• 대한기계학회논문집
• /
• 제13권4호
• /
• pp.653-659
• /
• 1989

본 연구에서는 실험방법과 해석방법 등의 차이가 Ｊ$_{IC}$ 값에 미치는 영향을 고찰하여 보았으며, E 813-81법으로 해석된 Ｊ$_{IC}$ 값으로 환산하는 방법을 제안하고 몇 가지 재료와 환경에서 그 오차를 검토하였다.하였다.

• 한국해양공학회지
• /
• 제8권2호
• /
• pp.38-46
• /
• 1994

The method of JSME S001-83 and ASTM E813-87 have been adapted for evaluation of the elastic-plastic fracture toughness J sub(IC) of SB41 steel. This SB41 steel have the characteristics of low-stength CT specimens. The test results obtained have been considered and compared on the basis of resulted data from two kinds of methods(JSME S001-83, ASTM E813-87) and two kinds of specimen configurations(smooth, side-grooved). On the basis of results from consideration and comparison, the difficulties for its application were presented in case when the standard ASTM E813-87 method was employed for the measurement of J sub(IC) in SB41 steel. A modified method was applied for measuring J sub(IC) in SB41 steel that it used the blunting line real-measured by experiment instead of the standard blunting line theoretically determined, and the result from that procedure was analyzed and the usefulness of that method was examined and considered.

• 한국해양공학회지
• /
• 제15권2호
• /
• pp.99-104
• /
• 2001

Elastic-plastic fracture toughness $J_{lc}$ can be used as an effective design criterion in elastic plastic fracture mechanics. Most of these systems are$J_{lc}$ $J_{lc}$ value at high temperature must be determined for use of integrity evaluation and designing of such systems. Elastic-plastic fracture toughness $J_{lc}$ tests were performed on SA516/70 carbon steel plate and test results were analyzed according to ASTM E 813-87, ASTM E 813-89 and ASTM E 1152-87.safety and integrity are required for reactor pressure vessels because, they are operated in high temperature. There are single specimen method, which used as evaluation of safety and integrity for reactor pressure vessels. In this study, elastic-plastic fracture toughness($J_{lc}$) and J-$\Delta$a of SA 516/70 steel used as reactor pressure vessel steel are measured and evaluated at room temperature, 150$^{\circ}C $, 250$^{\circ}C $ and 370$^{\circ}C $ according to unloading compliance method.

• Journal of Mechanical Science and Technology
• /
• 제16권7호
• /
• pp.902-910
• /
• 2002

Cast stainless steel may experience embrittlement when it is exposed approximately to 300$\^{C}$ for a long period. In the present investigation, the three classes of the thermally-aged CF8M specimen were prepared using an artificially-accelerated aging method. After the specimens were held for 300, 1800 and 3600hrs. at 430$\^{C}$, respectively, the specimens were quenched in water which is at room temperature. Load versus load line displacement curves and J-R curves were obtained using the unloading compliance method. talc values were obtained using the ASTM E813-87 and ASTM E 813-81 methods. In addition to these methods, talc values were obtained using the SZW (stretch zone width) method described in JSME S 001-1981. The results of the unloading compliance method are J$\_$Q/=543.9kJ/㎡ for virgin materials. The values of J$\_$IC/ for the degraded materials at 300, 1800 and 3600hrs. are obtained 369.25kJ/㎡, 311.02kJ/㎡, 276.7kJ/㎡, respectively. The results obtained by the SZW method are compared with those obtained by the unloading compliance method. Both results are quite similar. Through the elastic-plastic fracture toughness test, it is found that the value of loc is decreased with an increase of the aging time.

• 대한기계학회논문집A
• /
• 제24권10호
• /
• pp.2405-2412
• /
• 2000

A cast stainless steel may experience an embrittlement when it is exposed to approximately 30$0^{\circ}C$ for long period. In the present investigation, The three classes of the thermally aged CF8M specimie n are prepared using an artificially accelerated aging method. Namely, after the specimen are held for 300, 1800 and 3600hrs. at 43$0^{\circ}C$ respectively, the specimens are quenched in water to room temperature. Load versus load line displacement curves and J-R curves are obtained using the unloading compliance method. $J_{IC}$ values are obtained following ASTM E 813-87 and ASTM E 813-81 methods. In addition to these methods, JIC values are obtained using SZW(stretch zone width) method described in JSME S 001-1981. The results of the unloading compliance method are $J_Q$=485.7 kJ/m$^2$ for virgin material, $J_{IC}$ of the degraded materials associated with 300, 1800 and 3600hrs are obtained 369.25 kJ/m$^2$, 311.02 kJ/m$^2$, 276.7 kJ/m$^2$, respectively. The results of SZW method are similar to those of the unloading compliance method. Through the elastic-plastic fracture toughness test, it is found that the value of $J_{IC}$ is decreased with increasing of the aging time. The results obtained through the investigation can provide reference data for a leak before break(LBB) of reactor coolant system of nuclear power plants.