• International Journal of Naval Architecture and Ocean Engineering
• /
• v.10 no.6
• /
• pp.762-781
• /
• 2018

This paper presents the ballistic armor performance examination and thickness estimation for the latest naval ship structure materials in the Republic of Korea. Up to date, research regarding methods of ballistic experiments establishing database on the latest hull structure materials as well as a precise method of estimating required thickness of armor against specific projectiles have been rarely researched. In order to build a database and estimate proper thicknesses of structure materials, this study used four structure materials that have been widely applied in naval ships such as AH36 steel, AL5083, AL5086, and Fiber Reinforced Plastics (FRP). A $7.62{\times}39mm$ mild steel core bullet normally fired by AK-47 gun was considered as a threat due to its representativeness. Tate and Alekseevskii's penetration algorithm was also used to calculate a correction factor (${\alpha}$) and then estimate the armor thickness of naval ship hull structure materials with a given impact velocity. Through live fire experiments, the proposed method performance difference was measured to be 0.6% in AH36, 0.4% in AL5083, 0.0% in AL5086, and 8.0% in FRP compared with the experiment results.

• Corrosion Science and Technology
• /
• v.18 no.6
• /
• pp.292-299
• /
• 2019

The hull material of a high-speed ship may cause erosion damage from fluid impact. When physical erosion and electrochemical corrosion combine, erosion corrosion damage occurs. The aluminum ship is vulnerable to erosion corrosion because it can be operated at high speed. Thus, in this study, Al5052-O and Al6061-T6 aluminum alloys for the marine environment were selected as experimental materials. The erosion corrosion resistance of Al5052-O and Al6061-T6 aluminum alloys in seawater was investigated by an erosion test and potentiodynamic polarization test at the various flow rate (0 m/s, 5 m/s, 10 m/s, 15 m/s, 20 m/s). Erosion corrosion characteristics were evaluated by surface analysis, 3D analysis, SEM analysis, and the Tafel extrapolation method. The results of surface damage analysis after the erosion test showed that Al6061-T6 presented better erosion resistance than Al5052-O. The results of the potentiodynamic polarization test at the various flow rate, corrosion current density by Tafel extrapolation presented lower values of Al6061-T6 than Al5052-O. Al5052-O showed more surface damage than Al6061-T6 at all flow rates. Consequently, Al6061-T6 presented better erosion corrosion resistance than Al5052-O. The results of this study are valuable data for selecting hull material for an aluminum alloy vessel.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.18 no.5
• /
• pp.481-487
• /
• 2012

Recently, the construction of the small Al alloy ships is an increasing trend in viewpoint such as the disposal issue of a retired ship, the enhancement of environmental regulation and resources recycling etc. for FRP ships. However, Al alloy ship which can achieve high speed by light weight in marine environment is exposed to a problem on materials damage by cavitation-erosion which is generated by large impact pressure with the collapse of air bubbles due to cavitation. Consequently, in this study, water cavitation peening technology was applied in Al alloy for ship to enhance durability life by preventing cavitation damage. So, the water cavitaton peening application time that presented the excellent cavitation characteristic investigated. The weight-loss of 5456-H116, 5083-H321 and 5052-O Al alloy at the optimum water cavitation peening time were improved to 42.11 %, 50.0 % and 25.7 %, respectively.

• International journal of advanced smart convergence
• /
• v.11 no.3
• /
• pp.7-16
• /
• 2022

The targets of cyber-attacks are not limited to the websites and internal IT systems of shipping agencies. Ships and ports have become important targets for cyber attackers. This paper examines the current state of ship network security, introduces the International Maritime Organization's resolution on ship network security management, and summarizing the cyber-attacks in maritime so the readers can have a general understanding of maritime environment.

• Journal of Korea Ship Safrty Technology Authority
• /
• v.10
• /
• pp.14-21
• /
• 2003

• Journal of Advanced Marine Engineering and Technology
• /
• v.33 no.2
• /
• pp.313-321
• /
• 2009

The construction of fiber-reinforced plastic (FRP) boats is decreasing trend since the application of international regulations on the control of marine environmental pollution, which recommended the use of environmentally friendly materials. The aluminum alloy used with material for ship is a superior to FRP. It is environmental friendly, easy to recycle, and provides a high added value to fishing boats. However, the welding for Al alloy materials have many problems, such as deformation by welding heat and effect of the working environment. In this paper, it was carried out welding by robot with welding material of ER5183 and ER5556 on 6061-T6 Al alloy for ship. The mechanical and electrochemical characteristics evaluated for specimen welded by robot. The cathodic polarization trend for the base metal and welding metal showed the effects of concentration polarization due to oxygen reduction and activation polarization due to hydrogen generation. The hardnesses of welding zone and heat affected zone are lower than that of base metal. At the result of tensile test, the specimen welded with ER5183 presented excellent property compared with ER5556.

• Proceedings of KOSOMES biannual meeting
• /
• 2005.05a
• /
• pp.161-165
• /
• 2005

Recently, it is on the increase interest for Al alloy with new material for ship application to substitute for FRP ship. The reason is thatAl alloy ship has beneficial characteristics such as high sea speed, increase of loadage and easy to recycle compared with FRP ship. In this paper, mechanical and electrochemical properties are investigated by slow strain rate test experiment in various applied potential condition. These results will provide as reference data to design ship by deciding optimum protection potential regard to hydrogen embrittlement and stress corrosion cracking. In general, Al and Al alloys are not corroded with forming film which has the corrosion resistance property in neutral solution. However, it was observed that formation and destruction of passive film by $Cl^-$ ion in sea water environment. At comparison of current density after 1200 sec in potentiostatic experiment, the current density in the potential range of -0.68 $\~$-1.5 V is shown low value. The low current density means protection potential range. Elongation in applied potential of 0 V was high. However, the corrosion protection application in this condition is impossible potential because the toughness is low value by decreasing strength by active dissolution reaction at parallel part of specimen. The film composed with $CaCO_3$ and $Mg(OH)_2$ has a corrosion resistance property. However, the uniform electrodeposition coating at below -1.6 V potential is not formed since the time to form the uniform electrodeposition coating is short. Therefore, it is concluded that mechanical property is poor because effect by hydrogen gas generation is larger than that of electrodeposition coating. It is concluded that the optimum protection potential range from comparison of_maxim urn tensile strength, elongation and time to fracture is -1.3$\~$0.7 V (SSCE).

• 선박안전기술공단 소식
• /
• s.2
• /
• pp.4-4
• /
• 2006

"그림으로 보는 알기 쉬운 기관 점검 · 정비" 책자 발간/ "알루미늄 합금제 어선의 선형개발을 위한 해외사례 조사"/ 2종 스테인리스축 방식용 AL경량합금제 실용화 방안연구

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.245-246
• /
• 2009

The large and high-speed vessels have been greatly advanced, but ship materials have been caused the problem such as corrosion, cavitation and erosion. Cavitation can produce material damage such as pumps, turbines, valves and ship propellers etc. To solve these problems, the cavitation and electrochemical characteristics for thermal spray coating and the sealing are executed to obtain the excellent corrosion protection characteristics in sea water environment.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2011.06a
• /
• pp.283-283
• /
• 2011