• Korean Journal of Metals and Materials
• /
• v.49 no.11
• /
• pp.910-915
• /
• 2011

The microstructures and mechanical properties of roll-bonded STS439/Al1050/STS304 clad materials were investigated after an annealing process at various temperatures. Interfacial layer was developed at the STS439/Al1050 and Al1050/STS304 interfaces at $550^{\circ}C$. STS439/Al1050/STS304 clad metals fractured suddenly in a single step and the fracture decreased with increasing annealing temperatures at $450^{\circ}C$. After annealing at $550^{\circ}C$, samples fractured in three steps with each layer fracturing independently. Interfacial layers formed at $550^{\circ}C$ with a high Vickers microhardness were found to be brittle. During tensile testing, periodic parallel cracks were observed at the interfacial reaction layer. Observed micro-void between Al1050 and the interfacial layer was found to weaken the Al1050/reaction layer interface, leading to the total separation between Al1050 and the reaction layer.

• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.1
• /
• pp.47-54
• /
• 1999

Microstructure of Al-Si coated PWA 1426 alloy was studied. Diffusion coated specimens were heat treated for 4hr at $870{\sim}1087^{\circ}C$ and then were examined the changes of microstructure and interfacial compound by optical microscopy, SEM and EDS. According to the result of EDS, it is supposed that the coated layer was composed of $Ni_2Al_3$. When diffusion treatment was conducted at $1087^{\circ}C$, coated layer varied from $Ni_2Al_3$ to NiAl phase and composed of mixed, denuded and inter-diffusion layer.

• Korean Journal of Materials Research
• /
• v.27 no.7
• /
• pp.374-380
• /
• 2017

Properties of coatings produced by warm spray were investigated in order to utilize this technique as a repair method for Al tire molds. $Al-(0-10%)Al_2O_3$ composite powder was sprayed on Al substrate by warm spraying, and the microstructure and mechanical properties of the composite coating layer were investigated. For comparative study, the properties of the coating produced by plasma spray, which is a relatively high-temperature spraying process, were also investigated. The composite coating layers produced by the two spray techniques exhibited significantly different morphology, perhaps due to their different process temperatures and velocities of particles. Whereas the $Al_2O_3$ particles in the warm sprayed coating layer maintained their initial shape before the spray, flattened and irregular shape $Al_2O_3$ particles were distributed in the plasma sprayed coating layer. The coating layer produced by warm spray showed significantly higher adhesive strength compared to that produced by plasma spray. Hardness was also higher in the warm sprayed coating layer compared to the plasma sprayed one. Moreover, with increasing the fraction of $Al_2O_3$, hardness gradually increased in both spray coating processes. In conclusion, an $Al-Al_2O_3$ composite coating layer with good mechanical properties was successfully produced by warm spray.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.4
• /
• pp.278-285
• /
• 1996

The structure of coating layer formed by hot dip Al-Cu alloy coating on Monel 1400 metal was studied. The coating layer consists of alloyed layer adjacent to the Monel 400 substrate and Al-Cu alloy. It was found that the hardness of coating increased with dipping time and heat treatment associated with the diffusion and the formation of intermetallic compound at the interface. However the thickness of coating layer was decreased at high dipping temperature due to tile higher viscosity of liquid coating alloy. Diffusion heat treatment at $600^{\circ}C$ after coating resulted in the disappearence of adhered Al(Cu) and $CuAl_2$ phases, and then they transformed into the new phases of CuAl and Al7Cu4Ni at coating layer.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.6
• /
• pp.408-414
• /
• 2002

TiN and TiAlN coating layer were deposited on WC-Co steel substrates by an arc ion plating(AIP) technique. The crystallinity and morphology for the deposited coating layers were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The impact behaviors of the deposited TiN and TiAlN coating layer were investigated with a ball-on-plate impact tester. Beyond $10^2$ impact cycle, TiAlN coating layer showed superior impact wear resistance compared to TiN coating layer. On the other hand, both TiN and TiAlN coating layers started to be partially failed between $10^2$ and $10^3$ impact cycle. Above $10^3$ impact cycle, TiN and TiAlN coating layers showed similar impact behavior because of the substrate effect.

• Korean Journal of Materials Research
• /
• v.26 no.3
• /
• pp.160-165
• /
• 2016

To increase the capacitance of an Al electrolytic capacitor, the anodic oxide film, $Al_2O_3$, was partly replaced by an $Al_2O_3-ZrO_2$ (Al-Zr) composite film prepared by the vacuum infiltration method and anodization. The microstructure and composition of the prepared samples were investigated by scanning electron microscopy and transmission electron microscopy. The coated and anodized samples showed multi-layer structures, which consisted of an inner Al hydrate layer, a middle Al-Zr composite layer, and an outer $Al_2O_3$ layer. The thickness of the coating layer could go up to 220 nm when the etched Al foil was coated 8 times. The electrical properties of the samples, such as specific capacitance, leakage current, and withstanding voltages, were also characterized after anodization at 100 V and 600 V. The capacitances of samples with $ZrO_2$ coating were 36.3% and 27.5% higher than those of samples without $ZrO_2$ coating when anodized at 100 V and 600 V, respectively.

• Journal of Sensor Science and Technology
• /
• v.8 no.5
• /
• pp.421-426
• /
• 1999

In this paper, we present p-channel GaAs MOSFET having $Al_2O_3$ as gate insulator fabricated on a semi-insulating GaAs substrate, which can be operated in the depletion mode. $1\;{\mu}m$ thick undoped GaAs buffer layer, $4000\;{\AA}$ thick p-type GaAs epi-layer, undoped $500{\AA}$ thick AlAs layer, and $50\;{\AA}$ thick GaAs cap layer were subsequently grown by molecular beam epitaxy(MBE) on (100) oriented semi-insulating GaAs substrate and this wafer was oxidized. AlAs layer was fully oxidized as a $Al_2O_3$ thin film. The I-V, $g_m$, breakdown charateristics of the fabricated GaAs MOSFET showed that wet thermal oxidation of AlAs/GaAs epilayer/S I GaAs was successful in realizing depletion mode p-channel GaAs MOSFET.

• Korean Journal of Materials Research
• /
• v.19 no.4
• /
• pp.207-211
• /
• 2009

In this study, we attempted to develop a convenient aluminizing process, using Al-Ti mixed slurry as an aluminum source, to control the Al content of the aluminized layer as a result of a one-step process and can be widely adopted for coating complex-shaped components. The aluminizing process was carried out by the heat treatment on disc and rod shaped S45C steel substrates with Al-Ti mixed slurries that were composed of various mixed ratios (wt%) of Al and Ti powders. The surface of the resultant aluminized layer was relatively smooth with no obvious cracks. The aluminized layers mainly contain an Fe-Al compound as the bulk phase. However, the Al concentration and the thickness of the aluminized layer gradually decrease as the Ti proportion among Al-Ti mixed slurries increases. It has also been shown that the Al-Ti compound layer, which formed on the substrate during heat treatment, easily separates from the substrate. In addition, the incorporation of Ti into the substrate surface during heat treatment was not observed.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.4
• /
• pp.65-70
• /
• 2015

A study on thermal properties for a single-layer metal and two-layer composites was investigated for the heat-sink application. For the single-layer metal, an aluminum alloy (Al6061) was selected. A screen printed aluminum nitride (AlN) layer on the Al6061 substrate was chosen for the two-layer composites. The thermal conductivity of the sample was determined from the thermal diffusivity measured by the light flash analysis (LFA), specific heat and density. Measured thermal property values were compared to calculated values using the data from the references. The thermal conductivity of composites with screen printed AlN layer on the Al6061 substrate decreased linearly with increasing the thickness of AlN layer. Measured values of the thermal conductivity for composites with $53{\mu}m$ and $163{\mu}m$ thick AlN layers were $114.1W/m{\cdot}K$ and $72.3W/m{\cdot}K$, respectively. In particular, the thermal conductivity of the screen-printed AlN layer was demonstrated by appling the rule of mixture in view point of thermal resistivity. Measured values of the thermal conductivity for AlN layers with the thickness of $53{\mu}m$ and $163{\mu}m$ showed $9.35W/m{\cdot}K$ and $12.40W/m{\cdot}K$, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.9
• /
• pp.589-593
• /
• 2014

AlNO multi-layer thin films on aluminum substrates were prepared by DC reactive magnetron sputtering method. $Al_2O_3$/AlNO(LMVF)/AlNO(HMVF)/Al/substrate of 4 multi-layer has been prepared in an Ar and ($N_2+O_2$) gas mixture, and $Al_2O_3$ of top layer is anti-reflection layer on double AlNO(LMVF)/AlNO(HMVF) layers and Al metal of infrared reflection layer. In this study, the roughness and surface properties of AlNO thin films were estimated by field emission scanning electron microscopy(FE-SEM). The grain size of AlNO thin films increased with increasing sputtering power. The composition of thin films has been systematically investigated using electron probe microanalysis(EPMA). The optical properties with wavelength spectrum were recorded by UV-Vis-NIR spectrophotometry at a range of 200~1,500 nm. The absorptance of AlNO films shows the increasing trend with swelling ($N_2+O_2$) gas mixture in HMVF and LMVF deposition. The excellent optical performance showed above 98% of absorptance in visible wavelength region.