• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.10 no.1
• /
• pp.100-106
• /
• 2014

There is a growing need to introduce advanced pressure vessel steels with higher strength and toughness for the optimizatiooCn of the design and construction of longer life and larger capacity nuclear power plants. SA508 Gr.4N Ni-Cr-Mo low alloy steels have superior strength and fracture toughness, compared to SA508 Gr.3 Mn-Mo-Ni low alloy steel. Therefore, the application of SA508 Gr.4N low alloy steel could be considered to satisfy the strength and toughness required in advanced nuclear power plants. The purpose of this study is to characterize the microstructure and mechanical properties of SA508 Gr.4N low alloy steels. 1 ton ingot of SA508 Gr.4N model alloy was fabricated by vacuum induction melting followed by forging, quenching, and tempering. The predominant microstructure of the SA508 Gr.4N model alloy is tempered martensite having small packet and fine Cr-rich carbides. The yield strength at room temperature was 540MPa, and it was decreased with an increase of test temperature while DSA phenomenon occurred at around $288^{\circ}C$. Overall transition property of SA508 Gr.4N model alloy was much better than SA508 Gr.3 low alloy steel. The index temperature, $T_{41J}$, of SA508 Gr.4N model alloy was $-132^{\circ}C$ in Charpy impact tests, and reference nil-ductility transition temperature, $RT_{NDT}$ of $-105^{\circ}C$ was obtained from drop weight tests. From the fracture toughness tests performed in accordance with the ASTM standard E1921 Master curve method, the reference temperature, $T_0$ was $-147^{\circ}C$, which was improved more than $60^{\circ}C$ compared to SA508 Gr.3 low alloy steels.

• Korean Journal of Metals and Materials
• /
• v.48 no.8
• /
• pp.741-748
• /
• 2010

We studied the corrosion and oxidation properties of Fe-18Cr-0.4Nb-(0.1~0.6)Ti-(1~3)Si-(0.5~2)Mo stainless steel. The resistance to general and pitting corrosion was evaluated and the results were analyzed by Response Surface Methodology (RSM) as a function of alloy composition. The effects of alloy composition and heat treatment on the oxidation resistance were also examined. Mo increased both general corrosion resistance and pitting corrosion resistance. Si improved the resistance of the alloys to pitting corrosion. Si was also beneficial for general corrosion resistance of the alloys containing Mo at more than 1 wt.%. However, Mo was detrimental when its content was lower. Effects of Ti on general corrosion properties appeared to be weak and a high concentration of Ti appeared to deteriorate pitting resistance. The thickness of the oxidation scale increased and adhesion of the scale worsened as the temperature increased from $800^{\circ}C$ to $900^{\circ}C$. Weight gain of the alloys due to oxidation at $900^{\circ}C$ clearly showed that the resistance to oxidation is improved by annealing at $860^{\circ}C$ and an increase of Si content.

• Korean Journal of Metals and Materials
• /
• v.50 no.9
• /
• pp.645-651
• /
• 2012

This study investigated changes in phase fraction caused by the addition of Mo, as well as the subsequent behaviour of N and its effect on the mechanical properties of welded 24Cr-N duplex stainless steel weld metals. Filler metal was produced by fixing the contents of Cr, Ni, N, and Mn while adjusting the Mo content to 1.4, 2.5, 3.5 wt%. The delta ferrite fraction increased as the Mo content increased. In contrast, the ${\gamma}$ fraction decreased and changed from a round to an acicular shape. Secondary austenite (${\gamma}^{\prime}$) was observed in all specimens in a refined form, but it decreased as the Mo content increased to the extent that it was nearly impossible to find any secondary austenite at 3.5 wt% Mo. Both tensile and yield strengths increased with the addition of Mo. In contrast, the highest value of ductility was observed at 1.41 wt% Mo. At all temperatures, impact energy absorption showed the lowest value at 3.5 wt% Mo, at which the amount of ${\delta}$-ferrite was greatest. There was no significant temperature dependence of the impact energy absorption values for any of the specimens. As the fraction of ${\gamma}$ phase decreased, the amount of N stacked in the ${\gamma}$ phase increased. Consequently, the stacking fault energy decreased, while the hardness of ${\gamma}$ increased.

• Journal of Korea Foundry Society
• /
• v.17 no.5
• /
• pp.488-493
• /
• 1997

주방상태 및 열처리를 행한 다합금계백주철(Fe-5%Cr-5%V-5%Mo-5%W-X%C(X=0.5, 1.0, 1.5, 2.0, 2.5, 3.0)에 있어서 탄소함량이 탄화물의 형태 및 잔류오스테나이트의 함량에 미치는 영향에 관하여 연구하였다. 주방상태의 경우, 2.0% 이하의 탄소함량에서는 편상MC 및 층상 $M_2C$탄화물만 관찰되었으나 2.5%C 이상의 경우, 편상 및 괴상MC, 층상$M_2C$ 그리고 셀형 $M_7C_3$탄화물이 관찰되었다. 또한, 기지조직내 오스테나이트의 함량도 탄소첨가와 더불어 점차 증가하여 2.5%C에서 84.8%의 최대함량을 나타낸 후, 3.0%C에서는 다시 감소하였다. 또한 열처리한 시편의 경우, 1차탄화물의 형상은 주방상태의 그것과 비슷하였으나 열처리중 기지조직내 용해되었던 C, Cr, V, Mo, W등이 아주 미세한 2차탄화물의 형태로 석출되어 기지조직내 오스테나이트의 함량은 주방상태의 그것에 비해 감소하였다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.3
• /
• pp.576-584
• /
• 2020

The extruder screw material is mainly SKD11, but the recent development of synthetic resins have increased the occurrence of chemical corrosion and wear. To solve this issue, high chromium cast iron is needed because of its good abrasion resistance and corrosion resistance, but its use is avoided because of its poor machinability. In this study, to improve the machinability of high chrome cast iron, 0, 0.5, 1.0, 1.5% of nickel, which has excellent workability, was added to high chromium cast iron with a composition of Fe-23Cr-2.5C-1.2Si-1.08Mn-0.48Mo-0.3V, and annealed after casting. Subsequently, the effect of nickel on the machinability and corrosion resistance was analyzed using a turning test and coin polarization test, and compared with SKD11. After casting using a high-frequency vacuum induction furnace, the annealing treatment was performed at 750 ℃ for five hours and then reheated at 1100 ℃ for five hours. A turning test after annealing at 750 ℃ showed that the machinability was improved remarkably when the nickel content was over 1.0%. In the potentiodynamic polarization test in a 5% NaCl solution, the corrosion resistance decreased with increasing nickel content in the as-cast and annealing treatment. On the other hand, after reheating, the corrosion resistance was best with a 1.5% nickel content.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.563-564
• /
• 2006

The effect of different cooling rate on the structure and mechanical properties of Fe-3%Mn-(Cr)-(Mo)-0.3%C steels is described. Pre-alloyed Astaloy CrM and CrL, ferromanganese and graphite were used as the starting powders. Following pressing in a rigid die, compacts were sintered at $1120^{\circ}C$ and $1250^{\circ}C$ in $H_2/N_2$ atmospheres and cooled with cooling rates $1.4^{\circ}C/min$ and $6.5^{\circ}C/min$. Convective cooled specimens were subsequently tempered at $200^{\circ}C$ for 60 and 240 minutes.

• Journal of the Korean Society for Heat Treatment
• /
• v.36 no.4
• /
• pp.230-236
• /
• 2023

The current study deals with the effect of cooling rate and temperature for annealing on medium-carbon Cr-Mo alloy steel, especially for cold heading quality wire rod, to derive the optimum micro-structures for plastic deformation. This is to optimize the spheroidization heat treatment conditions for softening the material. Heat treatment was performed under seven different conditions at a temperature between A_c1 and A_c3, mostly within 720℃ to 760℃, and the main variables at this time were temperature, retention time and cooling rate. Microstructure and phase changes were observed for each test condition, and it was confirmed that they were greatly affected by the cooling rate. It was also confirmed that the cooling rate was changed in the range of 0.1℃/min to 5℃/min and affected by phase deformation and spheroidization fraction. The larger the spheroidization fraction, the lower the hardness, which is associated with the increasing connection of ferrite phases.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.4
• /
• pp.532-538
• /
• 1998

Emerald ($3BeO{\cdot}Al_2O_3{\cdot}6SiO_2:Cr^{3+}$) single crystal was grown by temperature gradient reflux method with using Korean natural beryl. The flux of lithium-molibudenium-vanadium oxide system was made by means of mixing the 2 sort of flux which were differently melted $Mo_3-Li_2O$ and $V_2O_5-Li_2O$ each other. The optimum composition of flux was 3 mole ratio of molibudenium. vanadium oxides to lithium oxide ($(MoO_3+V_2O_5)/Li_2O$), flux additives were substituted more less then 0.2 mole% of $K_2O$ or $Na_2O$ to the $Li_2O$ amount. The melting concentration of mixing beryl material was 3~10% content to the flux, that of $Cr_2O_3$ color dopant was 1% to the beryl amount. In the crystal growing apparatus with temperature gradient in the 3 zone furnace which was separated into the block of melt, growth and return, the solution have got to circulate continuously between $1100^{\circ}C$ and $1000^{\circ}C$ in steady state. When thermal fluctuation was treated to during 2 hrs once on a day at 950~$1000^{\circ}C$ in growth zone, the supersaturation solution was maintained, controled and emerald single crystal can be grown large crystal which was prevented from the nucleation of microcrystallite. The preferencial growth direction of hexagonal columnar emerald single crystal was the c(0001) plane of botton side and vertical to the m(1010) plane of post side.

• Journal of Magnetics
• /
• v.7 no.3
• /
• pp.106-114
• /
• 2002

To reduce the grain size and the media noise in a typical CrMo/CoCrPtB longitudinal media, a sputtering process which includes the exposure of oxygen onto the surface of CrW$_x$ (x=0, 25, 50, 75, 100 at.%) and CrTi$_{15}$ seedlayers with the thickness of 0.5 nm have been utilized. The main results are: (1) the media grain size and the media noise are reduced when using CrW$_x$ (x=0, 25, 50 at.%) seedlayers, and not reduced when using CrTils or CrW$_x$ (x=75, 100 at.%) seedlayers, (2) AES and RHEED results suggest that W seedlayer, which has the highest melting point, forms layer-like film with very small and dense island grain, due to its high free surface energy and low mobility. On the other hand, CrW$_{50}$ and Cr seedlayers, which have lower melting point than W seedlayer, form island film, (3) to effectively reduce the media grain size and improve the media signal to noise ratio, it is essential to utilize a very thin Cr-based seedlayer with high affinity for oxygen and which forms island-like structure, such as CrW$_{50}$ seedlayer.

• Bulletin of the Korean Chemical Society
• /
• v.18 no.10
• /
• pp.1050-1052
• /
• 1997

The complexes M(CO)4-1,2-(PPh2)2-1,2-C2B10H10 (M=Cr 2a, Mo 2b, W 2c) have been prepared in good yields from readily available bis-diphenylphosphino-o-carboranyl ligand, closo-1,2-(PPh2)2-1,2-C2B10H10 (1), by direct reaction with Group Ⅵ metal carbonyls. The infrared spectra of the complexes indicate that there is an octahedral disposition of chelate bis-diphenylphosphino-o-carboranyl ligand around the metal atom. The crystal structure of 2a was determined by X-ray diffraction. Complex 2a crystallizes in the monoclinic space group P21/n with cell parameters a = 12.2360(7), b = 17.156(1), c = 16.2040(6) Å, V = 3354.1(3) Å3, and Z =4. Of the reflections measured a total of 2514 unique reflections with F2 > 3σ(F2) was used during subsequent structure refinement. Refinement converged to R1 = 0.066 and R2 = 0.071. Structural studies showed that the chromium atom had a slightly distorted pseudo-octahedral configuration about the metal center with two phosphine groups of o-carborane occupying the equatorial plane cis-orientation to each other. These metal carbonyl complexes are rapidly converted to the corresponding metal carbene complexes, [(CO)3M=C(OCH3)(CH3)]-1,2-(PPh2)2-1,2-C2B10H10 (M= Cr 3a, Mo 3b, W 3c), via alkylation with methyllithium followed by O-methylation with CF3SO3CH3.