About 175 vehicular bridges and 160 pedestrian bridges in service now, worldwide, are made of composites, completely of partially. In this paper, the status of this application is briefly explained.

• Journal of the Korean Ceramic Society
• /
• v.48 no.3
• /
• pp.211-216
• /
• 2011

Nickel oxide-doped ACF and $TiO_2$ composites (NiO/ACF/$TiO_2$) were prepared by a sol-gel method. The composite obtained was characterized by BET surface area measurements, X-ray diffraction, transmission electron microscopy and energy dispersive X-ray analysis. A methylene blue (MB) solution under visible light irradiation was used to determine their photocatalytic activity. Excellent photocatalytic degradation of the MB solution was observed using the $TiO_2$, Ti-ACF and NiO/ACF/$TiO_2$ composite under visible light.

• Korean Journal of Metals and Materials
• /
• v.50 no.12
• /
• pp.961-966
• /
• 2012

Nano-sized Co and $Al_2O_3$ powders were successfully synthesized from $3/4Co_3O_4$ and 2Al by high-energy ball milling. A dense nanocrystalline $2.25Co-Al_2O_3$ composite was consolidated from mechanically synthesized powders by the pulsed current activated sintering (PCAS) method within 2 min. Consolidation was accomplished under the combined effects of a pulsed current and mechanical pressure. A dense $2.25Co-Al_2O_3$ with relative density of up to 95% was produced under simultaneous application of a 80 MPa pressure and a pulsed current of 2800 A. The fracture toughness and hardness of the $2.25Co-Al_2O_3$ composite were $8MPa{\cdot}m^{1/2}$, $870kg/mm^2$, respectively.

• Carbon letters
• /
• v.12 no.1
• /
• pp.26-30
• /
• 2011

For polyacrylonitrile (PAN) based carbon fiber (CF) process, we developed a lab scale wet spinning line and a continuous tailor-made stabilization system with ten columns for controlling temperature profile. PAN precursor was spun with a different spinning rate. PAN spun fibers were stabilized with a total duration of 45 to 110 min at a given temperature profile. Furthermore, a stabilization temperature profile was varied with the last column temperature from 230 to $275^{\circ}C$. Stabilized fibers were carbonized in nitrogen atmosphere at $1200^{\circ}C$ in a furnace. Morphologies of spun and CFs were observed using optical and scanning electron microscopy, respectively. Tensile properties of resulting CFs were measured. The results revealed that process conditions such as spinning rate, stabilization time, and temperature profile affect microstructure and tensile properties of CFs significantly.

• Carbon letters
• /
• v.16 no.3
• /
• pp.203-210
• /
• 2015

This study fabricated low thermal conductive polyacrylonitrile (PAN)-based carbon fibers containing cellulose particles while maintaining their mechanical properties. The high thermal conductivity of carbon fibers limits their application as a high temperature insulator in various systems such as an insulator for propulsion parts in aerospace or missile systems. By controlling process parameters such as the heat treatment temperature of the cellulose particles and the amount of cellulose added, the thermal and mechanical properties of the PAN-based carbon fibers were investigated. The results show that it is possible to manufacture composite carbon fibers with low thermal conductivity. That is, thermal conductivities were reduced by the cellulose particles in the PAN based carbon fibers while at the same time, the tensile strength loss was minimized, and the tensile modulus increased.

• Journal of the Korean Ceramic Society
• /
• v.56 no.5
• /
• pp.453-460
• /
• 2019

To reduce residual pores of composites and obtain a dense matrix, SiC_f/SiC composites were fabricated by chemical vapor deposition (CVI) using SiC nanorods. SiC nanorods were uniformly grown in the thickness direction of the composite preform when the reaction pressure was maintained at 50 torr or 100 torr at 1,100℃. When SiC nanorods were grown, the densities of the composites were 2.57 ~ 2.65 g/㎤, higher than that of the composite density of 2.47 g/㎤ for non-growing of SiC nanorods under the same conditions; grown nanorods had uniform microstructure with reduced large pores between bundles. The flexural strength, fracture toughness and thermal conductivity (room temperature) of the SiC nanorod grown composites were 412 ~ 432 MPa, 13.79 ~ 14.94 MPa·m^1/2 and 11.51 ~11.89 W/m·K, which were increases of 30%, 25%, and 25% compared to the untreated composite, respectively.

• Journal of Powder Materials
• /
• v.21 no.2
• /
• pp.93-96
• /
• 2014

Cobalt coated tungsten carbide-cobalt composite powder has been prepared through wet chemical reduction method. The cobalt sulfate solution was converted to the cobalt chloride then the cobalt hydroxide. The tungsten carbide powders were added in to the cobalt hydroxide, the cobalt hydroxide was reduced and coated over tungsten carbide powder using hypo-phosphorous acid. Both the cobalt and the tungsten carbide phase peaks were evident in the tungsten carbide-cobalt composite powder by X-ray diffraction. The average particle size measured via scanning electron microscope, particle size analysis was around 380 nm and the thickness of coated cobalt was determined to be 30~40 nm by transmission electron microscopy.

• Applied Microscopy
• /
• v.45 no.2
• /
• pp.37-43
• /
• 2015

In present work, work-hardening behavior of TiCu-based bulk metallic glass composite with B2 particles has been studied by systemic structural and mechanical investigations. After yield, pronounced work-hardening of the alloy was clearly exhibited, which was mainly related to the martensitic transformation as well as the deformation twinning in B2 particles during deformation. At the early plastic deformation stage (work-hardening stage), the stress-induced martensitic transformation from B2 phase to B19' phase and deformation-induced twinning of B19' phase was preferentially occurred in the around interface areas between B2 phase and amorphous matrix by stress concentration. The higher hardness value was observed in vicinity of interface within the B2 particles which are probably connected with martensitic transformation and deformation twinning. This reveals that the work-hardening phenomenon of this bulk metallic glass composite is a result of the hardening of B2 particles embedded in amorphous matrix.

• Composites Research
• /
• v.15 no.5
• /
• pp.44-52
• /
• 2002

To study numerically the mechanical behaviors of advanced composite materials considering the microscopic phenomena as well as the macroscopic properties and behaviors, a multi-scale modeling and analysis by the mathematical homogenization method with the help of the finite element method(FEM) are reviewed. The hierarchical modeling strategy and the formulation are briefly described first to give some idea of the multi-scale framework. The latter half of this article focuses on the verification of the multi-scale analysis by the homogenization method in its applications to real advanced materials. The first example is the verification of the predicted macroscopic(homogenized) properties based on the microstructure of porous ceramics. In spite of the complexity of the random microstructure, the error between the predicted and the measured values was only 1%. Next, two applications to the process simulation of fiber reinforced polymer matrix composites are presented. The permeability characteristics are evaluated for sheared weave fabrics for resin transfer molding(RTM) simulation, and the thermoforming of FRTP sheet is analyzed considering the large deformation of the knit structure during the deep-draw forming was verified by comparison with the experimental results.

• Textile Coloration and Finishing
• /
• v.25 no.1
• /
• pp.47-55
• /
• 2013

Physical properties of the composite yarn using low-melting(LM) polyester/Tencel were investigated with air-jet texturing conditions such as temperature, take-up overfeed, yarn speed and air pressure. Surface morphology, microstructure, tensile property, glossiness were evaluated. Surface morphology of a composite yarn had more damaged and loosened structure according to increase of take-up overfeed, yarn speed and air pressure. Crystallinity was affected by parameters such as temperature, yarn speed, take-up overfeed and air pressure and especially, yarn speed was most effective for increase of crystallinity. Also, it was found that temperature and air pressure had significantly affected tensile properties of a composite yarn. The glossiness of yarn increased with increase of temperature, yarn speed and air pressure.