• Journal of the Korean Ceramic Society
• /
• 제30권12호
• /
• pp.999-1006
• /
• 1993

Si3N4(p)-SiC(p) composites were prepared by gas pressure sintering at 190$0^{\circ}C$ for 1 hour. $\alpha$-SiC with average particle size of 0.48${\mu}{\textrm}{m}$ were dispersed from zero to 50vol% in $\alpha$-Si3N4 with average particle size of 0.5${\mu}{\textrm}{m}$. Y2O3-Al2O3 system was used as sintering aids. When 10vol% of SiC was added to Si3N4, optimum mechanical properties were observed; relative density of 98.8%, flextural strength of 930MPa, fracture toughness of 5.9MPa.m1/2 and hardness value of 1429kg/$\textrm{mm}^2$. Grain growth of $\beta$-Si3N4 was inhibited as the amount of added SiC was increased. SiC particles were found inside the $\beta$-Si3N4 intragrains in case of 10, 20 and 30vol%SiC added composites.

• Journal of Technologic Dentistry
• /
• 제42권4호
• /
• pp.326-333
• /
• 2020

Purpose: The purpose of this study was to evaluate the effects of various zirconia surface treatment methods on shear bond strength with resin cements. Methods: We prepared 120 cylindrical zirconia specimens (⌀10 mm×10 mm) using computer-aided design/computer-aided manufacturing (CAD/CAM). Each specimen was randomly subjected to one of four surface treatment conditions: (1) no treatment (control), (2) airborne-particle abrasion with 50 ㎛ of Al2O3 (A50), (3) airborne-particle abrasion with 125 ㎛ of Al2O3 (A125), and (4) ZrO2 slurry (ZA). Using a polytetrafluoroethylene mold (⌀6 mm×3 mm), we applied three resin cements (Panavia F 2.0, Super-Bond C&B, and Variolink N) to each specimen. The shear bond strength tests were performed in a universal testing machine. The surfaces of representative specimens of each group were evaluated under scanning electron microscope. We used one-way analysis of variance (ANOVA), two-way ANOVA, and post hoc Tukey honest significant difference test to analyze the data. Results: In the surface treatment method, the A50 group showed the highest bond strength, followed by A125, ZA, and control groups; however, no significant difference was observed between A50 and A125, A125 and ZA, and ZA and control (p>0.05). Among the resin cements, Super-Bond C&B showed the highest shear bond strength, followed by Panavia F 2.0 and Variolink N (p<0.05). Conclusion: Within the limitations of this study, application of airborne-particle abrasion and ZrO2 slurry improved the shear bond strength of resin cement on zirconia.

• Journal of the Korean Ceramic Society
• /
• 제35권8호
• /
• pp.783-790
• /
• 1998

The characterization of the complexation reaction of PVA and Al(III) ion at different pH and the sint-ering behaviour of UO2 containing the PVA-Al(III) complexes were investigated. Compared with pure PVA powder the complexed PVA-Al(III) powder had compacter shape and lower decomposition temperature The major phase of PVA-Al(III) complex decomposed at 90$0^{\circ}C$ was $\alpha$-Al2O3 The PVA-Al(III) complex formed at pH 9 had the lowest relative viscosity the highest Al content of 36% and the smallest particle size of 19${\mu}{\textrm}{m}$ While the pure UO2 pellet appeared with bimodal one. The grain size of the pure UO2 pellet was 7${\mu}{\textrm}{m}$ but that of the PVA-Al(III) complex added UO2 pellet was increased up to 36${\mu}{\textrm}{m}$ The largest grain size was ob-tained when the PVA-Al(III) complex formed at pH9 was added and the PVA-Al(III) complex formed at pH 11 had the greatest effect on increasing pore size.

• 연구논문집
• /
• 통권22호
• /
• pp.151-160
• /
• 1992

The wear resistance of electroless Ni-P-X(X A1203, Diamond) composite coating layers was studied by Taber abrasion test technique. The wear resistance of composite coating layers was particularly relied upon the codeposited content, particle size and distribution of particles, and heat treatment of coating layers, as well as the electroless nickel plating bath employed. In this study, we lay emphasis on the wear resistance of electroless composite coating layers containing A1203 particles(1.2~Im, 6.7hIm, 11.5lIm, 20l1m) or diamond particles (1.5jim, 5gm). From the result of composite coating A1203 and diamond particles, the wear resistance of composite coating layers is as follows.

• Proceedings of the IEEK Conference
• /
• 대한전자공학회 2001년도 The 6th International Symposium of East Asian Resources Recycling Technology
• /
• pp.353-356
• /
• 2001

The relation between the flocculation and dispersion of metal oxide powders and the properties of solvents, such as dielectric constant and solubility parameter, was investigated for TiO$_2$, $Al_2$O$_3$and Fe$_2$O$_3$particles. The particle size and median diameter of these metal oxides were measured in many organic solvents, from which the effect of solvents on the flocculation and dispersion of metal oxide powders was considered. The metal oxide powders of TiO$_2$, $Al_2$O$_3$and Fe$_2$O$_3$tend to disperse in a solvent of higher polarity, whereas they are apt to flocculate in a solvent of low dielectric constant, because the Hamaker constant between the particles becomes larger in such a solvent. There we, however, some solvents that do not obey these tendencies. It is possible to evaluate the flocculation and dispersion of these metal oxide powders in many solvents by using numeral balances of Hansen’s three-dimensional solubility parameter (f$_{d}$, f$_{p}$ and f$_{h}$). There exists a solvent giving the optimal dispersion for each metal oxide, and the optimal dispersion point of f$_{d}$, f$_{p}$ and f$_{h}$ is determined by the combination of various metal oxide powders and solvents.nts.nts.nts.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 한국전기전자재료학회 2002년도 추계학술대회 논문집 Vol.15
• /
• pp.116-119
• /
• 2002

A different route to the synthesis of $Eu^{3+}$ - activated matrices such as $YAlO_{3}$ and $GdAlO_{3}$ and luminiscent properties of these compounds, were studied. The new route (Combustion method) consist of the redox reactions between the respective metal nitrates and urea in a preheated furnace at ${500^{\circ}C}$. The Phosphor thus obtained were then heated at ${1000^{\circ}C}$ for 2-3 hours to get better luminiscent properties. The incorporation of $Eu^{3+}$ activator in these phosphors were checked by luminiscence investigations. Scanning electron microscopy (SEM) studies were carried out to understand surface morphological features and the particle size. X-ray energy dispersive analysis (EDAX) was also performed for the qualitative analysis of the phosphors.

• Journal of the Korean Ceramic Society
• /
• 제25권3호
• /
• pp.193-200
• /
• 1988

The starting materials were aluminum hydroxide prepared by precipitation method at the conditions of pH values; 7, 9, 10 and 11. The properties of alumina powder on heat-treatment were studied. After dehydrating structural water from amorphous aluminum hydroxide, the first formed phase was amorphous alumina and its specific surface are was decreased. The specific surface area was increased by dehydration of structural water from aluminum hydroxides except amorphous aluminum hydroxide. The specific surface area was increased with increase of the ratio of A1OOH to $A1(OH)_3$ in the region of transition aluminas. The rate of transition from aluminum hydroxide to alpha alumina occurred in the order of 7, 10, 9 and 11 of pH values. The morphology of alpha alumina powders was skeleton particles remaining outer shape of aluminum hydroxide. Both the elevation of heat-treatment temperature and the transition toalpha alumina decreased specific surface area and brought about the growth of particles.

• Journal of the Korea Institute of Building Construction
• /
• 제17권6호
• /
• pp.517-525
• /
• 2017

Red mud is an industrial by-product produced during the manufacturing aluminum hydroxide ($Al(OH)_3$) and aluminum oxide($Al_2O_3$) from Bauxite ores. In Korea, approximately 2 tons of red mud in a sludge form with 50% moisture content is produced when 1ton of $Al_2O_3$ is produced through the Bayer process. In the paper, dispersion characteristics of liquefied red mud that does not require heating and grinding process for recycling were investigated through viscosity and sediment index. The results showed that the sediment index of liquefied red mud increased but viscosity of that decreased with a higher W/R ratio. Also we proposed the range of initial viscosity from 2000cP to 8000cP and target sedimentation index below 20% at elapsed time 180days for stable dispersion of liquefied red mud.

• Resources Recycling
• /
• 제20권2호
• /
• pp.54-59
• /
• 2011

An investigation on the synthesis of aluminum tartrate, one of the aluminum organic compounds, has been performed using aluminum chloride solution as a raw material. For this aim, the effect of the ratio of ethanol/Al solution and pH on the synthesis of aluminum tartrate has been examined and aluminum tartrate synthesized has also been characterized in terms of the chemical composition, X-ray diffraction pattern, particle size distribution, and SEM analysis. As a result, the synthesis more than 97% could be obtained under the conditions of pH more than 3.0 at the ratio of ethanol/Al solution of 3.0. From the chemical analysis of aluminum tartrate synthesized in this work, the content of $NH_4$, Al and C was found to be 9.10, 4.83 and 25.8%, respectively. In addition, aluminum tartrate synthesized from the aluminum chloride solution was found to be $(NH_4)_3Al(C_4H_4O_6)_3$.

• The Journal of Advanced Prosthodontics
• /
• 제10권1호
• /
• pp.43-49
• /
• 2018

PURPOSE. The purpose of this in vitro study is to examine the effects of a nano-structured alumina coating on the adhesion between resin cements and zirconia ceramics using a four-point bending test. MATERIALS AND METHODS. 100 pairs of zirconium bar specimens were prepared with dimensions of $25mm{\times}2mm{\times}5mm$ and cementation surfaces of $5mm{\times}2mm$. The samples were divided into 5 groups of 20 pairs each. The groups are as follows: Group I (C) - Control with no surface modification, Group II (APA) - airborne-particle-abrasion with $110{\mu}m$ high-purity aluminum oxide ($Al_2O_3$) particles, Group III (ROC) - airborne-particle-abrasion with $110{\mu}m$ silica modified aluminum oxide ($Al_2O_3+SiO_2$) particles, Group IV (TCS) - tribochemical silica coated with $Al_2O_3$ particles, and Group V (AlC) - nano alumina coating. The surface modifications were assessed on two samples selected from each group by atomic force microscopy and scanning electron microscopy. The samples were cemented with two different self-adhesive resin cements. The bending bond strength was evaluated by mechanical testing. RESULTS. According to the ANOVA results, surface treatments, different cement types, and their interactions were statistically significant (P<.05). The highest flexural bond strengths were obtained in nano-structured alumina coated zirconia surfaces (50.4 MPa) and the lowest values were obtained in the control group (12.00 MPa), both of which were cemented using a self-adhesive resin cement. CONCLUSION. The surface modifications tested in the current study affected the surface roughness and flexural bond strength of zirconia. The nano alumina coating method significantly increased the flexural bond strength of zirconia ceramics.