• Journal of Conservation Science
• /
• v.35 no.1
• /
• pp.11-18
• /
• 2019

The adhesives joining Buddhist scripture scrolls from medieval Korea(Goryeo Dynasty, A.D. 918~1392) are different from wheat starch adhesive. The composition of the adhesive was analyzed using Attenuated Total Reflectance-Fourier Transform Infrared(ATR-FTIR) spectroscopy. In the adhesive used to join Buddhist scripture scrolls, peaks attributed to amide I and amide II of the protein and carbohydrate were detected in the ATR-FTIR spectra, and no carbonyl peak($1745cm^{-1}$) for oil was detected in the 2nd derivative ATR-FTIR spectra. The ATR-FTIR spectra almost coincided with those of defatted soybean powder adhesive. Hence, the adhesives joining Buddhist scripture scrolls were inferred to be soybean adhesive prepared from a defatted soybean cake.

• Polymer(Korea)
• /
• v.38 no.4
• /
• pp.425-433
• /
• 2014

In this study, microstructure and gel content (C-C) of polybutadiene rubber (PBR) were investigated using various techniques including ASTM D 3616, attenuated total reflectance Fourier transform infrared spectrometry (ATR FTIR), differential scanning calorimetry (DSC) and nuclear magnetic resonance spectroscopy (NMR). The ATR FTIR spectra of the samples were investigated to determine the cis, trans, 1, 2-vinyl and the C-C gel content in PBR. The absorbance ratios of specific peaks in different grades of PBR were correlated with the C-C gel content measured by the ATR FTIR techniques. Physico-mechanical and rheological properties of rubber compounds based on BR with various amounts of gel were determined. The results showed that there is an acceptable correlation between these properties and the C-C gel content of PBR.

• Polymer(Korea)
• /
• v.28 no.6
• /
• pp.545-550
• /
• 2004

The refractive index of thin copolymer film was controlled by photo-degradation of chromophores in the copolymer. FTIR and UV/Vis spectroscopy were employed to elucidate the effect of chemical structure on refractive index changes after photobleaching. The decrease of refractive index of the film by photobleaching can be ascribed to the decrease of polarizability of polymer molecules through breakage of C =C bond in the chromophore. Due to the selective photoreaction of the chromophores which align along the film plane, refractive index of the copolymer film measured in TE mode decreases faster than that in TM mode. Polarized ATR-FTIR spectroscopy was used to verify such a difference in refractive index of the film.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10b
• /
• pp.199-200
• /
• 2003

PEN (Polyethylene 2,6-dicarboxyl naphthalate)은 PET와 화학적 구조가 유사한 polyester 이다. PEN은 PET 의 benzene ring 대신 naphthalene ring이 있는 구조로서 rigid 한 구조를 바탕으로 PET 보다 훨씬 우수한 기계적 물성과 기체 차단성 및 전기 절연성을 가지고 있기 때문에, 현재 PEN에 대해서는 많은 연구가 진행되었고, 상업용으로도 생산되고 있다. 현재까지 진행된 PEN에 대한 연구 중 X-ray를 이용한 배향 거동에 대한 연구보고는 많았으나, 아직까지 FTIR-ATR 을 통해서 시료의 Machine Direction (MD), Transverse Direction (TD), Normal Direction (ND)의 세 방향으로 필름의 3차원적 분자 배향의 거동에 대한 연구보고는 없다. (중략)

• Proceedings of the Korean Fiber Society Conference
• /
• 1999.04a
• /
• pp.277-282
• /
• 1999

• Analytical Science and Technology
• /
• v.27 no.6
• /
• pp.300-307
• /
• 2014

For the application of chemical assessment standards by the extent of diagenetic alteration, we investigated three archaeological animal bones and a modern animal bone using Fourier transform infrared-attenuated total reflection (FTIR-ATR) spectroscopy and x-ray diffraction (XRD) analysis. The calculating results of crystallinity index (CI), carbonate-to-phosphate (C/P) and carbonate-to-carbonate (C/C) using FTIR-ATR spectra showed differences CI and C/P according to the preservative condition of animal bones. By comparison of the crystallinity contents using XRD patterns, the states of animal bones were distinguished to the range of $30^{\circ}-35^{\circ}$. As results of FTIR-ATR and XRD analysis, it is suggested that Mongolian large mammals bone presents the best preservative condition, and cattle bone from Naju site, and Haman site followed. In addition, those were correlated with the results of histological index. The results suggested that the chemical assessment standards may contribute to application of predictions of the states of animal bones discovered from Korea.

• Journal of the Mineralogical Society of Korea
• /
• v.21 no.2
• /
• pp.117-127
• /
• 2008

The characteristics of phosphate adsorption-desorption on kaolinite was studied by batch adsorption experiments and detailed adsorbed state of phosphate on kaolinite surface was investigated using ATR-FTIR (Attenuated Total Reflectance-Fourier Transform Infrared) spectroscopy. The phosphorous contents were measured using UV-VIS-IR spectrophotometer with 820 nm wavelength. The adsorbed P was generally increased with increasing pH value in the range of pH 4 to pH 9, however it is not distinct. Moreover the adsorbed P was significantly changed with different initial phosphate concentration. The adsorption isotherms were well fitted with the Langmuir equation, Temkin equation, and Freundlich equation in descending order. The maximum Langmuir adsorption capacity of kaolinite KGa-2 is 232.5 ($204.1{\sim}256.5$) mg/kg and has very higher value than that of kaolinite KGa-1b. Most of adsorbed phosphate on kaolinite were not easily desorbed to aqueous solution, but might fixed on kaolinite surface. However it needs further research about the exact desorption experiment. It was impossible to recognize phosphorous adsorption bands on kaolinite in ATR-FTIR spectrum from kaolinite bands themselves, because the absorption peaks of phosphorous have very similar positions with those of kaolinite, and the intensities of the former were very weak in comparison with those of the latter.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.100.2-100.2
• /
• 2015

반도체 산업이 성장하고 기술이 향상됨에 따라 소자의 소형화가 이루어지고 있다. 공정법으로는 atomic layer deposition (ALD), chemical vapor deposition (CVD) 등이 있다. 이러한 공정을 이용하여 수십 nm까지 미세화가 진행되고 있으며, 복잡한 구조의 박막을 실현하기 위해 전구체의 개발이 활발히 진행되고 있다. 전구체의 특성을 비실시간으로 분석하는 방법으로는 질량 분석법, 가스크로마토그래피, 적외선 분광법 등이 있다. 전구체의 특성을 실시간으로 분석하기 위해 Fourier transform infrared spectroscopy (FTIR)내에 attenuated total reflectance (ATR)를 거치시켰다. 본 연구는 구조를 개선한 ATR-FTIR을 이용하여 Tris-(dimethylamino) Zirconium (CpZr) 전구체의 흡착 거동을 분석하였다. ATR용 crystal은 Ge crystal을 사용했으며, 온도를 각각 30, 40, $50^{\circ}C$에서 CpZr 전구체의 흡착특성을 연구했다. 흡착성을 증가시키기 위해 Ge crystal 표면에 $ZrO_2$나노입자를 분포시켜 흡착특성을 비교 분석하였다. 또한 CpZr 전구체가 흡착된 Ge crystal 표면에 오존가스를 주입시킨 후 변화를 관찰하였다. Ge crystal표면에 나노입자를 분포시켜 CpZr 전구체를 흡착한 결과 나노입자를 분포시키지 않았을 때 보다 흡착강도가 높게 나타났다. 또한 CpZr 전구체가 흡착된 Ge crystal 표면에 오존가스를 주입한 결과 C-H 결합이 분해됨을 확인했다.

• 보존과학연구
• /
• s.35
• /
• pp.87-98
• /
• 2014

Fourier transform infrared spectroscopy(FTIR-ATR) was applied to chemical analysis for conservation status of 10 human bone remains from Joseon Dynasty. The result of crystallinity index (CI) is $4.25{\pm}0.78$, carbonate to carbonate ratio (C/C) is $0.91{\pm}0.04$ and cabonate content (C/P) is $0.19{\pm}0.06$. The higher histological index (HI) confirmed CI and C/P value was increased and C/C value was reduced. While C/C or C/P values analysis is possible. While DNA analysis can be extracted from the bone, C/C values are lower or C/P values are higher was found to the analysis is possible. Chemical assessment of FTIR and histological index consequence is expected to be applicable as a basis for comprehensive understanding of the conservation status excavated bones.

• Macromolecular Research
• /
• v.15 no.6
• /
• pp.560-564
• /
• 2007

The photostabilization and cure kinetics of UV-curable, optical resins containing various formulations of photostabilizers were investigated to determine the system with the highest cure conversion and durability. Photo-DSC analysis revealed that increasing the concentration of a UV absorber (UVA) decreased both the crosslink density and the cure rate due to competition for the incident photons between the photoinitiator and the UVA, whereas including a hindered amine light stabilizer (HALS) hardly affected either the cure conversion or the cure rate due to its very low absorption of 365 nm. This result was confirmed by FTIR-ATR spectroscopy and UV-visible spectroscopy analyses. QUV ageing experiments showed that the cure conversion and durability were the highest for the UVA/HALS formulation at a ratio of 1 : 2, which is due to their synergistic action.