Jo, Eun-Hye;Huh, Yoon-Hyuk;Ko, Kyung-Ho;Park, Chan-Jin;Cho, Lee-Ra
The Journal of Advanced Prosthodontics
/
v.10
no.5
/
pp.374-380
/
2018
PURPOSE. The effect of silica-based glass-ceramic liners on the tensile bond strength between zirconia and resin-based luting agent was evaluated and compared with the effect of 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-containing primers. MATERIALS AND METHODS. Titanium abutments and zirconia crowns (n = 60) were fabricated, and the adhesive surfaces of the specimens were treated by airborne-particle abrasion. The specimens were divided into 5 groups based on surface treatment: a control group, 2 primer groups (MP: Monobond Plus; ZP: Z Prime Plus), and 2 liner groups (PL: P-containing Liner; PFL: P-free Liner). All specimens were cemented with self-adhesive resin-based luting agent. After 24-hour water storage and thermocycling (5,000 cycles, $5^{\circ}C/55^{\circ}C$), the tensile bond strength was measured using a universal testing machine. Failure mode analysis and elemental analysis on the bonding interface were performed. The data were analyzed using Kruskal-Wallis test, Dunn's post hoc test, and Fisher's exact test. RESULTS. The liner groups and primer groups showed significantly higher tensile bond strengths than that of the control group (P<.05). PFL showed a significantly higher tensile bond strength than the primer groups (P<.05). The percentage of mixed failure was higher in the primer groups than in the control group (P<.001), and all the specimens showed mixed failure in the liner groups (P<.001). A chemical reaction area was observed at the bonding interface between zirconia and liner. CONCLUSION. The application of liner significantly increased the tensile bond strength between zirconia and resin-based luting agent. PFL was more effective than MDP-containing primers in improving the tensile bond strength with the resin-based luting agent.
Dental porcelain is one of the materials of choice for restoration where esthetics is of concern, but has a considerable potentials of wear. The wear of enamel is variable when opposed by different porcelain systems and surface conditions, and the exposed dentine and opaque porcelain due to clinical failure is expected to have high potentials of wear. The purpose of this study was to investigate the wear effects of self-glazed, polished incisal porcelain. polished dentine and opaque porcelain against human enamel in the laboratory by use of a pin-on-disk type wear tester. 4 types of dental porcelain($Vita-{\Omega}$, Ceramco-II, Vintage powder $Vita-{\alpha}$ of In-Ceram system) and type IV gold alloy as cotrol group were used for test specimens. Intact buccal cusps of maxillary premolar were used for enamel specimens, and the cusp converged to a point and was devoid of visible abrasion, caries, decalcification. The upper part was the cusp of a maxillary premolar and the lower part was a porcelain specimen. The enamel wear was deter-mined by weighing the cusp before and after each test. Surface profilometer was used to quantitate wear of the porcelain specimens. Vicker's hardness tester was used to evaluate the surface hardness of test specimens. The SEM was used to evaluate the wear surfaces. The results were as follows : 1 Self-glazed porcelain produced more enamel wear than polished porcelain, especially the enamel wear of $Vita-{\alpha}$ self-glazed porcelain was 3.2 times more than that of other groups. 2. Opaque porcelain produced least porcelain wear, $Vita-{\alpha}$ self-glazed porcelain produce greatest porcelain wear, but there was no statistically significant difference between the groups(p>0.05). 3. The enamel wear of dentine porcelain was 3.8 times more than that of polished inisal porcelain(p<0.05), and the enamel wear of opaque porcelain was 1.9 times more than that of polished inisal porcelain, but there was no statistically significant difference between the groups(p>0.05) 4. Overglazed porcelain produced less enamel wear than self-glazed porcelain, and more enamel wear than polished porcelain, but there was no statistically significant difference between the groups(P>0.05). 5. The hardness number of $Vita-{\Omega}$ dentine and Ceramco-II opaque porcelain was larger, but that of Vintage dentine and $Vita-{\alpha}$ self-glazed porcelain was similar to other groups. 6. Examination of SEM photographs revealed that overglazed porcelain had smoother surface than self-glazed porcelain, and self-glazed porcelain had smoother surface than polished porcelain. Much polishing scratches and larger porosities were observed on the opaque porcelain specimen, and much polishing scratchess and small porosities were observed on the dentine porcelain specimen.
Journal of the Korea Academia-Industrial cooperation Society
/
v.20
no.7
/
pp.8-15
/
2019
In this study, we synthesized a calcium sulfonate complex grease and a lithium complex grease to investigate their physical, rheological and tribological properties. The thermal stability of the calcium sulfonate was higher than $300^{\circ}C$ and the lithium complex grease was $245^{\circ}C$ in the dropping point test. In the grease viscosity measurement, the calcium sulfonate complex grease was measured as $7.0Pa{\cdot}s$ and the lithium complex grease was as $4.5Pa{\cdot}s$. Therefore, it was confirmed that the calcium sulfonate complex grease is superior to the lithium complex grease in terms of thermal stability and cohesiveness. In the 4-ball wear test, the calcium sulfonate complex grease was measured to be 0.43 mm and the lithium complex grease to 0.85 mm. In the 4-ball extreme pressure test, calcium sulfonate complex grease was measured as 620 kgf and the lithium complex grease was as 125 kgf. Therefore, it was confirmed that the calcium sulfonate complex grease is superior to the lithium complex grease in abrasion resistance and load-bearing property. It was found that the calcium sulfonate complex grease is more effective than the lithium complex grease in the lubrication at high temperature and high load.
Effects of silane modifier, bis(triethoxysilylpropyl) tetrasulfide (TESPT(S4)) and bis(triethoxysilylpropyl) disulfide (TESPD(S2)), on silica filled compound were investigated upon processability, dynamic, mechanical, heat build-up, blowout properties, and silica dispersion in natural rubber (NR). The temperature of the S2 treated silica compound generated higher than that of the S4 treated compound during internal mixer compounding. The shear viscosity of the S2 compound exhibited lower than that of the S4 compound and the viscosity measured in dynamic mode was close to each other. The elongation modulus of the S2 compound exhibited lower than that of the S4; however, the tear resistance strength of the S2 compound exhibited higher than that of the S4 compound. The loss tan$\delta$ values of the S2 compound exhibited higher than those of the S4 at room temperature. The augmentation of the test temperature lowered the tan$\delta$ values of each compound, which results in close tan$\delta$ values to each other at $100^{\circ}C$. The S2 compound deformed less than the S4 compound, and the blowout time of each compound was close to each other. The S2 compound generated more heat build-up than the S4 compound. The abrasion loss of the S2 compound was less than that of the S4 compound. The size of the silica agglomerate reduced on both S4 and S2 compounds upon vulcanization. The addition of the bifunctional silanes (S2 and S4) on silica filled NR compound improved the processability of each compound and their effects were more significant on the S2 compound than the S4 compound. After vulcanization the silica agglomerate size of each compound reduced compared with before vulcanization.
In this study, we have investigated microstructure, mechanical properties and wear characteristic of aluminum metal matrix composites with a high volume fraction and uniformly dispersed SiC particles which produced by a liquid pressing process. The volume fraction of bimodal SiC/Al7075 composite was 12% higher than that of the monomodal SiC/Al7075 composite and a compressive strength is increased about 200 MPa. As a result of the abrasion test, the wear width and depth of the bimodal SiC/Al7075 composite were $285.1{\mu}m$ and $0.45{\mu}m$, respectively. The coefficient of friction of bimodal SiC/Al7075 was 0.16.
This stusy was to investigate the marginal fitness of porcelain-fused-to- metal crown after succesive firing cycle. Main variables were the degree of marginal curvature of labiocervical margin and the type of alloy. The exaggerated marginal curvature(EMC) was created by additional reduction at the faciocervical wall of the normallized marginal curvature (NMC)-typed ivorine tooth by using milling machine. The difference in the shape was the mid facial margin was placed 2mm apical to cemento- enamel junction in labial surface. Three types of alloy were high noble, noble, and base metal alloy. Test specimens were divided into 8 groups and each group had 8 specimens. Sixty four ceramometal crowns were made totally. Measurement stages were following degassing, opaquing. body porcelain firing, and glazing, and measuring sites were 4. (midmesial, midfacial, middistal, and midlingual). Digital, travelling measuring microscope (0.5 um precision, Olympus. Japan) was used under ${\times}250$ magnification. Within the limitation of this investigation, it was concluded as belows: 1. The pattern of marginal distortion was varied. Degassing stage was not a specific, causative stage that induce most of total marginal distortion during whole procedure fabricating a ceramometal crown. Body firing stage induced discrepancy relatively more than other firing stages. 2. The specimens that were Ni-based alloy and had EMC were distorted persistently following successive fabricating procedures. But marginal openings were decreased after glazing. 3. The release of metal grinding-induced stress was presumed as a cause that induce marginal distortion. 4. The amount of discrepancies of the labial and lingual margins were greater than that of the mesial and distal margin in the specimen that had EMC. 5. Silver-plated die was not enough to resist abrasion during repeated seating of metal copings on the die-holding device.
Journal of the Korean Recycled Construction Resources Institute
/
v.7
no.4
/
pp.128-135
/
2012
Autoclaved lightweight concrete, also known as autoclaved aerated concrete(AAC) or autoclaved cellular concrete (ACC), is made with fine silica powder, quik lime, cement, and an Al powder. ALC contains 70~80% air. The lightweight material offers excellent sound and thermal insulation, and like all cement-based materials, is strong and fire resistant. However, ALC have high water absorption, low compressive strength and popout the origin of the low surface strength in its properties. These properties make troubles under construction such as cracking and popout. Thus, this study is to improve the fundamental strength by controls of increasing of admixtures, gypsum and silica powder size. Admixtures make use of metakaolin and silica fume. From the test result, the ALC using admixture have a good fundamental properties compared with plain ALC. Compressive strength, specific strength and abrasion's ratio were improved depending on increasing admixtures ratio's, gypsum and silica powder size.
Choi, Jae Hyung;Lim, Hyun-Gyu;Yoon, Jong Jin;Kang, Deuk Soo
Journal of the Korean Society for Aeronautical & Space Sciences
/
v.45
no.4
/
pp.292-299
/
2017
The KUH-1's Wheel Brake Assembly which is Brake System is an essential component to perform flight mission for pilot. It has function of taxing, differential braking and parking to sustain landing capability. However, the skid and abrasion of tire were occurred in mass-produce operation. Also, if it is occurred on the ground, the flight can not be performed. In this case, the defect is a major cause of the decrease in the operation rate of aircraft. In this paper, the cause of the defect in flight was identified and the failure process was organized. Also, it describes design improvements which was derived from troubleshooting and suggests verification results of flight test.
Won Jong-Pil;Seo Jung-Min;Lee Chang-Soo;Park Hae-Kyun;Lee Myeong-Sub
Journal of the Korea Concrete Institute
/
v.17
no.5
s.89
/
pp.743-750
/
2005
High performance concrete containing silica fume for use in bridge deck overlay emerged as a viable type of bridge deck overlay that economic advantage in construction. They have gained acceptance in Europe, America and Canada in a relatively short time due to their low cost. In this study, high-performance concretes containing silica fume were tested and evaluated in the laboratory to assess their applicability for use in bridge deck overlay. It was conducted with experiments of mechanical and durability characteristics in compressive strength, flexural strength, chloride permeability, abrasion resistance, repeated freezing and thawing cycles and deicing salt scaling resistance. Laboratory test result describe that high-performance concrete containing silica fume for bridge deck overlay application shows most outstanding capacity.
The usage of electric forklift truck is gradually increasing due to the convenience at conveying and arranging the materials in the industrial field. In this study, the author designed and suggested the optimum driving system and load tester which both of them are the most important part of the forklift truck. The planetary gear is chose to driving system because it makes big power even though the motor size is small. The gear teeth of planetary gear were designed and the designed planetary gear was tested considering the yield strength and the abrasion of gear teeth. The B-Type electric brake which consists of multiple plates and operates with non-magnetic type was connected with a single shaft in the driving system. So, it can be applied at the sudden braking situation which has the torque increment. And it has the compact size and excellent durability Load tester can give the various levels of load to the planetary gear of driving system in the electric forklift truck and it can also measure the levels of the load which were applied. Therefore, we can measure the noise, torque and perform the durability, vibration tests using load tester. It will be economical because many kinds of test can be performed using reasonable priced load tester The driving system of electric forklift truck which has sufficient competitive can be manufactured using our designed planetary gear reducer with reasonable price. The designed load tester can use for checking the performance of other reducers, as well.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.