It was succeeded in synthesizing the $Al_2O_3$-SiC refractory powders, which is main raw material of AlSiCa, from the domestic Hadong Kaolin. The oxidation reaction of the synthesized $Al_2O_3$-SiC powder was examined. The activation energy for SiC in $Al_2O_3$-SiC powder was calculated to be $\Delta$G=74.86 KJ/mol in air, however the poor sinterability of the powders is thought to be due to the vaporization of SiC in $H_2$ atmosphere. The formation of the whisker-SiC gives the possibility in use for high temperature structural material over high temperature refractory brick.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.4
• /
• pp.190-195
• /
• 2009

Na-tetrasilicic fluorine mica powders were synthesized by skull melting method. The staring materials having chemical composition of $Mg_3(OH)_2Si_4O_{10}:Na_2SiF_6:SiO_2=8.3:24.8:66.9$ mol% were charged into a cold crucible of 13 cm in diameter and 14cm in height and heated by R.F. generator at working frequency of 2.84 MHz. The materials were maintained for 1hr as a molten state and cooled down in the container. In this study, the specific electric resistance of mica was estimated and the columnar and plate shaped mica were synthesized.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.367-367
• /
• 2011

태양전지에서 광흡수층으로 널리 쓰이는 CuInSe2은 전기적, 광학적 특성이 우수하고 20%대의 고효율을 기록하며 큰 관심을 받고 있다. 하지만 증발법 및 스퍼터링 등의 기존 진공, 고온 기반 공정 기술은 원천적인 공정비용 절감이 어렵고, 고가의 희귀원소인 In 등의 원료 활용도가 떨어져 실험실 수준에 머무르고 있다. 최근 공정 비용을 최소화와 원료 활용을 극대화를 통해 고효율 CIGS 박막형 태양전지를 제조하기 위해 비진공 방식의 전구체 박막 코팅 및 열처리를 통한 광흡수층 제조에 관한 연구가 활발히 진행되고 있으며, 본 연구는 doctor-blade coating을 이용하여 전구체 박막을 기판 위에 형성하고 열처리 온도에 따른 박막 물성 변화를 관찰함으로써 박막 형성 메커니즘을 밝히는데 주력하였다. 또한 합성된 박막의 전기적, 광학적 특성을 분석하여 태양전지 응용 가능성을 살펴보았다. 본 연구에서는 SEM, XRD, TGA 분석을 통해 Cu, In, Se 전구체들이 각각 binary phase, 즉, Cu2-xSe 및 In2Se3의 metal chalcogenide을 형성하고, 고온에서 서로 결합하여 CuInSe2로 결정화 되는 현상을 관찰하였다. 또한 합성된 CIS 박막은 근적외선 및 가시광 영역에서 높은 광흡수도를 보였으며, 전기적으로 Mo 전극과 ohmic contact을 이룸으로써 CIGS계 태양전지의 광흡수층으로의 적합성을 나타내었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.665-665
• /
• 2013

박막형 태양전지에서 광흡수층으로 널리 쓰이는 metal chalcogenide 화합물 중, CuInS2(CIS)은 전기적, 광학적 특성이 우수하여 널리 연구되고 있다. CIS계 태양전지 최근 동시 증발법을 이용하여 20.3%의 고효율을 기록한 바 있으나 기존 진공, 고온 기반 공정 기술은 초기 투자 비용이 높고, 고가의 희귀원소인 In 등의 원료 활용도가 떨어져 원가 절감에 있어 한계가 있다. 이에 따라 제조 비용 절감과 원료 사용 효율을 향상시키기 위해 비진공 방식을 이용한 광흡수 층 증착 공정에 관한 연구가 활발히 진행되고 있다. 본 연구에서는 상온, 상압, 저온에서 합성이 가능한 CIS계 광흡수층을 전자 전달 및 빛 포집에 유리한 ZnO 나노구조와 응용함으로써 superstrate 구조의 박막형 태양전지를 구현하고 그 특성을 평가하였다. CIS 박막 태양전지에서 투명창층으로 쓰이는 ZnO 박막을 수열합성법으로 합성된 ZnO 나노로드 어레이로 대체하여 빛 산란 효과를 줄이고, 전하 수집 및 이동 효과를 극대화하였다. 또한 CIS 광흡수층은amine계 용매와 금속염 및 thiourea를 조합하여 저온에서 코팅 후 건조시켜 박막을 제조하였다. 각 요소 박막들의 물성을SEM, XRD, UV-transmittance 분석을 통해 살펴보았으며, 소면적 태양전지 제작을 통해 박막 구조 대비 30배 이상의 광변환효율(최고효율 3.30%)을 기록하였다.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.705-708
• /
• 2008

Diatomite, bentonite and zeolite were used as porous materials for fabricating hygroscopic panels. Moisture adsorption and desorption of porous materials were investigated and hydrothermal method was applied to fabricate panels. Cheolwon diatomite and Pohang zeolite showed excellent characteristics of moisture adsorption and desorption. These characteristics were caused by higher surface area and pore volume of porous materials. Moisture adsorption contents were influenced by surface area and pore volume of panels, and surface area more effected on moisture adsorption. Moisture adsorption content of panel with 10% Pohang zeolite was 180g/m$^2$and that of 10% Cheolwon diatomite was 170g/m$^2$. Moisture desorption content of panel with 10% Pohang zeolite was 105g/m$^2$. Moisture adsorption contents of panel with porous materials were higher than that of panel without porous materials.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.4
• /
• pp.172-178
• /
• 2007

Mica (muscovite) powders were synthesized by hydrothermal method (horizontal turning method). The hydrothermal conditions for the synthesis of mica were prepared by the ratio of $K_2O : Al(OH)_3 : SiO_2$ = 1 : 3 : 3 mol% as the starting materials with KOH (8 mol%) solution as the hydrothermal solvent and reaction temperature at $260^{\circ}C$ for 72hrs. The synthetic powder used for preparation of nano silver coated mica by vertical hydrothermal treatment. The hydrothermal conditions for the treated as nano silver coating were prepared by the synthetic powder as raw materials, triple distilled water ($0.5{\ell}$) solution as the hydrothermal solvent with nano silver sol (1,000 ppm) as the material of nano silver coating and reaction temperature at $160{\sim}260^{\circ}C$ for 72 hrs. After hydrothermal treatment, structural, judgment of nano silver coating and character of nano silver coated mica were examined by XRD, SEM, TEM-EDX and shake plask method.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2000.11a
• /
• pp.141-141
• /
• 2000

한지의 제조에 있어서 부원료인 점질물은 초지시 매우 중요한 역할을 하는데 그 주된 역 할은 다음과 같다. 먼저 점질물은 섬유의 분산을 용이하게 하고 종이의 강도를 증가시키며, 양지와는 달리 박엽지의 제조가 편리하고, 종이의 경도를 증가시키며, 습지의 처리를 용이하 게 하며, 점성으로 인하여 섬유의 침전올 방지하고, 종이의 광택을 향상시키는 둥 매우 중요 한 역할을 한다. 그러나 한지 제조시 이러한 식물성 점제의 미묘한 작용은 현재 대다수의 한지 제조 공장에서 사용하고 있는 합성점제인 PAM이나 PEO 등의 합성 고분자 화합물에 서는 기대하기 어려운 작용이라 여겨진다. 이와 같은 사실에서 본 연구에서는 전통적인 천 연점질물인 황촉규근의 점질물과 합성점제인 PAM 및 우리 나라에서 전혀 사용되지 않고 있는 나무수국 내수피의 점질물을 이용하여 한지를 제조하고 이들 한지의 특성을 SEM 및 A AFM(Atomic Force Microscopy)를 이용하여 분석하였다. 먼저 각각의 점질물로 제조한 한지를 SEM으로 관찰한 결과 닥나무 인피섬유의 최외층에 투명막이 존재하는 사실을 발견할 수 있었다. 이러한 투명막은 닥나무나 뽕나무 인피섬유에 만 존재하고 삼지닥나무나 산닥나무 둥과 같은 기타 인피섬유에는 존재하지 않으므로 한지 의 원료 섬유의 식별에 매우 중요한 요소가 된다. 또한 이러한 투명막은 섬유간 결합을 증 대시켜 한지의 강도 발현에 기여한다고 사료된다. 천연점질물인 황촉규근과 나무수국 점 질물을 이용하여 제조한 한지를 SEM 및 SEM-EDXA를 이용하여 분석한 결과, 황촉규근 점질물로 제조한 한지에는 상당량의 전분입자가 폰재하고 있었으며 나무수국 점질물로 제 조한 한지에는 침상의 수산칼슐 결정이 상당량 존재하고 있는 사실을 발견하였다. 이러한 사실은 한지 제조시 사용된 점질물의 식별에 중요한 요소라 사료된다. 한지의 원료인 닥나무 인피펄프와 침엽수 미표백 크라프트 펄프를 AFM을 이용하여 분석 한 결과, 닥나무 인피펄프의 마이크로피브릴 폭은 5-10nm로 Sw-UKP의 마이크로피브릴 폭 lO-20nm보다 매우 가늘고, 치밀한 세포벽 구조를 하고 있었다. 닥나무 인피펄프의 이러 한 세포벽 구조 및 마이크로피브렬의 형태가 Sw-UKP보다 높은 섬유강도를 나타내는 원인 이라 사료된다. 각각의 점질물을 이용하여 제조한 한지의 섬유표면을 AFM을 이용하여 관 찰한 결과, 원료펄프의 표면관찰에서와는 달리 초지시 사용된 점질물이 섬유표면을 피복하 고 있어 명확한 형태의 마이크로피브렬을 관찰할 수 가 없었다. 따라서 점질물의 이러한 역 할이 한지의 강도 및 보존성 향상에 기여하리라 사료된다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.415-415
• /
• 2012

ICP (RF) 열 플라즈마 분말 합성법은 초고온 열플라즈마(~10,000 K) 속으로 원료물질을 투입한 뒤, 용융, 기화 및 재합성의 과정을 거쳐 초미분(<1 ${\mu}s$)을 합성하는 방법으로 고출력 시스템의 경우 고온/고 엔탈피 열 유동을 통한 고융점 및 저융점 복합물질의 동시 기화에 의한 물질 조성이 제어된 나노 복합체의 대량 합성이 가능할 것으로 기대되고 있다. 본 연구에서는 전북대학교 고온플라즈마 응용연구센터의 60&200 kW의 고출력 ICP (RF) 열 플라즈마 시스템을 이용하여 LTO (Lithium Titanium Oxide)와 IZTO (Indium Zinc Tin Oxide), Barium Borosilicate Glass (K2O-BaO-B2O3-SiO2)의 다성분계 나노 복합체를 합성하였으며, FE-SEM, TEM, XRD, ICP-OES를 이용하여 그 특성을 분석하였다.

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.11a
• /
• pp.633-636
• /
• 2007

국내에서 발생되는 폐기물을 이용하여 가스화에 의해 생산되는 합성가스의 생산 및 활용기술에 대해 고찰하였다. 폐기물 가스화에 의해 생산되는 합성가스의 조성은 CO, $H_2$를 주성분으로 하며 부분산화 조건에 $CO_2$가 함께 생산된다. 생산된 합성가스는 CO $20{\sim}35$%, $H_{2}$ $20{\sim}35$% 정도의 조성으로 나타나며 발생량은 $1,365{\sim}2,125$ $Nm^3/hr$로 나타났다. 이러한 합성가스는 스팀생산, 전력생산 및 DME, SNG, 메탄올, 수소와 같은 고부가가치의 화학원료를 생산할 수 있다.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.05a
• /
• pp.165-168
• /
• 2002

본 연구에서는 칩인덕터 코어 소재로 사용되는 (NiCuZn)-ferrite를 습식합성법을 이용하여 나노크기의 초미세 분말을 합성하였으며, 합성된 (ZiCuZn)-ferrite 의 제조공정 및 전파기적 특성에 관하여 고찰하였다. 조성은 (N $i_{0.4-x}$C $u_{x}$Z $n_{0.6}$)$_{1+w}$ (F $e_2$ $O_4$)$_{1-w}$에서 x의 값을 0.05~0.25 범위로 변화시켰으며, w 값은 0.03으로 고정하였다. 소결은 8$50^{\circ}C$에서 9$50^{\circ}C$의 범위에서 진행하였다. 나노크기의(NiCuZn)-ferrite를 사용함으로서 시약급 원료로 제조된 것보다 소결온도를 낮출 수 있었고, 밀도가 높은 페라이트 소결체를 얻을 수 있었다. 또한 초투자율, 품질계수 등 전자기적 특성이 우수하게 나타났다. 그 밖에 습식합성법으로 합성한 (NiCuZn)-ferrite 의 결정성, 미세구조 등을 XRD, SEM 을 이용하여 고찰하였다.하였다.다.