• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.4
• /
• pp.35-40
• /
• 2010

In this study, the reliability of thermal shock, thermal cycle, and complex vibration test at high temperature were examined for 3 types of lead-free solder alloys, Sn-3.5Ag, Sn-0.7Cu and Sn-5.0Sb. For the reliability test, daisychained BGA chips with ENIG-finished Cu pad was assembled with the three lead-free solders on OSP-finished PCBs. Among the 3 types solder alloys, Sn-3.5Ag solder alloy showed the highest degradation rate of electrical resistance and joint strength. On the other hand, Sn-0.7Cu solder alloy had high stability after the reliability tests.

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.36-38
• /
• 2006

We investigated that the metallurgical, mechanical and electrical properties of the Sn-3.SAg/Cu ball grid array (BGA) solder joints at a reflow temperature of $255^{\circ}C$ for different reflow times of 10, 60, 300 and 1800 s. Two different intermetallic compound (IMC) layers, consisting of scallop-shaped $Cu_6Sn_5$ and very thin $Cu_3Sn$, formed at the solder/substrate interface, and their thicknesses increased with increasing reflow time. The shear force peaked after reflow for 60 s, and then significantly decreased with increasing reflow time. The fracture occurred along the solder ball in the initial reflow, but the fraction of the brittle fracture increased with increasing reflow time. The IMC growth and the volume of Cu dissolved in the solder balls affected the electrical property.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.12
• /
• pp.1856-1863
• /
• 2004

In the last 50 years, lead-contained solder materials have been the most popular interconnect materials used in the electronics industry. Recently, lead-free solders are about to replace lead-contained solders for preventing environmental pollutions. However, the reliability of lead-free solders is not yet satisfactory. Several researchers reported that lead-contained solders have a good fatigue property. The others published that the lead-free solders have a longer thermal fatigue life. In this paper, the reason for the contradictory results published on the estimation of fatigue life of lead-free solder is investigated. In the present study, fatigue behavior of 63Sn37Pb, and two types of lead-free solder joints were compared using pseudo-power cycling testing method, which provides more realistic load cycling than chamber cycling method does. Pseudo-power cycling test was performed in various temperature ranges to evaluating the shear strain effect. A nonlinear finite element model was used to simulate the thermally induced visco-plastic deformation of solder ball joint in BGA packages. It was found that lead-free solder joints have a good fatigue property in the small temperature range condition. That condition induce small strain amplitude. However in the large temperature range condition, lead-contained solder joints have a longer fatigue life.

• Corrosion Science and Technology
• /
• v.6 no.2
• /
• pp.50-55
• /
• 2007

The smaller size and higher integration of advanced electronic package systems result in severe electrochemical reliability issues in microelectronic packaging due to higher electric field under high temperature and humidity conditions. Under these harsh conditions, electronic components respond to applied voltages by electrochemical ionization of metal and the formation of a filament, which leads to short-circuit failure of an electronic component, which is termed electrochemical migration. This work aims to evaluate electrochemical migration susceptibility of the pure Sn, Sn-3.5Ag, Sn-3.0Ag-0.5Cu solder alloys in $Na_{2}SO_{4}$. The water drop test was performed to understand the failure mechanism in a pad patterned solder alloy. The polarization test and anodic dissolution test were performed, and ionic species and concentration were analyzed. Ag and Cu additions increased the time to failure of Pb-free solder in 0.001 wt% $Na_{2}SO_{4}$ solution at room temperature and the dendrite was mainly composed of Sn regardless of the solders. In the case of SnAg solders, when Ag and Cu added to the solders, Ag and Cu improved the passivation behavior and pitting corrosion resistance and formed inert intermetallic compounds and thus the dissolution of Ag and Cu was suppressed; only Sn was dissolved. If ionic species is mainly Sn ion, dissolution content than cathodic deposition efficiency will affect the composition of the dendrite. Therefore, Ag and Cu additions improve the electrochemical migration resistance of SnAg and SnAgCu solders.

• Journal of the Microelectronics and Packaging Society
• /
• v.21 no.3
• /
• pp.51-56
• /
• 2014

The reliability of solder joint is significantly affected by the property of surface finish. This paper reports on a study of high speed shear energy and failure mode for Sn-4.0wt%Ag-0.5wt%Cu (SAC405) solder joints with the time of Pd activation. The nodule size of electroless Ni-P deposit increased with increasing the time of Pd activation. The roughness (Ra) of electroless Ni-P deposit decreased with increasing the time of Pd activation. Then, with $HNO_3$ vapor, the quasi-brittle and brittle mode of SAC405 solder joint decreased with increasing the time of Pd activation. This results indicate that the increase in the Pd activation time for Electroless Ni/ Electroless Pd/ Immersion Au (ENEPIG) surface finish play a critical role for improving the robustness of SAC405 solder joint.

• Korean Journal of Materials Research
• /
• v.17 no.3
• /
• pp.152-159
• /
• 2007

When the electronics are tested with thermal shock for Pb-free solder joint reliability, there are temperature conditions with use environment but number of cycles for test don't clearly exist. To obtain the long term reliability data, electronic companies have spent the cost and times. Therefore this studies show the test method and number of thermal shock cycles for evaluating the solder joint reliability of electronic components and also research bonding strength variation with formation and growth of intermetallic compounds (IMC). SMD (surface mount device) 3216 chip resistor and 44 pin QFP (quad flat package) was utilized for experiments and each components were soldered with Sn-40Pb and Sn-3.0 Ag-0.5 Cu solder on the FR-4 PCB(printed circuit board) using by reflow soldering process. To reliability evaluation, thermal shock test was conducted between $-40^{\circ}C\;and\;+125^{\circ}C$ for 2,000 cycles, 10 minute dwell time, respectively. Also we analyzed the IMCs of solder joint using by SEM and EDX. To compare with bonding strength, resistor and QFP were tested shear strength and $45^{\circ}$ lead pull strength, respectively. From these results, optimized number of cycles was proposed with variation of bonding strength under thermal shock.

• Journal of the Microelectronics and Packaging Society
• /
• v.16 no.1
• /
• pp.7-11
• /
• 2009

In this study, solder joints were made with Sn-3.5Ag (wt%) solder ball. Electroless nickel / immersion gold (ENIG) printed circuit board (PCB) substrates were employed in this work. The mechanical and electrical properties were measured as a function of the number of reflow. Die shear strength was measured with increasing reflow number. Until the forth or fifth reflow, shear force increased and after the fifth reflow the shear force of die decreased. The electrical resistivity of solder joint linearly increased with increasing reflow number.

• Electronic Materials Letters
• /
• v.14 no.6
• /
• pp.678-688
• /
• 2018

The repeated-bending properties of Sn-0.7Cu, Sn-0.3Ag-0.7Cu (SAC0307), and Sn-3.0Ag-0.5Cu (SAC305) solders mounted on flexible substrates were studied using highly accelerated stress testing (HAST), followed by repeated-bending testing. In the Sn-0.7Cu joints, the $Cu_6Sn_5$ intermetallic compound (IMC) coarsened as the HAST time increased. For the SAC0307 and SAC305 joints, the $Ag_3Sn$ and $Cu_6Sn_5$ IMCs coarsened mainly along the grain boundary as the HAST time increased. The Sn-0.7Cu solder had a high contact angle, compared to the SAC0307 and SAC305 solders; consequently, the SAC0307 and SAC305 solder joints displayed smoother fillet shapes than the Sn-0.7Cu solder joint. The repeated-bending for the Sn-0.7Cu solder produced the crack initiated from the interface between the Cu lead wire and the solder, and that for the SAC solders indicated the cracks initiated at the surface, but away from the interface between the Cu lead wire and the solder. Furthermore, the oxide layer was thickest for Sn-0.7Cu and thinnest for SAC305, regardless of the HAST time. For the SAC solders, the crack initiation rate increased as the oxide layer thickened and roughened. $Cu_6Sn_5$ precipitated and grew along the grain and subgrain boundaries as the HAST time increased, embrittling the grain boundary at the crack propagation site.

• Journal of Welding and Joining
• /
• v.19 no.2
• /
• pp.176-181
• /
• 2001

Reflow soldering characteristics of Sn-3.5Ag and Sn-37Pb balls for BGA(Ball grid Array) were investigated. Diameter of 0.76mm ball was set on a Cu/Ni/Au-coated pad and reflowed in air with changing peak soldering temperature and conveyor speed. Peak temperatures were changed from 240 to 28$0^{\circ}C$ for Sn-3.5Ag, and from 220 to 26$0^{\circ}C$ for Sn-37Pb balls. As results, heights of solder balls increased and widths decreased with peak soldering temperature. Through aging treatment at 10$0^{\circ}C$ for 1.000 hrs, average hardness of Sn-3.5Ag balls bonded at 25$0^{\circ}C$ cecreased from 14.90Hv to 12.83Hv And with same aging conditions, average shear strength of Sn-3.5Ag balls bonded at 26$0^{\circ}C$ decreased from 1727gf to 1650gf.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.74-74
• /
• 2009

카본나노튜브(CNT) 복합체는 우수한 기계적 성질을 가지고 있어 다양한 분야에서 연구되고 있다. 본 연구에서는 카본나노튜브(CNT)를 간단한 볼밀공정을 사용하여 Sn3.5Ag solder ball과 SAC305 powder 표면에 혼합하고 이를 통해 접합부 특성을 관찰하였다. 볼밀을 실시하기 전 카본나노튜브(CNT)는 초음파을 이용하여 분산을 실시하였다. Sn3.5Ag solder ball의 직경은 450um이고 SAC305 powder의 직경은 약 30um이었으며 이때 사용한 볼밀볼의 직경은 각각 3mm, 1mm이다. 볼밀 회전속도는 약 300rpm이고 6, 12, 18, 24시간동안 볼밀을 실시하였다. 24시간 볼밀 후에도 solder ball과 solder powder의 모양은 크게 변하지 않았다. SEM을 통해 표면을 관찰한 결과 분산된 카본나노튜브(CNT)는 solder ball과 solder powder의 표면에서 관찰되었다. 카본나노튜브(CNT)가 삽입된 solder ball은 BGA coupon 위에 놓고 Reflow를 실시하여 접합하였고 solder powder은 flux를 첨가하여 paste로 제조하여 2012 chip에 대한 접합특성을 관찰하였다. 카본나노튜브(CNT)는 solder ball 내부의 표면근처에서 관찰되었으며 카본나노튜브(CNT)가 혼합된 solder ball은 Aging 실시 후에 IMC 두께가 카본나노튜브(CNT)가 혼합되지 않은 solder ball에 비해 두께가 작고 접합강도는 약 10% 증가하였다. 또한 카본나노튜브(CNT)가 혼합된 solder paste와 카본나노튜브(CNT)가 혼합되지 않은 solder paste를 비교한 결과 인쇄성은 모두 양호하였으며 카본나노튜브(CNT)가 혼합된 paste를 사용한 chip의 전단강도가 높게 나타났다.