• Polymer(Korea)
• /
• v.25 no.3
• /
• pp.399-405
• /
• 2001

Poly[3-octylthiophene-co-3-(4-fluorophenyl)thiophene]s were synthesized in 2:1, 1:1, and 1:2 mole ratios, and organic electroluminescent devices were fabricated using the copolymers. The opto-electrical properties of the copolymers were studied by PL, EL spectra, I-V, and V-L curves of the organic electroluminescent devices in conjunction with the energy band diagrams which were obtained from the cyclic voltammogram and the electronic absorption spectra. The LUMO energy level of P(OT/FPT)(1:1) is the lowest as -3.35 eV. In the copolymers P(OT/FPT)(2:1) and P(OT/FPT)(1:1) the ${\lambada}_{max}$ in the PL and EL spectra red-shifted as the mole ratio of fluorophenyl group increased while in P(OT/FPT)(1:2) it showed a blue-shift. This indicates that the backbone chain is twisted due to the steric hinderance of the fluorophenyl group leading to shorter ${\pi}$-conjugation length. P(OT/FPT)(1:1) showed the highest EL intensity and the highest power efficiency among the three copolymers. In P(OT/FPT)(1:2) the roughness of the film surface causes unusually high local leakage current leading to the low efficiency of electroluminescence.

• Polymer(Korea)
• /
• v.24 no.2
• /
• pp.149-158
• /
• 2000

Oil-absorptive expanded polyurethane (EPU) was prepared with a lypophilic polyol, polypropyleneglycol (PPG) as the soft segment, and toluenediisocyanate (TDI) and $H_2O$ as the hard segment. PPGs haying various average molecular weights ((equation omitted) : 1000, 2000, 3000) were employed to investigate that the soft segment content was consequent on the oil-absorptivity and the mechanical properties of the EPUs. As (equation omitted) of PPG was decreased from 3000 to 1000, the oil-absorptivity and the tensile strength of the EPUs increased from 1460 to 3010% and from 0.26 to 0.55 $kg_{f}$ /$cm^2$ respectively. As the hard segment content ratio, ${\gamma}$ ([NCO]/[OH]) was increased from 1.0 to 1.2, the tensile strength of the EPUs increased from 0.56 to 0.95 $kg_{f}$ /$cm^2$, due to the formation of allophanate and/or biuret bondings. However, as the surfactant (S-A) content was increased from 1.0 to 2.5 pbw, the oil-absorptivity was decreased from 3634 to 3312%, due to the formation of closed cell structures.

• Korean Journal of Soil Science and Fertilizer
• /
• v.35 no.3
• /
• pp.175-184
• /
• 2002

Soil chemical parameters of peach orchards and the concentration of nutrients in peach leaves were investigated. Results of soil analysis showed that pH value and content of exchangeable calcium was quite low, required to adjust soil acidity in many investigated soils. Nitrogen and phosphorous contents in leaves were founded to be excessive comparing to RDA's optimal levels(N $29.3{\sim}35.9g\;kg^{-1}$, P $1.7{\sim}2.2g\;kg^{-1}$), while calcium contents were lower than optimal levels($11.2{\sim}21.0g\;kg^{-1}$) in many sites and Potassium content was higher in peach cultivars than nectarine cultivars. Correlation analysis revealed that organic matter contents in subsoils and exchangeable calcium content in soils(top and subsoil) were increased with cultivation year, but available phosphate contents in subsoils were decreased. Organic matter and exchangeable magnesium contents in top soils were positively correlated with potassium and magnesium contents in leaves, whereas were negatively correlated with calcium contents in leaves, impling antagonistic absorption of calcium against potassium and magnesium. The findings indicated that most of soils ought to managed to adjust soil acidity and application amount of nitrogen, phosphorous fertilizer and compost should be controlled properly.

• Journal of the Korean Chemical Society
• /
• v.19 no.4
• /
• pp.269-279
• /
• 1975

Photosensitive properties of naphthoquinone-1,2-diazide-5-sulfonyl esters (PGND, BEND and PVAND) of polyglyceryl phthalate(PG), bisphenol A-epichlorohydrin condensate(BE) and polyvinyl alcohol(PVA) were investigated by the change of solubility before and after exposing to light. Various samples coated on glass or quartz plates were exposed to light under various conditions and steeped in aqueous alkali solution, and then the yield of residual film(W/W0) was determined. The yield of residual film, which was closely related to the sensitivity of the film, was affected by the degree of polymerization of the backbone resin, sensitizers and their concentration. In polymer homologs, the sensitivity was dependent on the degree of polymerization(the higher, the better). And also, it was most effective when 5 % of sensitizers to esters was used. The minimum exposed time was 0.6 min. for PGND-1, 1.0 min. for BEND-1, and 3.0 min. for PVAND-1. Most effective sensitizers for PGND, BEND and PVAND among those used here were benzanthrone, 5-nitroacenaphthene and picramide, respectively. The spectral sensitivities of PGND, BEND and PVAND were examined by comparing their spectrograms with UV-spectra in a solid state. Also, the sensitization and spectral sensitivity of the above polymers were studied. All the polymers containing the sensitizers showed optical sensitization. From the fact that in either case of sensitized or unsensitized sample, the ranges of absorption-maximum wave length were almost consistent with sensitivity maximum wave length, it was proved that the light absorbed by a sample served efficiently for photochemical reactions. Benzanthrone was found to be an excellent sensitizer for PGND.

• Journal of the Korean Magnetics Society
• /
• v.17 no.2
• /
• pp.60-64
• /
• 2007

Ba-Ferrite single crystals were prepared and characterized by X-ray, SEM and Mossbauer spectroscopy. The single crystal layers was cut in the c-axis and radiated to the surface by ${\gamma}-rays$ for Mossbauer spectroscopy. We found out that the spin states in Fe atoms were parallel to the ${\gamma}-rays$ direction. The temperature dependence of the hyperfine field is almost similar to that of powder samples. The crystal structure is a Magnetoplumbite without any other phases and the lattice parameters are found out with $a_0=5.892{\AA},\;b_0=5.892{\AA},\;c_0=23.198{\AA}$. $M\"{o}ssbauer$ spectrum in single crystal have 5 sets off absorption lines in each Fe site when the ${\gamma}-rays$ have the same radiation direction with the c-axis in the crystal, which mean that the whole crystal bulk formed only one crystal and same spin direction. The hysteresis curve shows the saturation moment and coercive force of 70.71 emu/g and 320 Oe respectively.

• Applied Chemistry for Engineering
• /
• v.8 no.4
• /
• pp.568-574
• /
• 1997

The effect of microencapsulation of maetal hydride (MH) with copper on the electrode performance of a Ni/MH battery has been investigated. The MH electrodes were prepared with a combination of cold press and paste methods. The discharge capacity of the electrode increased with an addition of small amounts if CMC into the electrode, but decreased when heat-treated in an oxygen-free nitrogen flow. The capacity of a Cu-coated $LaNi_5$ electrode was higher than that of LaNi5electrode. The discharge capacity of the electrode prepared with Cu-coated $LaNi_5$ increased with the increase of copper content in the electrode. It is considered that the increase of copper content enhanced the current density on the electrode surface, leading to the increase of the discharge capacity The MH electrode coated by an acidic electroless plating method showed much higher discharge capacity than that using an alkaline electroless plating method. The discharge capacity of the $LaNi_{4.5}Al_{0.5}$ electrode was higher than that of the $LaNi_5$ electrode. Also, the effect of microencapsulation on the deactivation of $LaNi_5$ was studied using an absorption-desorption cycle in CO-containing hydrogen.

• Environmental Mutagens and Carcinogens
• /
• v.25 no.2
• /
• pp.60-65
• /
• 2005

The human solute carrier, SLC41Al, is a $Mg^{2}+$ transporter that is regulated by extracellular magnesium. Although intracellular magnesium plays a fundamental role in cellular metabolism, little is known about how $Mg^{2}+$ is taken up and controlled by cells. Magnesium plays a fundamental role in cellular metabolism so that its control within the body is critical. Magnesium homeostasis is principally a balance between intestinal absorption of dietary magnesium and renal excretion of urinary magnesium. The kidney, mainly the distal convoluted tubule, controls magnesium reabsorption. Although renal reabsorption is under the influence of many hormones, selective regulation of magnesium transport is due to intrinsic control involving transcriptional processes and synthesis of transport proteins. Using microarray analysis, identification of the genetic elements involved with this transcriptional control has been begun. SLC41A1(GenBank Accession No. AJ514402), comprises 10 putative transmembrane domains, two of which are highly homologous to the integral membrane part of the prokaryote transports $Mg^{2}+$ and other divalent cations $Sr^2+,\;Zn^2+,\;Cu^2+,\;Fe^2+,\;Co^2+,\;Ba^2+,\;and\;Cd^2+,\;but\;not\;Ca^2+,\;Mn^2+,\;and\;Ni^2+.$ Transport of $Mg^{2}+$ by SLC41Al is rheogenic, voltage dependent, and not coupled to Na or Cl. Expressed SLC41Al transports a range of other divalent cations: $Mg^{2+},\;Sr^{2+},\;Zn^{2+},\;Cu^{2+},\;Fe^{2+},\;Co^{2+},\;Ba^{2+},\;and\;Cd^{2+}$. The divalent cations $Ca^{2+},\;Mn^{2+},\;and\;Ni^{2+}$and the trivalent ion $Gd^{3+}$ did not induce currents nor did they inhibit $Mg^{2+}$ transport. The nonselective cation $La^{3+}$ abolishes $Mg^{2+}$ uptake. Computer analysis of the SLC41Al protein structure reveals that it belongs to MgtE protein family & suggested that the human solute carrier, SLC41Al, might be a eukaryotic $Mg^{2+}$ transporter closely related $(60-70\%)$ protein encoded by SLC41A2 is a $Mg^{2}+$ transporter that might be involved in magnesium homeostasis in epithelial cells also transports a range of other divalent cations: $Ba^2,\;Ni^2,\;CO^2,\;Fe^2,\;or\;Mn^2,\;but\;not\;Ca^2,\;Zn^2,\;or\;Cu^{2+}$ that may have related functional properties.

• Journal of the Korea Concrete Institute
• /
• v.28 no.2
• /
• pp.205-212
• /
• 2016

This research investigates the influence of ground granulated blast furnace slag (GGBFS) composition on the alkali-activated slag cement (AASC). Aluminum oxide ($Al_2O_3$) was added to GGBFS binder between 2% and 16% by weight. The alkaline activators KOH (potassium hydroxide) was used and the water to binder ratio of 0.50. The strength development results indicate that increasing the amount of $Al_2O_3$ enhanced hydration. The 2M KOH + 16% $Al_2O_3$ and 4M KOH + 16% $Al_2O_3$ specimens had the highest strength, with an average of 30.8 MPa and 45.2 MPa, after curing for 28days. The strength at 28days of 2M KOH + 16% $Al_2O_3$ was 46% higher than that of 2M KOH (without $Al_2O_3$). Also, the strength at 28days of 4M KOH + 16% $Al_2O_3$ was 44% higher than that of 4M KOH (without $Al_2O_3$). Increase the $Al_2O_3$ contents of the binder results in the strength development at all curing ages. The incorporation of AASC tended to increases the ultrasonic pulse velocity (UPV) due to the similar effects of strength, but increasing the amount of $Al_2O_3$ adversely decreases the water absorption and porosity. Higher addition of $Al_2O_3$ in the specimens increases the Al/Ca and Al/Si in the hydrated products. SEM and EDX analyses show that the formation of much denser microstructures with $Al_2O_3$ addition.

• Journal of the Korea Concrete Institute
• /
• v.28 no.2
• /
• pp.197-204
• /
• 2016

Concrete walls of neutron generating facilities such as fusion reactors and fission reactors become radioactive by neutron irradiation. Both low-activation and neutron shielding are a critical concern at the dismantling stage after the shutdown of facilities with a requirement of radioactive waste management. To tackle this, two types of additives were investigated in fabricating mortar specimens: synthetic high polymers and boron carbide. It is well known that a hydrogen atom is effective in neutron shielding by an elastic scattering because its mass is almost the same as that of the neutron. And boron is an effective neutron absorber with a big neutron absorption cross section. In this study, the effect of the type, shape, and size of polymers were investigated as well as that of boron carbide. Total 16 mix designs were prepared to reveal the effect of polymers on mechanical properties and neutron shielding performance. The neutron does equivalent of polymers-based mortar for fast neutrons decreased by 36 %, and the count rate of boron carbide-based mortar with regard to thermal neutrons decreased by 90 % compared to conventional mortar. These results showed that a combination of polymers and boron carbide compounds has potential to reduce the thickness of neutron shields as well as radioactive waste from reactors.

• Journal of the Korean Society of Food Science and Nutrition
• /
• v.37 no.10
• /
• pp.1369-1374
• /
• 2008

This study investigated proximate compositions and quality characteristics of wet noodles with the addition of freeze dried garlic powders prepared at 0.5, 1.0, 2.0, and 4.0% based on flour source, respectively. The moisture, crude protein, crude fat, nitrogen free extract, crude fiber, and crude ash of the freeze dried garlic powder were $4.72{\pm}0.14%,\;19.46{\pm}0.28%,\;1.21{\pm}0.10%,\;68.45{\pm}2.06%,\;2.38{\pm}0.05%,\;and\;3.78{\pm}0.06%$, respectively. The cooked weight, volume, water absorption of cooked noodles were decreased, but the turbidity of soup was increased with the addition of garlic powder. Increased of L (lightness), a (redness) and b (yellowness) values were caused as the amount of garlic powder increased in dough. Decrease of L value and increase of a and b value were shown with the increase of garlic powder in cooked noodle. The cooked noodles with garlic powder were significantly lower in hardness, adhesiveness, springiness chewiness, gumminess and cohesiveness than those of 100% wheat noodle. Sensory evaluation indicated that cooked noodles with 0.5% garlic powder was not significantly different from the control.