallic and ceramic compounds from reactions between elemental constituents. The driving force for the SHS is the high thermodynamic stability during the formation of the intermetallic compound. Therefore, the advantages of the SHS method include a higher purity of the products, low energy requirements and the relative simplicity of the process. In this work, a Fe-aluminide intermetallic compound was formed from high-purity elemental Fe and Al foils via a SHS reaction in a hot press. The formation of iron aluminides at the interface between the Fe and Al foil was observed to be controlled by the temperature, pressure and heating rate. Particularly, the heating rate plays the most important role in the formation of the intermetallic compound during the SHS reaction. According to a DSC analysis, a SHS reaction appeared at two different temperatures below and above the metaling point of Al. It was also observed that the SHS reaction temperatures increased as the heating rate increased. A fully dense, well-bonded intermetallic composite sheet with a thickness of $700\;{\mu}m$ was formed by a heat treatment at $665^{\circ}C$ for 15 hours after a SHS reaction of alternatively layered 10 Fe and 9 Al foils. The phases and microstructures of the intermetallic composite sheets were confirmed by EPMA and XRD analyses.