• Journal of Korea Foundry Society
• /
• v.17 no.4
• /
• pp.356-364
• /
• 1997

In order to study effects of Cu and Be on the microstructure and tensile properties of rapidly solidified Al-Mg alloys, Al-Mg-Cu-Be alloys have been rapidly solidified by inert gas atomization process. Microstructure of rapidly solidified Al-Mg-Cu-Be powders exhibited refinement and good dispersion of Be particles as increasing of solidification rate. Solidification rate of atomized powders was estimated to be about $5{\times}10^{3{\circ}}C/s$. Inert gas atomized Al-Mg-Cu-Be powders were hot-processed by vacuum hot pressing at $450^{\circ}C$ under 100 MPa and hot extruded with reduction ratio in area of 25: 1 at $450^{\circ}C$. The extruded Al-Mg-Cu-Be powders consisted of recrystallized fine Al grains and homogeneously dispersed fine Be particles, and exhibited improved tensile properties with increase in Cu content. $Al_2CuMg$ compounds precipitated in grain and grain boundaries of Al-Mg-Cu-Be alloys with aging heat treatment after solution treatment. Hardness and tensile properties were improved by increasing Cu content and Be addition. Compared with extruded Al-Mg-Cu powders, the extruded Al-Mg-Cu-Be powders exhibited finer recrystallized grains and improved tensile properties by dispersion hardening of Be and subgrain boundaries pinned by fine Be particles. After aging treatment, hardness and tensile properties were improved due to restricted precipitation by increasing of dislocation density around Be particles in matrix.

• Archives of Metallurgy and Materials
• /
• v.66 no.3
• /
• pp.699-702
• /
• 2021

Effect of Cu addition on oxide growth of Al-7 mass%Mg alloy at high temperature was investigated. As-cast microstructures of Al-7 mass%Mg and Al-7 mass%Mg-1 mass%Cu alloys showed α-Al dendrites and area of secondary particles. The 1 mass%Cu addition into Al-7 mass%Mg alloy formed Mg₃₂(Al, Cu)₄₉ ternary phase with β-Al₃Mg₂. The total fraction of two Mg-containing phases in Cu-added alloy was higher than the β-Al₃Mg₂ fraction in Cu-free alloy. From measured weight gains depending on time at 500℃ under an air atmosphere, it was shown that all samples exhibited significant weight gains depending on time. Al-7mass%Mg-1mass%Cu alloy showed the relatively increased oxidation rate when compared with Cu-free alloy. All the oxidized cross-sections throughout the entire oxidation time showed coarse and dark areas regarded as oxides grown from the surface to inside, but bigger oxidized areas were formed in the Al-7mass%Mg-1mass%Cu alloy containing higher fraction of Mg-based phases in the as-cast microstructure. As a result of compositional analysis on the oxide clusters, it was found that the oxide clusters contained Mg-based oxides formed through internal oxidation during a long time exposure to oxidizing environments.

• Korean Journal of Materials Research
• /
• v.12 no.8
• /
• pp.656-660
• /
• 2002

It was investigated that $Al_2$$O_3$/Cu nanocomposite powder could be optimally prepared by dispersion and reduction of Cu oxide, and suitably consolidated by employing pulse electric current sintering (PECS) process. $\alpha$-$Al_2$$O_3$ and CuO powders were used as elemental powders. In order to obtain $Al_2$O$_3$ embedded by finely and homogeneously dispersed CuO particles, the elemental powders were high energy ball milled at the rotating speed of 900 rpm, with the milling time varying up to 10 h. The milled powders were heat treated at $350^{\circ}C$ in H$_2$ atmosphere for 30 min to reduce CuO into Cu. The reduced powders were subsequently sintered by employing PECS process. The composites sintered at $1250^{\circ}C$ for 5 min showed the relative density of above 98%. The fracture toughness of the $Al_2$$O_3$/Cu nanocomposite was as high as 4.9MPa.$m^{1}$2//, being 1.3 times the value of pure $Al_2$$O_3$ sintered under the same condition.

• Journal of Welding and Joining
• /
• v.3 no.2
• /
• pp.27-34
• /
• 1985

The mechanical properties and bonding mechanism of aluminum, copper and mild steel have been determined in cold pressure welding. The brittle cover layer to be established by scratch-brushing plays an important role in bond strength and has an influence on the threshold of deformation. The cold pressure welding was achieved at 54% of height reduction in A1-A1, 75% in Cu-Cu, 56% in Al-Cu, and 74% in Cu-steel. The height reduction at which the bond strength of weld interface was the same as the tensile strength of base metal should be over 76% in Al-Al, 82% in Cu-Cu, and 78% in Al-Cu.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.5
• /
• pp.257-261
• /
• 2006

Scandium(Sc) in Al-Zn-Mg-Cu based Al alloy on precipitation phenomenon was compared to a 7001(Al-7.2%Zn-3.2%Mg-1.8%Cu) Al alloy. GP zone and ${\eta}^{\prime}$ phases were the main strengthening phases at low aging temperature under $100^{\circ}C$, but ${\eta}^{\prime}$ and $Al_3Sc$ phases were the main strengthening phases at high aging temperature above $1600^{\circ}C$ in Sc added 7000(Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr) Al alloy. With the addition of 0.1%Sc in 7000 Al alloy, the activation energy for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phase decreased compared to the 7001 Al alloy. This result indicates that the Sc accelerated the precipitation for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phases in 7000 Al alloy. Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr-0.1 Sc alloy has higher strength than 7001 Al alloy, which has high strength.

• Journal of the Korean Chemical Society
• /
• v.30 no.5
• /
• pp.415-422
• /
• 1986

The metal-support interaction of copper oxide supported on ${\gamma}$-alumina and silica was studied by X-ray diffraction (XRD) and temperature-programmed reduction(TPR). It was found that XRD pattern of CuO can not be observed up to 5.0wt % copper content for CuO/${\gamma}-Al_2O_3$ while CuO/$SiO_2$ sample shows the CuO pattern even at 2.5wt% copper content. $H_2-$TPR of CuO/${\gamma}-Al_2O_3$ system shows four major peaks at 145${\circ}C$, 185${\circ}C$, 210${\circ}C$, and 250${\circ}C$. In the case of CuO/$SiO_2$, a large peak at 250${\circ}C$ was appeared accompanying a small peak at 425${\circ}C$. Comparing the TPR peaks with that of copper aluminate which was prepared from the calcination of CuO/${\gamma}-Al_2O_3$ at 1000${\circ}C$, the peaks at around 145${\circ}C$, 200${\circ}C$ (185${\circ}C$ and 210${\circ}C$), and 250${\circ}C$ were corresponded to $Cu^+$ ion in CuO interacting ${\gamma}-Al_2O_3$, $Cu^+$ ions in defect sites of ${\gamma}-Al_2O_3$ and $Cu^{2+}$ ion in the bulk CuO layer, respectively. From the results, it was concluded that there is considerable metal-support interaction in CuO on ${\gamma}-Al_2O_3$ and the interaction results in a stabilization of $Cu^+$ ion in the system.

• Journal of Korea Foundry Society
• /
• v.15 no.4
• /
• pp.351-359
• /
• 1995

The effects of In and Be additions on the aging behaviors and mechanical properties in the Al-Cu-Li alloy were investigated using the transmission electron microscope, the scanning electron microscope, hardness and tensile strength measurement. The aging is promoted and the double hardness peak is appeared by the addition of In and Be in the Al-Cu-Li alloy. The strength is increased, but the elongation and toughness are decreased by the addition of In in the Al-Cu-Li alloy. And the Al-Cu-Li-In-Be alloy has good combination with the strength, the elogation and toughness than Al-Cu-Li-In alloy.

• Tribology and Lubricants
• /
• v.27 no.1
• /
• pp.1-6
• /
• 2011

The possibility of Cu-Al-Ni intermetallic coating on the mild steel through the combustion synthesis has been investigated. In particular, the effect of the ball milling energy on the microstructure of the coating layer was examined to obtain the best coating condition. Experimental results show that Cu-Al-Ni powder compact was explosively synthesized and successfully coated with the steel matrix. It was revealed that the formation of $Cu_9Al_4$ intermetallic decreased with increase in the ball milling energy. This result supports that the high energy ball milling would be effective for obtaining the most suitable microstructure for Cu-Al-Ni coating layer. However, the excessive ball milling energy seems to decrease the bonding strength between the coating layer and the matrix.

• Korean Journal of Chemical Engineering
• /
• v.36 no.2
• /
• pp.191-196
• /
• 2019

The phase of Cu,Zn,Al precursors strongly affects the activity of their final catalysts. Herein, the Cu,Zn,Al precursor was prepared by precipitation of $Al^{3+}$ onto primitive, amorphous Cu,Zn precipitate. This precursor turned out to be a phase mixture of zincian malachite and hydrotalcite in which the latter phase was less abundant compared to the co-precipitated precursor. The final catalyst derived from this precursor exhibited a little higher copper surface area and methanol synthesis activity than the co-precipitated counterpart. Therefore, the two precursor phases need to be mixed in an adequate proportion for the preparation of active $Cu/ZnO/Al_2O_3$ catalyst.

• Journal of the Semiconductor & Display Technology
• /
• v.9 no.3
• /
• pp.1-4
• /
• 2010

First-principles calculations based on spin density functional theory are performed to study the spin-resolved electronic properties of AlN doped with a Cu concentration of 6.25%-18.75%. The ferromagnetic state is more energetically favorable state than the antiferromagnetic state or the nonmagnetic state. For $Al_{0.9375}Cu_{0.0625}N$, a global magnetic moment of 1.26 mB per supercell, with a localized magnetic moment of 0.75 $m_B$ per Cu atom is found. The magnetic moment is reduced due to an increase in the number of Cu atoms occupying adjacent cation lattice position. For $Al_{0.8125}Cu_{0.1875}N$, the magnetism of the supercell disappears by the interaction of the neighboring Cu atoms. The nonmagnetic to ferromagnetic phase transition is found to occur at this Cu concentration. The range of concentrations that are spin-polarized should be restricted within very narrow.