• Carbon letters
• /
• v.10 no.3
• /
• pp.181-189
• /
• 2009

Activated carbon spheres (ACS) were prepared at different heating rates by carbonization of the resole-type phenolic beads (PB) at $950^{\circ}C$ in $N_2$ atmosphere followed by activation of the resultant char at different temperatures for 5 h in $CO_2$ atmosphere. Influence of heating rate on porosity and temperature on carbon structure and porosity of ACS were investigated. Effect of heating rate and temperature on porosity of ACS was also studied from adsorption isotherms of nitrogen at 77 K using BET method. The results revealed that ACS have exhibited a BET surface area and pore volume greater than $2260\;m^2/g$ and $1.63\;cm^3/g$ respectively. The structural characteristics variation of ACS with different temperature was studied using Raman spectroscopy. The results exhibited that amount of disorganized carbon affects both the pore structure and adsorption properties of ACS. ACS were also evaluated for structural information using Fourier Transform Infrared (FTIR) Spectroscopy. ACS were evaluated for chemical composition using CHNS analysis. The ACS prepared different temperatures became more carbonaceous material compared to carbonized material. ACS have possessed well-developed pores structure which were verified by Scanning Electron Microscopy (SEM). SEM micrographs also exhibited that ACS have possessed well-developed micro- and meso-pores structure and the pore size of ACS increased with increasing activation temperature.

• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1016-1021
• /
• 1999

In this study activated carbon fibers were prepared from PAN-based carbon fibers by physical activation with steam or carbon dioxide. The variations in specific surface area amount of iodine adsorption and pore size distribution of the activated carbon fibers after the activation process were discussed. in steam activation BET surface area of about 1019 m2/g was obtained after 77% burn-off while carbn dioxide activation produced ACF with 694m2/g of BET surface area after 52% burn-off. However carbon dioxide activation produced at a similar degree of activation higher micropore volume(0.37 cc/g) and amount of iodine adsorption (1589mg/g) than steam activation. Nitrogen adsorption isotherms for (PAN based activated carbon fibers that prepared by physical activation were of type I in the Brunauer-Deming-Deming-Teller classification

• Korean Journal of Materials Research
• /
• v.24 no.6
• /
• pp.285-292
• /
• 2014

Commercial activated-carbon used as the electrode material of an electric double-layer capacitor (EDLC) was posttreated with various acids and alkalis to increase its capacitance. The carbon samples prepared were then heat-treated in order to control the amount of acidic functional groups formed by the acid treatments. Coin-type EDLC cells with two symmetric carbon electrodes were assembled using the prepared carbon materials and an organic electrolyte. The electrochemical performance of the EDLC was measured by galvanostatic charge-discharge, cyclic voltammetry, and electrochemical impedance spectroscopy. Among the various activated carbons, the carbon electrodes (CSsb800) prepared by the treatments of coconutshell-based carbon activated with NaOH and $H_3BO_5$, and then heat treated at $800^{\circ}C$ under a flow of nitrogen gas, showed relatively good electrochemical performance. Although the specific-surface-area of the carbon-electrode material ($1,096m^2/g$) was less than that of pristine activated-carbon ($1,122m^2/g$), the meso-pore volume increased after the combined chemical and heat treatments. The specific capacitance of the EDLC increased from 59.6 to 74.8 F/g (26%) after those post treatments. The equivalent series resistance of EDLC using CSsb800 as electrode was much lower than that of EDLC using pristine activated carbon. Therefore, CSsb800 exhibited superior electrochemical performance at high scan rates due to its low internal resistance.

• Analytical Science and Technology
• /
• v.12 no.2
• /
• pp.105-110
• /
• 1999

The studies on the adsorption properties and the antibacterial effects of the Cd and Cu-treated activated carbon were carried out. From the adsorption studies on the series of these metal-treated activated carbons, typical Type-I isotherm was observed. The surface areas of the treated carbon obtained from BET equation were in the range of $1101-1418m^2/g$ for Cd-AC and of $1084-1361m^2/g$ for Cu-AC. Using ${\alpha}_s$-plot, the micropore volumes and pore size distribution were obtained. From the SEM study, it is also observed that many of micropores in activated carbon are blocked by window blocking effect of metals after the impregnation. Finally, antibacterial effects of M-activated carbon against Escherichia coli was discussed. From the study, the area of antibacterial activity becomes larger with the increase of the amount of metal treated.

• Journal of the Korean Vacuum Society
• /
• v.2 no.4
• /
• pp.491-500
• /
• 1993

The adsorption of nitrogen (77K) and carbon dioxide(273K) was performed on a series of activated carbon fiber. Theadsorption iotherm of nitrogen was typical type 1 and that of carbon dioxide was convex. As the specific surface area increases, there are linear increases in BET constant C mean pore diameter, the width of pore size distribution, wide micropore volume, total micropore volume, total pore volume and external surface area, however, narrow micropore volume was nealy constant . The total micorpore volume fraction in total pore volume is above 97%.

• Journal of Adhesion and Interface
• /
• v.22 no.1
• /
• pp.1-7
• /
• 2021

The importance of high capacity energy storage devices has recently emerged for stable power supply through renewable energy generation. From this point of view, the Na-air battery (NAB), which is a next-generation secondary battery, is receiving huge attention because it can realize a high capacity through abundant and inexpensive raw materials. In this study, activated carbon-based catalysts for hybrid type Na-air batteries were prepared and their characteristics were compared and analysed. In particular, from the viewpoint of resource recycling, activated carbon (Orange-C) was prepared using discarded orange peel, and performance was compared with Vulcan carbon, which is widely used. In addition, a Pt/C catalyst (homemade-Pt/C, HM-Pt/C) was synthesized using a modified polyol method to check whether the prepared activated carbon can be used as a supported catalyst, and a commercial Pt/C catalyst (Commercial Pt/C) and electrochemical performance were compared. The prepared Orange-C exhibited a typical H3 type BET isotherm, which is evidence that micropore and mesopore exist. In addition, in the case of HM-Pt/C, it was confirmed through TEM analysis that Pt particles were evenly distributed on the activated carbon supported catalyst. In particular, the HM-Pt/C-based NAB showed the smallest voltage gap (0.224V) and good voltage efficiency (92.34%) in the 1st galvanostatic charge-discharge test. In addition, the cycle performance test conducted for 20 cycles showed the most stable performance.

• Carbon letters
• /
• v.15 no.3
• /
• pp.203-209
• /
• 2014

The adsorption of volatile organic compounds (VOCs) was carried out using an activated carbon fiber (ACF) filter in an automobile. The adsorption capacities of formaldehyde, toluene, and benzene on an ACF filter were far better than those of a polypropylene (PP) mat filter and combined (PP+activated carbon) mat filter by batch adsorption in a gas bag. In a continuous flow of air containing toluene vapor through an ACF packed bed, the breakpoint time was very long, the length of the unused bed was short, and sharp "S" -type breakthrough curve was plotted soon after breakpoint, showing a narrow mass transfer zone of toluene on the ACF. The adsorption amount of toluene on the ACF filter was proportional to the specific surface area of the ACF; however, the development of mesopores 2-5 nm in size on the ACF was very effective with regard to the adsorption of toluene. The ACF air clarifier filter is strongly recommended to remove VOCs in newly produced automobiles.

• Journal of the Korean Society of Radiology
• /
• v.11 no.5
• /
• pp.297-302
• /
• 2017

Recently, building materials and air purification filters with eco-friendly charcoal are actively studying to reduce the concentration of radon gas in indoor air. In this study, radon reduction performance was assessed by designing and producing new panel-type activated carbon filter that can be handled more efficiently than conventional charcoal filters, which can reduce radon gas. For the fabrication of our panel-type activated carbon filter, first the pressed molding product after mixing activated carbon powder and polyurethane. Then, through diamond cutting, the activated carbon filter of 2 mm, 4 mm and 6 mm thickness were fabricated. To investigate the physical characteristics of the fabricated activated carbon filter, a surface area and flexural strength measurement was performed. In addition, to evaluate the reduction performance of radon gas in indoor, the radon concentration of before and after the filter passes from a constant amount of air flow using three acrylic chambers was measured, respectively. As a result, the surface area of the fabricated activated carbon was approximately $1,008m^2/g$ showing similar value to conventional products. Also, the flexural load was found to have three times higher value than the gypsum board with 435 N. Finally, the radon reduction efficiency from indoor gas improved as the thickness of the activated carbon increases, resulting in an excellent radon removal rate of more than 90 % in the 6 mm thick filter. From the experimental results, the panel-type activated carbon is considered to be available as an eco-friendly building material to reduce radon gas in an enclosed indoor environment.

• Carbon letters
• /
• v.9 no.4
• /
• pp.275-282
• /
• 2008

Chemically activated carbons were prepared from maize cobs, using phosphoric acid of variable concentration. The textural parameters of the activated carbons were determined from the nitrogen adsorption isotherms measured at 77 K. The chemistry of the carbon surface was determined by measuring the surface pH, the pHPZC and the concentration of the carbon - oxygen groups of the acid type on the carbon surface. Kinetics of Cr(VI) sorption/reduction was investigated at 303 K. Two processes were investigated in terms of kinetics and equilibrium namely; Cr(VI) removal and chromium sorption were studied at various initial pH (1-7). Removal of Cr(VI) shows a maximum at pH 2.5. At pH<2.5, sorption decreases because of the proton competition with evolved Cr(III) for ion exchange sites. The decrease of sorption at pH>2.5 is due to proton insufficiency and to the decrease of the extent of Cr(VI) reduction. The chemistry of the surface of activated carbon is an important factor in determining its adsorption capacity from aqueous solutions particularly when the sorption process involves ion exchange.

• Journal of the Korea Furniture Society
• /
• v.22 no.1
• /
• pp.13-17
• /
• 2011

Recently, interest in indoor air quality is increasing. Especially, radon radioactivity among the indoor air is a well-known risk factor for lung cancer because of ionizing radiation in the form of ${\alpha}$-particles. This study was carried out to investigate effect of black charcoal and activated carbon for reduction of radon radiation that emitted from building materials. Black charcoal and activated carbon were used as a barrier which was against the infiltration of radon. The source of radon was gypsum board. Two types of charcoal barrier were powder- and board-type with 5 mm, 10 mm thickness respectively. The method for this determination is evaluated radon concentration in chamber. The measurements were performed with radon detector, SARAD3120. Results of this study are as following: Black charcoal and activated carbon confirmed the highly efficient barrier. Radon concentration was reduced from 72% to 85% as compared the control chamber. Radon reduction capability, however, was no difference as barrier's types. Results obtained in ventilation condition, radon concentration shows 5.93 pCi/L on average in the closed condition and shows 2.69 pCi/L in the opened condition.