• The Journal of the Institute of Internet, Broadcasting and Communication
• /
• v.18 no.4
• /
• pp.79-83
• /
• 2018

An accurate method to measure shielding effectiveness(SE) of EMI spray coating film is presented. After high frequency simulating, Circular coaxial standard test fixture is fabricated. A sample of EMI spray coating film was fabricated for insertion into a circular coaxial standard test fixture. The measuring instrument used an Agilent 8722ES vector network analyzer for the SE measurement. The exact SE of copper and silver mixed spray coating sample was measured by the composition of the measuring instrument and the measuring sample. The SE of copper sample was measured at 70 dB and the SE of copper and silver mixed spray coating sample was measured at 60 dB. As a result of the measurement, the reliability of the circular coaxial standard test fixture was confirmed.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.3
• /
• pp.176-185
• /
• 1996

플라즈마 용사된 열벽코팅의 수명을 평가하기 위하여 여러가지 양의 CeO$_2$(16,18,20,22,24 그리고 26 wt.% CeO$_2$)를 포함하는 지르코니아 코팅에 대한 상분석이 행하여 졌다. 플라즈마 용사된 후 16 및 18 wt.% CeO$_2$를 포함하는 지르코니아 코팅에서는 비평형 tetragonal 상 만이 생성되었으나 20-26 wt.% CeO$_2$를 포함하는 지르코니아 코팅에서는 비평형 tetragonal 및 cubic 상의 혼합상이 관찰되었다. 열순환 산화시험 동안에는 비평형 tetragonal 및 cubic 상은 평형 tetragonal 및 cubic 상으로 변태하였다. 평형 tetragonal 상의 일부는 열순환 산화시험의 냉각과정 중에 monoclinic 상으로 변태하였다. 그리고 16 wt.% CeO$_2$를 포함하는 지르코니아 코팅은 다른 조성의 지르코니아 코팅보다 열순환 산화시험 동안 더 많은 monoclinic 상이 생성되었으며 세라믹 코팅 수명이 짧았다.

• Rubber Technology
• /
• v.3 no.1
• /
• pp.62-64
• /
• 2002

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.6
• /
• pp.629-636
• /
• 2014

For surface modification, bulk metallic glass coatings were fabricated using metallic glass powder and a mixture of a self-fluxing alloy or/and hard metal alloys with a heat-resisting property using a high velocity oxy-fuel coating thermal spraying process. Microstructural analyses and mechanical tests were carried out using X-ray diffraction, a scanning electron microscope, an atomic force microscope, a three-dimensional optical profiler, and nanoindenation. As a result, the monolithic metallic glass coating was found to consist of solid particle and lamellae regions that included many pores. Second phase-reinforced composite coatings with a self-fluxing alloy or/and hard metal alloy additives were employed with in-situ $Cr_2Ni_3$ precipitate or/and ex-situ WC particles in an amorphous matrix. The mechanical behaviors of the solid particles and lamella regions showed large hardness and elastic modulus differences. The mechanical properties of the particle regions in the metallic glass composite coatings were superior to those of the lamellae regions in the monolithic metallic glass coatings, but indicated similar trends in matrix region of all the coating layers.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.502-502
• /
• 2011

기존 연구에서는 단일 타겟으로부터 증착된 코팅층 내에 다상으로 이루어진 나노 복합구조를 형성하기 위하여, 나노 합금분말을 방전플라즈마 소결법 등으로 급속 소결하여 타겟을 제조하는 방법이 고려되어 왔다. 반면, 비정질 재료가 우수한 비정질 형성능을 가지는 경우 주조 방법에 의해서도 타겟 제조가 가능하며, 특히 최근 들어 금속 비정질 합금에서 합금의 주요 구성 원소들이 양의 혼합열을 가지는 경우, 액상 또는 과냉각 액상에서 상분리 현상이 발생한다는 것이 밝혀졌다. 이러한 사실에 기초하면, 우수한 비정질 형성능을 가지는 합금 시스템에 합금 구성 원소와 양의 혼합열 관계를 갖는 원소를 첨가함으로써, 비정질 기지 내에 화학적 불균일성을 유도하여 다상으로 이루어진 복합 구조를 형성시키는 것이 가능하다. 본 연구에서는 이러한 합금 설계법을 이용하여, 비정질 기지 내에 존재할 수 있는 불균일성 정도를 합금 조성과 주조 조건의 변화를 통하여 나노 크기에서 원자 크기까지 조절하고, 이에 따른 재료 특성과의 상관관계를 밝히고자 하였다. 이를 위하여 우수한 비정질 형성능을 가지는 Cu-(Zr, Hf)-Al 벌크 비정질 합금계에서 (Zr, Hf)과 (Y, Gd)간의 양의 혼합열 관계에 주목하여 Cu-(Zr, Hf)-(Y, Gd)-Al 벌크 비정질 형성 합금계를 설계하였으며, 이 합금계 내에서 조성과 냉각속도의 조절에 따라 나타나는 불균일성의 정도와 특성변화의 영향을 체계적으로 고찰하였다. 결과로서, Cu-(Zr, Hf)-Al 합금계에서 (Zr, Hf)을 (Y, Gd)으로 15 at.% 이상 치환한 경우, Cu-(Zr, Hf)-rich 와 Cu-(Y, Gd)-rich 비정질상으로 이상분리가 일어났으며, 이렇게 생성된 비정질-비정질 복합재는 응력 하에서 소성 변형을 거의 보이지 않았다. 반면, 5 at.% 이하로 (Zr, Hf)을 (Y, Gd)으로 치환한 경우에는 비정질 기지에 SAXS 혹은 WAXS로 확인 가능한 원자 크기의 불균일성이 나타났으며, 이 경우 비정질 합금의 점성 유동의 변화를 통해 합금의 연신 특성이 향상되었다. 특히, 본 연구에서는 비정질 기지내 불균일 제어를 통한 기계적 특성 향상을 위해서 조성 제어뿐 아니라 동역학적인 요소를 고려한 냉각속도 조절을 통한 원자단위 불균일성의 최적화가 필요함을 규명하였다. 이러한 연구 결과는 분말화 및 소결 과정을 배제하고 제조된 단일 타겟을 통해 코팅층에 다수의 합금원소를 혼합하고 나노/원자 스케일의 복합구조 형성 및 고집적화가 가능한, 타겟 모물질 설계의 새로운 방향을 제시함으로써 다기능성 복합소재 코팅층의 연구에 크게 기여할 것으로 사료된다.

• Journal of the Earthquake Engineering Society of Korea
• /
• v.7 no.2
• /
• pp.59-66
• /
• 2003

A novel application of nano-technology in the field of engineering, called colloidal damper, is investigated. This device is complementary to the hydraulic damper, having a cylinder-piston construction. Particularly for colloidal damper, the hydraulic oil is replacedby a colloidal suspension, which is consisted from a nano-porous matrix with controlled architecture and a lyophobic fluid. In this experimental work, the porous matrix is composed from silica gel, with labyrinth architecture, coated by organo-silicones substances in order to achieve a hydrophobic surface. Water is considered as associated lyophobic fluid. The colloidal damper test rig and the measuring technique of the hysteresis are described. the influence of the hydrophobicity level upon the colloidal damper hysteresis is investigated, for silica gels with similar pores distribution. A certain desired shape of the hysteresis can be achieved by employing mixture of silica gels with different level of hydrophobicity and/or architecture. With these results, it is believed that the proposed damper can be designed and be applied to the desired structure.

• Korean Chemical Engineering Research
• /
• v.54 no.1
• /
• pp.114-119
• /
• 2016

In this study, we tried to add the conductivity to natural polymer like bacterial cellulose (BC) coated with the conductive polymer PEDOT:PEG, graphene and silver nano-wire (AgNW). Sulfuric acid of 10 to 20% was previously mixed with PEDOT:PEG and then the solution was electron spin-coated on the BC membrane. And then, additive coating with graphene and AgNW were done to improve conductivity, which was examined by hall effect. As the result, we confirmed a considerable improvement of conductivity compared to BC-coated film without sulfuric acid treatment as $2.487{\times}10^{10}$ vs $8.093{\times}10^{15}$ ($1/cm^3$), showing higher electron density with $3.25{\times}10^5$ times. Also, we identified that changed particle type to the polymer type by sulfuric acid using SEM analysis. For FT-IR analysis, it was confirmed that S-O radical ($1200cm^{-1}$) increased in the sulfuric acid treatment than non-treated sulfuric acid. As the method used very small amount of PEDOT:PEG, its transparency could be kept, and pre-treatment process of sulfuric acid will be able to simplify the production process.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.205-207
• /
• 2009

아크이온플래이팅 기술과 스퍼터링 기술이 결합된 하이브리드 코팅 시스템을 이용하여 STS 304와 Si 기판에 4성분계 Cr-Al-Mo-N 코팅을 증착하였다. $N_2$/Ar 혼합가스 분위기하에 아크 타겟은 Cr을 사용하였고 스퍼터링 타겟은 Al과 Mo를 사용하였으며 합성된 Cr-Al-Mo-N 코팅은 주로 치환고용된 (Cr, Al, Mo)N으로 구성되었다. 최고 경도값은 Mo 함량이 24.2 at.%일 때 35 GPa을 나타냈으며 마찰계수는 Mo의 함량이 0에서 33.2 at.%로 증가함에 따라 0.9에서 0.48로 감소하였다. 이는 $MoO_3$가 코팅면과 스틸볼 계면에서 고체 윤활제로 작용한 것으로 사료된다. 그러나 Cr-Al-Mo-N 코팅은 MoN의 낮은 내산화온도로 인하여 Cr-Al-N에 비하여 더 낮은 온도에서 산화되었다.

• Proceedings of the KAIS Fall Conference
• /
• 2003.06a
• /
• pp.340-342
• /
• 2003

본 연구의 목표는 난연화를 위한 기존 공법의 단점 보완과 환경 친화적인 난연제를 사용한 비 난연 XLPE 케이블의 난연화 방법과 최적의 난연 코팅액 배합에 있다. 전력용, 통신용 등과 같이 고난연성이 요구되는 경우 기존 컴파운드 방법으로는 난연제를 다량으로 첨가하여 사용하며, base polymer와의 혼합성, 기계적인 물성에도 영향을 끼쳐서는 안되는 등 여러 가지 요구 조건을 만족시켜야 하는 문제점을 가지고 있다. 각 난연 코팅액에 따른 코팅 표면을 고찰한 결과 모든 코팅의 표면은 깨끗하였으며, 코팅층의 두께는 약 10～20 ㎛로 일정하게 코팅이 되었다. Mg(OH)₂/Zinc Borate의 경우는 무게비(wt％)가 1 : 0.5, 1: 0.6에서 난연 효과를 보였으나. 1 : 0.7이상에서는 유연성이 떨어져 코팅층의 균일이 발생하여 연소 테스트시 난연 효과가 떨어지는 현상을 볼 수 있었다. Mg(OH)₂/AF100 S/Zinc Borate의 경우는 AF100 S의 첨가량이 증가할수록 탄화막 형성되어 난연성이 향상되었다.

• Proceedings of the KAIS Fall Conference
• /
• 2009.12a
• /
• pp.659-662
• /
• 2009

본 연구는 건축자재로 널리 사용되는 PVC 바닥상재 표면의 오염성 및 정전기로부터 보호하기 위하여 기존에 사용하는 광경화형 우레탄-아크릴 수지에 내오염/대전성을 향상시킨 광경화형 내오염 코팅액 개발에 관한 것이다. PVC 바닥상재용으로 사용되는 내오염성이 없는 우레탄-아크릴 수지에 4가 암모늄을 사용한 수용성 대전방지제와 아크릴용 대전방지제, 폴리우리탄용 대전방지제를 수지의 양 대비 함량(wt%) 5~20%로 변화하여 첨가한 후 1000rpm에서 30분간 고속 배합하여 수지의 내오염/대전성을 향상시킨 내오염 코팅액을 제조하였다. 제조한 내오염 코팅액은 코팅 층의 두께조절이 가능한 코팅(Bar-coating)을 사용하여 PVC 바닥상재에 코팅 한 후 내오염성, 대전성, 부착력, 코팅두께 등의 코팅 층 표면물성을 평가하였다. 연구결과, 수지에 수용성대전방지제 15%를 혼합하여 제조한 코팅액을 Bar-coater No.12로 코팅한 코팅표면이 전기저항($3.24{\times}10^9{\Omega}/cm^2$), 내오염도(매직 Test, 먼지부착 Test) 및 부착력(100%) 모두 가장 좋은 물성을 보였으며, 전반적으로 함량이 많을수록 전기저항과 오염도에서 우수한 것으로 나타났다. 그러나 대전방지제가 과량으로 들어간 경우 migration 현상이 보이는 것을 알 수 있었다.