• 한국재료학회지
• /
• 제25권3호
• /
• pp.125-131
• /
• 2015

Fluorine-doped $SnO_2$ (FTO) thin film/Ag nanowire (NW) double layers were fabricated by means of spin coating and ultrasonic spray pyrolysis. To investigate the optimum thickness of the FTO thin films when used as protection layer for Ag NWs, the deposition time of the ultrasonic spray pyrolysis process was varied at 0, 1, 3, 5, or 10 min. The structural, chemical, morphological, electrical, and optical properties of the double layers were examined using X-ray diffraction, X-ray photoelectron spectroscopy, field-emission scanning electron microscopy, transmission electron microscopy, the Hall effect measurement system, and UV-Vis spectrophotometry. Although pure Ag NWs formed isolated droplet-shaped Ag particles at an annealing temperature of $300^{\circ}C$, Ag NWs covered by FTO thin films maintained their high-aspect-ratio morphology. As the deposition time of the FTO thin films increased, the electrical and optical properties of the double layers degraded gradually. Therefore, the double layer fabricated with FTO thin films deposited for 1 min exhibited superb sheet resistance (${\sim}14.9{\Omega}/{\Box}$), high optical transmittance (~88.6 %), the best FOM (${\sim}19.9{\times}10^{-3}{\Omega}^{-1}$), and excellent thermal stability at an annealing temperature of $300^{\circ}C$ owing to the good morphology maintenance of the Ag NWs covered by FTO thin films.

• 한국해양환경ㆍ에너지학회지
• /
• 제12권4호
• /
• pp.302-306
• /
• 2009

이 연구에 사용된 9종류의 나노입자는 직경 100 nm 이하의 크기를 가진 입자로, 알테미아 cyst가 nauplius로 부화되는 과정에서 어떠한 영향을 미치는지 살펴보았다. 24시간 경과 후 나노입자를 첨가하지 않은 대조구에서는 82%가 nauplius로 부화하였다. 20 mg/L 농도에서는 AGZ020, Nano silver, P-25, Sb, 및 SnO 나노입자가 각각 18%, 20%, 13%, 50% 및 0%의 부화율을 보여 유해성이 큰 것으로 나타났으나, Ag-$TiO_2$, In, Sn, 및 Zn 나노입자에서는 각각 75%, 60%, 73% 및 73%로 대조구에 비해 유해성을 가졌지만, AGZ020, Nano silver, P-25, Sb, 및 SnO 나노입자에 비해 상대적으로 미약한 것으로 나타났다. 이는 나노입자가 가지고 있는 성분에 따라서 차이가 났다. AGZ020, Nano silver 및 P-25 나노입자는 은(Ag)이 2% 함유되어 항균제로서 널리 사용되어지고 있으며, 산소를 결합시킨 SnO 나노입자는 광촉매제로 사용되고 있다. 이들 나노입자들은 현재 가전, 기능성 화장품, 항균제 및 광촉매제 등 사용이 일반화되어 수중환경으로 유입될 가능성이 높아지고 있다. 이에 따라 수중생태계에 점차 영향을 줄 가능성이 높기에, 나노입자가 가지는 잠재적 위험성을 지속적으로 연구해야 할 것이다.

• 해양환경안전학회:학술대회논문집
• /
• 해양환경안전학회 2008년도 춘계학술발표회
• /
• pp.137-141
• /
• 2008

이 연구에 사용된 9종류의 나노입자는 직경 100nm 이하의 크기를 가진 입자로, 알테미아 cyst가 nauplius로 부화되는 과정에서 어떠한 영향을 미치는지 살펴보았다. 24시간 경과 후 나노입자를 첨가하지 않은 대조구에서는 82%가 nauplius의 부화하였다. 20mg/L 농도에서는 AGZ020, Nano silver, P-25, Sb, 및 SnO 나노입자가 각각 18%, 20%, 13%, 50% 및 0%의 부화율을 보여 유해성이 큰 것으로 나타났으나, Ag-$TiO_2$, In, Sn, 및 Zn 나노입자에서는 각각 75%, 60%, 73% 및 73%로 대조구에 비해 유해성을 가졌지만, AGZ020, Nano silver, P-25, Sb, 및 SnO 나노입자에 비해 상대적으로 미약한 것으로 나타났다. 이는 나노입자가 가지고 있는 성분에 따라서 차이가 났다. AGZ020, Nano silver 및 P-25 나노입자는 은(Ag)이 2% 함유되어 항균제로서 널리 사용되어지고 있으며, 산소를 결합시킨 SnO 나노입자는 광촉매제로 사용되고 있다. 이들 나노입자들은 현재 가전, 기능성 화장품, 항균제 및 광촉매제 등 사용이 일반화되어 수중환경으로 유입될 가능성이 높아지고 있다. 이에 따라 수중생태계에 전파 영향을 준 가능성이 높기에, 나노입자가 가지는 잠재적 위험성을 지속적으로 연구해야 할 것이다.

• 한국태양에너지학회 논문집
• /
• 제34권1호
• /
• pp.98-104
• /
• 2014

Photovoltaic (PV) cell is considered as one of the finest ways to utilize the solar power. A study of improving solar cell's efficiency is important because the lifetime of solar cell is determined by photovoltaic module technology. Therefore, oxidation (and/or corrosion) of solder materials will be one of the primary yield and long-term reliability risk factor. Recently, the development of lead-free solder alloy has been done actively about lead-free solder alloys of the thermodynamic and mechanical properties. However, the oxidation behavior have rarely been investigated In this study, the oxidations of 60 wt% Sn-40 wt% Pb, 62 wt% Sn-36 wt% Pb -2 wt% Ag, 50wt% Sn-48 wt% Bi-2 wt% Ag alloys for the interconnect ribbon after exposure in atmosphere at $100^{\circ}C$ for several times were investigated. The wettability of 62 wt% Sn-36 wt% Pb-2 wt% Ag and 50 wt% Sn-48 wt% Bi-2 wt% Ag solders was also studied to compare with that of 60 wt% Sn-40 wt% Pb alloy. The results howed that the zero cross time and the wetting time of 50 wt% Sn-48 wt% Bi-2 wt% Ag solder were better than other two samples. The surface of tested samples was analyzed by XPS. The XPS result showed that in all samples, SnO grew first and then the mixture of SnO and $SnO_2$ was detected. $SnO_2$ grew predominantly for the long time aging. Moreover XPS depth profile analysis has found surface enrichment of tin oxide.

• 한국전기전자재료학회논문지
• /
• 제31권6호
• /
• pp.408-411
• /
• 2018

We fabricated highly flexible Mn-doped $SnO_2$ (MTO)/Ag/MTO/polydimethylsiloxane (PDMS)/MTO multilayer transparent conducting films. To reduce refractive-index mismatching of the MTO/Ag/MTO/polyethylene terephthalate (PET), index-matching layers were inserted between the oxide-metal-oxide-structured films and the PET substrate. The PDMS layer was deposited by spin-coating after adjusting the mixing ratio of PDMS and hexane. We investigated the effects of the index-matching layer on the color and reflectance differences with different PDMS dilution ratios. As the dilution ratio increased from 1:100 to 1:130, the color difference increased slightly, while the reflectance difference decreased from 0.62 to 0.32. The MTO/Ag/MTO/PDMS/MTO film showed a transmittance of 87.18~87.68% at 550 nm. The highest value of the Haacke figure of merit was $47.54{\times}10^{-3}{\Omega}^{-1}$ for the dilution ratio of 1:130.

• 마이크로전자및패키징학회지
• /
• 제10권3호
• /
• pp.29-35
• /
• 2003

SnAg, SnAgCu, SnCu 무연솔더합금을 주조 상태에서 냉간압연한 후 열적으로 안정화한 시편 (TS)과, 실제 솔더 범프와 유사한 미세구조의 수냉에 급속 냉각(WQ)된 시편 두가지를 $100^{\circ}C$에서 크리프 실험을 행하였다. 급속냉각한 시편의 냉각속도는 140-150 K/sec로 primary $\beta-Sn$ 크기가 TS 시편보다 5∼10배 정도 작았으며, 기지내 primary $\beta-Sn$이 차지하는 분율은 증가하였다. 반면에 공정상 내의 $Ag_3Sn$상의 크기는 더 작아졌다. 크리프 실험 결과 WQ 시편의 최소크리프 변형율 속도($\{beta}_{min}$)가 TS 보다 약 $10^2$배 정도 작았으며. 더 큰 파괴시간을 보였다. TS-SnAg의 크리프파괴는 $Ag_3Sn$ 또는 $Cu_6Sn_5$에서의 공공의 핵생성, power-law 크리프에 의한 공공의 성장, 그리고 크리프 공공의 상호 연결로 일어났으며, WQ-SnAgCu는 시편이 두께가 얇아 네킹에 의해 파괴가 일어났다.

• Transactions on Electrical and Electronic Materials
• /
• 제17권2호
• /
• pp.121-124
• /
• 2016

ZnSnO₃ (ZTO)/Ag/ ZnSnO₃ (ZTO) trilayer films were prepared on glass substrates by radio frequency (RF) and direct current (DC) magnetron sputtering. The electrical resistivity and optical transmittance of the films were investigated as a function of the Ag interlayer thickness. ZTO films with a 15 nm thick Ag interlayer show the highest average visible transmittance (83.2%) in the visible range. In this study, the highest figure of merit (2.1×10⁻² Ω cm) is obtained with the ZTO 50 nm/Ag 15 nm/ZTO 50 nm films. The enhanced optical and electrical properties of ZTO films with a 15 nm thick Ag interlayer are attributed to the crystallization of the Ag interlayer, as supported by the distinct XRD pattern of the Ag (111) peaks. From the observed results, higher optical and electrical performance of the ZTO film with a 15 nm thick Ag interlayer seems to make a promising alternative to conventional transparent conductive ITO films.

• 한국세라믹학회지
• /
• 제49권2호
• /
• pp.155-160
• /
• 2012

This paper reported a simple deposition-precipitation method, introducing the metal (Ni, Ag and Sn) and $Na_2S{\cdot}5H_2O$ to preparedispersion metal sulfide nanoparticles on the surface of the Multi-walled carbon nanotube for synthesis of CNT-$M_xS_y$ ($NiS_2$, $Ag_2S$, SnS) composite photocatalysts. The characterization of the prepared CNT-$M_xS_y$ ($NiS_2$, $Ag_2S$, SnS) composites was performed by X-ray diffraction, scanning electron microscopy with energy dispersive X-ray analysis and BET analysis. Furthermore, the MB degradation rate constant for CNT-SnS composite was $5.68{\times}10^{-3}$ under visible light irradiation, which was much higher than the corresponding values for other samples. The detailed formation and photocatalytic mechanism are also provided here.

• 대한환경공학회지
• /
• 제22권12호
• /
• pp.2263-2273
• /
• 2000

희분식 고온/고압 미분반응기를 이용하여 습식산화 반응시 대표적 난분해성 중간 산화물질로 알려진 아세트산을 산화반응 기질로 하여 여러 가지 담체 및 촉매의 조합에 대한 산화반응성을 실험하였다. 사용된 담체는 다공성 실리카($SiO_2$), 티타니아($TiO_2$), 지르코니아($ZrO_2$), $ZrSiO_4$, $ZrO_2(10wt%)/TiO_2$ 등이었으며 촉매활성성분온 크게 Ru, Mn, Ce의 세 가지로서 단독 혹은 조합사용(2성분계 및 3성분계)시의 산화활성에 대하여 조사하였다. 이를 통하여 일차척인 활성이 우수한 것으로 나타난 $Mn(2.8)-Ce(7.2wt%)/TiO_2$ 혹은 $Ru(0.5)-Mn(2.7)-Ce(6.8wt%)/TiO_2$ 기준촉매의 활성증진을 위하여 p-type 반도체 물질(CoO, SnO 및 $Ag_2O$)를 첨가제로 소량 사용함으로써 이에 따른 습식산화 반응 상대 활성실험을 수행하였다. 우선, $Mn-Ce/TiO_2$ 기준촉매에 있어서, p-type 반도체 물질(CO, Sn Ag)을 첨가한 경우, 모두 활성증진효과를 보이며 크기 정도는 Co> Ag >Sn순이었다. 특히, $Mn(2.7)-Ce(6.8)-Co(0.5wt%) /TiO_2$에 있어서는 약 2.6배의 높은 활성상승이 나타났다. 이의 가시적인 주원인은 표면적 증가 및 시너지 효과에 기인하는 것으로 판단되었다. $Ru-Mn-Ce/TiO_2$ 기준 촉매에 있어서는 $Ru(O.5)-Mn(2.4)-Ce(6.1)-Co(1.0wt%)/TiO_2$에서만 활성증진효과를 보였으며 그 이외의 다른 경우에 있어서는 표면적 및 활성감소가 일어났다.

• 한국세라믹학회지
• /
• 제43권2호
• /
• pp.92-97
• /
• 2006

Dolomite type $BaSn(BO_3)_2$ ceramics with rhombohedral crystal structure has been synthesized via solid state reaction route. Dielectric properties were measured for the samples sintered at $1050\~1200^{\circ}C$ for 2 h in air. Dielectric constant, loss tangent, and temperature coefficient were increased with sintering temperature due to the evolution of $BaSnO_3$, secondary, phase. Optimum dielectric properties were obtained at the $BaSn(BO_3)_2$ ceramics sintered at $1100^{\circ}C.\;CuO/Bi_2O_3$ was added to $BaSn(BO_3)_2$ ceramics to lower the sintering temperature for LTCC application, then Co and Fe-based coloring agents were added for colorizing the LTCC tape. Typical dielectric properties of $BaSn(BO_3)_2$ ceramics with $5 wt\%\;CuO/Bi_2O_3\;and\;3wt\%$ Co-coloring agent that sintered at $900^{\circ}C$ were $\varepsilon_r=9.89,\;tan{\delta}=0.92\times10^{-3},\;and\;TCC=112ppm/^{\circ}C$. Thus obtained LTCC tape was co-fired with Ag paste for compatibility test and revealed no sign of Ag reaction with the ceramics.