• Journal of the Korea institute for structural maintenance and inspection
• /
• v.3 no.4
• /
• pp.163-171
• /
• 1999

In this study, we executed fundamental experiment to investigate properties of accelerated carbonation with changing chloride content of concrete used sea sand in order to examine durability. So we obtained the results of following properties of mechanics, durability, concrete with sea sand, determined concrete w/C 30%, 40%, 50%, and fine aggregate 40% and changing containing chloride 0, 0.3, 0.6, $0.9kg/m^3$ by the experiment of accelerated neutralization. The results of this study as follows: 1) As result of changing chloride content of concrete used sea sand augmented in stages $0.3kg/m^3$, accelerated carbonation was increased as increment chloride content. The increment depth was decreased as it went long term age. It was shown the chloride content effected increment of carbonation depth in concrete 2) As a result of changing W/C of concrete used sea sand augmented in stages 10% at a time from 30% to 50%, accelerated carbonation depth of concrete was increased as W/C ratio. 3) As the carbonation concrete used sea sand, compressive strength between 8 weeks and accelerated carbonation depth of 1 weeks, 2 weeks, 4 weeks, 8 weeks was inversion proportion.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.297-298
• /
• 2023

In the concrete industry, efforts are being made to reduce CO₂ emissions, and technologies that collect, store, and utilize CO₂ have recently been studied. This study analyzed the change in compressive strength after the accelerated carbonation test of Non-Sintered Cement(NSC) mortar. Type C Fly Ash and Type F Fly Ash were mixed in a 1:1 ratio and then mixed with Blast Furnace Slag fine powder to produce NSC. The mortar produced was cured underwater until the target age. In addition, an accelerated carbonation test was conducted under the condition of a concentration of 5 (±1.0%) of CO₂ gas for 14 days. The mortar compressive strength was measured before and after 14 days of accelerated carbonation test based on the 7th and 28th days of age. As a result of the experiment, the compressive strength was improved in all binder. In general, the compressive strength of NSC mortar subjected to the accelerated carbonation test was similar to that of Ordinary Portland Cement(OPC) mortar not subjected to the accelerated carbonation test.

• Journal of the Korea Concrete Institute
• /
• v.21 no.4
• /
• pp.449-455
• /
• 2009

The increase of industrial carbonic dioxide emissions has accelerated the carbonation of reinforced concrete structures, which drops off their durability. Although advanced countries have already taken safety control measures against the carbonation of RC structures, it is still difficult now to accurately predict the actual carbonation depth. Additionally, it requires much time and efforts. Recently, it is possible to get the data more rapidly through accelerated carbonation test with the $CO_2$ concentration of 100%. In this paper, the carbonation test results obtained by two test methods such as the normal carbonation test method and the accelerated carbonation test method, were compared to investigate the carbonation characteristics of fly ash concrete. The accelerated carbonation test on concrete specimens with the pre-curing age of 180 days was also carried out to examine the carbonation characteristics of fly ash concrete at long-term age. Consequently, fly ash concrete at early age was vulnerable to carbonation and however, its carbonation resistance at long-term ages was improved compared with OPC concrete.

• Journal of the Korean Ceramic Society
• /
• v.51 no.2
• /
• pp.64-71
• /
• 2014

Accelerated carbonation is a technique that can be used as a CCS technology for $CO_2$ sequestration of approximately 5~20% in a stable solid through the precipitation of carbonate. An alkaline inorganic waste material such as ash, slag, and cement paste are generated from incinerators, accelerated carbonation offers the advantage of lower transport and processing costs at the same generation location of waste and $CO_2$. In this study, we evaluated an amount of $CO_2$ sequestration in various types of inorganic alkaline waste processed by means of accelerated carbonation. A quantitative evaluation of $CO_2$ real sequestration based on a TG/DTA analysis, the maximum 118.88 $g/kg_{-waste}$ of $CO_2$ in paper sludge fly ash, the maximum 134.46 $g/kg_{-waste}$ of $CO_2$ in municipal solid waste incinerator bottom ash, the maximum 9.72 $g/kg_{-waste}$ of $CO_2$ in industrial solid waste incinerator fly ash, and the maximum $18.19g/kg_{-waste}$ of $CO_2$ in waste cement paste.

• Mineral and Industry
• /
• v.26
• /
• pp.1-12
• /
• 2013

In this study, an accelerated carbonation process was applied to stabilize hazardous heavy metals of industrial solid waste incineration (ISWI) bottom ash and fly ash, and to reduce $CO_2$ emissions. The most commonly used method to stabilize heavy metals is accelerated carbonation using a high water-to-solid ratio including oxidation and carbonation reactions as well as neutralization of the pH, dissolution, and precipitation and sorption. This process has been recognized as having a significant effect on the leaching of heavy metals in alkaline materials such as ISWI ash. The accelerated carbonation process with $CO_2$ absorption was investigated to confirm the leaching behavior of heavy metals contained in ISWI ash including fly and bottom ash. Only the temperature of the chamber at atmospheric pressure was varied and the $CO_2$ concentration was kept constant at 99% while the water-to-solid ratio (L/S) was set at 0.3 and $3.0dm^3/kg$. In the result, the concentration of leached heavy metals and pH value decreased with increasing carbonation reaction time whereas the bottom ash showed no effect. The mechanism of heavy metal-stabilization is supported by two findings during the carbonation reaction. First, the carbonation reaction is sufficient to decrease the pH and to form an insoluble heavy metal-material that contributes to a reduction of the leaching. Second, the adsorbent compound in the bottom ash controls the leaching of heavy metals; the calcite formed by the carbonation reaction has high affinity of heavy metals. In addition, approximately 5 kg/ton and 27 kg/ton $CO_2$ were sequestrated in ISWI bottom ash and fly ash after the carbonation reaction, respectively.

• Corrosion Science and Technology
• /
• v.4 no.4
• /
• pp.130-135
• /
• 2005

In this study, accelerated corrosion tests were conducted on concrete specimens with and without accelerated carbonation beforehand for the purpose of elucidating the effects of carbonation, cover depth, and water-cement ratio (W/C) on the reinforcement corrosion. During testing, the corrosion current between the anode steel and cathode stainless steel was measured to continuously monitor the progress of corrosion throughout the test period, thereby investigating the mechanism of reinforcement corrosion and the relationship between corrosion and crack width, as well as other parameters.

• KCI Concrete Journal
• /
• v.12 no.1
• /
• pp.79-89
• /
• 2000

This research developed an accelerated curing processe for cellulose fiber reinforced cement composites using vigorous reaction between carbon dioxide and cement paste. A wet-processed cellulose fiber reinforced cement system was considered. Carbonation curing was used to complement conventional accelerated curing. The parametric study followed by optimization investigation indicated that the carbonation curing can enhance the productivity and energy efficiency of manufacturing cellulose fiber reinforced cement composites. This also adds environmental benefits to the technical and economical advantages of the technology.

• International Journal of Concrete Structures and Materials
• /
• v.18 no.1E
• /
• pp.17-22
• /
• 2006

Artificial cracks were made in the cover concrete of specimens embedding ten types of steel rebars of different Cr contents. The research aims for developing Cr-bearing steel rebars resistant to macrocell corrosion environments induced by cracking in cover concrete. The cracks were subjected to intensive penetration of carbon dioxide (carbonation specimens) to form macrocells. The carbonation specimens were then treated with accelerated corrosion curing, during which current macrocell corrosion density was measured. The corrosion area and loss from corrosion were also measured at the end of 105 cycles of this accelerated curing. The results of the study showed that Cr-bearing steel with Cr content of 5% or more suppressed corrosion in a macrocell corrosion environment induced by the differences in the pH values due to carbonation of cracked parts. Cr-bearing steels with Cr content of 7% or more are proven to possess excellent corrosion resistance.

• Proceedings of the IEEK Conference
• /
• 2001.10a
• /
• pp.586-591
• /
• 2001

This research investigated the feasibility of the accelerated carbonation of cement waste forms with carbon dioxide in a supercritical state. Hydraulic cement has been used as a main solidification matrix for the immobilization of radioactive and/or hazardous wastes. As a result of the hydration reaction for major compounds of portland cement, portlandite (Ca(OH)$_2$) is present in the hydrated cement waste form. The chemical durability of a cement form is expected to increase by converting portlandite to the less soluble calcite (CaCO$_3$). For a faster reaction of portlandite with carbon dioxide, SCCD (supercritical carbon dioxide) rather than gaseous $CO_2$, in ambient pressure is used. The cement forms fabricated with an addition of slated lime or Na-bentonite were cured under ambient conditions for 28days and then treated with SCCD in an autoclave maintained at 34$^{\circ}C$ and 80atm. After SCCD treatment, the physicochemical properties of cement matrices were analyzed to evaluate the effectiveness of accelerated carbonation reaction. Conversion of parts of portlandite to calcite by the carbonation reaction with SCCD was verified by XRD (X-ray diffraction) analysis and the composition of portlandite and calcite was estimated using thermogravimetric (TG) data. After SCCD treatment, tile cement density slightly increased by about 1.5% regardless of the SCCD treatment time. The leaching behavior of cement, tested in accordance with an ISO leach test method at 7$0^{\circ}C$ for over 300 days, showed a proportional relationship to the square root of the leaching time, so the major leaching mechanism of cement matrix was diffusion controlled. The cumulative fraction leached (CFL) of calcium decreased by more than 50% after SCCD treatment. It might be concluded that the enhancement of the characteristics of a cement matrix by an accelerated carbonation reaction with SCCD is possible to some extent.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.655-660
• /
• 2002

Major deterioration in concrete structures are salt attack and carbonation. Especially severe problems due to carbonation occur in tile concrete structures of city, tunnel, underground structures. Cracks in concrete during service life including early age due to hydration heat and/or shrinkage accelerate the diffusion of concrete so that the deterioration is also accelerated. In this study, carbonation depths of both non-cracked concrete and cracked concrete are evaluated and weight change test and TGA are carried out. Through the tests, a relation between water-cement ratio and carbonation depth is derived and also carbonation increase rate is derived in the function of crack width.