• Polymer(Korea)
• /
• v.29 no.2
• /
• pp.177-182
• /
• 2005

Montmorillonite (MMT) modified with siloxane diamine was reacted with a reactant obtained from 4,4'-diphenyl methane diisocyanate (MDI) and polyester type polyol, $Nippollan4010(\bar{M}_n2000)$. Finally, polyurethane (PU)/MMT composites were prepared by using 1,4-butane diol as a chain extender in $25\;wt\%$ solution of N,N-dimethyl acetamide (DMAc). It was expected that these nanocomposites had superior exfoliation property to that of MMT dispersed polyurethanes produced by simple mixing due to insertion of siloxane main chain to the silicate interlayer of MMT. Extent of reaction and formation of final products were analysed by using FT-IR spectroscopy. Dispersion into the PU and intercalation of MMT were identified by applying X-ray diffraction (XRD) and transmission electron microscopy (TEM). Tensile data were acquired by universal test machine (UTM). Thermal stability and variation of surface energy were characterized by thermal gravimetric analysis (TGA) method and measurement of contact angle on the synthesized composites, respectively. As the results the organo-MMT modified with siloxane diamine in the PU composites has an intercalated structure relatively well-expanded rather than a completely exfoliated structure. The tensile strengths and the moduli for the PU/organo-MMT composites were drastically enhanced in comparison to those of $PU/Na^+-MMT$ composites.

• Polymer(Korea)
• /
• v.31 no.6
• /
• pp.518-525
• /
• 2007

The thermomechanical properties and morphologies of nanocomposite fibers of poly(ethylene terephthalate)(PET) incorporating thermally stable organoclays are compared. Dodecyltriphenyl-phosphonium-mica($C_{12}PPh-Mica$) and 1-hexadecane benzimidazole-mica ($C_{16}BIMD-Mica$) were used as reinforcing fillers in the fabrication of PET hybrid fibers. Dispersions of organoclays with PET were studied by using the in-situ polymerization method at various organoclay contents to produce nano-scale composites. The thermo-mechanical properties and morphologies of the PET hybrid fibers were determined using differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), wide angle X-ray diffraction (XRD), electron microscopy (SEM and TEM), and a universal tensile machine (UTM). Transmission electron microscopy (TEM) micrographs show that some of the clay layers are dispersed homogeneously within the polymer matrix on the nano-scale, although some clay particles are agglomerated. We also found that the addition of only a small amount of organoclay is enough to improve the thermal stabilities and mechanical properties of the PET nanocomposite fibers. Even polymers with low organoclay content (<5 wt%) were found to exhibit much higher thermo-mechanical values than pure PET fibers.

• Polymer(Korea)
• /
• v.29 no.4
• /
• pp.350-356
• /
• 2005

Poly(methyl methauylate)/montmorillonite nanocomposites were incorporated into acrylic bone cement in order to improve the mechanical properties and reduce the exotherm of acrylic bone cement. The nanocomposites were prepared using a suspension polymerization and characterized by scanning electron microscopy, X-ray diffraction, trans-mission electron microscopy, gel permeation chromatography, particle size analyzer and electron dispersive spectroscopy. The acrylic bone cements with poly (methyl methacrylate)/nanocomposite s were prepared and their thermal and mechanical properties were characterized. The prepared polymeric beads were composed of polymer-intercalated nanocomposites with partially exfoliated MMT layers, and the mean diameter of them was $50\~60$ fm with the spherical shape. The maximum setting temperature of the acrylic bone cements decreased from 98 to $81\~87^{circ}C$. The mechanical strengths and moduli of the acrylic bone cement with 0.1 $wt\%$ MMT were increased. compared to that without MMT. However, the mechanical properties were generally decreased with increasing incorporated MMT amounts. It is presumably due to the bubbles in nanocomposite beads generated during polymerization.

• Polymer(Korea)
• /
• v.31 no.2
• /
• pp.160-167
• /
• 2007

This paper proposes a model for the solutions predicting the coefficient of thermal expansion of composites including fiber-like shaped$(a_1>a_2=a_3)$ and disk-like shaped$(a_1=a_2>a_3)$ inclusions like two dimensional geometries, which was analyzed by one axis and a single aspect ratio, $(\rho_\alpha=a_1/a_3)$. The analysis follows the procedure developed for elastic moduli by using the Lee and Paul's approach. The effects of the aspect ratio on the coefficient of thermal expansion of composites containing aligned isotropic inclusions are examined. This model should be limited to analyze the composites with unidirectionally aligned inclusions and with complete binding to each other of both matrix and inclusions having homogeneous properties. The longitudinal coefficients of thermal expansion $\alpha_{11}$ decrease and approach the coefficient of thermal expansion of filler, as the aspect ratios increase. However, the transverse coefficients of thermal expansion $\alpha_{33}$ increase or decrease with the aspect ratios.

• Journal of the Korea Institute of Building Construction
• /
• v.4 no.3
• /
• pp.93-100
• /
• 2004

In recent years, it has widely been studied on the light-weight composites for the purpose of the large space and thermal insulation of building structures. The purpose of this study is to evaluate the properties of light-weight composites made by binders as cement, resin and polymer cement slurry. The concrete composites are prepared with various conditions such as polymer-cement ratio, void-filling ratio, type of resin, filler content and light-weight aggregate content, tested for thermal conductivity. From the test results, the thermal conductivity of concrete composites with the binder of cement tends to decrease with increasing polymer-cement ratio, and to increase with increasing void-filling ratio. The thermal conductivity of concrete composites with the binder of resin are markedly affected by the light-weight aggregate content, type of resin and filler content. The composites made by polymer-modified concrete and polymer cement slurry have a good thermal insulation property. From the this study, we can recommend the proper mix proportions for thermal insulation Panel or concrete. Expecially. the thermal conductivity of concrete composites made by polyurethane resin is almost the same as that of the conventional expanded polystyrene resin.

• Polymer(Korea)
• /
• v.33 no.4
• /
• pp.377-383
• /
• 2009

Ionic polymer-metal composite (IPMC) actuator generates bending actuation via ion/water flux to the cathode side under an electric field. Polyelectrolytes in IPMC should possess high water-retention capability, proton conductivity, and Young's modulus. In this study. for endowing IPMCs with these properties, Nafion-alumina composite membranes containing $\alpha$- or $\gamma$-aluminas of $4{\sim}8$ wt% were prepared. Mechanical moduli of Nafion-alumina composite membranes were $7{\sim}3$ MPa higher than that of Nafion, with the slight decrease in proton conductivity. At DC 3 V. the actuation performance of the Nafion-$\alpha$-alumina (8 wt%)-IPMC was superior to that of the typical Nafion-IPMC. exhibiting 2.7 times the displacement with an enhanced blocking force. The enhanced actuation performance with the Nafion-$\alpha$-alumina composite membranes was attributed to the higher proton conductivity, the elevated ion/water flux, and the lower interfacial electric resistance of platinum electrodes and membrane, compared with those containing $\gamma$-alumina.

• Journal of Platform Technology
• /
• v.6 no.4
• /
• pp.59-68
• /
• 2018

The objective of this study is to develop an embedded antenna structure with NFC and WPC composite functions. By selecting stable materials, the optimal component ratio of the polymer sheet was determined. The low cost embedded winding method compared to the existing FPCB was devised. During the winding process, characterization and process technology were developed. We also fabricated a ferrite mold to process the WPC grooves and developed the process technology for optimizing the WPC antenna. The following conclusions were obtained. (1) Optimum composition ratio was derived as Fe 87.5%, Si 7%, Al 5.5% and selected as the final material. (2) Optimal sheet conditions were derived from the experimental evaluation method and the experimental design method through the combination test of the optimized sheet and the conventional mass production FPCB. (3) According to coil diameter and inner diameter, Q value fluctuation, resistance value and efficiency fluctuation are obtained. Therefore, the most suitable coil condition is selected and Rx matching is performed. (4) The EMV load modulation test and the cognitive distance test of the polymer sheet and the ferrite sheet showed that the recognition distance of the polymer sheet at 1k and 4K was 32-33 mm and the recognition distance of the ferrite sheet at the same condition was 30-31 mm.

• Polymer(Korea)
• /
• v.27 no.4
• /
• pp.377-384
• /
• 2003

High impact polystyrene/organically modified layered silicate (HIPS/OLS) nanocomposites by in situ polymerization were synthesized to investigate the effect of clay on the particle size and properties of rubber. In the OLS, the montmorillonite having benzyl group showed best dispersion in polystyrene phase. With the addition of clay, the intercalated peak from XRB was confirmed, but the peak gradually shifted to lower angle as rubber concentration increased. Thus, it is speculated that the organoclay disperses better in rubber phase than in polystyrene phase. The average rubber particle size increased and the particle size distribution widened as the amount of clay increased, which may be caused by the increase of the viscosity ratio of rubber to polystyrene phases and the unstable dispersion. The materials having clay showed improved thermal properties from thermogravimetric analysis. Rheological properties such as complex viscosity and storage modulus increased as the amount of clay increased.

• Polymer(Korea)
• /
• v.25 no.5
• /
• pp.691-698
• /
• 2001

Nanocomposites based on epoxy acid nanoclay were prepared employing organically modified mica type silicate (OMTS), diglycidyl ether of bisphenol A (DGEBA) type epoxy. curing agent (dicyandiamide; DICY), and catalyst (benzyl dimethyl amine; BDMA). Both melt mixing and solution mixing were und for the sample preparation and structural developments with curing reaction were analyzed using X-ray diffractometer (XRD) and small angle X-ray scattering (SAXS). Because of the different curing rate between extra-gallery and intra-gallery reactions of epoxy mixtures, only intercalated structure was observed for the sample prepared by melt mixing while fully exfoliated structure was observed for the sample prepared by solution mixing. Mechanical properties of exfoliated epoxy nanocomposite were investigated using a dynamic mechanical analyzer (DMA). The dynamic storage modulus of the nanocomposite in both glass and rubbery plateau regions were increased with increasing OMTS contents, but glass transition temperatures ($T_g$) remained unchanged. Thermal properties of epoxy nanocomposite were investigated using thermogravimetric (TGA) and limit oxygen index (LOI) methods. Thermal decomposition onset points and LOI values were increased with increasing OMTS contents due to barrier effects of OMTS sheets.

• Polymer(Korea)
• /
• v.31 no.6
• /
• pp.474-478
• /
• 2007

Polymer substrate materials with low dielectric loss were obtained by fabricating the composite using dicyclopentadienyl bisphenol cyanate ester oligomer and polyphenylene ether (PPE). From the analysis of the curing reaction of oligomer and catalyst, it was observed that the optimum amount of catalyst was 0.02 phr of Zn content. It was applied to the fabrication of polymer composite. By changing oligomer/PPE weight ratio, the peel strength and the gel content of the fabricated composites were measured, and then, the dielectric constant and the dissipation factor were measured in the GHz frequency range. The amount of PPE affected the peel strength and the dielectric properties of composites. However, the amount of catalyst did not affect them at all. Resulting from all experiments, we obtained polymer composite laminates haying the peel strength of above 1 kN/m and the low dissipation factor of 0.004 at 1 GHz.