• 전기학회논문지
• /
• 제63권9호
• /
• pp.1227-1232
• /
• 2014

The purpose of this paper is to establish the optimum fabricating condition of specimens using silk screen printing, and to develop humidity sensor which has good humidity sensing properties. The specimens are fabricated under the condition of 90[wt%] $SnO_2$-10[wt%] $TiO_2$, and their microstructure, crystalline structure, humidity sensing properties are examined. From the microstructure analyses, porosity is best at 700[$^{\circ}C$]. From the crystalline structure analyses, intensity of peak becomes strong according to increasing heat treatment temperature. From the humidity sensing properties analyses, an overall results of capacitance changes, linearity and hysteresis for the specimens is best at 600[$^{\circ}C$] and 700[$^{\circ}C$]. Capacitance of specimens increases according to decreasing measurement frequency, and to increasing relative humidity.

• 한국재료학회지
• /
• 제2권3호
• /
• pp.163-171
• /
• 1992

$TiO_2$가 5-50wt%첨가된 $SnO_2/TiO_2$ 후막형 감습소자를 스크린 프린팅 법을 이용하여 제조 하였다. 소자의 표면결정구조를 XRD, SEM 그리고 FTIR로 조사하였으며, 전기적 특성에 의한 후막소자의 감습특성을 측정하였다. $SnO_2/TiO_2$ 후막은 $TiO_2$ 결정상 보다 주로$(SnO^2){\cdot}6T$ 결정상으로 나타났으며, $1300^{\circ}C$에서 소결된 후막소자의 평균입경은 $2.0{\mu}m$이었다. 또한 $1300^{\circ}C$에서 소결된 10wt% $TiO_2$가 첨가된 $SnO_2/TiO_2$ 후막소자는 상대습도 20-90%에서 높은 감습특성을 나타내었다.

• 한국세라믹학회지
• /
• 제39권4호
• /
• pp.386-393
• /
• 2002

본 연구는 티탄산칼륨 섬유(K2O·$nTiO_2$)를 제조한 후, 도전율이 우수한 Sb-doped $SnO_2$(ATO: Antimony Tin Oxide)를 티탄산 칼륨 섬유에 코팅하는 기술을 개발하는데 목적이 있다. 티탄산칼륨 섬유는 서냉 소성법으로 제조하였으며 섬유의 평균 길이는 $15{\mu}m$, 평균 직경은 $0.5{\mu}m$이었다. ATO를 졸-겔법, 공침법, 균일침전법등 세가지 방법으로 티탄산칼륨 섬유에 코팅 하였으며 ATO 코팅된 티탄산칼륨 섬유는 ATO 함량(5∼70 wt%), Sb 함량(0∼20 wt%), 온도($450∼800^{\circ}C$), 수세 여부 및 회수(3∼4회) 등을 변화 시키며 비저항 변화를 관찰하였다. 공침법의 경우 ATO 함량이 30wt%에서 103${\Omega}$·cm 낮은 비저항을 나타내었으며, 그 이상의 함량에서는 거의 일정한 값($60{\Omega}{\cdot}cm∼90{\Omega}{\cdot}$cm)을 보였다.

• 센서학회지
• /
• 제17권4호
• /
• pp.295-302
• /
• 2008

$TiO_2,\;ZrO_2$, and $SiO_2$ were added in the concentration of 1 - 3 wt.% to improve long-term stability for the $SnO2$ thick film gas sensor. Short-term sensor resistances up to 90 h were measured to investigate the stabilization time of initial resistance in air. Long-term resistance drifts in air and in gas to 5000 ppm methane for the sensors annealed at $750^{\circ}C$ for 1 h and continuously heated at an operating temperature of $400^{\circ}C$ were also measured up to 90 days at an interval of 1 day. The long-term drifts in methane sensitivity for the three metal oxide-doped $SnO2$ sensors are closely related to methane sensitivity level, catalytic activity, and long-term drift in sensor resistance in air. Those stabilities are mainly discussed in terms of oxidation state and catalytic activity.