• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.1
• /
• pp.101-110
• /
• 2014

Expansion agent is a very effective admixture for prevention of cracking due to autogenous/drying shrinkage and this can induce internal chemical prestress to embedded reinforcement. In this paper, tension-softening and hardening in cement mortar with steel and CSA expansion agent are experimentally evaluated. Cement mortar with steel reinforcement is prepared and tensile strength test is performed for evaluation of cracking and tensile behavior. In spite of slightly reduced strength and elasticity in CSA mortar, significantly increased tension-hardening behavior is evaluated in CSA mortar with induced chemical prestress. Furthermore previous tension softening models are compared with the test results and improvement are proposed.

• The Journal of Engineering Research
• /
• v.6 no.2
• /
• pp.141-151
• /
• 2004

The physical properties of gold investment materials are depending on it's thermal expansion coefficients, compressive strength, and particles size distributions. Normally the gold investment materials are consisted of cristobalite, quartz and plaster. Since the thermal expansion coefficient of cristobalite and quartz are $2.6\times10^{-6}/^\circC$, $2.32\times10^{-6}/^\circC$, respectively, the composition ratio of each components influence the thermal and clinical properties of gold investment materials. Recently are imported from overseas and the commercial market is expected to expand. Thus it is necessary to develop the optimum strength and compressive strength of gold investment materials which the an homogeneous size distribution and thermal expansion coefficients. Therefore two different experiments has been done. Firstly the homogeneous cristobalite and quartz are made by pulverizing milling. Secondly the compressive strength and thermal expansion coefficients are analysed by the composition ratio of cristobalite and quartz. As a results of experiments, homogeneous distribution of cristobalite and quartz are observed by pulverizing and milling. The optimum compressive strength was obtained at the ratio of 45:25 cristobalite, quartz respectively.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.1
• /
• pp.19-29
• /
• 2002

The purpose of this study was to compare the polymerization shrinkage and the compressive strength of composite and compomer cured with two different light sources ; conventional halogen-light curing unit and recently-developed plasma arc curing unit. The 'strain gauge method' was used for determination of polymerization shrinkage and the compressive strength was measured by universal testing machine. The results of the present study can be summarized as follows: 1. Filling materials in polyethylene molds showed the initial expansion in the early phase of polymerization. This was followed by the rapid contraction in volume during the first 60 seconds and gradually diminished as curing process continued. 2. The polymerization shrinkage in tooth samples was generally lower than in the mold samples. 3. The generally lower amount of linear polymerization shrinkage was observed in compomer and plasma arc curing unit group when compared to composite and conventional curing unit. 4. The higher compressive strength values was found in composite groups regardless curing methods. The results of this study strongly support the application of plasma arc system and fluoride-containing compomer in the field of clinical pediatric dentistry claiming its effectiveness in curing the esthetic dental materials and the anticariogenic capacity.

• Resources Recycling
• /
• v.25 no.6
• /
• pp.73-81
• /
• 2016

Geopolymers produced from aluminosilicate materials such as metakaolin and coal ash react with alkali activators and show higher fire resistance than portland cement, due to amorphous inorganic polymer. The percentage of thermal shrinkage of geopolymers ranges from less than 0.5 % to about 3 % until $600^{\circ}C$, and reaches about 5 ~ 7 % before melting. In this study, geopolymers paste having Si/Al = 1.5 and being mixed with carbon nanofibers, silicon carbide, pyrex glass, and vermiculite, and ISO sand were studied in order to understand the compressive strength and the effects of thermal shrinkage of geopolymers. The compressive strength of geopolymers mixed by carbon nanofibers, silicon carbide, pyrex glass, or vermiculite was similar in the range from 35 to 40 MPa. The average compressive strength of a geopolymers mixed with 30 wt.% of ISO sand was lowest of 28 MPa. Thermal shrinkage of geopolymers mixed with ISO sand decreased to about 25 % of paste. This is because the aggregate particles expanded on firing and to compensate the shrinkage of paste. The densification of the geopolymer matrix and the increase of porosity by sintering at $900^{\circ}C$ were observed regardless of fillers.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.4
• /
• pp.483-488
• /
• 2016

The present study proposes an economical embedded ring-sensor that can measure a strain behavior of cement paste and mortar in early age. Using the proposed ring-sensor, the experimental method is proposed that can measure the setting time of the cement paste and mortar conveniently. The experimental study has been conducted using the mixtures of which W/C are 0.30, 0.35, 0.40, and 0.45. From the test result, the setting times measured by convectional test methods such as vicat method and penetration resistance method are compared with the setting time proposed by this study. The result reveals that the proposed ring-sensor can effectively measure the early age behavior so that can evaluate the time when the contraction starts. In addition, the contraction starting time can be regarded as a rational setting time, which is similar to the initial setting of convectional test methods.

• Polymer(Korea)
• /
• v.37 no.6
• /
• pp.711-716
• /
• 2013

The effect of chain orientation and relaxation on the characteristics of poly(ethylene naphthalate) (PEN) flexible substrate has been studied. It was found that the coefficient of thermal expansion (CTE) of PEN under $100^{\circ}C$ decreased as low as $20ppm/^{\circ}C$ due to the lowering of chain mobility by chain orientation. The thermal shrinkage was found to appear near glass transition temperature because of chain relaxation. It could be minimized by thermal annealing but CTE increased again up to $70ppm/^{\circ}C$ which was 65% of intrinsic CTE of PEN. Unstrained thermal annealing made possible to avoid the thermal shrinkage with maintaining low CTE obtained by chain orientation. Chain orientation did not affect the optical transmittance; however, thermal annealing caused the decrease of optical transmittance up to 5%. This was understood by the minor crystallization due to the thermal annealing near glass transition temperature.

• Journal of the Korean GEO-environmental Society
• /
• v.22 no.10
• /
• pp.21-29
• /
• 2021

Most concrete gravity-type dams in and out of the country were constructed by column method to control cracks caused by concrete hydration heat generated during construction, resulting in a certain level of leakage after impoundment through various causes, such as contraction joints and construction joints. However, due to the characteristics of concrete structures that shrink and expand according to temperature, concrete dams have vertical joints and drains to allow penetration. PVC waterproof shows excellent effects in completion of the dam, which however increases the possibility of interfacial failure due to different thermal expansion. Other causes of penetration may include problems with quality control during installation, generation of cracks due to heat of hydration of concrete, waterproofing methods, etc. In the case of Bohyunsan Dam in Yeongcheon, North Gyeongsang Province, the amount of drainage in the gallery was checked and underwater, and it was confirmed that there are many penetrations from drainage holes connected to vertical joints, and that some of the PVC waterproofs are not fully operated. As a new method to prevent penetration through vertical joints, D.S.I.M. (Dam Sealing Innovation Method) developed by World E&C was applied to Bohyunsan Dam and checked the amount of drainage in the gallery. As a result of first testing three most leaking vertical joints, the drain in the gallery was reduced by 87% on the average and then applied to the remaining 13 locations, which showed a 83% reduction effect based on the total drain in the gallery. Summing up these results, it was found that D.S.I.M. preventing water leakage from the upstream face is a valid construction method to reduce the water see-through and penetration quantity seen in downstream faces of concrete dams. If D.S.I.M. is applied to other concrete dams at domestic and abroad, it is expected that it will be very effective to prevent water leakage through vertical joints that are visible from downstream faces.

• Journal of the Korea Concrete Institute
• /
• v.25 no.4
• /
• pp.371-379
• /
• 2013

This paper investigates the cracking and tension-stiffening behavior of 100 MPa shrinkage-compensated strain-hardening cement composite (SHCC) and conventional concrete tie elements in monotonic and cyclic tension. Strain and surface crack formation of tension ties were monitored with two strain displacement transducers and a photo microscope with a lens of magnification 50 times. Three different cement composites such as conventional concrete, shrinkage-compensated SHCC, and normal SHCC were used in the tie specimens to investigate the influence of the cement composite type on the tension stiffening and cracking behavior. Test results indicated that initial shrinkage of the ultra high-strength cement composites is greatly reduced as the 10% replacement of cement by the shrinkage-compensating admixture based on calcium sulfo-aluminate (CSA). The test results on the SHCC tension ties showed that the first cracking load decreases proportionally to the initial shrinkage strain. Reinforced ultra high-strength SHCC ties with the initial shrinkage compensation exhibited improved tension stiffening and smaller crack spacings, i.e. the reduction in crack width. Cyclic loading did not have a significant effect on tension stiffening and cracking behavior of tension ties with normal concrete and SHCC materials.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.39 no.6
• /
• pp.99-110
• /
• 1997

The study was conducted in order to investigate the basic geotechnical properties of sand-bentonite mixtures with the various bentonite contents. The results obtained are as follows : 1. Optimum moisture content of sand-bentonite mixtures was approximately 17.10~18.52% corresponding to the maximum dry density of 1.58~1 .64gf/$cm^3$. As the bentonite contents and curing peroid increased, both the maximum dry density and optimum moisture content of sand-bentonite mixtures increased. 2. The unconfined compressive strength of sand-bentonite mixtures increased as the increase of bentonite content, but it did not change along the curing period. 3. The sand-bentonite mixtures ruptured at 8~15% of the axial strain and the maxi-mum shearing stress was about O.7Okgf/$cm^2$. 4. According to the increase of bentonite content, the cohesion intercept and internal friction of the sand-bentonite mixtures increased slightly in the shear test, while the cohesion intercept increased largely, and the internal friction angle decreased largely in the triaxial test. 5. Both the initial void ratio and swelling of the sand-bentonite mixtures were very low with respect to the consolidation pressure increase. 6. The swelling and shrinkage of sand-bentonite mixtures increased slightly according to the increment of bentonite content.

• Polymer(Korea)
• /
• v.27 no.2
• /
• pp.159-166
• /
• 2003

For the purpose of obtaining surface-anionized poly(vinyl alcohol) (PVA) hydrogel beads, vinyl acetate(VAc) and methacrylic acid(MMA) were copolymerized by the suspension polymerization technique and followed by the saponification. It was confirmed by $^1$H-NMR that the copolymerized microspheres contained carboxylic acid groups in their surface. poly(VAc-co-MAA) microspheres were completely saponified in the heterogeneous system. The saponification reaction was laster than that of PVAc microspheres. We observed the swelling property of saponified PVA microspheres treated in the acidic solution and in the alkaline solution successively. Saponified microspheres shrank in acidic solution and swelled in alkaline solution respectively, which was reversible. from the result, saponified microspheres were highly water-absorbing hydrogel beads and were certified -COOH group at their surface by $^1$H-NMR and FT-IR.