• Clean Technology
• /
• v.11 no.1
• /
• pp.41-50
• /
• 2005

In this study, semibatch emulsion copolymerization of n-BA as adhesive component and MMA as coagulant component were carried out for the stable acrylic polymer latex in aqueous phase for polymer cement using LE-type nonionic surfactant as environmental friendly surfactant. The stable polymer emulsion was obtained with the increases of chain length(n) of this surfactant. The effect on the amount of LE-50 as nonionic surfactant were showed that the concentration of polymer latex were increased by increasing the amount of LE-50, whereas the average particle size were decreased by increasing the amount. The addition of functional monomer in initial reactor charge showed a significant effect on the final polymer concentration and the latex particle size. The single polymerization of each n-BA or MMA showed a very low concentration of polymer latex and very big particle size due to coagulation. In the polymerization composed of mixed monomer with MMA and n-BA, the larger the ratio of MMA to n-BA in the copolymers, the greater the amount of coagulum produced. It was found that a stable copolymers were obtained in the range of 15-35 % of n-BA. Moreover, incorporation of some functional monomers in addition to of main monomers became more stable polymer latex. Through DSC and IR analysis, the final polymer latex was composed by MMA/n-BA/AA/AM with a single Tg depending on the reaction conditions. As a result, the conditions of this acrylic polymerization could also be effectively controlled to get the desired final products.

• Polymer(Korea)
• /
• v.36 no.3
• /
• pp.315-320
• /
• 2012

Ultra violet (UV) curable pressure sensitive adhesives (PSA) were prepared by controlling both the structure of acryl copolymer and the functionality and content of multi-functional monomers. Acryl copolymer worked as the base polymer for giving the tackiness. Multi-functional monomers were used to vary the crosslinked structure and the degree of crosslink. Acryl copolymer showed the reduced peel strength after UV curing by decreasing the content of 2-ethylhexyl acrylate in the monomer composition. Both the peel strength of PSA and the content of residue found on silicon wafer decreased after UV curing by increasing the functionality of multi-functional monomers. UV curable PSA containing 20 phr six-functional monomer showed the higher peel strength before UV curing and the lower peel strength and the least residue on silicon wafer after UV curing.

• Applied Chemistry for Engineering
• /
• v.5 no.3
• /
• pp.395-405
• /
• 1994

The various functional groups, such as hydroxyl(-OH), carboxyl(-COOH) and quinonic oxygen(OC<) on the carbon black(abbreviated to CB) surface were activated with n-butyl lithium solution in n-hexane and then acrylate and methacrylate monomers were graft polymerized onto these activated anionic sites and CB-grafted polymers were obtained. To separate homopolymers from reaction mixture, non-solvent precipitation method or centrifugal separating method were applied. Subsequently, conversion, grafting ratio and efficiency were determined at various reaction temperatures and times. In case of acrylates, the grafting ratio showed 20~30% but methacrylates showed 150~200%. Also the anion polymerizations between CB and monomers were nearly reached to equilibrium state within one or two hours under each reaction temperatures but conversion and grafting ratio were increased a little with reaction temperature increase. In colloidal dispersion stability test, before heat-drying, the all CB-grafted polymers showed good dispersed stability in good solvents for acrylic and methacrylic homopolymers. Futhermore, CB-polymethacrylates were found to show excellent collidal properties for good solvents of methacrylic homopolymer even after heat-drying. Identification of the grafted polyacrylates and polymethacrylates onto the CB surface was performed by FT-IR spectroscopy. In addition, electric resistance values of CB-grafted polymers were measured by Four-probe method, and the increase of the grafting ratio showed the increase of the surface resistance.

• Journal of the Korea Concrete Institute
• /
• v.19 no.4
• /
• pp.475-482
• /
• 2007

The property and applicability of the organic-inorganic synthesized penetrating and reinforcing agent, which is developed in order to improve durability of concrete structures and prevent deterioration that may occur as service years increased, are researched with experimental works. TEOS (tetra-ethoxyorthosilicate) and acrylate monomer are synthesized by the solution polycondensation method in order to formulate silicate with sol-gel process and improve durability of concrete. Additional substances such as isobutyl-orthosilicate is supplemented in order to improve the performance of the agent. After the developed organic-inorganic penetrating reinforcing agent penetrates, a flexible impact alleviating layer is formed with organic monomers as well as the agent strengthens concrete by filling up the internal pore of concrete with stable compounds after penetration. Penetrating and reinforcing agent can be applied as an effective life management method because it makes concrete more durable against the aging factors, such as chloride ion, carbonation, freezing-thawing, and compound aging.

• Journal of the Korean Applied Science and Technology
• /
• v.33 no.4
• /
• pp.771-776
• /
• 2016

The acrylate copolymer having good thermal stability, coating and adhesion properties was designed and prepared. We prepared copolymers in >95% high yield using methyl methacrylate, isobornyl methacrylate and 2-hydroxyethyl methacrylate monomers by the bulk and emulsion polymerization techniques. The $^1H$-NMR spectrum was used to identify chemical structure and glass transition temperatures increased from $123^{\circ}C$ to $140^{\circ}C$ confirmed by DSC, DMA and TGA analysis. In addition, as the content of IBMA increased, storage modulus and thermal decomposition temperature increased. As the content of IBMA increased from 10% to 30% in the composition for the entire monomer, tensile strength increased from 22 to 30 MPa in both polymers prepared by bulk and emulsion techniques. The contact angle increased from 70 to up to 88 degrees due to hydrophobic property of IBMA.

• Applied Chemistry for Engineering
• /
• v.23 no.2
• /
• pp.157-163
• /
• 2012

Using six kinds of epoxy acrylates and a conductive carbon black, photosensitive resistor pastes were fabricated and then their developability in alkaline aqueous solution and the resistance values after thermal curing were evaluated. In order to impart the photocurability by UV exposure and the developability on alkaline solution, epoxy acrylate oligomers with carboxyl group, acrylate monomers, a photoinitiator and so forth were used. In addition, an organic peroxide was added into the paste to get a thermally curable composition. As a result, some of the pastes were not developed depending on the kinds of oligomers and, in the developed pastes, the measured resistance showed the different values depending on their compositions, even though they contain the same amount of carbon black. Finally, the optimum oligomer was selected and then, by adjusting the amount of carbon black, the kind of monomer and the curing temperature, the photosensitive resistor paste composition which showed the sheet resistance of about 0.5 $k{\Omega}/sq.$ could be obtained.

• Journal of the Korean Applied Science and Technology
• /
• v.22 no.3
• /
• pp.289-297
• /
• 2005

In order to improve resistant properties of water-borne acrylic pressure sensitive adhesives(PSAs) for automobiles, this study was carried out. Removable PSAs for automobiles were synthesized by emulsion polymerization of monomers, n-butyl acrylate(BA), n-butyl methacrylate(BMA), acrylonitrile(AN), acrylic acid(AA) and 2-hydroxyethyl methacrylate(2-HEMA), and AA and 2-HEMA could act as functional monomers for crosslink. Emulsion polymerization was carried out in a semi-batch type reactor. Water resistance, heat resistance, acid resistance, alkali resistance and smoke resistance were examined. As a result, water resistance increased with the amount of BMA, however, the effect of BMA content on the water resistance was insignificant at a range of over 14 wt%. The water resistance also increased with the amount of functional monomers, AA and 2-HEMA. The prepared PSAs satisfied all the standard for automobiles except heat resistance. However, the heat resistance comes nearly up to the standard. Also, acid resistance, alkali resistance and smoke resistance of the prepared PSAs satisfied with the standard.

• Applied Chemistry for Engineering
• /
• v.16 no.3
• /
• pp.449-455
• /
• 2005

Electron beam (EB) and ultraviolet (UV) curable monomers (AF-1 with mono functionality and AF-2 with tetra functionality) containing hydroxy and acrylate group for anti-fogging coating were synthesized and applied to EB and UV-curable coating systems. The synthesized reactive AF-1 and AF-2 monomers were first formulated into UV-curable system and the optimization of film properties for anti-fogging coating was investigated. The 5:17.5 ratio for AF-1 and AF-2 was found to be the best optimized formulation for anti-fogging coating without destroying the other essential properties such as hardness, solvent resistance, and adhesion. The optimized formulation was applied to the EB-curable system, and EB and UV-curable systems were compared. The results demonstrated that both EB and UV-cured films coated on PC sheet showed excellent anti-fogging properties; however, the EB-cured film exhibited better hardness, adhesion, and water repellent properties than the UV-cured film.

• Journal of Adhesion and Interface
• /
• v.18 no.1
• /
• pp.25-32
• /
• 2017

For application to display module junction process, the silk screen printing based on UV curable acrylic pressure sensitive adhesive(PSA) with silica nano-particles and the rheological properties were studied to investigate the effect on printability and adhesion. The monomers for PSA were based on 2-ethylhexyl acrylate(2-EHA) and acrylic acid(AA) 93:7, butyl acylate(BA), 2-hydroxyethyl acrylate(2-HEA) and tetrahydrofurfuryl acrylate(THFA) were added. Additionally, hydrophobic and hydrophilic nano-particles AEROSIL R974 and AEROSIL 200 were added, respectively. When the ratio of nano-particle was used above 4 or 7 phr, G' and ${\eta}^*$ were increased significantly. When the ratio of AEROSIL 200 was used above 7 phr, the penetration property was decreased during the silk screen printing. We found that the adhesion was decreased with increasing the nano-particle content, and it was decreased in the case of the hydrophilic nano-particle AEROSIL 200.

• Applied Chemistry for Engineering
• /
• v.30 no.2
• /
• pp.205-211
• /
• 2019

Over the past several decades, the polymer dispersed liquid crystal (PDLC) has received particular attention as a material for developing smart window due to their electro-optical switchable properties. In this study, PDLC cells were fabricated using acrylate monomers, namely 2-hydroxyethyl acrylate (2-HEA) and ethylene glycol phenyl ether acrylate (EGPA), and the effect of the monomer composition on their electro-optical properties was investigated. The monomer mixture with a low viscosity (~10 cps) was easily filled between indium tin oxide (ITO) glasses by capillary action at room temperature. PDLC cells prepared using the mixture ratio of 1 : 9 (2-HEA : EGPA) did not show a complete opaque state at a 0 V condition but exhibited unstable electro-optical properties under an electric field. As the LC composition increased in the reaction mixture for PDLC cell preparation, the $V_{th}$ (threshold voltage) and $V_{sat}$ (saturation voltage) values as well as contrast ratio (CR) increased. $V_{th}$ and $V_{sat}$ values also increased with the cell gap thickness. PDLC cells with a $20{\mu}m$ cell gap thickness exhibited higher CR than those with 10 and $40{\mu}m$ cell gap thicknesses. Particularly, PDLC cells prepared using the mixture ratio of 7 : 3 (2-HEA : EGPA) showed excellent electro-optical properties such as a low driving voltage and high contrast ratio.