• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.1349-1352
• /
• 2005

This paper is to investigate a defect for thermal barrier coating layers by acoustic emission method in 4-point bending test. The two-layer thermal barrier coating is composed of $150\mu{m}\;CoNiCrAlY\;bond\;coating\;by\;vacuum\;plasma\;spray(VPS)\;process\;and\;250\mu{m}\;ZrO_2-8wt%Y_2O_3$ ceramic coating layer by air plasma spray(APS) process on Inconel-718. The specimen prepared by cyclic thermal test(500, 1000, 2000cycle) at $1050^{\circ}C$ The AE monitoring system is composed of PICO type sensor, a wide band pre-amplifier(40dB), PC and AE DSP(16/32 PAC) board. The AE event, amplitude, Cumulative energy and count of coating specimens is evaluated according to cyclic thermal test.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2009.11a
• /
• pp.603-607
• /
• 2009

A Ni/Cr plating process has been developed for applying to inner wall of liquid rocket engine(LRE) thrust chamber. Ni plating conditions were selected through thermal shock test and endurance verification of the plating layers was performed through hot firing test of a subscale thrust chamber with Ni/Cr plating. Test results showed that a crack or separation of the plating layers was not found. Judging from the results, Ni/Cr plating could be applied to LRE thrust chamber as a substitute of air plasma sprayed ceramic coating which is presently being used.

• Journal of Power System Engineering
• /
• v.4 no.4
• /
• pp.48-53
• /
• 2000

This study was aimed at observing the influence of laser irradiation on a $ZrO_2-8%Y_2O_3$ ceramic coating layer fabricated by plasma spraying. The $ZrO_2-8%Y_2O_3$ ceramic powder was plasma sprayed onto SS400 carbon steel substrate and laser irradiated on the coating layer under various conditions of laser power and beam diameters. As to the as-sprayed specimen and laser-treated specimen, a hardness test and a microstructure analysis were performed. Hardness was measured by a microhardness tester; microstructure was observed by an optical microscope and a scanning electron microscope. The result was that the microstructure of the laser-irradiated coating layer was dense; porosities almost disappeared and hardness increased. It was also observed that microcracks occured in the laser-irradiated coating layer.

• Journal of Welding and Joining
• /
• v.14 no.4
• /
• pp.43-52
• /
• 1996

The plasma sprayed Cr$_{2}$C$_{2}$-NiCr coatings are widely used as wear-resistant and corrosion-resistant materials. The mechanical properties of the plasma sprayed Cr$_{2}$C$_{2}$-NiCr coatings were examined in this study. The distribution of the residual stress with the coating thickness was also examined by X-ray diffraction method. The pore in the coatings could be classified into two types ; one is the intrinsic pore originated from the spraying powder, the other is the extrinsic pore formed during spraying. During the tensile adhesion test, the fracture occurred at the interface of top coat and substrate or top coat and bond coat depending on the existence of bond coat. It was found that the compressive residual stress near the interface decreased with the increase of the top coat thickness. The tensile adhesion strength of the coating without bond coat was higher than that with bond coat, because the coating with bond coat has higher horizontal crack density near the interface between bond coat and top coat.

• Journal of the Korean Ceramic Society
• /
• v.39 no.1
• /
• pp.79-85
• /
• 2002

Plasma-sprayed Cr$_2$O$_3$-based coatings containing MoO$_3$were studied to gain a better understanding of the influence of MoO$_3$composition in the coatings on their tribological behaviour. A reciprocal type tribo-tester was employed to examine friction and wear behavior of the specimens at room temperature. The physical characteristics of worn surfaces were investigated by scanning electron microscopy and chemical composition of the coating surfaces was analyzed using a X-ray photoelectron spectrometer. The results showed that friction coefficient of the MoO$_3$-added coatings were lower than those without MoO$_3$addition. However pure Cr$_2$O$_3$coating showed the lowest wear loss at the self-mated test. The larger protecting layers were observed at the worn surface of plasma spray coated specimens with MoO$_3$addition. XPS analysis of the protecting layer indicated that MoO$_3$composition was dominantly formed at the surface. MoO$_3$composition in the protecting layer appears to be more favorable in reducing the friction.

• Journal of Welding and Joining
• /
• v.14 no.6
• /
• pp.109-118
• /
• 1996

Al$_2$O$_3$-TiO$_2$powders of six different compositions were plasma-sprayed on Ti substrate. The spray powders and the spray coated layers were analysed and compared using SEM and X-RD. The elastic properties (specific elastic constant and damping coefficient) of the coated specimens were measured in order to select the optimum composition range of ceramics for use in a speaker diaphragm. A correlation between the microstructure and elastic properties was also investigated. When $Al_2$O$_3$powders with 0- 13% TiO$_2$were plasma sprayed, the coated layers were composed of metastable y-Al$_2$O$_3$with small amount of $\alpha$-Al$_2$O$_3$and the content of $\alpha$-Al$_2$O$_3$was increased with TiO$_2$content. Specific elastic constant was rapidly increased with 2 and 13% TiO$_2$addition to $Al_2$O$_3$. The internal damping was nearly unchanged with TiO$_2$content The specific elastic constant seemed to be dependent on the content of $\alpha$-Al$_2$O$_3$in the coated layer.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2011.11a
• /
• pp.694-696
• /
• 2011

The high enthalpy plasma research center in Chonbuk national university is under construction for four types of plasma equipments. The equipments are 1set of 0.4 MW class enhanced Huels type plasma equipment, 1 set of 2.4 MW class enhanced Huels type plasma quipment, 1 set of 60 kW RF plasma equipment and 1 set of 200 kW RF plasma equipment. 60kW RF plasma system is R&D and pilot scale production equipment of nano powder synthesis and plasma spray coating. 200kW RF plasma system is mass production equipment with high power capacity of nano powder synthesis. 0.4MW plasma system can be applied to the ground test facility for material testing under re-entry conditions for space vehicles.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.298-298
• /
• 2013

플라즈마 전해산화기술은 알루미늄 소재에 대해 기존의 양극 산화막, 전해 경질크롬 도금 및 플라즈마 세라믹 용사기술 등에 의해 구현할 수 없는 고기능성을 부여하여 월등히 우수한 경도, 내부식, 내마모, 전기절연, 열저항, 피로강도 등을 얻을 수 있는 획기적인 기술이다. 또한 최근 환경에 대한 관심이 점차 높아지면서 친환경적 공정과정과 경금속 소재의 제품에 내구성을 향상시킬 필요성이 높아지고 있다. 이러한 요구에 부합하는 플라즈마 전해 산화기술은 알칼리 수용액 중에서 Al, Ti, Mg 등의 표면에 산화 피막을 형성시키는 기술로써 기존의 양극산화(Anodizing)을 대체 할 수 있다. 본 연구에서는 Al6061을 이용하여 플라즈마 전해산화 공정에 사용되는 전해액의 종류 및 농도, 시간의 변화에 따른 산화 피막의 변화를 내전압 측정 및 FE-SEM, EDS, XRD를 통해 분석하였다. 전해액에 sodium hexameta phosphate과 potassium phosphate를 이용하여 phosphate 종류의 변화에 따른 피막 특성의 변화를 연구하였다. 그로인해 phosphate의 종류 및 농도, 시간 변화를 이용하여 플라즈마 전해산화공정의 산화 피막 물성 제어를 할 수 있다.

• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.505-512
• /
• 1998

In this study, two-layer thermal barrier coatings composed of plasma sprayed 0.3mm $ZrO_2(8wt% Y_2o_3)$ ceramic coating layer and O.lmm $NiCrAlCoY_20_3$ bond coating layer on AISI 316 were investigated microstructure of the coating, oxidation of the metallic bond coating and adhesive strength to evaluate the durability of coating layer after cyclic and isothermal test at 90$0^{\circ}C$. And quantitative phase analysis of $ZrO_2(8wt% Y_2o_3)$ ceramic coating was performed as a function of thermal exposure time using XRD technique. The results showed that the amount of m - 2rO, phase in the coating was slightly increased with increasing thermal exposure time at 90$0^{\circ}C$. The c/a ratio of t' - $ZrO_2$ in the as-sprayed coating was 1.0099 and slightly increased to 1.0115 after 100 hours heat treatment. It was believed that $Y_2O_3$ in high yttria tetragonaJ(t') was transformed to low yttria tetragonaJ(t) by $Y_2O_3$ diffusion with increasing thermal exposure time. The adhesive strength was gradually decreased as thermal exposure time increased. After the isothermal test, the failure predominantly occured in ceramic coating layer. On the other hand. the specimens after cyclic thermal test were mostly failed at bond coating/ceramic coating interface. The failure was oeeured by decreasing the bond strength between bond coating and oxide scale which were formed by oxidation of the metallic elements within bond coating and by thermal stress due to thermal expansion mismatches between the oxide scale and ceramic coating.

• Journal of Powder Materials
• /
• v.15 no.6
• /
• pp.477-481
• /
• 2008

Formation and characteristics of spraying powder for BSCCO High-Tc superconductor prepared by plasma spray coating were investigated. The addition of 3% of binder gives the best flowability of the powder. Ball milling for 30h and 35h gives the best flowability of powder in the case of 2001 and 0212, respectively. The withdraw ratio increases upon binder addition from 12 to 27% in the case of 2001 and from 18 to 31% in the case of 0212 for sieving powder of $30-90{\mu}m$ in size. The built-up efficiency for $100{\mu}m$ thickness of spray coating is increased more than 30% by binder addition. The microstructure of the spray coated layers was investigated by XRD and EDS analysis.