• Journal of Powder Materials
• /
• v.23 no.1
• /
• pp.15-20
• /
• 2016

Niobium is one of the most important and rarest metals, and is used in the electronic and energy industries. However, it's extremely high melting point and oxygen affinity limits the manufacture of Nb coating materials. Here, a Nb coating material is manufactured using a kinetic spray process followed by hot isotactic pressing to improve its properties. OM (optical microscope), XRD (X-ray diffraction), SEM (scanning electron microscopy), and Vickers hardness and EPMA (electron probe micro analyzer) tests are employed to investigate the macroscopic properties of the manufactured Nb materials. The powder used to manufacture the material has angular-shaped particles with an average particle size of $23.8{\mu}m$. The porosity and hardness of the manufactured Nb material are 0.18% and 221 Hv, respectively. Additional HIP is applied to the manufactured Nb material for 4 h under an Ar atmosphere after which the porosity decreases to 0.08% and the hardness increases to 253 Hv. Phase analysis after the HIP shows the presence of only pure Nb. The study also discusses the possibility of using the manufactured Nb material as a sputtering target.

• Journal of Educational Research in Mathematics
• /
• v.13 no.1
• /
• pp.57-75
• /
• 2003

The goal of this paper is to offer material which make mathematising Fruedenthal(1991) proposed be experienced through the process of teaching and learning mathematics. In this paper, the number of unit squares a diagonal passes through for an m$\times$n lattice rectangle is studied and its generalization is discussed. Through this discussion, the adaptability of this material Is analysed. Especially, beyond inductional conjecture, the number of unit squares is studied by more complete way, and generalization in 3-dimension and 4-dimension are tried. In school mathematics, it is enough to generalize in 3-dimension. This material is basically appropriate for teaching and learning mathematising in math classroom. In studying the number of unit squares and unit cubes, some kinds of mathematising are accompanied. Enough time are allowed for students to study unit squares and unit cubes to make them experience mathematising really. To do so, it is desirable to give students that problem as a task, and make them challenge that problem for enough long time by their own ways. This material can be connected to advanced mathematics naturally in that it is possible to generalize this problem in n-dimension. So, it is appropriate for making in-service mathematics teachers realize them as a real material connecting school mathematics and advanced mathematics.

• Journal of Surface Science and Engineering
• /
• v.47 no.4
• /
• pp.210-214
• /
• 2014

We investigated emission characteristics of tandem organic light emitting devices (OLEDs) with p-type materials as charge generation layer. The tandem OLEDs were fabricated by using $MoO_x$, $WO_x$, C60 and HATCN as p-type material or not using p-type material for charge generation. When HATCN was used as p-type material, it showed high current density at low applied voltage, but increase of efficiency was small because of charge unbalance in emitting layer. In case of tandem OLED not using p-type material, applied voltage increased remarkably because of difficulty of hole injection. In case of $MoO_x$, $WO_x$ or C60 as p-type material, current emission efficiency increased greatly. In particular, current emission efficiency of tandem OLED using $MoO_x$ as p-type material increased up to 3 times than current emission efficiency of single OLED. The Commission Internationale de l'Eclairage (CIE) 1931 color coordinates were changed by overlapping of 504 nm emission wavelength. As a result, emission efficiency of tandem OLED improved compared with single OLED, but driving voltage also increased by increase of organic layer thickness.

• Journal of the Korean Ceramic Society
• /
• v.41 no.10 s.269
• /
• pp.742-748
• /
• 2004

Isopropanol of low boiling point was used as a solvent to prepare Al-doped ZnO(AZO) thin films. A homogeneous and stable sol was made from Zn acetate a solute whose mole concentration was 0.7mol/$\iota$ and Al chloride as a dopant. Al-doped ZnO thin films were prepared by sol-gel method as a function of post-heating temperature from 500 to $700^{\circ}C$ and the optical and electrical properties were investigated. The c-axis orientation along (002) plane was enhanced with the increasing of post-heating temperature and the surface morphology of the films showed a homogeneous and nano-sized microstructure. The optical transmittance of the films post-heated below $650^{\circ}C$ was over $86\%$, but decreased at $700^{\circ}C$. The electrical resistivity of the thin films decreased from 73 to 22 $\Omega$-cm as the post-heating temperature increased up to $650^{\circ}C$, but increased greatly to 580 $\Omega$-cm at $700^{\circ}C$. XPS analysis indicated that the deterioration of electrical and optical properties was attributed to the precipitation of $Al_2O_3$ phase on the surface of AZO thin film. This result suggests that the optimum post-heating temperature to improve electrical and optical properties is $600^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.42 no.3 s.274
• /
• pp.211-217
• /
• 2005

[ $Zn_{1-x}Co_{x}O$ (x=0-0.3) films were grown on Corning 7059 glasses by asymmetrical bipolar pulsed dc magnetron sputtering. The c-axis orientation along (002) plane was enhanced with increasing Co concentration. The $Zn_{1-x}Co_{x}O$ films are grown with fibrous grains of tight dome shape. The transmittance spectra measured from UV-visible showed that sp-d exchange interactions and typical d-d transitions become activated with increasing Co concentration. The electrical resistivity of $Zn_{1-x}Co_{x}O$ films increased with increasing Co concentration, especially it increased greatly at $30at\% Co. X-ray photoelectron spectroscopy and alternating gradient magnetometer analyses indicated that no Co metal cluster is formed and the ferromagnetic properties are exhibited. The low electrical resistivity and room temperature ferromagnetism of $Zn_{1-x}Co_{x}O$ thin films suggested the possibility of the application to Diluted Magnetic Semiconductors (DMSs).

• Journal of the Korean Ceramic Society
• /
• v.50 no.1
• /
• pp.18-24
• /
• 2013

This study was conducted to recycle fly ash containing an abundance of CaO generated from combustion in a circulating layer as a carbon storage medium. The study utilized XRD, TG-DTA and XRF analyses during the hydration of fly ash and identified calcium substances within fly ash that could be used in a carbonation process. $Ca^{2+}$ ions in the calcium substances were easily converted to hydrates. A carbonation experiment was done, which used the method of $CO_2$ gas injection to produce suspensions by mixing fly ash with distilled water. The results were analyzed using TG-DTA, XRD, and pH meter measurements. The study was able to verify that the reaction was completed at a $CO_2$ flow rate of 300cc/min approximately 30 minutes after an injection into a solution with a solid-liquid ratio of 1 : 10 of fly ash and distilled water. Moreover, the stirring time of the suspensions did not influence the reaction, and the reaction time was found to diminish as the portion of the fly ash became smaller. Thus, this study produced carbon storage fly ash having a $CO_2$ storage rate of about 71% through the utilization of the CaO content contained within fly ash.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.2
• /
• pp.72-75
• /
• 2000

For the purpose of developing the non-stoichiometric Zr-based Laves phase alloy with higher capacity and better performance for electrochemical application, extensive work has been carried out in KAIST. After careful alloy design of $ZrMn_2-based$ hydrogen storage alloys through varing their stoichiometry while susbstituting or adding some alloying elements, the $Zr-Ti-(Lh-V-Ni)_{2.2},\;Zr-Ti-(Mn-V-Cr-Ni)_{1.8\pm0.1}$ with high capacity and better performance was developed. Consequently the $Zr-Ti-(Mn-V-Ni)_{2.2}$ alloy has a high discharge capacity of 394mAh/g and shows a high rate capability equaling to that of commercialized $AB_5$ type alloys. On the other hand, in order to develop the hydrogen storage alloy with higher discharge capacity, the hypo-stoichiometric $Zr(Mn-V-Ni)_{2-\alpha}$ alloys substituted by Ti are under developing. As the result of competitive roles of Ti and $stocihiometry({\alpha})$, the discharge capacity of $Zr-Ti-(Mn-V-Cr-Ni)_{l.8\pm0.1}$ alloys is about 400mAh/g(410 mAh/g, which shows the highest level of performance in the Zr-based alloy developed. Our sequential endeavor is improving the shortcoming of Zr-based Laves phase alloy for commercialization, i.e., poor activation property and low rate capability, etc. It is therefore believed that the commercialization of Zr-based Laves phase hydrogen storage alloy for Ni-MH rechargeable battery is in near future.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.2
• /
• pp.84-89
• /
• 2009

The turbid/translucent, near colorless(milky) metamorphic sapphire samples from Sri Lanka have been characterized after the heat treatment in $N_2$ at $1650^{\circ}C$. As-received sapphire specimens became bluish-colored and exhibited more clarity after the heat treatment. It was found that the color change at inclusions zoning region is attributed by the dissolution. As received samples contain the micro/nano inclusions such as rutile($TiO_2$), ilmenite($FeTiO_3$), spinel($MgAl_{2}O_{4}$)/ulvospinel($Fe_{2}TiO_{4}$) and apatite($Ca_5(PO_4)_3$), which were dissolved by the heat treatment and form the blue color through $Fe^{2+}/Ti^{4+}$ charge transferring. The microstructures become different because as the dissolution of apatite($Ca_5(PO_4)_3(OH,F,Cl)$) in alumino silicates($Al_{2}SiO_{5}$) occurred, resulting in morphological change with the appearance of(Ca, Mg, Al) silicate on the surface. Both as-received and heat treated samples showed the rhombohedral crystal structure of $Al_{2}O_{3}$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.2
• /
• pp.90-94
• /
• 2009

Mong Hsu rubies from Myanmar were heat treated in oxidizing(oxygen) atmosphere at $1650^{\circ}C$ for 1 hour. The investigations of the micro-structural defects in the samples before and after heat treatment have been carried out by the variety of analysis techniques of FTIR, UV-VIS-NIR and SEM-EDS. It was found that after heat treatment the dark blue cores region were disappeared and turned to orange red color with the presence of the dense cloudy brownish colored tiny particles in and near former blue zoning. As-received ruby samples only revealed the presence of FTIR absorption peaks of diaspore, boehmite and O-H stretching, at 1986, 2115 and $3078/3319\;cm^{-1}$ respectively. The UV-VIS-NIR absorption of as-received and heat treated ruby samples similarly showed peaks at 405, 554 and 693 nm associated with $Cr^{3+}$, but for the same samples, the absorption peak of heat-treated ruby samples at 693 nm was somewhat stronger than that of the untreated ruby samples. Especially the presence of $Cr^{3+}$ peaks at 659 and 675 nm was found obviously in as-received ruby samples only. The SEM-EDS investigation disclosed the micro-porous defect structures commonly related to the core regions of the untreated ruby samples, which after heat treatment in an oxidizing environment those defect features have been dissolved into the host phase resulting in the lightening or disappearance of the dark coloration of ruby core.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2004.11a
• /
• pp.47-52
• /
• 2004

The purpose of this study is to investigate the friction characteristics of brake pads according to different ratios of $BaSO_4/CaCO_3$. Four brake pads with different ratios of $BaSO_4/CaCO_3$ were manufactured. The friction characteristics of brake pads were tested using 1/5 reduced scale tester. With increasing of the amount of $BaSO_4$ density and shear strength of brake pads were increased and hardness of brake pads were decreased. In effectiveness, the friction coefficient of brake pad was higher and the stability of friction coefficient was better as the ratio of $BaSO_4$ increased. In fade test, friction coefficient of B3 sample used only $CaCO_3$ was decreased rapidly. B1 sample showed a good noise performance without noise generation. The wear resistance of samples were decreased with increasing of the ratio of $CaCO_3$.