• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.9
• /
• pp.999-1004
• /
• 2014

In the present paper, the effects of initial crack location on spatial randomness of fatigue crack growth resistance (FCGR) in friction stir welded (FSWed) AA7075-T651 plates were studied. The objective of this study is to characterize the statistical properties of FCGR for three different types of initial crack location (ICL) specimens. In this work, the FCGR coefficients were treated as a spatial random process. It was found that the FCGR coefficients for all initial crack location specimens closely followed a two parameter Weibull distribution. The shape parameter of the Weibull distribution for BM-ICL specimens showed the largest value of 7.50, and that for the WM-ICL specimens showed the smallest value of 2.61. In addition, the autocorrelation functions for all the ICL specimens followed the exponential function.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.22.1-22.1
• /
• 2011

산업의 발달과 더불어 수송기기를 포함한 각종 구조물의 경량화에 따라 피로파괴에 대한 관심이 높아지고 있다. 과거에는 피로균열생성과 피로균열전파를 구분하지 않는 S-N (stress-cycles to failure) 피로 개념을 이용하여 구조재의 피로 거동을 이해하고자 하였다. 그러나 최근에는 모든 구조물에는 균열이 존재한다는 가정에서 시작된 파괴역학(fracture mechanics)에 기초한 피로균열성장 개념을 이용하여 피로에 대한 저항성이 큰 구조재를 개발하고 있으며, 구조물의 피로수명을 예측하고 있다. 본 발표에서는 미세조직, 인장특성, 용접이나 부식 환경 등이 금속의 피로 및 피로균열성장(fatigue crack propagation)에 미치는 영향에 대한 논하고자 한다.

• Journal of Power System Engineering
• /
• v.16 no.4
• /
• pp.66-73
• /
• 2012

본 연구는 횡방향 TIG 용접된 Al6013-T4 알루미늄 합금 용접부의 피로균열전파거동에 미치는 용접후열처리(PWHT)의 영향을 조사하는 것이 주목적이다. 기초적으로 인장시험, 경도 및 미세조직이 조사되었으며, 피로균열전파거동을 고찰하기 위한 피로 시험은 모두 중앙균열인장(CCT) 시험편에 대하여 수행되었다. T82열처리에 있어서 시효시간은 피로균열전파율, 인장강도 및 경도에 대단히 민감함을 나타내었으며, 모재와 열영향부재의 경우가 용접재보다 기계적 성질이 우수하였다. 횡방향 TIG 용접한 Al6013-T4 시험재의 용접후열처리 조건에 따라서 피로균열전파 저항에는 차이가 나타났으며, 본 실험의 조건하에서 24시간 인공시효 PWHT-82 시험편이 피로균열전파 저항이 가장 우수한 결과를 나타내었다.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.11 no.1
• /
• pp.29-36
• /
• 1991

The effects of heat treatment on fatigue crack growth behavior were studied in continuously reinfored, magnesium-based composite (FP/ZE41A). Following an earlier TEM investigation, specimens were thermally aged to modify the interfacial zone between the alumina fibers and mg alloy matrix. The fatigue crack growth experiments were conducted with specimens having the fiber orientation normal to the crack growth direction(longitudinal) and also specimens with the fibers oriented parallel to the crack growth direction(transverse). A comparision of the fatigue crack growth behavior indicates that aged longitudinal specimens are more resistant to fatigue crack growth than as-fabricated longitudinal specimens. Conversely, as-fabricated transverse specimens are more resistant to fatigue crack growth than aged transverse specimens. SEM observations of fiber pullout and ductile tearing on the fatigue fracture surfaces indicate that the aging weakens the strength of the fiber/matrix interface, giving rise to the observed fatigue crack growth behavior.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1997.05b
• /
• pp.36-41
• /
• 1997

액체금속로는 고온 하중 효과(피로, 크립, 크립-피로)를 고려한 내열응력설계가 중요하다. 최근에는 액금로 후보재료로서 종래의 스테인레스강에 질소를 첨가하여 고온강도를 계량한 316LN 스테인레스강이 개발되었다. 본 연구에서는 액체금속로 재료의 가장 지배적인 손상 기구로 인식되고 있는 피로-크립 파손에 대한 설계자료를 확보하기 위해 DCPD(Direct Current Potential Drop)법에 의한 고온피로균열 측정 시스템을 개발하고 316L 및 스테인레스강인 316LN 스테인레스강에 대한 고온 피로균열진전시험을 수행하였다. 본 연구에 의해 개발된 피로균열진전속도 측정 시스템에 의하면 25$\mu\textrm{m}$ 이하의 분해능으로 균열길이를 측정할 수 있다. 한편 316L 스테인레스강에 질소를 적당량 첨가하면 상온에서 $600^{\circ}C$사이의 온도에서 피로균열진전에 대한저항성이 증가하는 것을 확인하였다.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.33 no.2
• /
• pp.187-192
• /
• 2013

Fatigue crack was detected from a temperature change around surface crack using the thermographic technique. Thermal gradient across the crack decreased very much due to thermal resistance of contact surface in the crack. Heat diffusion flow passing through the discontinuity was visualized in temperature by infrared camera to find and locate the crack. A fatigue crack specimen(SM-45C), which was prepared according to KS specification and notched in its center to initiate fatigue crack from the notch tip, was heated by halogen lamp at the end of one side to generate a heat diffusion flow in lateral direction. A abrupt jump in temperature across the fatigue crack was observed in thermographic image, by which the crack could be located and sized from temperature distribution.

• CORROSION AND PROTECTION
• /
• v.12 no.1
• /
• pp.30-38
• /
• 2013

Austenitic stainless steels and Ni-base alloys are widely used as structural materials for major components and piping system in pressurized water reactors (PWRs). These austenitic alloys are known to be susceptible to environmental assisted cracking (EAC), such as environmentally-assisted fatigue (EAF) and primary water stress corrosion cracking (PWSCC) during long-term exposure to PWR primary water environment. In this paper, the current understanding on the phenomena and mechanisms of these EAC are briefly introduced using experimental results and literature review. The mechanisms for EAF and PWSCC for austenitic stainless steels and Ni-base alloys are discussed. Currently, austenitic stainless steels are known to be more susceptible to EAF, while less susceptible to PWSCC than Ni-base alloys. The possible explanations to such behaviors are proposed and discussed in view of the role of hydrogen and internal oxidation.

• Journal of Korean Society of Steel Construction
• /
• v.9 no.4 s.33
• /
• pp.515-521
• /
• 1997

The effects of heat treatment and fiber orientation on tensile strength and fatigue behavior were studied in a continuously reinforced. magnesium-based composite Following an earlier TEM investigation, specimens were thermally aged to modified the interfacial zone between the alumina fibers and the magnesium alloy matrix. From the tensile experimental results, the ultimate tensile strength of the aged specimens were lower than that of the as-fabricated due to weak fiber-matrix interfacial strength with chemical reaction during the thermal processing. The fatigue crack growth experiments were conducted with specimens having the fiber orientation normal to the crack growth direction (longitudinal) and also specimens with the fibers oriented parallel to the crack growth direction(transverse). A comparison of the fatigue crack growth behavior indicates that aged longitudinal specimens are more resistant to fatigue crack growth the as-fabricated longitudinal specimens. Conversely, as-fabricated transverse specimens are more resistant to fatigue crack growth than aged transverse specimens.

• Journal of Korean Society of Steel Construction
• /
• v.8 no.4 s.29
• /
• pp.95-103
• /
• 1996

단순 전단연결 구조를 가진 강철도교의 세로보 단부의 절취부위에서 많은 피로균열이 발견되었으며, 이러한 부위의 피로균열은 피로손상의 전형적인 예이다. 피로균열을 가진 세로보 절취부위의 보강방법을 연구하기 위하여 가로보 및 세로보의 상부 플랜지에 인장판을 부착한 경우와 부착하지 않은 경우로 구분하여 피로실험을 수행하였다. 피로실험에 사용된 하중은 현장에서 측정된 실동응력을 기초하여 빈도해석을 통해 산정하였다. 피로실험 결과, 인장판으로 보강한 모멘트 저항 연결구조상세가 철도교에서 균열성장을 효과적으로 정지시킬 수 있는 것으로 판명되었으며, 피로손상을 가진 절취부위의 보강방법으로 제시될 수 있을 것으로 사료된다.

• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.4 s.97
• /
• pp.13-18
• /
• 1999

섬유강화금속적층재(Fiber Reinforced Metal Laminates. FRMLs)는 고강도금속과 섬유강화복합재료(Fiber Reinforced Composite Materials)를 적층한 새로운 종류의 하이브리드 재료이다. 국산 아라미드 섬유인 헤라크론(Heracron, 코오롱)과 국내 복합재료 제작기술(한국화이바)을 사용하여 섬유강화금속적층재를 제작하고, 이를 HERALL(Heracron Reinforced Aluminum Laminate)이라 명명하였다. HERALL(Heracron Reinforced Aluminum Laminate)의 피로균열성장특성 및 피로균열진전 방해기구를 ARALL(Aramid-fiber Reinforced Aluminum alloy Laminates) 및 Al 2024-T3과 비교해석하였다. HERALL과 ARALL은 균열진전을 저지하는 아라미드 섬유로 인해 뛰어난 피로균열성장특성 및 피로저항성을 보여주었다. 아라미드 섬유의 균열브리드징으로 인한 $K_{max}$의 감소량과 Al 2024-T3의 균열닫힘으로 인한 $K_{max}$의 증가량을 구할 수 있는 응력-COD법을 사용하여 실제로 균열성장에 영향을 준 유효응력확대계수범위를 측정하였다. 균열선단으로부터 균열을 가공하면서 COD 변화량을 측정하여 균열브리징 영역을 구하였다.