• 한국표면공학회지
• /
• 제50권6호
• /
• pp.510-515
• /
• 2017

In this study, a transient liquid phase sintering (TLPS) process of Ag pastes mixed with a fusible metal alloy of Bi58Sn42 with the melting temperature of $138^{\circ}C$, was examined. After screen printing of the Ag pastes with and without Bi58Sn42 powders on polyimide (PI) substrates, the electrodes were heat-treated at different temperatures in the range between 150 and $300^{\circ}C$ for 60 min in air. Comparing the electrical conductivity of the Ag pastes with and without Bi58Sn42 alloy powder after the heat treatment, it was manifested that the low melting temperature alloy definitely played a major role in an increased conductivity when it is added into the Ag pastes by providing more electrical conduction paths between Ag particles. This can be explained by the fact that capillary force of the melts of Bi58Sn42 can contribute to the rearrangement of the Ag particles during the heat-treatment inducing better connectivity between the Ag particles.

• 한국결정성장학회지
• /
• 제32권2호
• /
• pp.51-54
• /
• 2022

연료전지에 사용되는 귀금속 전류집전체의 물성은 소재 기공도에 크게 영향을 받는다. 따라서 소재 기공도를 제어 위한 다양한 노력들이 진행되어왔다. 이중 많이 사용되는 전략으로 재료 열처리 시 기공형성제를 첨가하는 것이다. 기존의 기공형성제는 3차원 구조체였다. 본 연구에서는 차별화 전략으로 Ag 전류집전체의 기공도를 높이기 위해 2차원 구조 나노시트를 소결방지제로 첨가하였다. 실제로 나노시트 첨가에 의해 소결밀도가 감소되는 것을 보여주었다. 2차원 소재로는 초나노 두께(~ 1 nm)를 갖는 RuO₂ 나노시트가 이용되었다.

• 마이크로전자및패키징학회지
• /
• 제29권4호
• /
• pp.35-40
• /
• 2022

본 연구에서는 실버 파우더의 입자 크기, 즉 평균입자 크기가 2㎛, 7㎛, 이들의 혼합(50:50wt%), 이렇게 3가지 실버 페이스트를 제조하여 점도 및 점탄성, 경화후에 잔류용제 유무 확인을 위한 TGA측정, Strain에 따른 저항변화 및 전극 표면구조 변화에 대해서 검토한 결과 다음과 같은 결론을 얻을 수 있었다. 이러한 결과를 정리하면 Strain에 따른 저항변화를 최소화하기 위해서는 실버 파우더의 입자를 2㎛정도인 것이 가장 바람직함을 알 수 있었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 센서 박막재료 반도체 세라믹
• /
• pp.53-56
• /
• 2003

The properties of YBCO thick film coated on Ag wire with YBCO powder is deeply affected by cracking on its surface which was deposited in organic solution by electrophoretic method. YBCO superconducting thick films were prepared on Ag wire$({\Psi}0.8mm)$ by electrophoresis in acetone with added PEG (Poly-Ethylene Glycol, 3% in Acetone), 1ml for being crack-free. The surface properties of YBCO superconducting wire was evidently improved with adding PEG. Added PEG which molecular weight is 600, 1000, 3400 was affected with variation of deposition voltages to the surface properties of samples. As a result, with adding PEG (its molecular weight is 3400), YBCO superconducting wire was better on its surface properties.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2003년도 추계학술발표회초록집
• /
• pp.58-58
• /
• 2003

Silver doped ZnO (SZO) films were prepared by rf magnetron sputtering on glass substrates with extraordinary designed ZnO target. With the doping source for target, use AgNO$_3$ powder on a various rate (0, 2, and 4 wt.%). We investigated dependence of coating parameter such as dopant content in target and substrate temperature in the SZO films. The SZO films have a preferred orientation in the (002) direction. As amounts of the Ag dopant in the target were increased, the crystallinity and the transmittance and optical band gap were decreased. And the substrate temperature were increased, the crystallinity and the transmittance were increased. But the crystallinity and the transmittance of SZO films were retrograde at 200$^{\circ}C$. Upside facts were related with composition. In addition, the Oxygen K-edge features of the SZO films were investigated by using near edge X-ray absorption fine structure (NEXAFS) spectroscopy. Changes of optical band gap of the SZO films were explained compared with XRD, XPS and NEXAFS spectra.

• 한국분말재료학회지
• /
• 제26권3호
• /
• pp.231-236
• /
• 2019

Ni hydroxides ($Ni(OH)_2$) are synthesized on Ni foam by varying the hexamethylenetetramine (HMT) concentration using an electrodeposition process for pseudocapacitor (PC) applications. In addition, the effects of HMT concentration on the $Ni(OH)_2$ structure and the electrochemical properties of the PCs are investigated. HMT is the source of amine-based $OH^-$ in the solution; thus, the growth rate and morphological structure of $Ni(OH)_2$ are influenced by HMT concentration. When $Ni(OH)_2$ is electrodeposited at a constant voltage mode of -0.85 V vs. Ag/AgCl, the cathodic current and the number of nucleations are significantly reduced with increasing concentration of HMT from 0 to 10 mM. Therefore, $Ni(OH)_2$ is sparsely formed on the Ni foam with increasing HMT concentration, showing a layered double-hydroxide structure. However, loosely packed $Ni(OH)_2$ grains that are spread on Ni foam maintain a much greater surface area for reaction and result in the effective utilization of the electrode material due to the steric hindrance effect. It is suggested that the $Ni(OH)_2$ electrodes with HMT concentration of 7.5 mM have the maximum specific capacitance (1023 F/g), which is attributed to the facile electrolyte penetration and fast proton exchange via optimized surface areas.

• 한국전기전자재료학회논문지
• /
• 제26권12호
• /
• pp.858-862
• /
• 2013

The front electrode should be used to make solar cell panel so as to collect electron. The front electrode is used by paste type, printed on the Si-solar cell wafer and sintered at about $800^{\circ}C$. The paste is composed Ag powder and glass frit which make the ohmic contact between Ag electrode and n-type semiconductor layer. From the previous study, the Ag electrodes which used two commercial glass frit of Bi-system were so different on the interface resistance. The main composition of them was Bi-Zn-B-Si-O and few additives added in one of them. In this study, glass frit was made with the ratio of $Bi_2O_3$ and ZnO on the main composition, and then paste using glass frit was prepared respectively. And, also, the paste using the glass frit added oxide additives were prepared. The change of interface resistance was not large with the ratio of $Bi_2O_3$ and ZnO. In the case of G6 glass frit, 78 wt% $Bi_2O_3$ addition, the interface resistance was $190{\Omega}$ and most low. In the glass frit added oxide, the case of Ca increased over 10 times than it of G6 glass frit on the interface resistance. It was thaught that after sintering, Ca added glass frit was not flowed to the interface between Ag electrode and wafer but was in the Ag electrode.

• 한국지하수토양환경학회:학술대회논문집
• /
• 한국지하수토양환경학회 2006년도 총회 및 춘계학술발표회
• /
• pp.41-44
• /
• 2006

The objective of this study was to evaluate the stabilization of As and heavy metals in tailings from the Samkwang Au-Ag mine with $Ca(OH)_2$. In order to evaluate the stabilization ability of As and heavy metals in the tailings, column test was implemented with various conditions as 1) particle size of $Ca(OH)_2$, 2) mixing method and 3) flow rate of eluents during 60 days. The results showed that addition with 5% of $Ca(OH)_2$ in 1kg of the tailings had the most effective ability of stabilization up to 95%. In addition, stabilization ability of As and heavy metals in tailings was enhanced using a fine powder of $Ca(OH)_2$. Therefore, stabilization technology can be used as a remediation of As and heavy metals in mine wastes including tailings and a nearby soils from abandoned metal mines.

• 한국전기전자재료학회논문지
• /
• 제36권1호
• /
• pp.81-87
• /
• 2023

Heaters using the resistance heating principle are used in various industrial fields that require heat and are also essentially used in bidet among small home appliances. A planar heater and a coil-inserted heater mounted on a conventional commercially used bidet have disadvantages and limitations of complicated manufacturing process and local heating. In this study, silver-palladium (Ag-Pd) powder material was used for a screen-printing process that is more advantageous in achieving simplification than the existing process, and a rod-type heater for bidet was manufactured. The on-off cycle test under actual conditions was conducted to confirm the durability and the capability of the fabricated heater, and the fabricated heater operated more than 2,600 on-off cycles, which means it could be applied for a commercial product. In addition, through the on-off cycles under harsh conditions, the cause of failure was identified after the test that the durability limit temperature of the heater was 850℃. Through Ag-Pd rod heater in this study, it is expected to contribute to the efficient development of electrode materials for heaters and the improvement of the durability of heaters in the future.

• 한국세라믹학회지
• /
• 제39권2호
• /
• pp.159-163
• /
• 2002

Relaxor 유전체 물질인 PMN-PT-BT를 modified mixed oxide 공정과 단일 하소로 페로브스카이트 단일상으로 제조할 수 있는 공정을 시도하였다. PbO, Nb2O5, BaCO3 와 $TiO_2$ 대신 $Ti(OC_3H_7)_4$를, MgO 대신 $Mg(NO_3)_2$을 사용하여 볼밀로 혼합한 후 건조된 분말을 900$^{\circ}C$/2시간 하소하고, 이어서 1100$^{\circ}C$/2시간 열처리하여 얻은 소결체는 소결 밀도 7.83 g/$cm^3$, 실온 유전율 22000, 유전손실 2.5%의 우수한 유전 특성을 나타내었다. 소결조제로 Ag을 $AgNO_3$로 1.0 몰%(0.3wt%) 첨가한 경우 550$^{\circ}C$/2시간 하소한 분말은 900$^{\circ}C$/2시간 열처리로 소결밀도 7.88 g/$cm^3$, 실온 유전율 20000, 유전손실 2.4%을 나타내었다.