• Corrosion Science and Technology
• /
• v.23 no.4
• /
• pp.302-309
• /
• 2024

The purpose of this study was to elucidate effects of a thin (tens to hundreds of nanometers) Ni-flash coating layer on hydrogen embrittlement (HE) and liquid metal embrittlement (LME) in ultra-high-strength electrogalvanized steel with a tensile strength of more than 1 GPa. Various experimental and analytical methods, including thermal desorption spectroscopy, slow strain rate testing, resistance spot welding, X-ray diffraction, and metallographic observation, were employed. Results showed that an increase in Ni target amount for flash coating resulted in a decrease in diffusible hydrogen content during electrogalvanizing, resulting in a significant decrease in HE sensitivity. Moreover, a Ni target amount of more than 1000 mg/m² drastically reduced the occurring frequency and average depth of LME. This reduction could be primarily attributed to formation of Zn-Ni intermetallic phases during the welding process that could inhibit liquefaction of intermetallic phases in the heat-affected zone. This study provides a desirable Ni target amount for Ni-flash coating on ultra-high-strength steels conducted in a continuous galvanizing line or a high-speed batch line to achieve high resistance to both HE and LME.

• Journal of the korean Society of Automotive Engineers
• /
• v.5 no.3
• /
• pp.24-32
• /
• 1983

전기 동저항 제어실험을 통해 다음과 같은 결론을 얻었다. (1) 점용접 과정에서 동 저항이 용접질(용접강도)을 잘 나타내 준다. 1) 동저항 곡선의 peak가 발생하는 시간이 이르면 일반적으로 늦게 나타난 것보다 용접질이 좋다. (단, expulsion이 발생하지 않을 때까지). 2) peak에서의 저항값과 용접시간 끝에서의 저항값 차이가 클수록 일반적으로 용접질이 좋다. (2) 한 동 저항곡선에 다른 동 저항곡선을 맞추려는 제어를 할 때는 다음과 같은 관계가 있다. 1) P-control로는 동저항을 추적하는 효과를 충분히 얻을 수 없고 적분제어기를 추가한 PI-control을 하면 잘 추적한다. 2) 용접질의 관점으로 볼 때 원하는 용접강도를 얻으려고 PI제어를 하면 그 용접 평균강도에 아주 근사한 강도를 얻을 수 있다.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.2
• /
• pp.229-235
• /
• 1989

The influence of monogalvanized layer to fatigue strength of two different mating metal specimens (HS*GA, HS*GAB) of high strength steels(HS) and of monogalvanized steel sheets(GA, GAB) were investigated under tensile-shear repeated load, and hardness test. Some of the results are; (1) The main cause of crack initiation and growth at high load range is plastic bending hinge. (2) In low load range, the cracks initiated near the nugget front where the hardness variation is steep.

• Hip & pelvis
• /
• v.36 no.2
• /
• pp.155-160
• /
• 2024

We report two cases of postoperative total hip arthroplasty periprostehtic fracture of the acetabulum which treated by open reduction with internal fixation without acetabular cup revision. From these cases, we should consider open reduction with internal fixation as the first treatment option in cases where spot welding of the cup to the host bone is observed.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.11 no.1
• /
• pp.53-62
• /
• 1987

High power lasers provide a controllable and precise energy source in surface transformation hardening. A careful control of the process is needed in order that the surface layer of the material reaches the austenizing temperature, but that it does not melt. In order to achieve this the results of theoretical and experimental studies on the laser surface hardening of a medium carbon steel are described. A two-dimensional computer program, which can be used generally for the determination of transient temperature distributions in welding and heat treatment, was established on the basis of the finite element method. For the confirmation of the accuracy of the numerical analysis, a medium carbon steel (SM 45C) of 5mm thickness was heat-treated with a 1kW CW CO$_{2}$ laser machine, while the traverse speed and the distance from the focal point (defocused distance) were varied. Experimental and numerical results showed a similar tendency in correlations between the hardened zone shape and the process parameters. With increasing beam spot diameter the width and depth of the hardened zone increased for relatively small beam spot diameters, but decreased rapidly after reaching the maximum value, while with increasing traverse speed the width and depth of the hardened zone decreased monotonously. Too small beam spot diameters are to be avoided, since the surface melting would lower the surface hardness and produce an uneven surface which may be unacceptable because of the possible requirement for subsequent machining. It could be observed that for a given traverse speed and laser power input there exists a optimal range of the beam spot diameter, which produce a large width of the hardened zone but no melting on the surface.

• Journal of Welding and Joining
• /
• v.35 no.2
• /
• pp.58-62
• /
• 2017

A319 aluminum alloy containing 6.5% Si and 3.5% Cu as major alloying elements has been widely used in machinery parts because of its excellent castability and crack resistance. However it needs more wear resistance to extend its usage to the severe wear environments. It has been known that hyper-eutectic Al-Si alloy having more than 12.6% Si contains pro-eutectic Si particles, which give better wear resistance and lubrication characteristics than hypo-eutectic Al-Si alloy like A319 alloy. In this study, it was tried to clad hyper-eutectic Al-Si alloy on the surface of A319 alloy. In the experiments, Al-36%Si alloy powder was mixed with organic binder to make a fluidic paste. The paste was screen-printed on the A319 alloy surface, melted by pulsed Nd:YAG laser and alloyed with the A319 base alloy. As experimental parameters, the average laser power was changed to 111 W, 202 W and 280 W. With increasing the average laser power, the melting depth was changed to $142{\mu}m$, $205{\mu}m$ and $245{\mu}m$, and the dilution rate to 67.2 %, 72.4 % and 75.7 %, and the Si content in the cladding layer to 16.2 %, 14.6 % and 13.7 %, respectively. The cross-section of the cladding layer showed very fine eutectic microstructure even though it was hyper-eutectic Al-Si alloy. This seems to be due to the rapid solidification of the melted spot by single laser pulse. The average hardness for the three cladding layers was HV175, which was much higher than HV96 of A319 base alloy. From the block-on-roll wear tests, A319 alloy had a wear loss of 5.8 mg, but the three cladding layers had an average wear loss of 3.5 mg, which meant that an increase of 40 % in wear resistance was obtained by laser cladding.

• Transactions of the KSME C: Technology and Education
• /
• v.5 no.2
• /
• pp.89-95
• /
• 2017

LCD robot vertical frame lets a arm assembly with glass substrate move up and down, so it must have high stiffness and strength. We applied new manufacturing process by using design optimization process such as topology and size optimization in order to satisfy the request of high stiffness and light weight. The proposed model should be evaluated for endurance strength. Therefore fatigue assessment for weak point of aluminum welding area of vertical frame studied with hot spot stress approach. And the actual stress measuring from test was compared and evaluated with the dynamic stress calculated from multi-body dynamics considering flexible body.

• Journal of the Institute of Electronics and Information Engineers
• /
• v.49 no.9
• /
• pp.353-361
• /
• 2012

In this paper, we propose a improvement method of vision inspector for T type welding nut using an auto sorting system. We used edge and thread detection with histogram of image which is captured by machine vision camera. We also used a binary morphology operation for a detection of spot. A major problem in this vision inspector is abnormal operation caused by degradation of image acquired. These degradations caused by oil pollution on conveyer belt. For overcome this problem, we introduce a pre-processing using a masked histogram equalization on the image acquired. Histogram equalization is applied on masked region (nut part) for increase contrast. As a result, we can remove features caused by oil pollution on background and reduce a ratio of abnormal operation from 10.0 % to 0.2 %.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.5 no.1
• /
• pp.144-149
• /
• 2001

There are many types of seam tracking methods actually used in industrial spot. Lately, Non-contact sensor technics are mostly used because non-contact sensor has more advantage than contact sensor in many parts. This paper also concerned about fiber sensor a kind of non-contact sensor. X-Y robot and fiber sensor scan the seam tracking to be weld. After scanning, X-Y robot moves the first working point of being scanned and welding starts automatically. It makes an experiment on some types of Seam tracking like straight line tracking, leaned line tracking and curved line tracking to confirm how well the fibers sensor tracks the seam pass to be weld. And the seam pass that had been tracked was welded by inverter $CO_2$ voiding machine.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.20 no.5
• /
• pp.608-619
• /
• 2017

In this paper, the effects of parameters related to the residual stress induced due to laser shock peening process to determine mitigation of the initial tensile residual stresses are discussed, such as the maximum pressure, pressure pulse duration, laser spot size and number of laser shots. In order to estimate the influence of the initial tensile residual stresses, which is generated by welding in 35CD4 50HRC steel alloy, the initial condition option was employed in the finite element code. It is found that $2{\times}HEL$ maximum pressure and a certain range of the pressure pulse duration time can produce maximum mitigation effects near the surface and depth, regardless of the magnitudes of tensile residual stess. But plastically affected depth increase with increasing maximum pressure and pressure pulse duration time. For the laser spot size, maximum compressive residual stresses have almost constant values. But LSP is more effective with increasing the magnitudes of tensile residual stress. For the multiple LSP, magnitudes of compressive residual stresses and plastically affected depths are found to increase with increasing number of laser shots, but the effect is less pronounced for more laser shots. And to conclude, even though the initial tensile residual stresses such as weld residual stress field are existed, LSP is enough to make the surface and depth reinforcement effects.