• Polymer(Korea)
• /
• v.34 no.3
• /
• pp.247-252
• /
• 2010

This paper investigates the effects of the monomer ratios on the typical properties of polymer-modified mortars that contain methyl methacrylate-based latexes. Basic data are also obtained to develop appropriate latexes for cement modifiers. Polymer-modified mortars that contain methyl methacrylate latexes copolymerized with butyl acrylate or ethyl acrylate are prepared for different polymer-cement ratios. They are then tested to obtain the tensile and tensile adhesive strengthes of polymer-modified mortar with methyl methacrylate-based latexes. From the test results, the tensile strength of MB7 polymer-modified mortar was higher than normal cement mortar by a maximum of 94% with a 20% polymer-cement ratio, which was almost twice higher than normal. The tensile adhesive strength of the MB polymer-modified mortar was higher for higher MMA monomer contents and polymer-cement ratios, and increased up to four times than that of normal cement mortar. The basic properties of the polymer-modified mortars are more affected by the polymer-cement ratio than by the monomer ratio, and are improved over unmodified mortar.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.159-160
• /
• 2022

The purpose of this study is to evaluate the adhesion in flexure depending on the cement type, polymer type, polymer-cement ratio, and silica fume ratio of the polymer-cement composites(PCCs) for crack repair in RC structures to induce optimal mix proportions. The adhesion in flexure of PCCs for crack repair of RC structure has a significant effect on the polymer type and polymer-cement ratio, and the adhesion in flexure is generally improved with mixing of silica fume as a mixture. The adhesion in flexure according to the type of polymer is slightly higher in the order of SAE, EVA, and SBR, and it is relatively high at the polymer-cement ratio of 60% or 80%. In addition, the adhesion in flexure of PCCs with silica fume ratio of 10% or 20% to the cement weight is higher than that without silica fume. In order to improve the adhesion in flexure of PCCs for repairing cracks in RC structures, the optimal mix design is to properly adjust the cement type, polymer type, polymer-cement ratio, and silica fume ratio.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.11a
• /
• pp.181-182
• /
• 2023

This study is a study on the flexural adhesion performance of polymer cement composites(PCCs) repair section according to the crack depth, and the flexural adhesion strength was obtained through a flexural strength test of cement mortar that was filled into cracks and repaired to a certain thickness using PCCs made of ultra high-early strength cement and polymer dispersion of EVA. As a result of the study, the flexural adhesion performance according to the crack width and crack depth was expected to decrease the flexural adhesion strength as the crack depth increased at the crack width 3.0mm, but the crack width 2.0mm and 1.5mm did not show any tendency according to the crack depth. In addition, even in the final destruction, the fact that the cracks and bottoms filled with PCCs were not cut or dropped proves that PCCs have excellent adhesion and rich toughness.

• Journal of the Korea Institute of Building Construction
• /
• v.12 no.3
• /
• pp.275-283
• /
• 2012

Nitrite-type hydrocalumite (calumite) is a material that can adsorb the chloride ions ($Cl^-$)that cause the corrosion of reinforcing bars and liberate the nitrite ions ($NO_2{^-}$) that inhibit corrosion in reinforced concrete, and can provide a self-corrosion inhibition function to the reinforced concrete. In this study, VA/E/MMA-modified mortars with calumite were prepared with various calumite contents and polymer binder-ratios, and tested for corrosion inhibition, chloride ion penetration, carbonation and drying shrinkage. As a result, regardless of polymer-binder ratio, the replacement of ordinary Portland cement with hydrocalumite has a marked effect on the corrosion inhibiting property of the polymer-modified mortars. However, chloride ion penetration and carbonation depths are somewhat increased with higher calumite content, but can be remarkably decreased depending on the polymer-binder ratios. The 28-d drying shrinkage shows a tendency to increase with the polymer-binder ratio and calumite content. VA/E/MMA-Modified mortars with 10 % calumite did not satisfy KS requirements. Accordingly, a calumite content of 5 % is recommended for the VA/E/MMA-modified mortars with calumite.

• Magazine of the Korea Concrete Institute
• /
• v.4 no.1
• /
• pp.107-118
• /
• 1992

In order to examine the mechanical properties of carbon fiber reinforced cement composites with silica powder PAN - based carbon fiber and Pitch- based carbon fiber, and polymer impregnators experimental studies on CFRC impregnated in polymer were carried out. The effects of types, length, and content~i of carbon fibers and matrices of fresh and hardened CFRC impregnated in polymer were examined. The test results show that compressive, tensile, and flexural strength of CFRC impregnated in polymer were much more iriCreased than those of air cured and autodaved CFIIC CFRC impregnated in polymer was also considerably effective in improving toughness, freeze thaw resistance, loss of shrinkage, and creep resist ance, compared with air cured and autoclaved CFRC.

• Composites Research
• /
• v.12 no.3
• /
• pp.84-90
• /
• 1999

High alumina cement(HAC) and polyvinyl alcohol(PVA) based macro-defect-free(MDF) cement composites were reinforced using short carbon fibers, 3mm in length, 1-4% in weight fraction and insoluble polymers such as polyurethane, epoxy, phenol resin, in order to increase mechanical properties and water stability. The specimens were manufactured by the low heat-press(warmpress) method. In addition, the interface and the cross-linking reaction of cement and polymers was also studied by the SEM and TEM. Flexural strength of HAC/PVA based MDF cementitious composites was proportionally decreased with increasing fiber contents due to the undensified structure around fibers. The flexural strength of insoluble polymer added specimen was decreased with increasing fiber contents, while water stability was dramatically improved. Epoxy resin added specimen showed the highest strength with increasing fiber contents, compared with other specimens. The water stability of fiber content 4% added specimen immersed in water presented about 95%, 87% at 3 and 7 days immersed in water, respectively. The interfacial adhesive strength of fiber-matrix was very much improved due to cross linking reaction of polymer and metal ions of cement. Tensile strength of insoluble polymers added composites as linearly increased with increasing the fiber contents. The epoxy resin added specimen also showed highest tensile strength. The 4% fiber added specimen presented 30~80% higher strength than controlled specimen.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.1
• /
• pp.15-22
• /
• 2017

This study focuses on the investigation of bond strength of magnesium potassium phosphate cement mortar(MKPC) according to moisture condition of substrate. Tensile bond test, shear bond test and interfacial bond test are adopted for evaluating the adhesion characteristics of MKPC to conventional cement mortar substrate. The main experimental variables are test methods and moisture levels of substrate. Because the moisture condition of the substrate may be critical to achieving bond, optimum moisture condition for a conventional concrete substrate has evaluated in this study. The results are as follows ; The effects of moisture condition at substrate into the bonding of MKPC are less different than polymer cement mortar and epoxy mortar. But the saturated and surface dry condition is the most appropriate moisture level among the considered, followed by saturated condition and wet condition. Thus, an adequate moisture level of substrate for MKPC is essential for good bond strength.

• Polymer(Korea)
• /
• v.29 no.4
• /
• pp.350-356
• /
• 2005

Poly(methyl methauylate)/montmorillonite nanocomposites were incorporated into acrylic bone cement in order to improve the mechanical properties and reduce the exotherm of acrylic bone cement. The nanocomposites were prepared using a suspension polymerization and characterized by scanning electron microscopy, X-ray diffraction, trans-mission electron microscopy, gel permeation chromatography, particle size analyzer and electron dispersive spectroscopy. The acrylic bone cements with poly (methyl methacrylate)/nanocomposite s were prepared and their thermal and mechanical properties were characterized. The prepared polymeric beads were composed of polymer-intercalated nanocomposites with partially exfoliated MMT layers, and the mean diameter of them was $50\~60$ fm with the spherical shape. The maximum setting temperature of the acrylic bone cements decreased from 98 to $81\~87^{circ}C$. The mechanical strengths and moduli of the acrylic bone cement with 0.1 $wt\%$ MMT were increased. compared to that without MMT. However, the mechanical properties were generally decreased with increasing incorporated MMT amounts. It is presumably due to the bubbles in nanocomposite beads generated during polymerization.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.5
• /
• pp.20-29
• /
• 2022

In this study, in order to improve the durability of the cement composite printed with the ME type 3D printer, PDMS, sodium silicate, and a surface hardener were employed. Post-treatment was performed on 3D-printed cement composite by coating after immersion, and the degree of improvement in durability was evaluated. As a result, in all evaluations, the durability performances of the post-processed specimens were improved compared to those of the plain specimens. Water absorption resistance, chloride penetration resistance, and carbonation resistance of the PDMS treated specimens were improved by 36.3 %, 77.1 %, and 50.4 % when compared to plain specimens. Freeze-thaw resistance of the specimens treated with sodium silicate was found to be the most excellent, with an average enhancement of 47.5% compared to plain specimens. It was found that PDMS was the most efficient post-treatment materials for 3D-printed cement composite. However, as suggested in this study, the post-treatment method by coating after immersion may not be applicable to cement composite structures printed with a 3D printer in field. Therefore, a follow-up study needs to be preformed on the durability enhancing materials suitable for 3D printing.

• Journal of the Korea Institute of Building Construction
• /
• v.4 no.3
• /
• pp.93-100
• /
• 2004

In recent years, it has widely been studied on the light-weight composites for the purpose of the large space and thermal insulation of building structures. The purpose of this study is to evaluate the properties of light-weight composites made by binders as cement, resin and polymer cement slurry. The concrete composites are prepared with various conditions such as polymer-cement ratio, void-filling ratio, type of resin, filler content and light-weight aggregate content, tested for thermal conductivity. From the test results, the thermal conductivity of concrete composites with the binder of cement tends to decrease with increasing polymer-cement ratio, and to increase with increasing void-filling ratio. The thermal conductivity of concrete composites with the binder of resin are markedly affected by the light-weight aggregate content, type of resin and filler content. The composites made by polymer-modified concrete and polymer cement slurry have a good thermal insulation property. From the this study, we can recommend the proper mix proportions for thermal insulation Panel or concrete. Expecially. the thermal conductivity of concrete composites made by polyurethane resin is almost the same as that of the conventional expanded polystyrene resin.