• Proceedings of the KAIS Fall Conference
• /
• 2004.06a
• /
• pp.54-57
• /
• 2004

알루미늄 용해반사로 gas 배출기의 bag cage에서 사용 6개월만에 균열이 발생하였다. 이러한 bag cage의 용접부에서 발생한 균열의 원인조사를 위해 bag cage의 성분분석, 용접부에서의 파단면과 미세조직을 SEM과 금속현미경으로 관찰한 결과 bag cage의 균열의 원인이 배기가스중의 황화물과 대기중의 습기, 산소와 반응에 의해 형성된 Polythionic acid이 생성되어 용접에 의해 예민화 된 부위에 부식을 일으켰다는 것을 확인할 수 있었다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.5 no.5
• /
• pp.462-465
• /
• 2004

After 6 month of using, cracking of gas exhaustion bag cage of Type 304 stainless steel wire for Al melting reverberatory furnace was founded in welds. Analysis of crack causes in the wire were tested by electrochemical method, SEM images of structure and analysis of composition. Resulted from the test, it could be observed that cracks in the welds were a accelerated by formed polythionic acid on surface of bag cage in sensitized region of HAZ, tensile stress and using environment.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.31 no.5
• /
• pp.529-535
• /
• 2011

In this study, evaluation of acoustic emission signals characteristics for the post weld heat treated (PWHT) multi-pass weldment and weldment was dealt. Charpy standard specimens were taken from the lowest, middle and highest regions of the weld block. Pre-crack was made using the repeated load. Four point bend and AE tests were conducted simultaneously. Regardless of the specimens, AE signals were absent within elastic region and produced in the process of plastic deformation. AE signals for all specimens were not emitted after the maximum load. Value of signal strength for the all PWHT specimens was lower than that of the weldment. Besides, relations of plastic deformation zone size and accumulated AE counts for the PWHT specimens were more simple compared with the weldment. In case of the PWHT specimen, particles on the fractured surface decreased prominently compared with the weldment due.to PWHT. From these results, it can be concluded that PWHT was effective in reducing the AE sources for the weldment.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2001.11a
• /
• pp.28-28
• /
• 2001

$Bi_2Te_3$계 열전반도체 재료는 200 ~ 400K 정도의 저온에서 에너지 변환 효율이 가장 높은 재료로서 열전냉각 및 발전재료로 제조볍 및 특성에 관한 많은 연구가 진행되어 왔다. 전자냉각 모듈의 제조에는 P형 및 N형 $Bi_2Te_3$계 단결정이 주로 사용되고 있으나. $Bi_2Te_3$ 단결정은 C축에 수직한 벽개면을 따라 균열이 쉽게 전파하기 때문에 소자 가공사 수윤 저하가 가장 큰 문제점으로 지적되고 있다. 이에 따라 최근 열전재료의 가공방법에 따른 회수율 증가 및 열전특성 향상에 관한 열간압출, 단조와 같은 연구가 활발히 이루어지고 있다. 본 연구는 가스분사법(gas atomizer)을 이용하여 용질원자 편석의 감소, 고용도의 증가,균일고용체 형성, 결정립미세화 둥 급속응고의 장점을 이용하여 화학적으로 균질한$Bi_2Te_3$계 열전재료 분말을 제조하고, 제조된 분발을 압출가공하여 기계적성질, 소자의 가공성 및 열전 성능 지수율 향상시키는데 연구 목적이 있다. 본 설험에서는 99.9%이상의 고순도 Bi. Te. Se. Sb를 이용하여, 고주파 유도로에서 Ar 분위기로 용융하고, 가스분사법를 이용하여 균질한 $Bi_2Te_3$계 열전재료 분만을 제조하였다. 분말표면의 산화막을 제거하기 위하여 수소분위기에서 환원처리를 행하였고, 된 분말을 Al 캔 주입하여 냉간성형 한 후 진공중에서 압출온도를 변화시켜 열간압출 가공을 행하였다. 압출 온도변화에 따른 압출재의 미세조직 및 열전특성에 중요한 영향을 미치는 C면 배향에 대한 결정방위 해석, 압출재의 압축강도 등을 분석하였으며, 압출온도에 따삼 미세조직 변화와 결정방위의 변화에 따른 열전특성의 관계를 해석하였다성시켰고 이들이 산인 HNO3에서 녹았기 때문이다. 본 연구에서 개발된 새로운 에칭 용액인 90H2O2 - 10HNO3 (vol%)의 에칭 원리가 똑같이 적용 가능한 다른 종류의 초경 합금에서도 사용이 가능할 것으로 판단된다.로 판단된다.멸과정은 다음과 같다. 출발물질인 123 분말이 211과 액상으로 분해될 때 산소가스가 배출되며, 이로 인해 액상에서 구형의 기공이 생성된다. 이들 중 일부는 액상으로 채워져 소멸되나, 나머지는 그대로 남는다. 특히, 시편 중앙에 서는 수십-수백 마이크론 크기의 커다란 기공이 다수 관찰된는데, 이는 기공의 합체로 만들어진 것이다. 포정반응 열처리 시 기공 소멸로 만들어진 액상포켓들은 주변 211 입자와 반응하여 123 영역으로 변한다. 이곳은 다른 지역과 비교하여 211 밀도 가 낮기 때문에, 미반응 액상이 남거나 211 밀도가 낮은 123 영역이 된다. 액상으로 채워지지 못한 구형의 기공들 중 다수가 123 결정 내로 포획되며, 그 형상은 액상/ 기공/고상 계면에너지에 의해 결정된다.단의 경우, 파단면이 매끄럽고 파변상의 결정립도 매우 미세하였으며, 산확물 의 용집도 찾아보기 어려웠 나, 접합부 파단의 경우에는 파변의 굴곡이 비교척 심하고 연성 입계파괴의 형태를 보였￡며, 결정립도 모채부 파단의 경우에 비해 조대하였다. 조대하였다. 셋째, 주상기간 중 총 에너지 유입률 지수와 $Dst_{min}$ 사이에 높은 상관관계가 확인되었다. 특히 환전류를 구성하는 주요 입자의 에너지 영역(75~l13keV)에서 가장 높은(0.80) 상관계수를 기록했다. 넷째, 회복기 중에 일어나는 입자들의 유입은 자기폭풍의 지속시간을 연장시키는 경향을 보이며 큰 자기폭풍일수록 현저했다. 주상에서 관측된 이러한 특성은 서브스톰 확장기 활동이 자기폭풍의

• Polymer(Korea)
• /
• v.31 no.5
• /
• pp.399-403
• /
• 2007

Trans-esterification behavior of polycarbonate/poly(butylene terephthalate) (PC/PBT) blends was investigated during the melt mixing process. Rheological and fracture behaviors, and fracture morphology were also investigated as a function of PC/PBT blend ratio. Based on FT-IR and $^1H-NMR$ results, a trans-esterification reaction was confirmed to occur between PC and PBT during the melt mixing process. The melt index(MI) decreased with increased PC content, indicating the higher flow resistance of PC. The storage and loss moduli were increased by increasing the PC loading, and the PC/PBT blends were rheologically incompatible based on the Cole-Cole plot. The tensile property increased linearly with the increased PC content. However, the impact strength increased until 50 wt% of PC loading, notably around $30{\sim}40wt%$, and then was levelled off at 50 wt%. Rough ridges were formed on the impact fracture surfaces above the 40 wt% of PC content, supporting the observed higher impact strength in this range.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.3
• /
• pp.72-83
• /
• 2022

This paper studied the effect on the microstructure, electrical properties, and compressive strength of cement mortar containing carbon fiber (CF) and steel fiber (SF), which are conductive materials. The resistivity of conductive fiber-reinforced cement mortar (FRCM) was measured using the 4-probe method, and the compressive strength was measured based on the compression test. Their performance was compared and reviewed with plain mortar (PM). Furthermore, the surface shape and composition of the fracture surface of the conductive FRCM were analyzed using a scanning electron microscope (SEM) and an energy disperse X-ray spectrometer (EDS). The results showed that the resistivity gradually increased as the curing time increased in all specimens, whereas the resistivity decreased significantly as the fiber volume fraction increased. Adding steel fibers up to 1.25% did not affect the resistivity of cement mortar considerably. On the contrast, the resistivity of carbon fiber was somewhat decreased even at low contents (ie, 0.1 to 0.3%), and thereafter, it was significantly decreased. The percolation threshold of the conductive CFRCM containing CF used in this experiment was 0.4%, and it is judged to be the optimum carbon fiber dosage to maximize the conductive effect while maintaining the compressive strength performance as much as possible. For the surface shape and composition analysis of conductive FRCM, the fracture surface was observed through SEM-EDS. These results are considered to be very useful in establishing the microstructure mechanism of reinforcing fibers in cement mortars.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.31 no.7
• /
• pp.112-117
• /
• 2003

The brazing of copper alloys and duplex stainless steels is an indispensable manufacturing technology for thrust chambers with regenerative cooling. For setting up the optimized brazing conditions, C18200 copper alloy plate with machined cooling channels and S31803 stainless steel plate are brazed with AMS4764 filler metals of which thickness is 50${\mu}m$ and 80${\mu}m$ They are tested by X-ray radiography, strength/leakage and fracture tests, and fracture surface inspection. The results obtained by the suggested conditions are that the specimen brazed with filler metal thickness of 50${\mu}m$ has good strength properties and brazed zone. However, the specimen with filler metal thickness of 80${\mu}m$ has the brazed zone with cooling channel obstruction and enlargement.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.111-111
• /
• 2018

ASTM A387-Gr.91 강은 우수한 고온 강도, 크리이프 저항성 그리고 내산화성 등으로 인해 화력 및 바이오매스 발전 시설과 같은 고온 설비의 구조재료로 널리 사용되고 있다. 고온 환경에서 높은 강도는 탄화물과 탄질화물에 의한 석출강화가 주 요인으로 작용한다. 열처리 과정에서 Mo, Cr, Mn, 그리고 Fe는 구-오스테나이트 및 마르텐사이트 라스 입계에 $M_{23}C_6$ 탄화물로 석출되며, V, Nb, 및 N은 조직 내부에 미세한 MX 탄질화물로 석출된다. 따라서 합금의 고온 강도는 조직 내 석출물의 개수밀도와 크기에 크게 의존한다. 그러나 적용 환경의 특성 상 고온 노출에 따른 2차상 석출 및 조대화의 조직열화 현상이 발생하며, 이는 재료의 강도를 저하시킨다. 본 연구에서는 ASTM A387-Gr.91 강의 미세조직 열화에 따른 강도저하 및 파괴 양상을 고찰하는데 그 목적을 두었다. 본 연구에서 사용된 ASTM A387-Gr.91 강의 화학성분(wt, %)은 0.1 C, 0.38 Si, 0.46 Mn, 0.25 Ni, 8.38 Cr, 0.93 Mo, 0.18 V, 0.09 Nb, 그리고 나머지는 Fe 이다. 조직열화 및 기계적 강도저하 특성을 평가하기 위한 등온열화는 $650^{\circ}C$의 대기 환경에서 최대 1000시간동안 실시하였다. 열화된 시험편의 미세조직 및 탄화물에 대한 분석은 SEM과 EDS를 이용하여 실시하였다. 그리고 기계적 강도 평가는 인장실험과 비커스 경도시험을 통해 실시하였다. 또한 열화 시간에 따른 파단양상의 변화를 관찰하기 위해 인장시험편의 파단면을 SEM과 EDS를 이용하여 분석하였다. 그 결과, 열화에 따른 마르텐사이트 라스의 소실, 탄화물의 조대화, 그리고 2차상 석출의 조직 열화현상이 나타났다. 또한 기계적 강도는 조직 열화에 따라 저하되는 경향을 나타냈다.

• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.1
• /
• pp.55-61
• /
• 2010

An impact bending test method was used to evaluate the reliability for the solder joint of lead-free solder ball. In order to standardize the test method, the four point impact bending test was applied under the conditions of various frequencies and amounts of +/-amplitude respectively. Effects on the results were analysed. The optimum condition for impact bending test achieved in this study was the frequency of 10 Hz, and the amplitude of (+12/-1)~(+15/-1). 3 kinds of surface finishes Cu-OSP (Organic Solderability Preservative), ENIG (Electroless Nickel Immersion Gold), and ENEPIG (Electroless Nickel, Electroless Palladium, Immersion Gold) were used. Fracture surface showed that cracks were initiated and fractured along the intermetallic layer in the case of surface finishes of Cu-OSP and ENIG, while in the case of ENEPIG the cracks were initiated and propagated in the solder region.

• Restorative Dentistry and Endodontics
• /
• v.20 no.2
• /
• pp.685-698
• /
• 1995

This study was conducted to the effect of temporary cement on the adhesiveness of dentin bonding agent to dentin surface. One hundred freshly extracted bovine mandibular incisors were grinded to expose flat labial dentin surface. The dentin surfaces were temporarized with either eugenol-containing temporary cement(TemBond and Zinc Oxide Eugenol cement) or non-eugenol temporary cement(Nogenol and TempBond NE) for 7days, and then the temporarization was removed with surgical currette and the exposed dentin surfaces were water-rinsed. Bonding specimens were made by use of All-Bond 2 and Super-Bond C&B dentin bonding agent, and stored in $37^{\circ}C$ distilled water for 24hours. The tensile bond strenth and the cohesive failure rate were measured, and then the pretreated dentin surfaces which the temporary cement had been applied to and removed from and the fractured dentin surfaces after bonding test were examined under scanning electron microscope. The results were as follows : In case of bonding with All-Bond 2, tensile bond strength of each experimental group was lower than that of the control group(p<0.05), but there was no significant difference between the bond strengths of the control group and each experimental group in case of bonding with Super-Bond C&B(p>0.05). No significant difference between tensile bond strength of experimental group, whether temporary cement contains eugenol or not, was seen(p>0.05). In case of bonding with All-Bond 2, the control group showed cohesive-adhesive mixed failure mode and the experimental groups mainly showed adhesive failure mode, but in case of bonding with Super-Bond C&B, almost of the control and the experimental groups mainly showed cohesive failure mode. On SEM examination, all of the dentin specimens pretreated with either 10 % phosphoric acid or 10% citric acid after application of the temporary cements demonstrated remnants of temporary cement attached to dentin surface.