• The korean journal of orthodontics
• /
• v.26 no.5 s.58
• /
• pp.497-507
• /
• 1996

The aim of present study in vitro was to evaluate and compare the effects of different washing times of enamels etched with low phosphoric acid solution which makes unsoluble salts and etched but contaminated with saliva on shear bond strength of an orthodontic adhesive to enamel, and to observe the washing effect on the etched enamel surface by scanning electron microscope. All brackets were bonded with Mono-$Lok2^{TM)}$) on the labial surface of extracted human bicuspids after etching with $20w/w\%\;and\;37w/w$ and phosphoric acid solution for 60seconds and then washing for 0,5,10 and 20seconds respectedly. After etching with $37w/w\%$ phosphoric acid solution and contaminating with saliva for 30seconds and then washing for 0,5,20 and 30seconds and re-etching for 10seconds. After 24hours passed in the $37^{\circ}C$ water bath, the shear bond strengths were measured on Universal Test Machine. The data were evaluated and tested by ANOVA and Duncan's multiple range test, and those results were as follows. 1. There was no significant differences between (p>0.05) shear bond strength of bonded brackets with 5, 10, 20seconds washing etched enamel using $37{\%}w/w{\%}$ phosphoric acid solution. 2. The shear bond strength of bonded brackets with $20w/w\%$ phosphoric acid and then washing for 5seconds showed bonded strength durable to occlusal force but its coefficiency score was high and etched surface was not cleaned completely and therefore it was assumed that its clinical application is not applicable. 3. There was no significant differences between (p>0.05) shear bond strengths of bonded brckets with washing for 5seconds etched enamel using $37w/w\%$ phosphoric acid solution and 10,20 seconds washing etched enamel using $20w/w\%$ phosphoric acid solution. 4. The shear bond strength of washing for 5seconds etched enamel which was contaminated with saliva showed sufficient bonded strength durable to occlusal force but its coefficiency score was high and therefore its clinical application was not applicable. 5. After etching, the sample contaminated with saliva showed the sufficient shear bond strength even washing 20seconds without re-etching.

• Journal of Adhesion and Interface
• /
• v.9 no.1
• /
• pp.9-15
• /
• 2008

EVA foam was treated by oxygen plasma under a various treatment time for surface modification. The effect of plasma treatment on surface properties of EVA foam was investigated in terms of FT-IR ATR, XPS, contact angle, and SEM analysis and the adhesion characteristic of the EVA foam was studied in peel strength. As a results, EVA foam treated by plasma led to an elimination of organic compound, an increase of oxygen content, and an increase of surface roughness, resulting in improving the adhesion properties of the EVA foam. As the plasma treatment time increased, the hydrophilicity and physical change of surface of the EVA foam were increased and showed maximum value at 180 s and 420 s, respectively. The maximum adhesion strength appeared at plasma treatment time of 420 s and therefore, in this study the physical change was thought to be a major factor for improving the adhesion of the EVA foam.

• The korean journal of orthodontics
• /
• v.26 no.5 s.58
• /
• pp.569-579
• /
• 1996

• 대한치과보철학회:학술대회논문집
• /
• 1995.12a
• /
• pp.66-66
• /
• 1995

• 대한치과보철학회:학술대회논문집
• /
• 1998.11a
• /
• pp.46-46
• /
• 1998

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.169-169
• /
• 2015

Poly(dimethysiloxane, PDMS)은 그 다양한 사용분야 때문에 지속적으로 연구분야에서 연구주제가 되고 있었다. 본 논문에서는 산소 플라즈마 처리에 의한 PDMS/기판에서의 접착강도를 peel 테스트를 통하여 정량적으로 측정하였다.

• Restorative Dentistry and Endodontics
• /
• v.28 no.4
• /
• pp.314-325
• /
• 2003

이 연구의 목적은 수종 상아질 접착 시스템과 복합 레진 및 resin-modified glass ionomer를 상아질 표면에 접착하여 재료 및 상아질내 위치에 따른 미세전단결합강도를 측정, 비교하는 것이다. 상아질 접착 시스템으로는, 3-step인 Scotchbond Multi-Purpose Plus, 2-step인 Single Bond와 자가 부식형 시스템인 Clearfil SE Bond를, 1-step인 Prompt L-Pop을 사용하였다. 이와 함께 hybrid type의 복합 레진인 Clearfil AP-X와 2250을 사용하였으며 resin-modified glass ionomer로는 Fuji II LC를 사용하였다. 상악 소구치를 치아의 근원심 중앙부를 절단하여 상아질면을 노출시켰다. 5개 실험군으로 분류하고 상아질면을 위치에 따라 치관부의 occlusal $\frac{1}{3}$, middle $\frac{1}{3}$, cervical $\frac{1}{3}$과 치근부로 구분지어 시편을 부착하였다. 미세전단결합강도측정는 Universal testing machine(EZ-test; Shimadzu, Japan)에서 측정하였다. Occlusal 1/3부위에서는 SE가 가장 높은 값을, SM과 SB간에는 유의차가 없었으며, PL, GI순으로, Middle 1/3부위에서는 $SM{\;}{\geq}{\;}SE{\;}{\geq}{\;}SB{\;}{\geq}{\;}PL{\;}{\geq}{\;}GI$순으로, cervical 1/3부위에서는 SM, SE, SB간에 유의차가 없었다. Root dentin에서는 SM이 가장 높은 값을 보였으며 SE, PL, GI간에 유의차가 없었다. SE만이 치관부 상아질에 비해 치근부에서 유의할만한 결합강도의 감소를 나타냈다(p<0.05). GI는 치관부 상아질에서는 다른 군에 비해 유의성 있게 낮은 결합강도를 보였으나 치근부에서는 SE, PL과 유의차가 없었다.

• Journal of the Society of Disaster Information
• /
• v.12 no.1
• /
• pp.54-61
• /
• 2016

The use of advanced composite materials in strengthening and repair of existing structures is increasing rapidly. This paper describes an effectiveness of a bonding of carbon fiber reinforced sheets to corroded steel members for the repair. Three types of surface treatment, what we call cleaning, of corroded plate are chosen as parameters. They are "without cleaning","removal of painting by brushing" and "complete removal of painting". From the experimental study, the following findings are obtained. 1) When the steel plate is subjected to tensile force, carbon fiber sheets adhered to the painted steel gives a higher strength against peeling compared to that of the plate without painting, 2) The grade of surface treatment, or cleaning of the corroded steel plate affects the strengthening effect.

• Journal of Adhesion and Interface
• /
• v.23 no.4
• /
• pp.122-129
• /
• 2022

In this study, the hydrophilicity of the metal fiber is improved by introducing an oxygen-containing functional group to the fiber surface after treatment of the metal fiber using the oxygen plasma treatment time as an experimental variable. For the surface modification of metal fibers, changes in surface properties before and after plasma treatment were observed using SEM and x-ray photoelectron spectroscopy (XPS). In order to observe the effect of the plasma treatment time on the surface of the metal fiber, the change in contact angle of the metal fiber with respect to a polar solvent and a non-polar solvent was measured. After calculating the change in surface free energy using the measured contact angle, the contact angle and the surface free energy for metal fibers before and after oxygen plasma treatment were compared, and the correlation with the adhesion work was also considered. The microdroplet specimens were prepared to investigate the effect of surface changes of these metal fibers on the improvement of shear strength at the interface when combined with other materials and the interfacial shear strength was measured, and the correlation with the adhesion work was also identified. Therefore, the oxygen plasma treatment of the metal fiber results in an increase in the physical surface area on the fiber surface and a change in contact angle and surface energy according to the introduction of the oxygen-containing functional group on the surface. This surface hydrophilization resulted in improving the interfacial shear strength with the polymer resin.

• The korean journal of orthodontics
• /
• v.27 no.3 s.62
• /
• pp.493-502
• /
• 1997

This study was conducted to evaluate the tensile bond strength by bonding the dental bracket with Super-bond after treating the surface of dental Nickel-Chromium alloy with sandblasting, sandblasting & tin-plating, respectively, and tin-plating. 10 pieces of Nickel-Chromium alloys with brackets bonded with Super-bond without their surface treatment were sampled as a control group, 20 pieces of Nickel-Chromium alloy brackets bonded with Super-bond after treating them with sandblasting as group I, 20 pieces of Nickel-Chromium alloys tin-plated and bonded with Super-bond after sandblasting as group II, and then 20 pieces of alloys with brackets bonded with Super-bond after tin-plating as group III. The result of those examination and comparison is summarized as follows: 1. Group I showed the mean tensile bond strength of $14.41{\pm}2.24MPa$ which was highest among 4 groups, followed by group III($13.59{\pm}.51MPa$), group II($12.27{\pm}.45MPa$), and control group($10.50{\pm}1.57MPa$), respectively. However, it was shown that there was no statistically significant difference between group I and III, group III and II, and group II and control group(p>0.05). 2. The main failure pattern of those brackets showed that $70\%$ of the control group had an adhesive failure at the bracket-Superbond interface, and $30\%$ at the Nickel-Chromium alloy-Superbond interface, while other groups did the adhesive failure at the bracket-Superbond interface. 3. When examined under SEM, it was shown that adhesives were mostly attached to the surface of the Nickel-Chromium alloy for all groups while a considerable quantity of adhesives were attached to the bracket base. Then, those samples treated only with sandblasting showed the most even and remarkable roughness of their surface.