• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2008년도 제39회 하계학술대회
• /
• pp.1209-1210
• /
• 2008

According to previous report, aged sleeves for old transmission lines have variable defects such as biased installed case or corrosion of steel sleeve. Biased installed sleeve occupied 20 percent among the investigated aged sleeves. This defect must cause local heating of splice connector and limit power transmission capacity. It even inspire falling out of overhead conductor from sleeves. This paper studies thermal properties and tension for ACSR conductor in case of biased installed sleeve model. The detailed results were presented in the text.

• 한국전기전자재료학회논문지
• /
• 제19권3호
• /
• pp.287-291
• /
• 2006

This paper describes mechanical and electric properties of ACSR $410\;mm^2$ conductor from many of older overhead conductor. Samples of conductors itemized two division according to operation sector, green area, salt and pollution area. Samples of conductors operated various environment conditions have undergone laboratory metallurigical investigation and tensile strength torsional ductility and electrical performance. The steel core were found to have retained their original properties to a large degree in both tensile strength and the number of turns to failure. On the other hand the aluminum conductor showed reductions in tensile strength. To determine the remaining useful life of aged conductor, an unacceptable deterioration level has to established for each diagnostic procedure.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.78-83
• /
• 2004

Environmental fatigue crack propagation of CF8M and CF8A steels used in the domestic PWR were investigated on the simulated PWR condition(Temperature: $316^{\circ}C$, Pressure: 15MPa). The test equipment for environmental fatigue(high temperature-high pressure loop, autoclave, load frame, measurement system) were designed. As-received and 60-year aged specimens were used in the test. To compare with environmental fatigue test, another test was performed in the air condition. The fracture surface of specimens were difficult to verify the fracture modes such as striation, intergranular crack and cleavage and so on. As the ferrite content of CF8M is increased, more particles covered fracture surface were peeled.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2013년도 추계 학술논문 발표대회
• /
• pp.134-136
• /
• 2013

In general, the seismic retrofit is almost essential to extend and remodel aged buildings. Because domestic seismic design code has been enhanced, seismic performance should be secure for aged building remodeling. Seismic response reduction device (damper) is lately appling to ensure seismic performance. This device is economical efficiency method that can reduce the load to foundation and the range of structural reinforcements, shorten of construction period. New shaped steel damper was applied for extension and remodeling construction for Boramae Deakyo building. As a result, the economy and shortening of construction period was achieved.

• 비파괴검사학회지
• /
• 제30권5호
• /
• pp.464-470
• /
• 2010

고온, 고압에서 운용되고 있는 설비의 안전성을 평가하기 위해서는 사용시간 동안 열화된 역학물성을 정기적으로 점검하여야 한다. 비파괴적으로 열화된 설비의 역학적 특성을 점검하기 위하여 표면형 프로브(surface type probe)를 사용한 가역투자율 측정방법이 제시된다. 가역투자율 측정방법은 가역투자율이 자기 이력곡선의 미분값임에 근거하고 있다. 가역투자율은 교류 섭동 자기장의 주파수에 동조된 록-인 증폭기로 측정된 탐지코일에 유도된 전압의 제 1 고조파이다 가역투자율의 첨두값은 보자력 영역에서 나타난다. 실험에 사용된 강재는 12Cr 페라이트 내열강으로 $700^{\circ}C$의 등온에서 열처리 시간을 달리한 11개의 시편을 제작하였다. 가역투자율 첨두값 사이의 간격 (peak interval of reversible permeability: PIRP), 비커스 경도 및 인장강도는 열화가 진행됨에 따라 초기에는 급격하게, 후반에는 완만하게 감소하였다. PIRP가 감소함에 따라 인장강도와 비커스 경도가 선형적으로 감소하였고 이 상관관계를 이용하면 측정한 가역투자율로 12Cr 페라이트 내열강의 열화된 역학적 물성을 비파괴적으로 평가할 수 있다.

• Journal of Welding and Joining
• /
• 제5권2호
• /
• pp.53-59
• /
• 1987

The effect of applied stress, current density and heat-treatment after welding on the time to fracture, fracture behavior was investigated by the method of constant load tensile testing under catholic charging with hydrogen in E.B. welded 250,300 Grade 18% Ni Maraging steel sheet. The main results obtained are as follows: 1. All specimen showed the characteristic delayed failure and the time to fracture showed decreasing tendency with the increase in current density and applied stress. 2. Hydrogen embitterment susceptibility of notched specimen after solution-treatment and aging after welding was more increased than that of aged smooth specimen and as welded specimen. 3. Fracture surface showed a typical intergranular fracture on the border, a dimple pattern in the center of specimen and some quasi-cleavage fracture between the intergranular and the dimple.

• 한국공작기계학회논문집
• /
• 제10권3호
• /
• pp.61-67
• /
• 2001

The remaining life estimation for the aged component is very important because mechanical properties of the compo-nents are degraded with time of service exposure in high temperature etc. The destructive method is widely used for the estimation of material degradation, but it has a difficulty in preparing specimens from in-service industrial facilities. In order to evaluate the feasibility of ultrasonic evaluation method for properties of high temperature materials, 2.25Cr-1Mo steel specimens which were prepared by the isothermal aging heat treatment at 63$0^{\circ}C$ were evaluated by ultra-sonic measurements investigating the change of velocities and attenuation coefficient. In this results, attenuation coefficient was found to be sensitive to material degradation mainly attributed to the change of grain size and the precipitation of impurities in grain boundaries, but velocity was not for all specimens.

• Nuclear Engineering and Technology
• /
• 제29권5호
• /
• pp.361-367
• /
• 1997

The phase separation in ferrite phase of duplex stainless steel is the primary cause of thermal aging embrittlement of the LWR primary pressure boundary components. In this study the phase separation of simulated duplex stainless steel was detected by Mossbauer spectroscopy and magnetic property analysis by VSM(Vibrating Specimen Magnetometer). The simulated duplex stainless steels, Fe-Cr binary, Fe-Cr-Ni ternary, and Fe-Cr-Ni-Si quarternary allots, were aged at 370 and 40$0^{\circ}C$ up to 5,340 hours. It was observed from Mossbauer spectra analysis that internal magnetic field increases with aging time and from VSM that the specific saturation magnetization and Curie temperature increase with aging time. These result are indicative that phase separation into Fe-rich region and Cr-rich region is caused by thermal aging in the temperature range of 370~40$0^{\circ}C$ In cases of specimens containing Ni, the increase of specific saturation magnetization is much higher. This implies that Ni seems to promote Fe-Cr interdiffusion, which accelerates the phase separation into Fe-rich $\alpha$ phase and Cr-rich $\alpha$' phase.

• 비파괴검사학회지
• /
• 제31권6호
• /
• pp.642-649
• /
• 2011

The long-term aging of ferritic 2.25CrMo steel was characterized using the acoustic nonlinear effect in order to apply to diagnose the degradation behavior of structural materials. We measured the acoustic nonlinearity parameter for each thermally aged specimen by the higher harmonic-generation technique. The acoustic nonlinearity parameter increased with aging time due to equilibrium M6C carbide precipitation, and has a favorable linear relation with Rockwell hardness. This study suggests that acoustic nonlinearity testing may be applicable to diagnostics on strength degradation in rotor steels.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년도 춘계 학술대회 개요집
• /
• pp.313-315
• /
• 2006