• Journal of Powder Materials
• /
• v.23 no.5
• /
• pp.353-357
• /
• 2016

In this study, $TiO_2$ powders are synthesized from ammonium hexafluoride titanate (AHFT, $(NH_4)_2TiF_6$) as a precursor by heat treatment. First, we evaluate the physical properties of AHFT using X-ray diffraction (XRD), particle size analysis (PSA), thermogravimetric analysis (TGA), and field-emission scanning electron microscopy (FE-SEM). Then, to prepare the $TiO_2$ powders, is heat-treated at $300-1300^{\circ}C$ for 1 h. The ratio of anatase to rutile phase in $TiO_2$ is estimated by XRD. The anatase phase forms at $500^{\circ}C$ and phase transformation to the rutile phase occurs at $1200^{\circ}C$. Increase in the particle size is observed upon increasing the reaction temperature, and the phase ratio of the rutile phase is determined from a comparison with the calculated XRD data. Thus, we show that anatase and rutile $TiO_2$ powders could be synthesized using AHFT as a raw material, and the obtained data are utilized for developing a new process for producing high-quality $TiO_2$ powder.

• Journal of Powder Materials
• /
• v.25 no.3
• /
• pp.226-231
• /
• 2018

F-containing $TiO_2$ nanopowders are synthesized using simple wet processes (precipitation-based and hydrothermal) from ammonium hexafluorotitanate (AHFT, $(NH_4)_2TiF_6$) as a precursor to apply as a photocatalyst for the degradation of rhodamine B (RhB). The surface properties of the prepared samples are evaluated using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), field-emission scanning electron microscopy (FESEM), and transmission electron microscopy (TEM). The results confirm that the synthesized anatase $TiO_2$ has sphere-like shapes, with numerous small nanoparticles containing fluorine on the surface. The photocatalytic activity of F-containing $TiO_2$ compared with F-free $TiO_2$ is characterized by measuring the degradation of RhB using a xenon lamp. The photocatalytic degradation of F-containing $TiO_2$ exhibits improved photocatalytic activity, based on the positive effects of adsorbed F ions on the surface.

• Journal of Korea Foundry Society
• /
• v.20 no.2
• /
• pp.104-109
• /
• 2000

Three different white cast irons alloyed with Cr, V, Mo and W were prepared in order to study their abrasion wear behavior in as-cast and heat-treated conditions. The specimens were produced using a 15㎏-capacity high frequency induction furnace. Melts were super-heated to $1600^{\circ}C$, and poured at $1550^{\circ}C$ into Y-block pepset molds. Three combinations of the alloying elements were selected so as to obtain the different types of carbides : 3%C-10%Cr-5%Mo-5%W(alloy No. 1: $M_7C_3$ and $M_6C$), 3%C -10%V-5%Mo-5%W(alloy No. 2: MC and $M_2C$) and 3%C-17%Cr-3%V(alloy No. 3: $M_7C_3$ only). A scratching type abrasion test was carried out in the states of as-cast(AS), homogenizing(AH), air-hardening(AHF) and tempering(AHFT). First of all, the as-cast specimens were homogenized at $950^{\circ}C$ for 5h under the vacuum atmosphere. Then, they were austenitized at $1050^{\circ}C$ for 2h and followed by air-hardening in air. The air-hardened specimens were tempered at $300^{\circ}C$ for 3h. 1 ㎏ load was applied in order to contact the specimen with abrading wheel which was wound by 120 mesh SiC paper. The wear loss of the test piece(dimension: $50{\times}50{\times}5$ mm) was measured after one cycle of wear test and this procedure was repeated up to 8 cycles. In all the specimens, the abrasion wear loss was found to decrease in the order of AH, AS, AHFT and AHF states. Abrasion wear loss was lowest in the alloy No.2 and highest in the alloy No.1 except for the as-cast and homogenized condition in which the alloy No.3 showed the highest abrasion wear loss. The lowest abrasion wear loss of the alloy No.2 could be attributed to the fact that it contained primary and eutectic MC carbides, and eutectic $M_2C$ carbide with extremely high hardness. The matrix of each specimen was fully pearlitic in the as-cast state but it was transformed to martensite, tempered martensite and austenite depending upon the type of heat-treatment. From these results, it becomes clear that MC carbide is a significant phase to improve the abrasion wear resistance.

• Korean Journal of Materials Research
• /
• v.10 no.6
• /
• pp.409-414
• /
• 2000

Three different white cast irons alloyed with Cr, V, Mo and W were prepared in order to study their transformation behavior of matrix structures in heat-treated conditions. The specimens were produced using a 15kg-capacity high frequency induction furnace. Melts were super-heated to $1600^{\circ}C$, and poured at $1550^{\circ}C$ into Y-block pepset molds. Three combinations of the alloying elements were selected so as to obtain the different types of carbides and matrix structures : 3%C-10%Cr-5%Mo-5%W(alloy No. 1), 3%C-10%V-5%Mo-5%W(alloy No. 2) and 3%C-17%Cr-3%V(alloy No. 3). The heat-treatments were conducted as follows: frist of all, as-cast specimens were homogenized at $950^{\circ}C$ for 5h under the vacuum atmosphere. Then, they were austenitized at $1050^{\circ}C$ for 2h and followed by air-hardening in air. The air-hardened specimens were tempered at $300^{\circ}C$ for 3h. The observation of morphology of the matrix structures was carried out in the states of as-cast(AS), air-hardened(AHF) and tempered(AHFT). The matrix structures of each alloy were almost fully pearlitic in the as-cast state but it was transformed to martensite, tempered martensite and retained austenite by the heat-treatments such as air-hardening and tempering.