• 한국결정성장학회지
• /
• 제13권2호
• /
• pp.73-78
• /
• 2003

Tetraethyl orthosilicate (TEOS)로부터 유도된 동결건조 실리카 젤의 기공구조에 미치는 하소온도의 영향이 질소 등온흡착 및 수은압입법에 의하여 조사되었다. 동결건조물은 다소간의 마이크로기공을 함유하고 있었으나 주로 4~6nm 크기의 매크로기공 및 7~20$\mu\textrm{m}$ 크기의 매크로기공으로 구성되어 있었다. 하소온도의 증가에 따른 기공구조변화는 치밀화 정도에 의존하였다.

• 한국세라믹학회지
• /
• 제29권9호
• /
• pp.750-756
• /
• 1992

Reaction bonded si-SiC composites were prepared by silicon infiltration technique at temperature of 1$600^{\circ}C$ for 30 minutes in vaccum atmosphere. The microstructure and mechanical properties of Si-SiC composites were investigated and characterized. UF-15 and SE-10 as SiC powders, phenolic resin and carbon black as carbon source, and metallic silicon powder as molten Si source were used as starting materials. New SiC crystallines nucleatd and grown by reaction of Si and C were detected by TEM and SEM-EDS. The bonding between new and original SiC was found to be strong. But the wetting of SiC by unreacted metallic Si and the rapid grain growth of new SiC decreased density and fracture toughness. Fracture toughness and modulus of rupture of Si-SiC composite were about 3.2 MPa.m1/2 and 480 MPa, respectively.

• 한국세라믹학회지
• /
• 제30권7호
• /
• pp.571-577
• /
• 1993

The effect of $\alpha$-Al2O3 seeding on preparation of zirconia/alumina gel fragment prepared by sol-gel processing was characterized through XRD, SEM, TG/DTA and IR analysis. Aluminum isopropoxide and zirconium butoxide were used as starting materials. $\alpha$-Al2O3 seeding restrained grain growth of alumina and zirconia, and decreased tetragonal to monoclinic phase transformation of zirconia on cooling. Therefore, fine zirconia-toughened alumina composite having the relative sintered density of about 98% of theoretical at 140$0^{\circ}C$ for 2h could be obtained.

• 한국세라믹학회지
• /
• 제38권6호
• /
• pp.537-544
• /
• 2001

뮬라이트, 지르코니아, 뮬라이트/지르코니아 비수성 현탁액의 분산 및 레올로지에 미치는 공정보조제의 영향이 침전밀도, 점도, 입자크기를 측정함으로써 검토되었다. 현탁액의 분산안정성 (높은 침전밀도와 낮은 점도로 특징 된)은 분산제+가소제+결합제를 함유하는 경우에 비하여 분산제 또는 분산제+가소제를 함유하는 경우가 우수하였다. Ball mulling 후의 입자크기분포는 공정보조제의 종류에 거의 영향을 받지 않았다. 결합제를 부가적으로 함유하는 현탁액은 상대적으로 강한 shear thinning 거동을 나타내었다.

• 한국세라믹학회지
• /
• 제23권6호
• /
• pp.71-75
• /
• 1986

The forming reaction processes of magnesium aluminate spinel by a thermal decomposition of sulfate hydrate were studied with DTA, TG. SEM and X-ray powder diffraction methods. The hydrous salt composed of the mixture of the two compounds of $MgSO_4$ $6H_2O$ and ${AL_2}({SO_4})_17H_2O_3$ in which both sulfates were crystalline. On heating the hydrous slat the crystalline magnesium and aluminum sulfate anhydride to amorphous alumina magnesium sulfate anhydride decomposed to amorphous magnesia and these amorphous oxides reacted completely each other to form a spinel at $1000^{\circ}C$ The apparent activation energy of forming reaction of spinel was 36.5 kcal/mole($900^{\circ}C$~$1000^{\circ}C$) The crystallite size of spinel obtained at $1000^{\circ}C$ after 1 h was 380$\AA$.

• 한국세라믹학회지
• /
• 제27권7호
• /
• pp.916-924
• /
• 1990

The preparatin of the fine TiN powders by reduction-nitridation of TiCl3-Al-N2 system was attempted in the temperature range from 350$^{\circ}$to 100$0^{\circ}C$. The formation mechanism and kinetics of TiN were examined, and the resultant TiN powder was characterized by means of XRD, PSA and SEM-EPMA methods. TiN was formed at temperatrue higher than $600^{\circ}C$. As an intermediate phase, AlTi was obtained. The apparent activation energy for the formation of TiN was approximately 4.2kcal/mole(600$^{\circ}$~90$0^{\circ}C$). The crystallite size and lattice constnat of TiN powder obtained in the temperature range from 600$^{\circ}$to 100$0^{\circ}C$ for 2h at the Al/TiCl3 molar ratio of 1.0 were 160~255A and 4.231~4.239A, respectively. According to PSA measurement, the mean particle size ranged from 14.0 to 14.8${\mu}{\textrm}{m}$.

• 한국세라믹학회지
• /
• 제45권10호
• /
• pp.589-593
• /
• 2008

The hydroxyapatite with different amounts of strontium was synthesized with wet chemical technique. The structural, morphological and chemical characterizations for the prepared hydroxyapatite with various strontium amounts were carried out with XRD, SEM, EDS, and FT-IR. Strontium is quantitatively incorporated into hydroxyapatite where its substitution for calcium provokes a well distribution in the EDS mapping and a linear shift of the infrared absorption bands of the hydroxyl and phosphate groups, coherent with the greater ionic radius of strontium.

• 정보학연구
• /
• 제12권4호
• /
• pp.25-32
• /
• 2009

Iris recognition is a biometric technology which can identify a person using the iris pattern. It is important for the iris recognition system to extract the feature which is invariant to changes in iris patterns. Those changes can be occurred by the influence of lights, changes in the size of the pupil, and head tilting. This paper is appropriate for the embedded environment using local gradient histogram embedded system using iris feature extraction methods have implement. The proposed method enables high-speed feature extraction and feature comparison because it requires no additional processing to obtain the rotation invariance, and shows comparable performance to the well-known previous methods.

• 한국세라믹학회지
• /
• 제31권5호
• /
• pp.471-476
• /
• 1994

The influence of TiO2 addition on the sintering and microstructure of magnesia ceramics was studied. An excess amount of TiO2 over the solid solubility limit reacted with magnesia to form Mg2TiO4 compound above 130$0^{\circ}C$. The deviation of lattice parameter of MgO was estimated to be under 0.2% when existence of TiO2 in MgO. The addition of TiO2 markedly promoted the densification of MgO at comparatively low temperature and the sintered density of about 98% of the theorectical was obtained at 150$0^{\circ}C$, 2h. The densification was mainly governed by grain growth of MgO and the effect of Mg2TiO4 existing as a second phase on depression of grain growth of MgO was not exhibited.

• 한국세라믹학회지
• /
• 제40권7호
• /
• pp.667-671
• /
• 2003

테이프 캐스팅법을 이용하여 알루미나/지르콘(반응결합 뮬라이트/지르코니아 유도)을 내부층으로 하고 알루미나/지르코니아 혹은 뮬라이트/지르코니아를 외부층으로 하는 산화물 층상 복합체를 고온가압소결법으로 제조하였다. 나노압입시험법을 이용하여 층상 산화물 복합체의 기계적 성질(경도 및 탄성계수)을 측정하고, SEM을 통하여 복합체의 미세구조를 관찰하였다. 산화물 층상 복합체의 제조를 위한 가열·냉각시 유도된 구성 산화물간의 열팽창 계수의 차이로 인하여 생성된 잔류응력을 하중-변위곡선을 이용하여 확인할 수 있었다.