• 한국세라믹학회지
• /
• 제29권5호
• /
• pp.410-418
• /
• 1992

Si3N4, AlN and Y2O3 powder mixtures of the Y0.1(Si, Al)12(N, O)16 composition were hot-pressed at 1900℃ for 0 to 60 min under 30 MPa in order to fabricate the partially-stabilized α-Sialon ceramics (X=0.1). Room and high temperature flexural strengths of the specimens were compared with those of Si3N4-5 wt%Y2O3, Si3N4-5 wt%Y2O3-2 wt%Al2O3, and β-Sialon (Z=0.5) ceramics. The flexural strength of the α-Sialon ceramics which was hot-pressed for 15 min showed the highest value of 820 MPa at 1400℃ that is relatively higher temperature. It is guessed that a little amount of glassy phase existed in grain boundary because Y2O3 and AlN components were incoperated in Si3N4 grains, or transient liquid phase sintering, and microstructure with the smaller grain size and the interlocked grains of α'-and β-Si3N4 was obtained by the hot-pressing at high temperature of 1900℃ for the short time (15 min).

• 한국세라믹학회지
• /
• 제24권1호
• /
• pp.23-32
• /
• 1987

Synthesis of high purity ultrafine Si3N4 and ${\beta}$-Sialon powders was investigated via the simultaneous reduction and nitriding of amorphous SiO2, SiO2-Al2O3 system prepaerd by hydrolysis of alkoxides, using carbonablack as a reducing agent. In Si(OC2H5)4-C2H5 OH-H2 O-NH4OH system, hydrolysis rate increased with increasing reaction temperature and pH. Pure ${\alpha}$-Si3N4 was formed at 1350$^{\circ}C$ for 5 hrs in N2 atmosphere. In Si(OC2H5)4-Al(OC3H7)3-C6H6-H2 O-NH4OH system, weight loss increased as Si/Al ratio decreased. Single phase ${\beta}$-Sialon consisted of Si/Al=2 was formed at 1350$^{\circ}C$ in N2 and minor phases of ${\alpha}$-Si3N4, AIN, and X-phase were existed besides theSialon phase at other Si/Al ratios. The Si3N4 and Sialon powders synthesized from alkoxides consisted of uniform find particles of 0.05-0.2$\mu\textrm{m}$ in diameter, respectively.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.364.1-364.1
• /
• 2014

고효율 태양전지로 가기 위해서는 태양전지의 후면 패시베이션은 중요한 역할을 한다. 후면 패시베이션 막으로 사용되는 $Al_2O_3$ 막은 $Al_2O_3/Si$ 계면에서 높은 화학적 패시베이션과 Negative Fixed Charge를 가지고 있어 적합한 Barrier막으로 여겨진다. 하지만 이후에 전면 Metal paste의 소성 공정에 의해 $800^{\circ}C$이상 온도를 올려주게 됨에 따라 $Al_2O_3$ 막 내부에 결합되어 있던 수소들이 방출되어 blister가 생성되고 막 질은 떨어지게 된다. 우리는 blister가 생성되는 것을 방지하기 위한 방법으로 PECVD 장비로 SiNx를 증착하는 공정 중에 $N_2O$ 가스를 첨가하여 SiON 막을 증착하였다. SiON막은 $N_2O$가스량을 조절하여 막의 특성을 변화시키고 변화에 따라 소성시 막에 미치는 영향에 대하여 조사하였다. 공정을 위해 $156{\times}156mm2$, $200{\mu}m$, $0.5-3.0{\Omega}{\cdot}cm$ and p-type 단결정 실리콘 웨이퍼를 사용하였고, $Al_2O_3$ 막을 올리기 전에 RCA Cleaning 실행하였다. ALD 장비를 통해 $Al_2O_3$ 막을 10nm 증착하였고 RF-PECVD 장비로 SiNx막과 SiON막을 80nm 증착하였다. 소성로에서 $850^{\circ}C$ ($680^{\circ}C$) 5초동안 소성하고 QSSPC를 통해 유효 반송자 수명을 알아보았다.

• 한국세라믹학회지
• /
• 제29권11호
• /
• pp.837-842
• /
• 1992

SiC and Si mixtures dispersed by 0.5~10.0 wt% of Al2O3 and reinforced by SiC whisker were sintered to Si3N4 bonded SiC bodies at 140$0^{\circ}C$ in a N2 gas atmosphere, and the nitridation and mechanical properties of sintered bodies were investigated. From these observation, it is concluded that relative density and bending strength increased with the rising of nitridation and the highest nitridation ratio was obtained for a specimen having 1.5 wt% Al2O3. On the other hand, the amount of $\beta$-Si3N4 in the specimens containing Al2O3 more than 5.0 wt% was increased abruptly and the best in fracture toughness was sintered for a composits having 30 wt% SiC whiskers.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1994년도 춘계 학술발표 강연 및 논문 개요집
• /
• pp.154-154
• /
• 1994

• 센서학회지
• /
• 제2권1호
• /
• pp.29-34
• /
• 1993

본 연구에서는 영상센서를 위해 a-Si : H 광다이오드를 제작하고 그 특성을 조사하였다. a-SiN : H와 p-a-Si : H막의 차단층이 없는 ITO/a-Si : H/Al 광다이오드의 광감도는 5 V의 인가전압에서 0.7로 나타났으며 가시광영역에서의 분광감도는 620 nm의 파장에서 가장 높게 나타났다. ITO/a-SiN : H/a-Si : H/p-a-Si : H/Al 광다이오드의 암전류는 정공차단막과 전자차단막의 작용으로 인하여 10V의 인가전압까지 1.5pA이하로 억제되었다. 또한 광감도는 3 V의 인가전압에서 약 1로 가장 높게 나타났으며 분광감도는 540 nm의 파장에서 최대응답을 보였다.

• 한국진공학회지
• /
• 제10권1호
• /
• pp.27-30
• /
• 2001

절연보호막 처리된 Al-1%Si 박막배선에서 DC와 PDC 조건하에서의 Electromigration 현상에 관하여 조사하였다. $SiO_2$와 PSG/$SiO_2$ 절연보호막 층을 갖는 박막배선은 표준 사진식각 공정으로 제작되었고, 테스트라인 길이는 100, 400, 800, 1200, 1600 $\mu\textrm{m}$이다. Al-l%Si 박막배선에 고정된 전류밀도 $1.19\times10^7\textrm{A/cm}^2$의 DC와 duty factor가 0.5인 1Hz의 주파수에 고정된 전류밀도 $1.19\times10^7\textrm{A/cm}^2$의 PDC를 인가하였다. Electromigration 테스트에서 PSG/$SiO_2$ 절연보호막 시편의 Electromigration 저항성이 $SiO_2$ 절연보호막 시편보다 우수함을 알 수 있었다. PDC 에서 박막 배선의 수명이 DC 보다 2-4배 정도 길게 나타났으며, 박막 배선의 길이가 증가 할 수록 수명이 감소하다가 임계길이 이상에서 포화되는 경향을 보인다. Electromigration에 의한 결함 형태로는 전기적 개방을 야기시키는 보이드와 전기적 단락을 야기시키는 힐록이 지배적이다.

• 한국주조공학회지
• /
• 제23권2호
• /
• pp.77-85
• /
• 2003

Some alloying elements such as Cr, B, Ti and Si were added individually or as a mixture to Fe-30 at.%Al alloys. The alloys were melted using an arc furnace and then heat-treated for homogenization at 1000$^{\circ}C$ for 7 days and followed by rolling at 1000$^{\circ}C$. The alloying elements on rolling characteristics were investigated by the microstructures and fracture mode before and after rolling. The microstructures before rolling showed that all of the alloys had equiaxed grains. On the other hand, the microstructures of rolling plane as well as its perpendicular plane became elongated after rolling. The alloys such as Fe-30Al, Fe-30Al-3Ti, Fe-30Al-0.5B, Fe-30Al-5Cr and Fe-30Al-3Ti-0.5B revealed better rolling behaviour from the point that intergranular and cleavage fractures were not fundamentally occurred. But the addition of 5Ti or 3Si to Fe-Al alloys had detrimental effects. The Ti-added alloy system such as Fe-30Al-5Ti, Fe-30Al-5Ti-5Cr, Fe-30Al-3Ti-5Cr and Fe-30Al-5Ti-0.5B were cracked through grain and showed cleavage fracture. The Si-added alloy system such as Fe-30Al-5Si, Fe-27Al-3Si and Fe-27Al-5Cr-3Si were cracked along the grain boundary and showed intergranular fracture. $DO_3{\leftrightarrow}B_2$ transition temperature of Fe-30at.%Al alloy was 520$^{\circ}C$, whereas the addition of 3Ti and 3Ti+0.5B comparably increased the temperature to 797 and 773$^{\circ}C$, respectively.

• 한국주조공학회지
• /
• 제15권4호
• /
• pp.416-421
• /
• 1995

Recently Al-Cu-P alloys are used to refine primary Si of hypereutectic Al-Si alloys. Because it has inside AlP compound that acts as nucleation site in the melt, Al-Cu-P alloy has good refinement effect in lower holding temperature and after shoter holding times. In this study Al-Cu-P refinement agent was made by mechanical alloying method. When Al-13.5wt%Cu-1.5wt%P was alloyed mechanically for 30hr in Ar atmosphere by high energy ball mill, it had the refinement effect that showed primary Si size of about $30{\mu}m$ in Al-20wt%Si at $760^{\circ}C$, treated for 15min.

• 한국재료학회지
• /
• 제31권3호
• /
• pp.156-161
• /
• 2021

Cr-Si based alloys are not only excellent in corrosion resistance at high temperatures, but also have good wear resistance due to the formation of Cr3Si phase, therefore they are promising as metallic coating materials. Aluminum is often added to Cr-Si alloys to improve the oxidation resistance through which stable alumina surface film is formed. On the other hand, due to the addition of aluminum, various Al-containing phases may be formed and may negatively affect the heat resistance of the Cr-Si-Al alloys, so detailed investigation is required. In this study, two Cr-Si-Al alloys (high-Si & high-Al) were prepared in the form of cast ingots through a vacuum arc melting process and the microstructural changes after high temperature heating process were investigated. In the case of the cast high-Si alloy, a considerable amount of Cr3Si phase was formed, and its hardness was significantly higher than that of the cast high-Al alloy. Also, Al-rich phases (with the high Al/Cr ratio) were not found much compared to the high-Al alloy. Meanwhile, it was observed that the amount of the Al-rich phases reduced by the annealing heat treatment for both alloys. In the case of the high temperature heating at 1,400 ℃, no significant microstructural change was observed in the high Si alloy, but a little more coarse and segregated AlCr phases were found in the high Al alloy compared to the cast state.